Partial Hydrogenation of Benzene to Cyclohexene over Ru-Zn/MCM-41

Zhang, Tongtong; Wang, Zhimiao; Zhao, Qingqing; Li, Fang; Xue, Wei

doi:https://doi.org/10.1155/2015/670896

Journal of Nanomaterials

On this page

Abstract Introduction Experimental Results and Discussion Conclusions Acknowledgments References Copyright Related Articles

Research Article | Open Access

Volume 2015 | Article ID 670896 | https://doi.org/10.1155/2015/670896

Partial Hydrogenation of Benzene to Cyclohexene over Ru-Zn/MCM-41

Tongtong Zhang,¹Zhimiao Wang,¹Qingqing Zhao,¹Fang Li,¹and Wei Xue¹

Academic Editor: Yongchun Hong

Received28 Dec 2014

Accepted06 Feb 2015

Published19 May 2015

Abstract

Ru-Zn/MCM-41 catalysts for the partial hydrogenation of benzene with differing Zn contents were prepared by the incipient-wetness impregnation method. The evaluation results indicate that Zn simultaneously depresses the catalysts activity and cyclohexene selectivity. This can be attributed to the change in the amount of the different hydrogenation sites affected by Zn. The weak hydrogenation sites can promote benzene conversion, and the strong hydrogenation sites, a novel kind of hydrogenation site found on the surface of the catalysts under the influence of Zn, are beneficial for cyclohexene hydrogenation.

1. Introduction

Cyclohexene is of great industrial importance as it can be used as intermediate material for producing adipic acid, nylon-6, nylon-66, and other fine chemicals. Owing to its atom economy over the dehydration of cyclohexanol, the partial hydrogenation of benzene to cyclohexene has recently been the focus of much attention [1–35]. Ru has been found to be the most efficient catalyst for this process. To improve cyclohexene selectivity, the addition of a second element to the Ru-based catalyst, such as Zn [1, 3, 6, 9, 13, 21, 25, 29, 30], Co [4, 16], Ce [20], Ba [19], Fe [17], La [2, 5, 9, 33], B [7, 8, 28, 35], and Cu [24], is needed. Among these additives, Zn is the most popular, and to date the only industrialized production process for cyclohexene via the partial hydrogenation of benzene, developed by Asahi Chemical Industry Co., employs the Ru-Zn catalyst.

Though the use of Zn in the Ru catalyzed partial hydrogenation of benzene is extensive, its effect has not been fully understood up to now. Hu and Chen [6] have studied the partial hydrogenation of benzene over Ru-Zn/SiO₂ catalysts. The results of this study showed that the catalysts activity decreased with the increasing Zn content, whilst cyclohexene selectivity increased. Hydrogen temperature programmed desorption (H₂-TPD) tests revealed that two kinds of hydrogen, both strongly and weakly bonded on the surface of the Ru-Zn/SiO₂ catalyst, were formed under the influence of Zn. The catalytic activity could be correlated to the total amount of hydrogen desorption on its surface, and as the amount of the weakly bonded hydrogen increases with Zn content this might be responsible for the increased cyclohexene selectivity. From the adsorption point of view, Yuan et al. [21] investigated the effect of Zn on a Ru-based catalyst for the partial hydrogenation of benzene. Density functional theory (DFT) calculations suggested that the chemisorption of benzene and cyclohexene on the catalyst was depressed by Zn, especially for the latter. Undesired deep hydrogenation from cyclohexene to cyclohexane in the middle and late reaction stages was effectively retarded, leading to an improved cyclohexene yield.

It has been shown that the addition of Zn can increase cyclohexene selectivity and give better results for the partial hydrogenation of benzene. In this study we have demonstrated a different phenomenon for the influence of Zn on the partial hydrogenation of benzene over Ru/MCM-41 catalysts.

