Facile Method for Preparation of Silica Coated Monodisperse Superparamagnetic Microspheres

Pham, Xuan-Hung; Kyeong, San; Jang, Jaein; Kim, Hyung-Mo; Kim, Jaehi; Jung, Seunho; Lee, Yoon-Sik; Jun, Bong-Hyun; Chung, Woo-Jae

doi:https://doi.org/10.1155/2016/1730403

Journal of Nanomaterials

On this page

Abstract Introduction Experimental Results and Discussion Conclusions Abbreviations Acknowledgments Supplementary Materials References Copyright Related Articles

Research Article | Open Access

Volume 2016 | Article ID 1730403 | https://doi.org/10.1155/2016/1730403

Facile Method for Preparation of Silica Coated Monodisperse Superparamagnetic Microspheres

Xuan-Hung Pham,¹San Kyeong,²Jaein Jang,³Hyung-Mo Kim,¹Jaehi Kim,²Seunho Jung,¹Yoon-Sik Lee,²Bong-Hyun Jun,¹and Woo-Jae Chung³

Academic Editor: Zhisong Lu

Received15 Oct 2015

Revised28 Dec 2015

Accepted10 Jan 2016

Published01 Feb 2016

Abstract

This paper presents a facile method for preparation of silica coated monodisperse superparamagnetic microsphere. Herein, monodisperse porous polystyrene-divinylbenzene microbeads were prepared by seeded emulsion polymerization and subsequently sulfonated with acetic acid/H₂SO₄. The as-prepared sulfonated macroporous beads were magnetized in presence of Fe²⁺/Fe³⁺ under alkaline condition and were subjected to silica coating by sol-gel process, providing water compatibility, easily modifiable surface form, and chemical stability. FE-SEM, TEM, FT-IR, and TGA were employed to characterize the silica coated monodisperse magnetic beads (~7.5 μm). The proposed monodisperse magnetic beads can be used as mobile solid phase particles candidate for protein and DNA separation.

1. Introduction

Manipulation of biological objects at the cellular scale is necessary for both fundamental studies and the purification of biological products. For example, optical tweezers [1, 2] allow studying the strength of interactions between single molecules with piconewton accuracy such as DNA and protein. Due to the advantage of noncontact with biomolecules or cell during separation, the magnetic manipulation has been attracted in bioapplication over the several decades [3–9].

The dimension of the magnetic nano-/microparticles, the key factor for the successful magnetic separation, is usually less than 10 μm to ensure perfect and selective interaction with biological objects. These particles’ surface must be modified with biocompatible inorganic or organic materials to both prevent aggregation caused by hydrophobic or magnetic attraction and facilitate the immobilization of specific ligands such as antibody, aptamer, and DNA [3, 10].

The magnetic microparticles have been attracted for use in bioapplication for many years, due to the advantages that they offer easily scalable, time-efficient, cost-effective, and gentle separation of biological compounds by using external magnetic field gradient [11–17]. The magnetic microspheres offered many exciting applications in biomedical field as a solid support for protein purification [18–20], targeted drug delivery [21–24], cell separation [25–27], medical diagnosis [28–30], immunoassays [31], DNA sequencing [32], and cell analysis [33]. Various materials have been used for matrices embedding superparamagnetic nanoparticles in the form of microbeads including mesoporous silica, polysaccharides, poly(ethylene glycol), and many other synthetic polymers [26, 34–39]. By doing so, the resulting microbeads retain superparamagnetic property with tunable size.

The porous PS-DVB (polystyrene-divinylbenzene) beads usually give a very rigid structure resulting from their highly cross-linked matrix and, thus, they had less possibility of collapsing in most solvents, which allows the solvents and reagents to freely access the internal reactive sites through the interconnected pore networks [40–43]. The microbeads with pore networks can act as monodisperse core structures and provide the space within the beads where in situ forming nanomagnetite resides. Recently, we reported on the use of porous PS-DVB based monodisperse magnetic beads with SERS (surface-enhanced Raman scattering) active property (magnetic SERS beads) in protein separation [44, 45].

Despite extensive efforts made by many research groups, the demand for magnetic polymeric particles having uniform size, superparamagnetic property, chemical stability, user-defined magnetic contents, biocompatibility, and the readily tailorable surface is still increasing in potential application to biochips and bioseparation. In this paper, we demonstrate our strategy to prepare monodisperse porous PS-based superparamagnetic beads (~7.5 μm), which on surface were coated with silica that can result in improving biocompatibility and capability for facile surface modification [46–48].

