Effects of Substrate Temperature on the Corrosion Behaviour of Nanochromium Coatings Deposited by Direct Current Magnetron Sputtering

<div>Nyquist and Bode plots for nanochromium coatings with substrate temperature 500°C after various exposure times at open circuit potential in 0.5 M H<sub>2</sub>SO<sub>4</sub> + 2 ppm F<sup>−</sup> solution. Symbols: experimental data; line: fitted data.</div>

Journal of Nanomaterials

fig8

Figure 8

Figure 8: Effects of Substrate Temperature on the Corrosion Behaviour of Nanochromium Coatings Deposited by Direct Current Magnetron Sputtering 