Ultrasonic-Assisted Synthesis, Characterization, and Photocatalytic Application of SiO2@TiO2 Core-Shell Nanocomposite Particles
Table 1
Elemental analysis of SiO2@TiO2 samples using EDX and XPS analysis.
| Sample | TBOT loading (mol) | Elemental analysis from XRF analysis | Elemental analysis from XPS analysis | Si | Ti | Si | C | O | Ti |
| Uncoated SiO2 | — | 100 | | 25.4 | 21.0 | 53.6 | 0.00 | Uncoated TiO2 | | | 100 | 0.00 | 23.8 | 51.6 | 24.6 | SiO2-TiO2-1 | | 95.7 | 4.3 | 23.5 | 16.7 | 55.7 | 4.1 | SiO2-TiO2-2 | | 90.3 | 9.7 | 20.2 | 14.8 | 56.2 | 8.8 | SiO2-TiO2-3 | | 85.7 | 14.3 | 15.6 | 11.6 | 55.4 | 15.4 | SiO2-TiO2-4 | | 80.3 | 19.7 | 8.7 | 12.1 | 59.4 | 19.8 | SiO2-TiO2-5 | | 71.2 | 28.8 | 3.2 | 12.2 | 59.8 | 24.8 |
|
|