Abstract
This research reports a microfluidic device for producing small droplets via a microorifice and a T-junction structure. The orifice is fabricated using an isotropic undercut etching process of amorphous glass materials. Since the equivalent hydraulic diameter of the produced microorifice can be as small as 1.1 μm, the microdevice can easily produce droplets of the size smaller than 10 μm in diameter. In addition, a permanent hydrophobic coating technique is also applied to modify the main channel to be hydrophobic to enhance the formation of water-based droplets. Experimental results show that the developed microfluidic chip with the ultrasmall orifice can steadily produce water-in-oil droplets with different sizes. Uniform water-in-oil droplets with the size from 60 μm to 6.5 μm in diameter can be formed by adjusting the flow rate ratio of the continuous phase and the disperse phases from 1 to 7. Moreover, curable linear polymer of chitosan droplets with the size smaller than 100 μm can also be successfully produced using the developed microchip device. The microfluidic T-junction with a micro-orifice developed in the present study provides a simple yet efficient way to produce various droplets of different sizes.
1. Introduction
Droplets of the size in micrometer or nanometer for advanced pharmaceutical and biomedical applications have become a popular research field in the recent years [1]. The production of medicine embedded microemulsion droplets is one of the important topics in this research field [2]. Droplet-based microfluidic devices have played important roles in the formation of various functional droplets in a high-throughput and high precision way [3]. A number of so-called “emulsification” techniques including T-junction shearing [4–7], flow focus necking [8, 9], and pneumatic pumping [10] have been reported to generate droplets in a continuous manner.
Over the reported microfluidic devices for droplets formation, micro-T-junction generator is the most popular scheme for producing droplets in devices. This droplet formation technique relies on the inherence properties of the employed liquids. T-junction microchannel devices provide a sharp edge where the continuous liquid phase cuts the dispersed liquid phase into small droplets by shearing force. The surfactant between the two immiscible liquids prevents the combination of these two liquids. Droplets with the size from tens to hundreds micrometers can be easily formed with this simple microfluidic structure. In general, the operation of this kind of microfluidic device depends on the geometry of the T-junction as well as the capillary number, flow ratio, and viscosity ratio of the two phases [11, 12]. However, this method is difficult to generate droplets with the size smaller than 10 μm due to the large hydraulic diameter of the T-junction structure due to the big surface tension from the long circumference. Wu et al. reported a pneumatic pressure driven T-junction structure for producing droplets in microfluidic channel. The smallest droplet with the size of 13.9 μm was formed [13].
This work proposed a simple and effective way to produce a micro-orifice structure to reduce the surface tension effect of the T-junction. The T-junction and the orifice structures are fabricated utilizing the isotropic undercut etching technique in a single etching process. The produced structure is then used to produce the water-based droplets via the micro-orifice. The relationship between the formed droplet size and the flow rate ratios of the two immiscible fluids is systematically investigated.
2. Materials and Methods
2.1. Chip Design
Figure 1 shows the mask design for the physical dimension of the proposed microfluidic device. Since a one-step isotropic wet etching technique is adopted to produce the micro-orifice at the T-junction, a gap of 30 μm was designed between the main channel and the side channel. The target depth for the etching microfluidic channel is 15 μm, resulting in just etching through the designed gap, and forms a small etch-through hole beneath the etching mask. Note that a number of poststructures with the diameter of 300 μm were designed at the downstream expansion channel to prevent the collapse of the channel during the thermal fusion bonding process.