2. Experimental

2.1. Materials

Tetraethylorthosilicate (TEOS), ammonium hydroxide (NH₄OH), styrene, 2,2′-azobis-isobutyronitrile (AIBN), dibenzoyl peroxide (BPO, including 97% of active compound), dibutyl phthalate (DBP), sodium silicate, Fe₃Cl₃·6H₂O, FeCl₂·4H₂O, ethylene glycol, N,N-dimethylformamide (DMF), sodium dodecyl sulfate (SDS), polyvinylpyrrolidone-40 (PVP-40, Mr: 40,000), N,N-diisopropylethylamine (DIEA), and (3-aminopropyl)triethoxysilane (APTS) were purchased from Sigma-Aldrich (MO, USA).

2.2. Methods

2.2.1. Preparation of Monodisperse Macroporous PS-DVB Beads

Monodisperse macroporous PS-DVB (polystyrene-divinylbenzene) beads were prepared by seeded polymerization methods. Monodisperse PS seeds (4 μm) were prepared using dispersion polymerization method [49]. Dispersion medium was ethanol/2-methoxyethanol (3 : 2) which contains 1 g of PVP-40 as a steric stabilizer (90 mL). AIBN (150 mg) was dissolved in styrene (15 mL) in which inhibitor was removed and then was added to the as-prepared dispersion medium. After sonication for 10 min, dispersion polymerization was performed in a cylindrical reaction chamber with shaking (120 cpm) at 70°C for 20 h. The suspension was centrifuged and the precipitates were washed intensively with distilled water by repeating centrifugation and vortexing. Finally, the PS seeds were washed with ethanol and vacuum-dried overnight affording PS seeds (4 μm, 8.3 g).

Swelling and polymerization processes were performed in a glass reactor equipped with overhead stirrer and a reflux condenser in an oil bath equipped with a temperature controller. The two-step seeded polymerization method was employed for preparation of monodisperse macroporous poly(styrene-co-DVB) (PS-DVB) beads. The PS seeds (4 μm, 700 mg) were dispersed in DBP (0.7 mL) emulsified aqueous medium (100 mL) containing 0.25% (w/w) SDS. The resultant dispersion medium was stirred (400 rpm) at room temperature for 20 h for swelling the PS seeds with DBP. Mixture of styrene (4.6 mL) and DVB (2.3 mL) in which BPO (240 mg) was dissolved was emulsified in an aqueous medium (100 mL) containing 0.25% (w/w) SDS by using homogenizer for 1 min. The emulsified monomer solution was added to the DBP-swollen PS seeds dispersion medium being stirred. Monomer swelling was performed for 20 h at room temperature with continuous stirring (400 rpm). After swelling process, an aqueous solution of 10% (w/v) PVA in deionized water (10 mL) was added to the dispersion medium and the medium was purged with nitrogen stream for 30 min. The seeded polymerization was performed at 70°C for 20 h with continuous stirring (200 rpm) to obtain monodisperse PS-DVB beads. The polymer beads were intensively washed with warm deionized water (50°C) by repeating washing and centrifugation. Subsequently, the collected beads were washed with ethanol and THF intensively to remove DBP and linear polymer. Finally, the beads were dried in vacuum at 30°C for 24 h to obtain macroporous PS-DVB beads (7.5 μm, 2.5 g).

2.2.2. Sulfonation of Macroporous PS-DVB Beads

Sulfonation of the PS-DVB beads was performed with reference to the reported method [50]. Briefly, monodisperse PS-DVB beads (1 g) were added to 5 mL of acetic acid in an ice bath. Sulfuric acid (50 mL) was then slowly added to the beads at room temperature and the temperature was increased up to 90°C and the resin mixture was stirred for 30 min to 2 hr. The dispersion was poured into iced water (400 mL) to quench the reaction and the sulfonated PS-DVB beads were collected by centrifugation. The beads were extensively washed with deionized water by repeating centrifugation-decantation. Subsequently, the sulfonated microspheres were washed three times with ethanol and dried under vacuum (1.1 g).

2.2.3. Magnetization of Sulfonated Macroporous PS-DVB Beads

The sulfonated macroporous PS-DVB beads (500 mg) were dispersed in deionized water (10 mL) at room temperature with mechanical stirring (200 rpm) and purging with nitrogen. A freshly prepared mixture of FeCl₃·6H₂O (618 mg, 2.26 mmol) and FeCl₂·4H₂O (257 mg, 1.28 mmol) in deionized water (10 mL) was added to the dispersion for adsorption. After 2 h, with continuous stirring 28% ammonium hydroxide (50 mL) was added dropwise to the beads suspension for 40 min. The magnetized microspheres were isolated from the mixture by centrifugation and briefly washed with 25% TFA and then extensively with deionized water and ethanol. Finally, the magnetized microspheres were dried under vacuum (magnetized microspheres, 7.5 μm, 653 mg).

2.2.4. Preparation of Silica Coated Magnetic Beads

APTS solution (1% (v/v), 100 mL) was added to 100 mg of magnetic sulfonated PS-DVB beads and was shaken for 10 min at room temperature. Thereafter, ammonium hydroxide (28%, 2 mL) was added to the bead dispersion and was shaken for 20 min at room temperature. To the dispersion TEOS (2 mL) was added and vigorously shaken for 12 h at room temperature. The resulting beads (silica coated magnetic beads) were collected by magnet and washed with ethanol five times.