MCM-41, one of the first developed mesoporous materials [36], has been widely used in catalysis [37, 38], adsorption [39], microreactor [40], and other fields because of its remarkable features, such as well-defined pore shape, narrow distribution of pore size, high surface area (~700–1500 m² g⁻¹), and large amount of internal hydroxyl (silanol) groups (~40–60%). As for the hydrogenation of benzene, MCM-41 is more often used as catalyst support in the reaction to obtain cyclohexane [41, 42] and hardly used for the partial hydrogenation of benzene to cyclohexene. This difference could be attributed to its relatively smaller pore size with large specific surface area, which increases the diffusion resistance for the obtained cyclohexene from catalyst surface to bulk phase. Therefore, deep hydrogenation to cyclohexane can easily occur.

In our previous study [30], Ru-Zn/MCM-41 catalysts were prepared for partial hydrogenation of benzene and effect of different Zn precursors was evaluated. Herein, Ru-Zn/MCM-41 catalysts with different Zn contents were prepared by an incipient-wetness impregnation method. The role of Zn in the catalysts was discussed by studying the catalytic performance for partial hydrogenation of benzene and catalysts characterization. Interestingly, benzene conversion and cyclohexene selectivity decreased simultaneously with increasing Zn content, with the characterization results showing the appearance of a novel, strong hydrogenation site with the addition of Zn.

2. Experimental

2.1. Catalyst Preparation

First of all, the pure siliceous mesoporous MCM-41, with a BET specific surface area of 743.3 m²/g and a total pore volume of 0.77 cm³/g, was synthesized according to the procedure described in [43]. The Ru-Zn/MCM-41 catalysts were then prepared by an incipient-wetness impregnation method. RuCl₃ and ZnSO₄ were used as precursors for Ru and Zn, respectively. They were dissolved into appropriate amount of deionized water and impregnated on MCM-41 support. Within all the catalysts, norminal contents of Ru were kept constant at 1 wt%. After the impregnation, the catalysts were dried at 353 K overnight and reduced with H₂ at 573 K for 6 h.

2.2. Catalyst Characterization

X-ray diffraction (XRD) was carried out using a Rigaku D/Max-2500 X-ray diffractometer and Cu K_α radiation, at 40 kV and 100 mA.

Temperature programmed reduction (TPR) was carried out with a Micromeritics 2920 AutoChem II chemisorption analyzer. 100 mg of catalyst and a 10% (v/v) H₂-Ar mixture (50 cm³ (STP) ) were used. The sample was preheated to 573 K under Ar (50 cm³ (STP) ) for 1 h and subsequently cooled to room temperature. The temperature was then increased under the H₂-Ar mixture at 10 K and TPR profiles recorded at temperatures up to 773 K.

The dispersion of Ru metal was measured by CO pulse chemisorption method using a Micromeritics 2920 AutoChem II chemisorption analyzer. The stoichiometry of CO to Ru was assumed to be 1. Before CO chemisorption was performed, catalyst samples of approximately 500 mg were rereduced in a quartz reactor with pure H₂ (50 cm³ (STP) ) for 3 h at 573 K and then purged in He flow. The temperature of samples was decreased to 323 K in He flow. The CO chemisorption was performed by pulse injection of pure CO gas at 323 K.

Hydrogen temperature programmed desorption (H₂-TPD) was carried out also with a Micromeritics 2920 AutoChem II chemisorption analyzer. About 100 mg of sample was preheated to 573 K under He (50 cm³ (STP) ) for 1 h and subsequently cooled to 323 K. The sample was then saturated with H₂ under a 10% (v/v) H₂-Ar mixture (25 cm³ (STP) ) for 30 min and then purged with He to remove the physisorbed H₂. Finally, the temperature was increased under He atmosphere (50 cm³ (STP) ) at 10 K and TPD profiles were recorded at temperatures up to 1073 K.

Transmission electron microscopy (TEM) images were obtained with a FEI TECNGI G² microscope.

