Table 2: The iron core diameter average and its standard deviation of all our samples in relation to the two set parameters, He flow rate and ferrocene/isooctane concentration. Samples with 1.1 < < 1.4 are quite monodisperse. Samples having above 1.4 (He flow of 60 sccm and low ferrocene concentration) are bimodal.

He flow rate
(sccm)
Iron core size (nm)/geometric standard deviation,
[Ferrocene/isooctane] 1% w/w[Ferrocene/isooctane] 2% w/w [Ferrocene/isooctane] 4% w/w

308.18/1.22
(Figure 2(a))
5.43/1.34
(Figure 2(b))
5.34/1.33
(Figure 2(c))
606.23/1.476.12/1.465.22/1.22
(Figure 3)
1205.22/1.25