Liquid Phase Plasma Synthesis of Iron Oxide/Carbon Composite as Dielectric Material for Capacitor
Table 1
Chemical composition of YP-50F and composites synthesized with different LPP process times.
| LPP process time | C | O | Fe | Wt % | At % | Wt % | At % | Wt % | At % |
| Bare YP-50F | 97.03 | 97.75 | 2.97 | 2.25 | — | — | 15 min | 95.97 | 97.41 | 3.15 | 2.40 | 0.88 | 0.19 | 30 min | 94.82 | 96.84 | 3.69 | 2.83 | 1.49 | 0.33 | 45 min | 93.41 | 96.28 | 4.08 | 3.16 | 2.51 | 0.56 | 60 min | 92.88 | 96.11 | 4.15 | 3.23 | 2.97 | 0.66 |
|
|