Synthesis, Characterization, and Catalytic Performance of Sb<sub>2</sub>Se<sub>3</sub> Nanorods

Hu, Ning; Cheney, Marcos A.; Hanifehpour, Younes; Joo, Sang Woo; Min, Bong-Ki

doi:https://doi.org/10.1155/2017/5385908

Journal of Nanomaterials

On this page

Abstract Introduction Results and Discussion Conclusion Conflicts of Interest Acknowledgments References Copyright Related Articles

Research Article | Open Access

Volume 2017 | Article ID 5385908 | https://doi.org/10.1155/2017/5385908

Synthesis, Characterization, and Catalytic Performance of Sb₂Se₃ Nanorods

Ning Hu,¹Marcos A. Cheney,²Younes Hanifehpour,³Sang Woo Joo,³and Bong-Ki Min⁴

Academic Editor: Yasuhiko Hayashi

Received19 Jan 2017

Revised22 Mar 2017

Accepted02 Apr 2017

Published04 Jul 2017

Abstract

Antimony selenide has many potential applications in thermoelectric, photovoltaic, and phase-change memory devices. A novel method is described for the rapid and scalable preparation of antimony selenide (Sb₂Se₃) nanorods in the presence of hydrazine hydrate and/or permanganate at 40°C. Crystalline nanorods are obtained by the addition of hydrazine hydrate in a reaction mixture of antimony acetate and/or chloride and sodium selenite in neutral and basic media, while amorphous nanoparticles are formed by the addition of KMnO₄ in a reaction mixture of antimony acetate/chloride and sodium selenite. The powder X-ray diffraction pattern confirms orthorhombic phase crystalline Sb₂Se₃ for the first and second reactions with lattice parameters nm, nm, and nm and amorphous Sb₂Se₃ for the third reaction. Scanning electron microscopy (SEM), transmission electron microscopy (TEM), and high-resolution TEM (HRTEM) images show the diameter of nanorods for the first and second reactions to be in the order of 100 nm to 150 nm and about 20 nm particles for the third reaction. EDX and XPS suggest that the nanorods are pure Sb₂Se₃. The UV-vis analysis indicates a band gap of 4.14 and 4.97 eV for the crystalline and amorphous Sb₂Se₃, respectively, corresponding to a blue shift. The photocatalytic study shows that the decolorization of Rhodamine in solution by nanoparticles is slightly greater than nanorods.

1. Introduction

Structure, morphology, and composition of nanorods and nanoparticles are important parameters that give rise to their properties and thus applications. Morphological and structural changes associated with semiconducting V2VI3 compounds such as Sb₂Se₃ are not well understood.

The semiconducting V₂VI₃ compounds (Sb₂S₃ and Sb₂Se₃) are highly anisotropic semiconductors with a layered structure parallel to the growth direction with orthorhombic phase crystal structure, which is known to adopt a number of packing structures resulting in either trigonal prismatic or octahedral coordination of the metals within a layered matrix of chalcogens [1]. Semiconductor selenides find applications as laser materials, optical filters, sensors, and solar cells. Antimony selenide, an important member of these V₂VI₃ compounds, is a layer-structured semiconductor of orthorhombic crystal structure and exhibits good photovoltaic properties and high thermoelectric power (TEP) which allows possible applications for optical and thermoelectronic cooling devices [2–7]. Over the past two decades, many methods have been employed to prepare Sb₂Se₃ nanotubes, nanoribbons, nanowires, nanosheets, nanorods, nanobelts, nanospheres, and nanoflakes, including thermal decomposition [8, 9], complex decomposition approach [10], solvothermal reaction [11, 12], microwave irradiation [13], vacuum evaporation [14], and other chemical reaction approaches [15, 16]. However, most of the reports were focused on the preparation of Sb₂Se₃ with reaction times much more than 10 h [17–22]. Hence, the synthesis of 1D nanomaterials in high yield via a quick process is still a challenge. In this study, antimony selenide (Sb₂Se₃) nanomaterials with uniform size and morphology are prepared by a soft hydrothermal process using hydrazine hydrate and permanganate in just 30 min. The surprising morphological and structural changes occurring in the presence of permanganate are also presented. The present route is simple, cost-effective, and reproducible.

2. Experimental Section

2.1. Synthesis

All chemicals were of analytical grade and were used as received. All glassware were acid-cleaned, and the ultrapure water was devoid of any trace of organics. The synthesis of Sb₂Se₃ is performed by a new redox method using antimony acetate and/or chloride salts, sodium selenite, hydrazine hydrate (N₂H₄H₂O), and/or permanganate in neutral and basic aqueous solution, respectively. For the first reaction, Sb(CH₃COO)₃ (0.227 g, 0.750 mmol) and Na₂SeO₃ (0.259 g, 1.49 mmol) were weighted independently and then placed together into a 50 mL volumetric flask followed by the addition of 25 mL of pure water at room temperature. It is important to dissolve all the salts simultaneously via sonication to obtain the results desired. After the salts were completely dissolved, 3 mL of 80% hydrazine hydrate and NaOH (0.01 mol, pH = 10) is added dropwise to the solution followed by dilution to the 50 mL mark with pure water and then placed in a sonicator bath at 40°C for 40 min. After the addition of hydrazine, the solution turned turbid, and a white/beige precipitate appeared, which rapidly settled down, leaving a colorless solution. The solids are separated by filtration (Whatman filter paper) and washed with ethanol and pure water, followed by air drying at room temperature for characterization. The first reaction is summarized as Note that we run the above reaction in the absence of NaOH as well. Since there were no noticeable differences in the color of the product with and without NaOH, we proceeded to change the salt type of the reaction. The only difference observed was in the amount of solids produced which were more in the presence of NaOH.