2.2. Chip Fabrication
Figure 2 shows the simplified fabrication process for producing the microfluidic chip with the micro-orifice at the T-junction. The device was fabricated in low-cost soda-lime glasses with a rapid prototyping process. The details for the fabrication process can be found in our previous publication [14, 15]. Briefly, commercial microscope slides were cleaned and patterned with a standard photolithography process. A thin layer of AZ4620 photoresist was used as the etching mask for etching microfluidic channels in BOE solution (Figures 2(a)–2(c)). Due to the reflective index difference between BOE solution and the glass substrate, the undercut etched region could be clearly observed using an optical microscope. The etching process was stopped while etching through the undercut region between the mail channel and side channel, resulting in an ultrasmall pore structure at the T-junction (Figure 2(d)). The etched substrate then stripped the photoresist etching mask and sealed with the thermal fusion bonding method at 580°C for 10 min (Figure 2(f)). Finally, the inlet and outlet ports were connected with Teflon tubing with the outer and inner diameters of 1.5 mm and 0.5 mm, respectively.
Since the water-in-oil droplet formation system was used in the present study such that a hydrophobic layer was coated on the surface of the main channel to enhance the formation of water-based droplet. A thin layer of the organic-based spin-on glass (SOG, 400F, Filmtronics, USA) was applied only on the main channel with the assistance of vacuum suction. The coated SOG layer was then cured at 400°C for 1 hr. in N2 atmosphere.
2.3. Experimental Setup
Figure 3 shows the experiment setup for producing and observing the formation of the water-in-oil droplets. Two immiscible liquids of dispersed phase and continuous phase (commercial olive oil) were injected into the microfluidic channels from the corresponding inlets using two syringe pumps (KDS 200, KD Scientific Inc., USA). Note that the employed continuous phase liquid was doped with 3% of Span 80 (Sigma, USA) as the surfactant to enhance the formation of droplets. For forming chitosan droplets, 1% of (by weight) aqueous chitosan solution (Sigma, USA) was used as the dispersed phase. Note that all the liquids were filtered with polymer filter with 0.2 μm in size (Millipore, Ireland) prior to the test. An optical microscope (Eclipse TE2000-U, Nikon, Japan) equipped with a high speed digital camera (1200 fps, EX-F1, Casio, Japan) was used for observing the formation of droplets in the microchannel.
3. Results and Discussions
Figure 4 shows the scanning electron microscope (SEM) images of the undercut etched orifice structure at the T-junction right after peeling the photoresist etching mask and after sealing. As described previously, the etching process could be easily observed using an optical microscope. In addition, the size of the etched orifice also could be precisely adjusted by controlling the etching time. It is clear that the undercut region formed a small notch at the T-junction (Figure 4(a)). Due to the limitation of the designed mask pattern (20 μm in resolution), the width of the undercut structure was around 10 μm in width. This can be improved by using the photo mask with higher optical resolution. The dark region near the top glass substrate in Figure 4(b) presents the formed micro-orifice after sealing the channel. The image shows that the thermal fusion bonding did not collapse the micro-orifice structure and the depth for the orifice was around 1.5 μm. The calculated equivalent hydraulic diameter for this micro-orifice was around 2.4 μm. The smaller hydraulic diameter is beneficial for producing small droplets. Note that the orifice with smaller hydraulic diameter could also be formed by controlling the etching time.
(a)
(b)
In order to further improve the hydrophobicity of the produced microfluidic channel for droplet formation, a simple yet efficient permanent coating of organic-based spin-on-glass layer (SOG 400F, Filmtronics, USA) was used to modify the channel surface. Figure 5 presents the measured contact angles for a glass substrate without and with coating the organic-based SOG layer. Results showed that the SOG layer significantly increased the contact angle of water drop on the glass substrate. The photo images of the fabricated chip and the droplet formation process are given in Figure 6. The inset images at the bottom show that the dispersed fluid was squeezing out from the formed micro-orifice at the T-junction and formed the small droplets downstream. The sheath flow in the main channel cut the squeezed fluid and formed the droplets by shearing force. Small droplets could be easily formed using the developed microfluidic chip with the micro-orifice.
