Review Article
A Review Study on Mechanical Properties of Obtained Products by FDM Method and Metal/Polymer Composite Filament Production
Table 1
Literature studies on composite filament production.
| Study | Matrix materials | Additive materials | Fiber volume percentage (%) | Tensile strength (MPa) | Tensile modulus (GPa) | Compression strength (MPa) | Flexural strength (MPa) | Flexural modulus (GPa) | Breaking elongation (%) |
| Çantı [2] | ABS | ZrB2 | 1.5 | 40.2 | 2.14 | | — | — | 5.88 | SiO2 | 1.5 | 44.72 | 2.49 | — | — | — | 4.84 | MWCNTs | 1.5 | 41.2 | 1.68 | — | — | — | 4.05 | Al | 1.5 | 44.56 | 2.55 | | | | 6.99 | Patan [5] | ABS | CF | 12 | 31.70 | 2.72 | 70.51 | 43.80 | — | 1.64 | Hodzic and Pandzic [6] | PLA | CF | 20 | 29.96 | 4.54 | — | — | — | — | PET-G | CF | 20 | 32.79 | 4.26 | — | — | | — | Mori et al. [7] | ABS | C | 1.6 | 43 | — | — | — | — | — | Van Der Klift et al. [8] | Nylon | C | 6.9 | 140 | 14 | — | — | — | — | C | 20.7 | 464.4 | 35.7 | — | — | | — | Matsuzaki et al. [9] | PLA | C | 6.6 | 185.2 | 19.5 | — | — | — | — | Jut | 6.1 | 57.1 | 5.11 | — | — | — | — | Li et al. [10] | PLA | C | 34 | 91 | 23.8 | — | 156 | — | — | Yang et al. [11] | ABS | C | 6.5 | 147 | 4.18 | — | 127 | 7.72 | — | Bettini et al. [12] | PLA | Aramid | 8.6 | 203 | 9.34 | — | — | — | — | Akhoundi et al. [13] | PLA | Glass fiber | 49 | 478 | 29.41 | — | — | — | — | Saini [14] | — | ABS/PETG | 50/50 | 32.5 | — | — | — | — | — | Nagendra and Prasad [15] | Nylon | Aramid | 2 | 51.45 | — | — | 98.16 | — | — | Ning et al. [16] | ABS | CF | 7.5 | 41.5 | 2.5 | — | — | — | — | CF | 15 | 35 | 2.25 | — | — | — | — | Tambrallimath et al. [17] | PC70%+ABS30% | GF | 0.8 | — | 4.03 | — | — | — | — | Liu et al. [18] | PLA | Cu | — | 58.3 | 1.01 | — | 118.7 | 3.84 | — | Wood | — | 38.7 | 0.8 | — | 71 | 2.65 | — | Ceramic | — | 46.5 | 1.05 | — | 100.1 | 4.62 | — | Al | — | 51.1 | 0.83 | — | 97.8 | 3.27 | — | CF | — | 41.3 | 0.74 | — | 75.6 | 2.93 | — | Tian et al. [19] | PLA | CF | 27 | — | — | — | 335 | 30 | — | Hwang et al. [20] | ABS | Cu | 10 | 42 | 0.93 | — | — | — | — | Cu | 30 | 26.5 | 0.91 | — | — | — | — | Fe | 10 | 43.4 | 0.96 | — | — | — | — | Fe | 40 | 36.2 | 0.95 | — | — | — | — | Rajpurohit and Dave [21] | PLA | GF | 0 | 44.75 | 0.71 | — | 75.50 | 2.52 | — | GF | 1 | 43.65 | 0.81 | — | 56.65 | 2.25 | — | GF | 3 | 31.60 | 0.60 | — | 61.80 | 2.34 | — | GF | 5 | 24.65 | 0.57 | — | 50.55 | 2.11 | — | Zhong et al. [22] | ABS | Glass fıber | 18 | 58.6 | — | — | — | — | — | Tekinalp et al. [23] | ABS | CF | 10 | 52 | 7.7 | — | — | — | — | CF | 20 | 60 | 11.5 | — | — | — | — | CF | 30 | 62 | 13.8 | — | — | — | — | CF | 40 | 67 | 13.7 | — | — | — | — | Love et al. [24] | ABS | CF | 13 | 70.69 | 8.91 | — | — | — | — | Hill et al. [25] | ABS | CF | 20 | 66.8 | 8.4 | — | — | — | — | Duty et al. [26] | ABS | CF | 20 | 65.7 | 11.9 | — | — | — | — | GF | 20 | 54.3 | 5.7 | — | — | — | — | GF | 40 | 51.2 | 10.8 | — | — | — | — | Kunc [27] | ABS | CF | 13 | 53 | 8.15 | — | — | — | — | Gardner et al. [28] | PEI | CNT | 4.7 | 125.3 | 3 | — | — | — | — | DeNardo [29] | PPS | CF | 50 | 92.2 | 26.4 | — | — | — | — | Perez et al. [30] | ABS | Jute fiber | 5 | 25.9 | 1.54 | — | — | — | — | Mahajan and Cormier [31] | Epoxy | CF | 15 | 66.3 | 4.05 | — | — | — | — | Ferreira et al. [32] | PLA | CF | 15 | 53.4 | 7.54 | — | — | — | — | Compton and Lewis [33] | Epoxy | SİC CF | 10 | 66.2 | 24.5 | — | — | — | — | Dickson et al. [34] | Nylon | CF | 11 | 198 | 8.46 | — | — | — | — | AF | 8 | 110 | 4.23 | — | — | — | — | GF | 8 | 156 | 3.29 | — | — | — | — | AF | 10 | 161 | 4.76 | — | — | — | — | GF | 10 | 212 | 4.91 | — | — | — | — | Shofner et al. [35] | ABS | VGCF | 10 | 37.4 | 0.8 | — | — | — | — | Melenka et al. [36] | Nylon | Kevlar | 4.04 | 31 | 1.77 | — | — | — | — | Kevlar | 8.08 | 60 | 6.92 | — | — | — | — | Kevlar | 10.1 | 84 | 9 | — | — | — | — | Gao et al. [37] | PLA | Talc | 2 | 57.9 | 1.47 | — | — | — | 7.3 | CF | 5 | 31.7 | 1.10 | — | — | — | 13 | Nabipour et al. [38] | PE | Cu | 25 | 17.12 | 0.7 | — | — | — | 8.46 | Cu | 50 | 18.25 | 0.79 | — | — | — | 7.45 | Cu | 75 | 19.41 | 1.2 | — | — | — | 5.95 | Wang et al. [39] | SCF/PA | C-CFRP | 25 | 288.65 | 28.97 | — | — | — | — | PLA | C-CFRP | 25 | 277.11 | 29.12 | — | — | — | — | PA | C-CFRP | 25 | 252.36 | 26.68 | — | — | — | — | PC | C-CFRP | 25 | 238.85 | 26.28 | — | — | — | — | PET-G | C-CFRP | 25 | 256.04 | 28.21 | — | — | — | — | Gregor-Svetek et al. [40] | HDPE | Cardboard | 20 | 9.04 | 0.32 | — | — | — | 36.2 | Cardboard | 50 | 2.05 | 0.12 | — | — | — | 7.6 | Cardboard | 75 | 1.89 | 0.10 | — | — | — | 7.8 | He et al. [41] | PA6 | CF | — | 939.7 | 83.2 | — | 1051.8 | 57.3 | — | Karaman and Çolak [42] | ABS | CF | 10 | 32.78 | 1.67 | — | — | — | — |
|
|