2.3. Catalytic Activity Test

The partial hydrogenation of benzene was carried out in a 200 mL stainless steel autoclave fitted with a magnetic stirrer. In a typical experiment, 30 mL benzene and 0.48 g Ru-Zn/MCM-41 catalyst with 3.4 g ZnSO₄7H₂O, the cocatalyst, were introduced into the autoclave, together with 60 mL H₂O to act as solvent. The autoclave was sealed and pressurized with N₂ for leak testing and then purged by low pressure H₂ four times to remove N₂ and the temperature adjusted to 403 K. Pressurized H₂ (5.5 MPa) was then introduced into the autoclave and reacted with benzene. At the end of the reaction the autoclave was cooled in an ice bath and vented. The catalyst was separated by centrifugation, and the liquid was separated into water and an oil phase.

The reaction products in the oil phase were identified and quantified by capillary gas chromatography using a BAIF SP-3420 instrument with a 30 m × 0.25 mm PEG 20 M column and FID.

3. Results and Discussion

The Ru-Zn/MCM-41 catalysts with differing contents of Zn were evaluated for their activity to partial hydrogenation of benzene and the results are shown in Figure 1 and Table 1. When Ru/MCM-41 was used as catalyst, benzene content decreased gradually and the completely hydrogenated product cyclohexane increased monotonically with reaction time. Regarding cyclohexene content, a maximum was obtained at a certain reaction time, exhibiting the well-known behavior of consecutive reactions. The maximum cyclohexene yield was 17.5% with 62.3% benzene conversion at 35 min over Ru/MCM-41 catalyst. When 0.25 wt% Zn was introduced into the catalyst, hydrogenation rate decreased obviously. This is in accordance with the other results previously obtained using other Ru-based catalysts [6, 21]. However, in contrast to the usual assumption the cyclohexene content significantly decreased likewise. Most of benzene was hydrogenated completely to cyclohexane. The maximum cyclohexene yield was only 3.5% with 23.3% benzene conversion over Ru-Zn/MCM-41 catalyst with 0.25 wt% Zn. With increasing Zn content the catalyst activity reduces further. A 1 wt% of Zn content gave a maximum cyclohexene yield of 0.6% with 1.0% benzene conversion. That is to say, the catalyst lost almost all of its hydrogenation activity under these conditions. And the high cyclohexene selectivity over Ru-Zn/MCM-41 catalysts with high Zn content may be the results of ultralow hydrogenation activity.

(a)

(b)

(c)

(d)

Characterizations were carried out to understand the influence of Zn on the Ru/MCM-41 catalysts. Figure 2(a) shows the small-angle XRD pattern of Ru-Zn/MCM-41 catalyst in 1 : 1 ratio. The sample gave a well-defined hexagonal XRD pattern with a main peak at 2° and up to three signals in the region 3–8°. Figure 2(b) shows the wide-angle XRD patterns of Ru-Zn/MCM-41 catalysts with differing contents of Zn. There is no diffraction peak corresponding to the crystalline compound in the patterns of all samples, which suggested that Ru and Zn compounds were highly dispersed in the catalysts.

(a)

(b)

To investigate the effect of Zn on the reducibility of Ru species over MCM-41, H₂-TPR measurements of the Ru-Zn/MCM-41 catalysts with differing Zn contents, before reduction by hydrogen, were carried out. The profiles are shown in Figure 3.

The TPR profile of Ru/MCM-41 catalyst (Figure 3(a)) shows a peak with maximum () at about 440 K, which is related to RuCl₃ reduction in the preparation method. However, this peak is a little beyond the range reported for the complete reduction of unsupported RuCl₃ (433 K, [44]). This difference could be due to the interaction between RuCl₃ and MCM-41 support. Zonetti et al. [14] found two peaks in the TPR profile of Ru/CeO₂, a principal peak at 453 K with a shoulder around 423 K. They considered the peak at lower temperature corresponding to the reduction of RuCl₃ weakly interacting with CeO₂ and the peak at higher temperature relating to RuCl₃ reduction strongly interacting with the support. There is still a weak peak at 485 K in the TPR profile of Ru/MCM-41, which can be assigned to the reduction of . It has been found that RuCl₃ can be oxidized at the surface by exposure to air at room temperature [45].

