Dielectric and Electrical Properties of WS2 Nanotubes/Epoxy Composites and Their Use for Stress Monitoring of Structures
Table 1
Samples dimensions and measured average DC conductivities. Sample 7 contained 25 Vol.% of INT-WS2 which were mixed thoroughly with the epoxy resin without compression (cast only). Samples 8–11 containing 25 Vol.% of nanotubes were only lightly mixed and were compressed by applying pressures of 0.8 (sample 8), 13.9 (sample 9), 27.8 (sample 10), and 55.6 (sample 11) MPa.
|