2.2.5. Streptavidin Separation of Silica Coated Magnetic Beads

APTS (240 μL) and ammonium hydroxide (40 μL) were added to 4 mL absolute ethanol containing 200 mg of silica coated magnetic beads and incubated for 6 h at room temperature. The resulting beads (amine-silica coated magnetic beads) were collected by magnet, washed with ethanol five times, and dispersed into PBS, pH 7.2, to obtain 10 mg/ml of amine-silica coated magnetic beads.

Biotin (5 mg) was activated with EDC (40 mg) and NHS (20 mg) in PBS, pH 7.2, for 1 h at room temperature. Then, this solution was added into amine-silica coated magnetic beads (1 mg, 100 μL) to modify biotin on its surface. The biotinylated silica coated magnetic beads were collected by magnet, washed with ethanol five times, and dispersed into 100 μL PBS, pH 9.0. The biotinylated silica coated magnetic beads were passivated with 5% BSA in PBS, pH 9.0, for preventing nonspecific binding.

Streptavidin-FITC (100 μg) in PBS pH 9.0 was added into the biotinylated silica coated magnetic beads and incubated for 30 mins at room temperature. The biotinylated silica coated magnetic beads after incubation with streptavidin-FITC were collected by magnet, washed with PBS, pH 9.0, containing 0.1% Tween 20 for five times, and dispersed into 100 μL PBS, pH 9.0. The fluorescent images were collected by the Olympus BX-UCB at room temperature with 200 ms exposure.

2.2.6. Characterization

Cross-sectional images of the beads were obtained using transmission electron microscopy (TEM, Jeol Inc., JEM 1010). The slices for the TEM analysis were prepared by means of an ultramicrotome (RCM, MTX). The surface and cross-sectional images of the beads were obtained using field emission scanning electron microscopy (FE-SEM, Carl Zeiss, SUPRA 55VP). The existence of the magnetic NP particles was confirmed by means of an energy dispersive X-ray spectrometer (EDX, Bruker, EDX). The amount of magnetic particles embedded in the beads was measured by a thermogravimetric analyzer (TGA, PerkinElmer Pyris 6).

3. Results and Discussion

For preparing magnetic beads, we employed a method using magnetization of uniform porous microbeads. As shown in Scheme 1, monodisperse superparamagnetic microbead has a spherical core-shell structure with silica layer over magnetized core PS-DVB bead.

Monodisperse polystyrene-divinylbenzene (PS-DVB) beads (7.5 μm, cross-linked with 33% DVB) were prepared using the seeded polymerization method that was previously reported by Ugelstad [49]. The seeded polymerization is a useful method for preparation of monodisperse microbeads which is essential for bioapplications including relative quantitative flow cytometry and biochip applications. The PS seeds were prepared in the range of 4.0~4.2 μm (61% solid yield) (Figure 1(a)) and the molecular weight was 29,000 (determined by GPC analysis). The final PS-DVB beads were prepared with repolymerization of the seeds (4 μm, 2.5 g, 47% solid yield) using DBP as a porogen and activated swelling agent.

(a)

(b)

The prepared PS-DVB microbeads showed a macroporous surface (Figure 1(b)), which enables the magnetite particles to form easily inside the microbeads upon magnetization from iron salts adsorbed in the porous structures. However, the PS-DVB microbead itself was not compatible in aqueous solution to adsorb the ferrous and ferric salts. Thus, we introduced sulfonate groups onto the PS-DVB microbeads to make them compatible in aqueous solution and the sulfonate group might have the effect that the iron salt is drawn into the microbeads and is considerably bound therein.

Sulfonated PS-DVB polymers have been used for many years in cationic exchange chromatography, as well as other analytes [51–53]. Recently, Chambers and Fritz have reported on the simple preparation of sulfonated PS-DVB with the -SO₃H loading range of 0.27~2.63 mmol/g using sulfonic acid and acetic acid [50]. To demonstrate the effect of sulfonation loading level of beads to magnetization, various loading levels of sulfonate group were prepared by controlling temperature and reaction time (data not shown). As a result from applying Chamber’s method to the as-prepared PS-DVB microbeads, we obtained high loaded sulfonated PS-DVB (PS-DVB-SO₃H) of 4.1 mmol/g by elemental analysis. FT-IR analysis showed that the sulfonation of the phenyl groups of the PS-DVB was successfully achieved (Figure 2). In the FT-IR spectra of PS-DVB before (Figure 2(a)) and after sulfonation (Figure 2(b)), the changes in the combination vibrations (finger bands) between 1950 and 1650 cm⁻¹ particularly characterize the phenyl group in the microbeads. The band centered around 1200 cm⁻¹ (Figure 2(b)) represents the characteristic peak of the O_yS_yO asymmetric stretching vibration. The absorbance peaks at 1005 and 1126 cm⁻¹ result from the vibrations of phenyl ring substituted with a sulfonate group and sulfonate anion, respectively, that are attached to phenyl ring [54]. A broad band centered around 3450 cm⁻¹ is associated with OH stretching vibration of the sulfonic acid group (Figure 2(b)).