With the addition of Zn, the reduction peaks changed significantly as observed in Figure 3. Starting with 0.25 wt% Zn content the two reduction peaks resolved into one at about 405 K. With each further addition of Zn, decreased slightly down to 391 K for 1 wt% Zn. These results showed that Zn promoted the reduction of Ru, which differs from that previously reported by Hu and Chen [6]. da-Silva and Cobo [17] showed that the addition of Fe to Ru/TiO₂ and Ru/SiO₂ catalysts favored the reduction of RuO₂. This might be the result of higher dispersion of the RuO₂ particles, induced by Fe. Fan et al. [4] also reported a better dispersion of Ru caused by a high content of cobalt in the Ru-Co-B/Al₂O₃ catalyst. From the literature mentioned above, it is reasonable to presume that the lowering of reduction temperature of Ru resulted from the better dispersion caused by Zn.

To determine Ru dispersion in Ru-Zn/MCM-41 catalysts, CO chemisorption was carried out. The molar ratio of CO/Ru of the catalysts was 0.475, 0.398, 0.354, and 0.386, respectively, with Zn content of 0, 0.25 wt%, 0.64 wt%, and 1 wt%. Contrary to our assumption Ru dispersion decreases with the addition of Zn, and this indicates that there must be other factors that favor the reduction of Ru species.

Figure 4 shows the H₂-TPD profiles of Ru-Zn/MCM-41 catalysts with differing Zn contents, with all the profiles demonstrating two main peaks. One is in the range of 350 K–500 K and the other is higher than 600 K. This indicates two forms of hydrogenation active sites. With the addition of Zn, the integrated area of the low-temperature peak decreased, while that of the high-temperature peak increased. This change represents changes in the number of the two forms of hydrogenation active sites. With increasing Zn content, the number of relative weak hydrogenation sites (WHS) decreases and that of the strong hydrogenation sites (SHS) increases on the surface of Ru-Zn/MCM-41 catalysts. Hu and Chen [6] have reported the desorption peak with about 423 K on Ru/SiO₂, which may be assigned to the H₂ desorption from the Ru surface. Therefore, it is reasonable to conclude that the lower-temperature desorption peak is related to the H₂ desorption from the free Ru surface, the WHS, and the latter is related to the H₂ desorption from Ru surface affected by Zn and/or MCM-41, which is the SHS. In view of the catalytic activity results shown in Figure 1, it might be concluded that the number of WHS is correlated to benzene conversion, while the SHS is beneficial for cyclohexene hydrogenation. Therefore, with increasing Zn content, benzene hydrogenation activity decreases whilst cyclohexene hydrogenation activity increased.

To show more direct and convincing evidence for the existence of the novel Ru species, TEM photos were recorded. Figure 5(a) shows the TEM photo of Ru/MCM-41 and Figures 5(b) and 5(c) show the photos of Ru-Zn/MCM-41 catalyst with Zn content equaling 1 wt%. In Figure 5(a), there are small Ru particles, with average size about 2.2 nm calculated from 25 particles, in the pores of MCM-41. When Zn is added to the catalyst, besides the small Ru particles shown in Figure 5(b), a novel kind of Ru conglomeration comes into being as shown in Figure 5(c). The conglomeration of Ru particles, with diameter about 30–50 nm, was composed of small Ru particles less than 3 nm. Its formation might be due to the effect of Zn, because Zn can spread on the Ru particle surface as an overlayer [6] and then may act as a kind of adhesive to bind the Ru particles with each other. In addition, the slight decrease of Ru dispersion, caused by Zn, indicates the loose combination of Ru particles in the conglomeration. In other words, there is space in the conglomeration to ensure the diffusion and adsorption of CO.

(a)

(b)

(c)

The decrease of Ru reduction temperature could be explained by the loose conglomeration structure with confined space effect. During the reduction process, part of the Ru(III) was firstly reduced to Ru(0). Then H₂ adsorbed dissociatively on the Ru(0) surface to form H atoms, which were more active. Furthermore, there was a high concentration of H atoms in the conglomeration. So, Ru(III) could be reduced at low temperature by the active H atoms.

