Microstructure and Superparamagnetic Properties of Mg-Ni-Cd Ferrites Nanoparticles

<table>Composition dependence of saturation magnetization at low and room temperature of the system Mg<sub><i>x</i></sub>Ni<sub>0.6−<i>x</i></sub>Cd<sub>0.4</sub>Fe<sub>2</sub>O<sub>4</sub>. Inset shows the composition dependence of the coercive field at low temperature.</table>

Journal of Nanomaterials

fig7

Figure 7

Figure 7: Microstructure and Superparamagnetic Properties of Mg-Ni-Cd Ferrites Nanoparticles 