Preparation of Nanosized LaCoO3 through Calcination of a Hydrothermally Synthesized Precursor
Table 1
Phase and elemental composition of the precursor powder and the samples obtained at different calcination temperature.
| (°C) | Phase composition (XRD) | La : Co : O, at.% (EDS average) |
| Precursor | La(OH)3 + Co3O4 | 12.16 : 13.73 : 73.01 | 380 | La(OH)3 + LaO(OH) + Co3O4 | 11.48 : 14.19 : 74.33 | 490 | LaO(OH) + Co3O4 | 20.08 : 22.38 : 57.54 | 740 | La2O3 + Co3O4 + LaCoO3 | 20.69 : 23.50 : 55.81 | 850 | La2O3 + Co3O4 + LaCoO3 | 20.95 : 22.02 : 57.02 | 950 | La2O3 + LaCoO3 | 29.47 : 26.32 : 44.21 | 1050 | LaCoO3 | 30.37 : 27.85 : 41.78 |
|
|
Majority phase.
|