4. Conclusions

With addition of Zn into Ru/MCM-41 catalysts, a kind of Ru particles conglomeration, with diameter about 30–50 nm, comes into being on the support. Its formation might be due to the fact that Zn can spread on the Ru particle surface as an overlayer and then may act as a kind of adhesive to bind the Ru particles with each other.

Ru-Zn/MCM-41 catalysts showed a decreased hydrogenation activity and cyclohexene selectivity with increasing Zn content. It can be attributed to the change of the amount of the hydrogenation sites affected by Zn. The amount of weak hydrogenation sites, which can promote benzene conversion, decreases with the addition of Zn. However, the amount of strong hydrogenation sites, which are beneficial for cyclohexene hydrogenation, changes in the reverse. And Ru species in the conglomeration were thought to be the strong hydrogenation sites.

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

Acknowledgments

This work was supported by the National Natural Science Foundation of China (nos. 21236001, 21176056, and 21106031), the Programme for 100 Excellent Talents in University of Hebei Province (II) (no. BR2-208), and the Natural Science Foundation of Hebei Province (no. B2015202228).

References

H. Nagahara, M. Ono, M. Konishi, and Y. Fukuoka, “Partial hydrogenation of benzene to cyclohexene,” Applied Surface Science, vol. 121-122, pp. 448–451, 1997.
View at: Publisher Site | Google Scholar
S.-C. Liu, Z.-Y. Liu, Z. Wang, Y.-M. Wu, and P. Yuan, “Characterization and study on performance of the Ru-La-B/ZrO₂ amorphous alloy catalysts for benzene selective hydrogenation to cyclohexene under pilot conditions,” Chemical Engineering Journal, vol. 139, no. 1, pp. 157–164, 2008.
View at: Publisher Site | Google Scholar
W. Xue, Y. Song, Y. Wang, D. Wang, and F. Li, “Effect of hydrazine hydrate on the Ru-Zn/SiO₂ catalysts performance for partial hydrogenation of benzene,” Catalysis Communications, vol. 11, no. 1, pp. 29–33, 2009.
View at: Publisher Site | Google Scholar
G.-Y. Fan, W.-D. Jiang, J.-B. Wang, R.-X. Li, H. Chen, and X.-J. Li, “Selective hydrogenation of benzene to cyclohexene over RuCoB/γ-Al₂O₃ without additive,” Catalysis Communications, vol. 10, no. 1, pp. 98–102, 2008.
View at: Publisher Site | Google Scholar
S. C. Liu, Z. Y. Liu, Z. Wang, S. H. Zhao, and Y. M. Wu, “A novel amorphous alloy Ru-La-B/ZrO₂ catalyst with high activity and selectivity for benzene selective hydrogenation,” Applied Catalysis A: General, vol. 313, no. 1-2, pp. 49–57, 2006.
View at: Publisher Site | Google Scholar
S.-C. Hu and Y.-W. Chen, “Partial hydrogenation of benzene on Ru-Zn/SiO₂ catalysts,” Industrial & Engineering Chemistry Research, vol. 40, no. 26, pp. 6099–6104, 2001.
View at: Publisher Site | Google Scholar
S. H. Xie, M. H. Qiao, H. X. Li, W. J. Wang, and J.-F. Deng, “A novel Ru-B/SiO₂ amorphous catalyst used in benzene-selective hydrogenation,” Applied Catalysis A: General, vol. 176, no. 1, pp. 129–134, 1999.
View at: Publisher Site | Google Scholar
Z. Liu, W.-L. Dai, B. Liu, and J.-F. Deng, “The effect of boron on selective benzene hydrogenation to cyclohexene over ruthenium boride powders,” Journal of Catalysis, vol. 187, no. 1, pp. 253–256, 1999.
