Dielectric Properties of PE/Clay Nanocomposites
Table 3
Breakdown strength of various PE/nanoclay composites.
| Sample | Average thickness (mm) | (kV/mm) | | (kV/mm) |
| LLDPE—lab#1 | 0.59 | 60.7 | 25.5 | 59.7–61.6 | LLDPE—lab#2 | 0.59 | 61.0 | 29.7 | 60.1–61.8 | LLDPE—lab#2 | 0.61 | 58.8 | 17.1 | 57.4–60.1 | LLDPE—lab#1 | 0.53 | 72.9 | 18.8 | 71.3–74.3 | LLDPE/0/1—lab#1 | 0.59 | 65.8 | 14.6 | 63.9–67.5 | LLDPE/0/1—lab#1 | 0.53 | 72.3 | 19.6 | 70.8–73.7 | LLDPE/0/1—lab#2 | 0.59 | 66.1 | 17.2 | 64.5–67.5 | LLDPE/0/1—lab#2 | 0.58 | 62.9 | 17.9 | 61.4–64.2 | LLDPE/0/3—lab#1 | 0.58 | 69.6 | 19.7 | 68.1–70.9 | LLDPE/0/3—lab#1 | 0.53 | 72.1 | 19.3 | 70.6–73.5 | LLDPE/0/3—lab#2 | 0.58 | 69.8 | 18.1 | 68.2–71.2 | LLDPE/0/3—lab#2 | 0.57 | 66.6 | 18.2 | 65.1–68.0 | LLDPE/10/3—lab#2 | 0.56 | 69.6 | 17.9 | 68.0–71.1 |
|
|