Magneto-Optic Properties of Ultrathin Nanocrystalline Ferrite Garnet Films in the 8K to 300K Temperature Interval
Figure 9
Temperature dependency of MCD signal strength near 440 nm peak measured in 3.7 nm-thick garnet sample. Dichroghraph sensitivity scale was 5 × 10−6.