View at: Publisher Site | Google Scholar
S.-C. Hu and Y.-W. Chen, “Partial hydrogenation of benzene to cyclohexene on ruthenium catalysts supported on La₂O₃-ZnO binary oxides,” Industrial & Engineering Chemistry Research, vol. 36, no. 12, pp. 5153–5159, 1997.
View at: Publisher Site | Google Scholar
V. Mazzieri, F. Coloma-Pascual, A. Arcoya, P. C. L'Argentière, and N. S. Fígoli, “XPS, FTIR and TPR characterization of Ru/Al₂O₃ catalysts,” Applied Surface Science, vol. 210, no. 3-4, pp. 222–230, 2003.
View at: Publisher Site | Google Scholar
J.-B. Ning, J. Xu, J. Liu, and F. Lu, “Selective hydrogenation of benzene to cyclohexene over colloidal ruthenium catalyst stabilized by silica,” Catalysis Letters, vol. 109, no. 3-4, pp. 175–180, 2006.
View at: Publisher Site | Google Scholar
V.-A. Mazzieri, P.-C. L'Argentière, F. Coloma-Pascual, and N.-S. Fígoli, “Effect of chlorine on the properties of Ru/Al₂O₃,” Industrial & Engineering Chemistry Research, vol. 42, no. 11, pp. 2269–2272, 2003.
View at: Publisher Site | Google Scholar
S.-C. Hu and Y.-W. Chen, “Effect of preparation on Ru-Zn ultrafine catalysts in partial hydrogenation of benzene,” Industrial & Engineering Chemistry Research, vol. 40, no. 14, pp. 3127–3132, 2001.
View at: Publisher Site | Google Scholar
P. D. C. Zonetti, R. Landers, and A.-J.-G. Cobo, “Thermal treatment effects on the Ru/CeO₂ catalysts performance for partial hydrogenation of benzene,” Applied Surface Science, vol. 254, no. 21, pp. 6849–6853, 2008.
View at: Publisher Site | Google Scholar
Y.-J. Zhao, J. Zhou, J.-G. Zhang, and S.-D. Wang, “Monolithic Ru-based catalyst for selective hydrogenation of benzene to cyclohexene,” Catalysis Communications, vol. 9, no. 3, pp. 459–464, 2008.
View at: Publisher Site | Google Scholar
G.-Y. Fan, R.-X. Li, X.-J. Li, and H. Chen, “Effect of organic additives on partial hydrogenation of benzene,” Catalysis Communications, vol. 9, no. 6, pp. 1394–1397, 2008.
View at: Publisher Site | Google Scholar
J.-W. da-Silva and A.-J.-G. Cobo, “The role of the titania and silica supports in Ru-Fe catalysts to partial hydrogenation of benzene,” Applied Catalysis A: General, vol. 252, no. 1, pp. 9–16, 2003.
View at: Publisher Site | Google Scholar
E. V. Spinacé and J. M. Vaz, “Liquid-phase hydrogenation of benzene to cyclohexene catalyzed by Ru/SiO₂ in the presence of water-organic mixtures,” Catalysis Communications, vol. 4, no. 3, pp. 91–96, 2003.
View at: Publisher Site | Google Scholar
J. Bu, J.-L. Liu, X.-Y. Chen et al., “Ru/SBA-15 catalysts for partial hydrogenation of benzene to cyclohexene: tuning the Ru crystallite size by Ba,” Catalysis Communications, vol. 9, no. 15, pp. 2612–2615, 2008.
View at: Publisher Site | Google Scholar
J.-L. Liu, L.-J. Zhu, Y. Pei et al., “Ce-promoted Ru/SBA-15 catalysts prepared by a ‘two solvents’ impregnation method for selective hydrogenation of benzene to cyclohexene,” Applied Catalysis A: General, vol. 353, no. 2, pp. 282–287, 2009.
View at: Publisher Site | Google Scholar