(a) 23.7°
(b) 87.9°
The relationship between the diameter of the water droplets and the oil/water flow rate ratio is shown in Figure 7. The flow rate for the dispersed phase was set from 75 μL/hr to 125 μL/hr. The equivalent hydraulic diameter for the orifice in this test was 1.5 μm. Results show that the higher flow rate ratio formed smaller droplets. Results also indicated that bigger droplets were formed at a slower water flow rate for the same flow rate ratio due to the grater shearing force for the faster flowing continuous phase. Compared to the two flow rate conditions of 125 μL/hr and 100 μL/hr, the size for the formed droplets did not show significant difference. However, higher water flow rate required higher driving pressure to squeeze the dispersed fluid through the small orifice, resulting in the risk for damaging the orifice and tubing connection. Therefore, the dispersed phase flow rate for the following tests was set at 100 μL/hr. The inset in Figure 7 presents the same size relationship while using a smaller orifice with the hydraulic diameter of 1.1 μm. Results show that droplets of the size smaller than 10 μm could be produced for the flow rate ratio greater than 2.8. The smallest droplet size formed with this approach was 6.5 μm at the flow rate ratio of 3.5, which was smaller than the reported droplet size formed with the chip having similar T-junction structure [13]. It is also noted that the flow rate ratio was difficult to be further increased since the increased driving pressure would cause the diameter expansion of the Teflon tubing and reduce the fluid pressure. This effect limited the smallest size of the formed droplets with this approach.
One of the issues for producing microdroplets via the small orifice is the great pressure drop at the orifice since the small orifice resulted in a small Reynolds number. In this regard, the flow at the orifice was stable such that the droplet production rate was only affected by the fluid flow rate in the side channel. Figure 8 shows the measured droplet production rate for the developed T-junction. Results showed that the droplet production rate was around 2 droplets per second while using the T-junction with the orifice of the equivalent hydraulic diameter of 1.1 μm. Note that the flow rate for the dispersed phase in this test was 100 μL/hr. The size uniformity for the formed droplets is also an important issue for practical applications of the microfluidic device. The size distribution for the droplets formed at the flow rate ratios of 2 and 3.5 was analysed. The captured images of 150 individual droplets were analysed using the digital image processing technique. Figure 9 shows the measured size distribution for the droplets formed with these two conditions. The statistical results show that the average diameters were 13.5 ± 0.47 μm and 6.9 ± 0.40 μm for these two cases. The calculated corresponding coefficient of variation (CV) was 3.13% and 5.7%, respectively. Results indicated that the generated droplets exhibited good size uniformity.
Chitosan is a linear polymer and has a number of potential biomedical applications, especially for drug encapsulation in pharmaceutical applications. The viscosity of chitosan at room temperature is around 5–10 cP which is much higher than the viscosity of water at the same condition. Therefore, the T-junction structure with a bigger orifice was required to produce chitosan droplets. Figure 10 shows the relationship between the size of formed chitosan droplets and the applied flow rate ratio. The equivalent hydraulic diameter for the orifice at the T-junction was 21.2 μm. Results show that chitosan droplets of the size ranging from 27 to 59 μm could be successfully produced, which were much smaller than the chitosan droplets formed with similar hydrodynamic approaches [16, 17].
4. Conclusions
This study reported a novel undercut etching method to produce a T-junction structure with microorifices using a single wet-etching process. Microdroplets of small sizes could be easily generated via the orifice with smaller hydraulic diameters. Results showed that the developed device could successfully produce uniform water-based droplets in olive oil with the size of smaller than 10 μm. The droplet production rate kept stable with the oil/water flow rate ratio in the range of 1 to 3.6 while using the T-junction with the orifice of the equivalent hydraulic diameter of 1.1 μm. In addition, chitosan droplets of the size as small as 27 μm could also be produced with the orifice of the hydraulic diameter of 21.2 μm. The present study provides a simple yet reliable way to produce small droplets in microfluidic systems.
Acknowledgment
The financial support from the National Science Council of Taiwan is greatly acknowledged.