Direct polymerization of ion-binding monomers during the seeded emulsion polymerization process can be an alternative method of preparing functional macroporous microbeads. However, formation of uniformly macroporous structures using the ionic monomers is often challenging. In contrast, the postmodification of highly cross-linked macroporous beads as described above can preserve the structure of monodisperse microbeads.

After magnetization of sulfonated PS-DVB microbeads with a mixture of ferrous ions and ferric ions (2 : 1 molar ratio) in the excess basic solution of ammonium hydroxide, precipitates of magnetite were observed in the solution as well as in the beads as they turned blackish. The surface morphology of microbeads was not significantly changed after magnetization, meaning that the magnetite was formed and precipitated mostly inside the porous structure of the microbeads (Figures 3(a) and 3(b)). After purifying the magnetized beads from the mixture by centrifugation, we confirmed that the precipitate is indeed iron oxide from energy dispersive X-ray spectroscopy (Figure 3(c)). These magnetized microbeads indeed responded to external magnetic field (Figure 3(d), inset). The magnetic property was maintained even after keeping the beads for 4 h in 100% TFA.

(a)

(b)

(c)

(d)

The saturation magnetization value of the resulting beads was 7.6 emu/g (Figure 3(d)), which is relatively lower than that of commercial magnetites (~70 emu/g). However, the magnetized beads showed strong magnetic property enough in that they can be separated from the solvent by 4,000 gauss magnet in 4 sec. The magnetized sulfonated PS-DVB microbeads consist of many isolated, around a few tens nm, iron oxide grains that are embedded in a polymer matrix which can lead to their superparamagnetic behavior. The sulfonation of the beads and the subsequent magnetization successfully provided a means for preparing magnetic microbeads in straightforward and cost-effective way.

Iron oxide contents of the magnetized beads were measured by TGA (Figure 4). Iron oxide content was in the range of 18–26% whose value was suitable for further application of the magnetic beads comparing with the conventional magnetic beads. In the magnetization process, we attempted to simplify the purification by washing the beads after iron salts adsorption to prevent the formation of the magnetite in the solution after precipitation of iron salts using ammonium hydroxide (MAG 1). The iron oxide content of the magnetized beads was lower than that of beads prepared by in situ precipitation method without additional washing step (MAG 2).

Finally, the magnetic beads were coated with a silica shell using APTS and tetraethoxyorthosilicate (TEOS) for their surface to be water-compatible and amenable to chemical modification using various types of functional silane compounds. The amino silane compound APTS is prone to promote the adhesion of silane layer on the negatively charged sulfonated beads, thereby facilitating the further base-catalyzed condensation of TEOS from the surface. We found that this pretreatment greatly enhanced the silica coating efficiency as compared to no pretreatment (data not shown) and pretreatment with (3-mercaptopropyl)triethoxysilane solution [44]. The surface morphology of the beads significantly changed after the sol-gel process (Figures 5(a)–5(d)) revealing formation of silica grains on the surface (Figures 5(b) and 5(d)). From the cross-sectional analysis, the silica shell of 200–300 nm was observed around the core magnetic beads. The silica coated magnetic beads were also homogeneous in size and could be obtained in gram scale.

(a)

(b)

(c)

(d)

(e)

(f)

To support the presence of silica coating on the magnetic beads, we carried out EDX analysis of the sulfonated PS-DVB, magnetic PS-DVB, and silica coated magnetic PS-DVB beads. The result was shown in Figure 6. The sulfonated PS-DVB beads contained C, O, and S elements with the atomic composition of 86.5%, 9.1%, and 4.4%, respectively, in Figure 6(a). After magnetic nanoparticles were deposited on the sulfonated PS-DVB beads, C element decreased dramatically to 67.2% while O element increased up to 20.3%. Particularly, the presence of Fe element with 5.7% confirmed the successful deposition of magnetic nanoparticles on the sulfonated PS-DVB beads. When the silica shell was coated on the magnetic PS-DVB beads, the silica coated magnetic PS-DVB beads contained C (50.3%), O (33.3%), S (5.9%), Fe (3.8%), and Si (6.7%) element as shown in Figure 6(c). Comparing to that of the magnetic PS-DVB beads, O element of the silica coated magnetic beads increased by 13%, which is about two times Si element that demonstrated the presence of SiO₂ on the surface of magnetic PS-DVB beads. Therefore, EDX data was consistent with TEM images and evidenced the successful deposition of silica shell on the magnetic PS-DVB beads surface.