P.-Q. Yuan, B.-Q. Wang, Y.-M. Ma, H.-M. He, Z.-M. Cheng, and W.-K. Yuan, “Partial hydrogenation of benzene over the metallic Zn modified Ru-based catalyst,” Journal of Molecular Catalysis A: Chemical, vol. 309, no. 1-2, pp. 124–130, 2009.
View at: Publisher Site | Google Scholar
M.-F.-F. Rodrigues and A.-J.-G. Cobo, “Influence of the support nature and morphology on the performance of ruthenium catalysts for partial hydrogenation of benzene in liquid phase,” Catalysis Today, vol. 149, no. 3-4, pp. 321–325, 2010.
View at: Publisher Site | Google Scholar
H.-Z. Liu, T. Jiang, B.-X. Han et al., “Highly selective benzene hydrogenation to cyclohexene over supported Ru catalyst without additives,” Green Chemistry, vol. 13, no. 5, pp. 1106–1109, 2011.
View at: Publisher Site | Google Scholar
H.-Z. Liu, S.-G. Liang, W.-T. Wang, T. Jiang, and B.-X. Han, “The partial hydrogenation of benzene to cyclohexene over Ru–Cu catalyst supported on ZnO,” Journal of Molecular Catalysis A: Chemical, vol. 341, no. 1-2, pp. 35–41, 2011.
View at: Publisher Site | Google Scholar
H.-J. Sun, X.-D. Zhang, Z.-H. Chen et al., “Monolayer dispersed Ru-Zn catalyst and its performance in the selective hydrogenation of benzene to cyclohexene,” Chinese Journal of Catalysis, vol. 32, no. 2, pp. 224–230, 2011.
View at: Google Scholar
H.-J. Sun, W. Guo, X.-L. Zhou, Z.-H. Chen, Z. Liu, and S. Liu, “Progress in Ru-based amorphous alloy catalysts for selective hydrogenation of benzene to cyclohexene,” Chinese Journal of Catalysis, vol. 32, no. 1, pp. 1–16, 2011.
View at: Google Scholar
Y.-F. Qin, W. Xue, F. Li, Y.-J. Wang, and J.-F. Wei, “Preparation of Ru-[bmim]BF₄ and its catalytic performance for selective hydrogenation of benzene,” Chinese Journal of Catalysis, vol. 32, no. 11, pp. 1727–1732, 2011.
View at: Publisher Site | Google Scholar
J. Liu, S.-M. He, C. Li et al., “Confined synthesis of ultrafine Ru-B amorphous alloy and its catalytic behavior toward selective hydrogenation of benzene,” Journal of Materials Chemistry A, vol. 2, no. 20, pp. 7570–7577, 2014.
View at: Publisher Site | Google Scholar
L.-Q. Yu, Q.-Q. Wang, C.-G. Liu, Y.-P. Zhang, and L.-Z. Hao, “Magnetically stabilized bed for selective hydrogenation of benzene,” Chemical Engineering and Technology, vol. 37, no. 3, pp. 392–397, 2014.
View at: Publisher Site | Google Scholar
W. Xue, Q.-Q. Zhao, D.-D. Wang, W.-M. Du, and Y.-J. Wang, “Selective hydrogenation of benzene to cyclohexene over RU/MCM-41 catalysts,” Acta Petrolei Sinica, vol. 25, supplement 2, pp. 120–124, 2009.
View at: Google Scholar
F. Schwab, M. Lucas, and P. Claus, “Simple selective hydrogenation of benzene to cyclohexene in the presence of sodium dicyanamide,” Green Chemistry, vol. 15, no. 3, pp. 646–649, 2013.
View at: Publisher Site | Google Scholar
W.-T. Wang, H.-T. Liu, T.-B. Wu et al., “Ru catalyst supported on bentonite for partial hydrogenation of benzene to cyclohexene,” Journal of Molecular Catalysis A: Chemical, vol. 355, pp. 174–179, 2012.
View at: Publisher Site | Google Scholar
H. Liao, J. Zhang, P.-L. Liu, F. Hao, K. You, and H. Luo, “Hydrophilicity modification of MCM-41 with zirconia and supported ruthenium-lanthanum for benzene hydrogenation to cyclohexene,” Synthesis and Reactivity in Inorganic, Metal-Organic and Nano-Metal Chemistry, vol. 43, no. 9, pp. 1206–1211, 2013.
