The Poisoning Effect of Na Doping over Mn-Ce/TiO2 Catalyst for Low-Temperature Selective Catalytic Reduction of NO by NH3
Table 1
Physical properties of the catalysts prepared with different Na precursors.
| Catalysts | BET surface area (m2/g) | Pore volume (×10−2 cm3/g) | Average pore diameter (nm) |
| Mn-Ce/TiO2 | 44.52 | 28.39 | 25.51 | 2% Mn-Ce/TiO2 (C) | 31.48 | 22.04 | 30.85 | 2% Mn-Ce/TiO2 (Cl) | 32.42 | 25.65 | 31.64 | 2% Mn-Ce/TiO2 (N) | 36.58 | 27.58 | 28.61 |
|
|