(a)

(b)

(c)

(d)

(e)

(f)

To demonstrate the application of the silica coated magnetic beads, we used streptavidin-FITC as model biomolecules for bioseparation. Briefly, the silica coated magnetic beads surface was modified with amine group and conjugated with biotin through EDC/NHS. The fluorescent images were shown in Figures 6(d)–6(f). The fluorescence of the biotinylated silica coated magnetic beads without reaction with streptavidin-FITC was negligible comparing to the biotinylated silica coated magnetic beads treated with streptavidin-FITC as shown in Figure 6(e). Also we carried out the nonspecific binding test of silica coated magnetic beads without biotinylation and BSA blocking in Figure 6(f). Streptavidin-FITC easily adsorbed into the silica coated magnetic beads. Therefore, BSA blocking step played an important role in our protocol.

4. Conclusions

In conclusion, we successfully prepared monodisperse silica coated superparamagnetic magnetic beads using the macroporous polystyrene microbeads as template materials. The sulfonation of the porous PS-based beads and the subsequent magnetization successfully provided a means for preparing magnetic microbeads in straightforward and cost-effective way, which can be readily modified with silica shell as a water-compatible protective layer and surface modification site for various functional silane compounds. When used with flow cytometry or in a microfluidic system, the monodisperse magnetic microbeads may have great potentials for drug screening, medical diagnostics, and combinatorial chemical synthesis in more simple, convenient, and cost-effective way.

Abbreviations

FE-SEM:	Field emission scanning electron microscopy
TEM:	Transmission electron microscopy
FT-IR:	Fourier transform infrared spectroscopy
TGA:	Thermogravimetric analysis.

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

Acknowledgments

This work was supported by the National Research Foundation of Korea Grant funded by the Korean Government (NRF-2014S1A2A2027641) and by the Ministry of Science, ICT & Future Planning (2014-A002-0065) and by the 2015 KU Brain Pool of Konkuk University.

Supplementary Materials

After modified with magnetic nanoparticles, magnetic sulfonated PS-DVB beads (100 mg) was modified with APTES solution (1% (v/v), 100 mL). Thereafter, ammonium hydroxide (28%, 2 mL) was added to the bead dispersion and was shaken for 20 min at room temperature. To the dispersion TEOS (2 mL) was added and vigorously shaken for 12 h at room temperature. The silica coated magnetic beads were collected by magnet and washed with ethanol five times and redispersed in to absolute ethanol to obtained 1 mg/ml silica coated silica coated magnetic beads. The magnetic ability of silica coated magnetic beads under magnetic field was seen in Figure S1.

