Tab 6
/
Research Article
Thermal Stresses Analysis and Optimized TTP Processes to Achieved CNT-Based Diaphragm for Thin Panel Speakers
Table 6
Mechanical properties of CNT-based diaphragm with different TTP curing temperature.
Temperature
Properties
Thicknesses (mm)
Young’s modulus
(GPa)
Failure strength (MPa)
100°C
0.245
2.23
35.51
120°C
0.237
2.58
41.12
130°C
0.237
2.59
41.08
140°C
0.237
2.57
41.10