Investigation of Theoretical Models for the Elastic Stiffness of Nanoparticle-Modified Polymer Composites
Table 1
Material properties of the amine-cured epoxy polymer and silica/epoxy nanocomposites, obtained from tensile testing and DMA testing.
| Silica content | Tensile testing | DMA | wt% | vol% | | | | | | (GPa) | (MPa) | (%) | (GPa) | (°C) |
| 0.0 | 0.0 | 2.61 ± 0.03 | 69 ± 4 | 4.8 ± 0.6 | 2.61 ± 0.03 | 186 ± 2 | 6.6 | 3.7 | 2.80 ± 0.05 | 68 ± 2 | 4.1 ± 0.2 | 2.87 ± 0.05 | 186 ± 2 | 13.4 | 7.8 | 3.04 ± 0.07 | 66 ± 2 | 3.5 ± 0.3 | 3.09 ± 0.03 | 187 ± 1 | 20.3 | 12.3 | 3.31 ± 0.08 | 69 ± 1 | 3.3 ± 0.2 | 3.37 ± 0.06 | 185 ± 1 | 27.5 | 17.2 | 3.68 ± 0.11 | 67 ± 4 | 2.7 ± 0.3 | 3.70 ± 0.05 | 182 ± 1 |
|
|