Textural Properties of Hybrid Biomedical Materials Made from Extracts of Tournefortia hirsutissima L. Imbibed and Deposited on Mesoporous and Microporous Materials

Table 2

Pore structural parameters of the studied substrates including or not including Tournefortia hirsutissima L. extract nanodeposits, as calculated from N₂ adsorption analyses performed at 77 K.

Sample	(m^2 g^−1)	(m^2 g^−1)	(m^2 g^−1)	(cm^3 g^−1)
LTA	545.3	386.2	119.1	0.171
ZSM5	386.7	264.69	76.68	0.186
CLINON	30.69	19.61	15.25	0.007
CLINOH	223.8	157.80	44.05	0.132
NABE	44.50	26.16	24.72	0.009
PZX	47.61	30.41	26.66	0.064
LTA-T	43.12	18.98	18.98	0.024
ZSM5-T	211.1	147.07	39.19	0.099
CLINON-T	46.87	30.60	25.53	0.064
CLINOH-T	154.2	108.47	46.83	0.119
NABE-T	32.88	21.64	21.64	0.052
PZX-T	30.92	18.98	19.28	0.051

surface area is calculated by Langmuir method and surface area is calculated by the BET method and external surface is calculated by the t method and is the total pore volume.