Supplementary Material

References

C.-H. Chiou, Y.-Y. Huang, M.-H. Chiang, H.-H. Lee, and G.-B. Lee, “New magnetic tweezers for investigation of the mechanical properties of single DNA molecules,” Nanotechnology, vol. 17, no. 5, pp. 1217–1224, 2006.
View at: Publisher Site | Google Scholar
C.-H. Chiou and G.-B. Lee, “A micromachined DNA manipulation platform for the stretching and rotation of a single DNA molecule,” Journal of Micromechanics and Microengineering, vol. 15, no. 1, p. 109, 2005.
View at: Publisher Site | Google Scholar
L. Yi, G. Yu, and X. Chenjie, “Using magnetic nanoparticles to manipulate biological objects,” Chinese Physics B, vol. 22, no. 9, Article ID 097503, 2013.
View at: Publisher Site | Google Scholar
E. Cho, M. N. Tahir, J. M. Choi, H. Kim, J. H. Yu, and S. Jung, “Novel magnetic nanoparticles coated by benzene- and β-cyclodextrin-bearing dextran, and the sorption of polycyclic aromatic hydrocarbon,” Carbohydrate Polymers, vol. 133, pp. 221–228, 2015.
View at: Publisher Site | Google Scholar
Y. S. Park, C. Shin, H. S. Hwang et al., “In vitro generation of functional dendritic cells differentiated from CD34 negative cells isolated from human umbilical cord blood,” Cell Biology International, vol. 39, no. 9, pp. 1080–1086, 2015.
View at: Google Scholar
S. Kyeong, C. Jeong, H. Kang et al., “Double-layer magnetic nanoparticle-embedded silica particles for efficient bio-separation,” PLoS ONE, vol. 10, no. 11, Article ID e0143727, 2015.
View at: Publisher Site | Google Scholar
M. Lee, Y. L. Kang, W. Y. Rho et al., “Preparation of plasmonic magnetic nanoparticles and their light scattering properties,” RSC Advances, vol. 5, no. 27, pp. 21050–21053, 2015.
View at: Publisher Site | Google Scholar
S. Kyeong, C. Jeong, H. Y. Kim et al., “Fabrication of mono-dispersed silica-coated quantum dot-assembled magnetic nanoparticles,” RSC Advances, vol. 5, no. 41, pp. 32072–32077, 2015.
View at: Publisher Site | Google Scholar
H. Mok and M. Q. Zhang, “Superparamagnetic iron oxide nanoparticle-based delivery systems for biotherapeutics,” Expert Opinion on Drug Delivery, vol. 10, no. 1, pp. 73–87, 2013.
View at: Publisher Site | Google Scholar
J.-Y. Hyeon, J.-W. Chon, I.-S. Choi, C. Park, D.-E. Kim, and K.-H. Seo, “Development of RNA aptamers for detection of Salmonella Enteritidis,” Journal of Microbiological Methods, vol. 89, no. 1, pp. 79–82, 2012.
View at: Publisher Site | Google Scholar
V. N. Morozov and T. Y. Morozova, “Active bead-linked immunoassay on protein microarrays,” Analytica Chimica Acta, vol. 564, no. 1, pp. 40–52, 2006.
View at: Publisher Site | Google Scholar
Z. Jiang, J. Llandro, T. Mitrelias, and J. A. C. Bland, “An integrated microfluidic cell for detection, manipulation, and sorting of single micron-sized magnetic beads,” Journal of Applied Physics, vol. 99, no. 8, Article ID 08S105, 2006.
View at: Publisher Site | Google Scholar
Y. Sun, Y. Bai, D. Song, X. Li, L. Wang, and H. Zhang, “Design and performances of immunoassay based on SPR biosensor with magnetic microbeads,” Biosensors and Bioelectronics, vol. 23, no. 4, pp. 473–478, 2007.
View at: Publisher Site | Google Scholar
J. Broomberg, S. Gélinas, J. A. Finch, and Z. Xu, “Review of magnetic carrier technologies for metal ion removal,” Magnetic and Electrical Separation, vol. 9, no. 3, pp. 169–188, 1999.
View at: Publisher Site | Google Scholar
T. R. Sathe, A. Agrawal, and S. Nie, “Mesoporous silica beads embedded with semiconductor quantum dots and iron oxide nanocrystals: dual-function microcarriers for optical encoding and magnetic separation,” Analytical Chemistry, vol. 78, no. 16, pp. 5627–5632, 2006.
View at: Publisher Site | Google Scholar
R. F. H. Dekker, “Immobilization of a lactase onto a magnetic support by covalent attachment to polyethyleneimine-glutaraldehyde- activated magnetite,” Applied Biochemistry and Biotechnology, vol. 22, no. 3, pp. 289–310, 1989.
View at: Publisher Site | Google Scholar
C. H. Lochmuller and L. S. Wigman, “Affinity separations in magnetically stabilized fluidized beds: synthesis and performance of packing materials,” Separation Science and Technology, vol. 22, no. 11, pp. 2111–2125, 1987.
View at: Publisher Site | Google Scholar
Y. Pan, X. Du, F. Zhao, and B. Xu, “Magnetic nanoparticles for the manipulation of proteins and cells,” Chemical Society Reviews, vol. 41, no. 7, pp. 2912–2942, 2012.
View at: Publisher Site | Google Scholar
J. Bao, W. Chen, T. Liu et al., “Bifunctional Au-Fe₃O₄ nanoparticles for protein separation,” ACS Nano, vol. 1, no. 4, pp. 293–298, 2007.
View at: Publisher Site | Google Scholar