View at: Publisher Site | Google Scholar
W. Xue, Y.-F. Qin, F. Li, Y.-J. Wang, and Z.-M. Wang, “Preparation of Ru-[bmim]BF₄ catalyst using NaBH₄ as reducing agent and its performance in selective hydrogenation of benzene,” Chinese Journal of Catalysis, vol. 33, no. 11-12, pp. 1913–1918, 2012.
View at: Publisher Site | Google Scholar
X.-H. Tan, G.-B. Zhou, R.-F. Dou et al., “Partial hydrogenation of benzene to cyclohexene over novel Ru-B/MoF catalysts,” Acta Physico—Chimica Sinica, vol. 30, no. 5, pp. 932–942, 2014.
View at: Publisher Site | Google Scholar
C.-T. Kresge, M.-E. Leonowicz, W.-J. Roth, J.-C. Vartuli, and J. S. Beck, “Ordered mesoporous molecular sieves synthesized by a liquid-crystal template mechanism,” Nature, vol. 359, no. 6397, pp. 710–712, 1992.
View at: Publisher Site | Google Scholar
H. Wang, Y. Yuan, L. Wei, K. Goh, D. Yu, and Y. Chen, “Catalysts for chirality selective synthesis of single-walled carbon nanotubes,” Carbon, vol. 81, no. 1, pp. 1–19, 2015.
View at: Publisher Site | Google Scholar
D. Rath, S. Rana, and K.-M. Parida, “Organic amine-functionalized silica-based mesoporous materials: an update of syntheses and catalytic applications,” RSC Advances, vol. 4, no. 4, pp. 57111–57124, 2014.
View at: Google Scholar
L.-T. Gibson, “Mesosilica materials and organic pollutant adsorption: part A removal from air,” Chemical Society Reviews, vol. 43, no. 15, pp. 5163–5172, 2014.
View at: Publisher Site | Google Scholar
Z. Yuan and F. Liang, “Photoreactions in amphiphilic microreactors with ‘soft’ cavities: controlling product selectivity in solution,” Current Organic Chemistry, vol. 18, no. 15, pp. 2016–2036, 2014.
View at: Publisher Site | Google Scholar
R. Wojcieszak, S. Monteverdi, M. Mercy, I. Nowak, M. Ziolek, and M. M. Bettahar, “Nickel containing MCM-41 and AlMCM-41 mesoporous molecular sieves: characteristics and activity in the hydrogenation of benzene,” Applied Catalysis A: General, vol. 268, no. 1-2, pp. 241–253, 2004.
View at: Publisher Site | Google Scholar
N.-H.-H. Abu Bakar, M.-M. Bettahar, M. Abu Bakar, S. Monteverdi, and J. Ismail, “Low temperature activation of Pt/Ni supported MCM-41 catalysts for hydrogenation of benzene,” Journal of Molecular Catalysis A: Chemical, vol. 333, no. 1-2, pp. 11–19, 2010.
View at: Publisher Site | Google Scholar
H.-X. Chen and Y. C. Wang, “Preparation of MCM-41 with high thermal stability and complementary textural porosity,” Ceramics International, vol. 28, no. 5, pp. 541–547, 2002.
View at: Publisher Site | Google Scholar
P.-G.-J. Koopman, A.-P.-G. Kieboom, and H. van Bekkum, “Activation of ruthenium on silica hydrogenation catalysts,” Reaction Kinetics and Catalysis Letters, vol. 8, no. 3, pp. 389–393, 1978.
View at: Publisher Site | Google Scholar
P.-G.-J. Koopman, A.-P.-G. Kieboom, and H. van Bekkum, “Characterization of ruthenium catalysts as studied by temperature programmed reduction,” Journal of Catalysis, vol. 69, no. 1, pp. 172–179, 1981.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2015 Tongtong Zhang et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

3941

Downloads

1479

Citations