[Retracted] Wire Electrical Discharge Machining (WEDM) of Hybrid Composites (Al-Si12/B4C/Fly Ash)
Table 4
Experimental results of MRR and SR (Al-Si12/B4C/fly ash).
| Ex. no | | | | | | MRR (mm3/min) | SR (μm) | S/N for MRR | S/N for SR | Gap voltage (V) | Pulse on time (μs) | Pulse off time (μs) | Wire feed (m/min) | Reinforcement (wt%) |
| 1 | 30 | 2 | 2 | 4 | 3 | 25.514 | 3.38 | 28.14 | -10.58 | 2 | 30 | 2 | 6 | 6 | 6 | 21.423 | 3.06 | 26.62 | -9.71 | 3 | 30 | 2 | 10 | 8 | 9 | 17.262 | 3.57 | 24.74 | -11.05 | 4 | 30 | 6 | 2 | 6 | 9 | 33.112 | 3.97 | 30.40 | -11.98 | 5 | 30 | 6 | 6 | 8 | 3 | 26.104 | 3.3 | 28.33 | -10.37 | 6 | 30 | 6 | 10 | 4 | 6 | 25.705 | 3.51 | 28.20 | -10.91 | 7 | 30 | 10 | 2 | 8 | 6 | 39.086 | 3.98 | 31.84 | -12.00 | 8 | 30 | 10 | 6 | 4 | 9 | 31.122 | 3.74 | 29.86 | -11.46 | 9 | 30 | 10 | 10 | 6 | 3 | 25.689 | 3.59 | 28.19 | -11.10 | 10 | 50 | 2 | 2 | 4 | 3 | 21.058 | 3.3 | 26.47 | -10.37 | 11 | 50 | 2 | 6 | 6 | 6 | 16.457 | 3.43 | 24.33 | -10.71 | 12 | 50 | 2 | 10 | 8 | 9 | 13.54 | 4.02 | 22.63 | -12.08 | 13 | 50 | 6 | 2 | 6 | 9 | 26.772 | 3.4 | 28.55 | -10.63 | 14 | 50 | 6 | 6 | 8 | 3 | 20.165 | 3.66 | 26.09 | -11.27 | 15 | 50 | 6 | 10 | 4 | 6 | 19.543 | 3.07 | 25.82 | -9.74 | 16 | 50 | 10 | 2 | 8 | 6 | 31.742 | 3.45 | 30.03 | -10.76 | 17 | 50 | 10 | 6 | 4 | 9 | 22.764 | 3.57 | 27.15 | -11.05 | 18 | 50 | 10 | 10 | 6 | 3 | 20.549 | 3.59 | 26.26 | -11.10 | 19 | 70 | 2 | 2 | 4 | 3 | 12.321 | 3.24 | 21.81 | -10.21 | 20 | 70 | 2 | 6 | 6 | 6 | 9.995 | 3.86 | 20.00 | -11.73 | 21 | 70 | 2 | 10 | 8 | 9 | 8.378 | 4.21 | 18.46 | -12.49 | 22 | 70 | 6 | 2 | 6 | 9 | 16.365 | 3.97 | 24.28 | -11.98 | 23 | 70 | 6 | 6 | 8 | 3 | 12.339 | 3.4 | 21.83 | -10.63 | 24 | 70 | 6 | 10 | 4 | 6 | 11.429 | 3.45 | 21.16 | -10.76 | 25 | 70 | 10 | 2 | 8 | 6 | 18.475 | 3.49 | 25.33 | -10.86 | 26 | 70 | 10 | 6 | 4 | 9 | 14.489 | 3.65 | 23.22 | -11.25 | 27 | 70 | 10 | 10 | 6 | 3 | 12.719 | 3.29 | 22.09 | -10.34 |
|
|