Y. Zhang, W. Ma, D. Li, M. Yu, J. Guo, and C. Wang, “Benzoboroxole-functionalized magnetic core/shell microspheres for highly specific enrichment of glycoproteins under physiological conditions,” Small, vol. 10, no. 7, pp. 1379–1386, 2014.
View at: Publisher Site | Google Scholar
J. Kim, H. S. Kim, N. Lee et al., “Multifunctional uniform nanoparticles composed of a magnetite nanocrystal core and a mesoporous silica shell for magnetic resonance and fluorescence imaging and for drug delivery,” Angewandte Chemie—International Edition, vol. 47, no. 44, pp. 8438–8441, 2008.
View at: Publisher Site | Google Scholar
B. Luo, S. Xu, A. Luo et al., “Mesoporous biocompatible and acid-degradable magnetic colloidal nanocrystal clusters with sustainable stability and high hydrophobic drug loading capacity,” ACS Nano, vol. 5, no. 2, pp. 1428–1435, 2011.
View at: Publisher Site | Google Scholar
D. Li, J. Tang, C. Wei et al., “Doxorubicin-conjugated mesoporous magnetic colloidal nanocrystal clusters stabilized by polysaccharide as a smart anticancer drug vehicle,” Small, vol. 8, no. 17, pp. 2690–2697, 2012.
View at: Publisher Site | Google Scholar
A. Chandna, D. Batra, S. Kakar, and R. Singh, “A review on target drug delivery: magnetic microspheres,” Journal of Acute Disease, vol. 2, no. 3, pp. 189–195, 2013.
View at: Publisher Site | Google Scholar
D. Wang, J. He, N. Rosenzweig, and Z. Rosenzweig, “Superparamagnetic Fe₂O₃ beads-CdSe/ZnS quantum dots core-shell nanocomposite particles for cell separation,” Nano Letters, vol. 4, no. 3, pp. 409–413, 2004.
View at: Publisher Site | Google Scholar
B.-H. Jun, M. S. Noh, J. Kim et al., “Multifunctional silver-embedded magnetic nanoparticles as SERS nanoprobes and their applications,” Small, vol. 6, no. 1, pp. 119–125, 2010.
View at: Publisher Site | Google Scholar
J. Gao, W. Zhang, P. Huang, B. Zhang, X. Zhang, and B. Xu, “Intracellular spatial control of fluorescent magnetic nanoparticles,” Journal of the American Chemical Society, vol. 130, no. 12, pp. 3710–3711, 2008.
View at: Publisher Site | Google Scholar
J. Kim, Y. Piao, and T. Hyeon, “Multifunctional nanostructured materials for multimodal imaging, and simultaneous imaging and therapy,” Chemical Society Reviews, vol. 38, no. 2, pp. 372–390, 2009.
View at: Publisher Site | Google Scholar
H.-S. Cho, Z. Dong, G. M. Pauletti et al., “Fluorescent, superparamagnetic nanospheres for drug storage, targeting, and imaging: a multifunctional nanocarrier system for cancer diagnosis and treatment,” ACS Nano, vol. 4, no. 9, pp. 5398–5404, 2010.
View at: Publisher Site | Google Scholar
E.-Q. Song, J. Hu, C.-Y. Wen et al., “Fluorescent-magnetic-biotargeting multifunctional nanobioprobes for detecting and isolating multiple types of tumor cells,” ACS Nano, vol. 5, no. 2, pp. 761–770, 2011.
View at: Publisher Site | Google Scholar
T. Alefantis, P. Grewal, J. Ashton, A. S. Khan, J. J. Valdes, and V. G. Del Vecchio, “A rapid and sensitive magnetic bead-based immunoassay for the detection of staphylococcal enterotoxin B for high-through put screening,” Molecular and Cellular Probes, vol. 18, no. 6, pp. 379–382, 2004.
View at: Publisher Site | Google Scholar
J. Lundeberg, B. Pettersson, and M. Uhlén, “Direct DNA sequencing of PCR products using magnetic beads,” in PCR Sequencing Protocols, R. Rapley, Ed., pp. 57–66, Springer, New York, NY, USA, 1996.
View at: Google Scholar
S.-Q. Gu, Y.-X. Zhang, Y. Zhu, W.-B. Du, B. Yao, and Q. Fang, “Multifunctional picoliter droplet manipulation platform and its application in single cell analysis,” Analytical chemistry, vol. 83, no. 19, pp. 7570–7576, 2011.
View at: Publisher Site | Google Scholar
T.-J. Yoon, K. N. Yu, E. Kim et al., “Specific targeting, cell sorting, and bioimaging with smart magnetic silica core-shell nanomaterials,” Small, vol. 2, no. 2, pp. 209–215, 2006.
View at: Publisher Site | Google Scholar
J.-S. Choi, Y.-W. Jun, S.-I. Yeon, H. C. Kim, J.-S. Shin, and J. Cheon, “Biocompatible heterostructured nanoparticles for multimodal biological detection,” Journal of the American Chemical Society, vol. 128, no. 50, pp. 15982–15983, 2006.
View at: Publisher Site | Google Scholar
C.-W. Lu, Y. Hung, J.-K. Hsiao et al., “Bifunctional magnetic silica nanoparticles for highly efficient human stem cell labeling,” Nano Letters, vol. 7, no. 1, pp. 149–154, 2007.
View at: Publisher Site | Google Scholar
J. Kim, S. Park, J. E. Lee et al., “Designed fabrication of multifunctional magnetic gold nanoshells and their application to magnetic resonance imaging and photothermal therapy,” Angewandte Chemie—International Edition, vol. 45, no. 46, pp. 7754–7758, 2006.
View at: Publisher Site | Google Scholar
G. L. Liu, Y. Lu, J. Kim, J. C. Doll, and L. P. Lee, “Magnetic nanocrescents as controllable surface-enhanced raman scattering nanoprobes for biomolecular imaging,” Advanced Materials, vol. 17, no. 22, pp. 2683–2688, 2005.
View at: Publisher Site | Google Scholar
P. A. Mosier-Boss and S. H. Lieberman, “Surface-enhanced raman spectroscopy substrate composed of chemically modified gold colloid particles immobilized on magnetic microparticles,” Analytical Chemistry, vol. 77, no. 4, pp. 1031–1037, 2005.
View at: Publisher Site | Google Scholar
S. H. Choi, Y. N. Ko, K. Y. Jung, and Y. C. Kang, “Macroporous Fe₃O₄/carbon composite microspheres with a short Li⁺ diffusion pathway for the fast charge/discharge of lithium ion batteries,” Chemistry—A European Journal, vol. 20, no. 35, pp. 11078–11083, 2014.
View at: Publisher Site | Google Scholar
K. Deepankumar, S. P. Nadarajan, S. Mathew et al., “Engineering transaminase for stability enhancement and site-specific immobilization through multiple noncanonical amino acids incorporation,” ChemCatChem, vol. 7, no. 3, pp. 417–421, 2015.
View at: Publisher Site | Google Scholar
M. S. Ramasamy, S. S. Mahapatra, and J. W. Cho, “Functionalization of graphene with self-doped conducting polypyrrole by click coupling,” Journal of Colloid and Interface Science, vol. 455, pp. 63–70, 2015.
View at: Publisher Site | Google Scholar
M. Luqman, J.-W. Lee, K.-K. Moon, and Y.-T. Yoo, “Sulfonated polystyrene-based ionic polymer-metal composite (IPMC) actuator,” Journal of Industrial and Engineering Chemistry, vol. 17, no. 1, pp. 49–55, 2011.
View at: Publisher Site | Google Scholar
B.-H. Jun, M. S. Noh, G. Kim et al., “Protein separation and identification using magnetic beads encoded with surface-enhanced Raman spectroscopy,” Analytical Biochemistry, vol. 391, no. 1, pp. 24–30, 2009.
View at: Publisher Site | Google Scholar
B. H. Jun, G. Kim, S. Jeong et al., “Silica core-based Surface-Enhanced Raman Scattering (SERS) tag: advances in multifunctional SERS nanoprobes for bioimaging and targeting of biomarkers,” Bulletin of the Korean Chemical Society, vol. 36, no. 3, pp. 963–978, 2015.
View at: Publisher Site | Google Scholar
W. Zhao, J. Gu, L. Zhang, H. Chen, and J. Shi, “Fabrication of uniform magnetic nanocomposite spheres with a magnetic core/mesoporous silica shell structure,” Journal of the American Chemical Society, vol. 127, no. 25, pp. 8916–8917, 2005.
View at: Publisher Site | Google Scholar
M. S. Noh, B.-H. Jun, S. Kim et al., “Magnetic surface-enhanced Raman spectroscopic (M-SERS) dots for the identification of bronchioalveolar stem cells in normal and lung cancer mice,” Biomaterials, vol. 30, no. 23-24, pp. 3915–3925, 2009.
View at: Publisher Site | Google Scholar
J.-H. Kim, J.-S. Kim, H. Choi et al., “Nanoparticle probes with surface enhanced Raman spectroscopic tags for cellular cancer targeting,” Analytical Chemistry, vol. 78, no. 19, pp. 6967–6973, 2006.
View at: Publisher Site | Google Scholar
J. Ugelstad, “Swelling capacity of aqueous dispersions of oligomer and polymer substances and mixtures thereof,” Die Makromolekulare Chemie, vol. 179, no. 3, pp. 815–817, 1978.
View at: Publisher Site | Google Scholar
T. K. Chambers and J. S. Fritz, “Effect of polystyrene-divinylbenzene resin sulfonation on solute retention in high-performance liquid chromatography,” Journal of Chromatography A, vol. 797, no. 1-2, pp. 139–147, 1998.
View at: Publisher Site | Google Scholar
F. Schoebrechts, E. Merciny, and G. Duyckaerts, “Contribution de la chromatographie en phase liquide à haute performance à la séparation des lanthanides trivalents sur résine cationique en présence d'edta. I. Synthèse et propriétés générales des résines pelliculaires polystyrène-divinylbenzǹe sulfonates,” Journal of Chromatography A, vol. 174, no. 2, pp. 351–360, 1979.
View at: Publisher Site | Google Scholar
A. Klingenberg and A. Seubert, “Comparison of silica-based and polymer-based cation exchangers for the ion chromatographic separation of transition metals,” Journal of Chromatography A, vol. 640, no. 1-2, pp. 167–178, 1993.
View at: Publisher Site | Google Scholar
T. Hargitai, P. Reinholdsson, B. Törnell, and R. Isaksson, “Functionalized polymer particles for chiral separation,” Journal of Chromatography A, vol. 630, no. 1-2, pp. 79–94, 1993.
View at: Publisher Site | Google Scholar
R. A. Weiss, A. Sen, C. L. Willis, and L. A. Pottick, “Block copolymer ionomers: 1. Synthesis and physical properties of sulphonated poly(styrene-ethylene/butylene-styrene),” Polymer, vol. 32, no. 10, pp. 1867–1874, 1991.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2016 Xuan-Hung Pham et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

5141

Downloads

2436

Citations