For the second reaction, the above process was repeated, except that SbCl₃ was used in place of Sb(CH₃COO)₃ with no NaOH, to study the effect of salt type and pH on the reaction. In this case, the solids produced are black:

For the third reaction, the above process (reaction 1) is also repeated with minor changes; SbCl₃ is used in place of Sb(CH₃COO)₃; KMnO₄ is used together with hydrazine and NH₃ in place of NaOH. The pH of this mixture was around 10. The solids produced are a mixture of reddish brown and black in color: The pH of the permanganate solution was near neutral and unstable (reacts with water). The addition of NH₃ (weak base) made the solution basic and stable. At this pH, the permanganate solution is purple and stable and the manganese is mostly Mn(VII).

2.2. Characterization Techniques

The Sb₂Se₃ solids produced were characterized by X-ray powder diffraction (XRD) using a PANalytical X’Pert PRO X-ray diffractometer with a Cu-K_α radiation (40 KV, 30 mA), and a PIXcell solid state detector. The samples were prepared on glass sample holder. The patterns were recorded at room temperature with step sizes of 0.02°.

Surface structure and morphology of the sample were obtained with the aid of a Field Emission Scanning Electron Microscope (FESEM, Hitachi S-4200, Japan). The samples for FESEM analysis were prepared by suspending about 3 mg of the solid Sb₂Se₃ oxide in 1 mL of isopropanol. After the isopropanol was evaporated, the dry solid was placed on a double-sided black tape and then coated with sputtered platinum thin film prior to FESEM imaging.

Transmission electron microscopy (TEM) images were obtained with a Tecnai G² F20 S-Twin TEM instrument. The TEM operates at 200 KV using a field emission gun in Schottky mode as an electron source. The samples for TEM analysis were prepared by placing 3 mg of the air-dried solid Sb₂Se₃ in 10 mL of 2-propanol and sonication for 5 min for homogeneity. The holey carbon copper grid is dipped into the sonicated solution for a few seconds and then air-dried in the dark before analysis. UV-vis absorptions were carried out using a Shimadzu 160A (Japan) spectrophotometer. Photocatalytic performance of the Sb₂Se₃(s) rods and Sb₂Se₃(s) particles was evaluated by monitoring the decolorization of Rhodamine B in aqueous solution. The catalytic reaction is carried out in a 20 mL glass vial, which contained 10 mL of the Rh B (0.05 mM) dye solution and 15 mg of Sb₂Se₃ rods and/or Sb_2-xSe₃ particles. The mixture was allowed to react at 25°C under stirring. After reaction, the suspension was centrifuged and filtered and the supernatant analyzed using a UV-vis spectrometer (Shimadzu 160A UV, Japan). The efficiency of the catalysts is determined by difference in concentration of RhB between the initial and final readings at λmax = 501 nm.

3. Results and Discussion

3.1. Creation of Sb₂Se₃ Nanorods Using Hydrazine Hydrate (N₂H₄H₂O) and Morphological Changes Induced by Permanganate ()

The synthesis of Sb₂Se₃ nanorods consists of the reaction between N₂H₄H₂O and Se in the presence of Sb(CH₃COO)₃ and/or SbCl₃ in near neutral and strongly basic media with incubation at 40°C and sonication for 30 min. In this complex reaction, N₂H₄H₂O in basic aqueous solutions shows a strong reducing power according to the following redox reactions:In our experiments, Sb(CH₃COO)₃ and are used to react in molar ratios.

The temperature of 40°C was chosen because at this temperature a balance is maintained between minimum input of energy (more cost-effective) and a good product yield.

3.2. X-Ray Powder Diffraction, EDX, and XPS

The phases formed by the new method described above are characterized by XRD. Figure 1 shows the XRD patterns of ((a) and (b)) the crystalline nanorods of Sb₂Se₃ produced using Sb(CH₃COO)₃ and/or SbCl₃, Na₂SeO₃, and N₂H₄H₂O with OH⁻ (reaction (1)) and without OH⁻ (reaction (2)) at 40°C and sonication for 40 min. These graphs indicate that the profile parameters of the diffraction peaks of the two types of Sb₂Se₃ produced by reactions (1) and (2) are very similar. The intensity of the peaks indicates that the samples are not highly crystalline. All peaks in Figures 1(a) and 1(b) can be indexed to an orthorhombic phase with lattice parameters: nm, nm, and nm with intensity and positions comparable with the values given in JCPDS (file card number: 15-861). The extra peak seen in Figure 1(b), at a 2θ value of 23.5°, is a result of a different orientation of the sample. It appears that no other phases are observed arising from impurities such as Sb₂O₃. Based on the standard redox potential shown in reactions (4), (5), and (6), the following possible redox half reactions (for reactions (1) and (2)) between N₂H₄ and are possible for the production of Sb₂Se₃ rods:The XRD pattern in Figure 1(c) reveals only the main peaks at around 25°–30°, suggesting the poorly crystalline nature of this sample obtained from reaction (3), where N₂H₄ and are used together and Sb(CH₃COO)₃ is replaced with SbCl₃, respectively. Permanganate, which is an oxidizing agent, was used together with hydrazine firstly to slow down the reaction between hydrazine, Sb(CH₃COO)₃, and Na₂SeO₃, since this reaction is extremely fast at pH 10 and difficult to control, secondly to see the influence of permanganate in rod formation, and thirdly to see whether Mn²⁺ could be incorporated into the matrix of Sb₂Se₃ as an Sb_2-xMn_xSe₃ doped material, since hydrazine is capable of reducing Mn⁷⁺ to Mn⁴⁺ and possibly even to Mn²⁺. The XRD pattern for this reaction suggests that the choice of counter ions used for Sb when is used is important to obtain a highly crystalline product. When this reaction was repeated using SbCl₃, the product was completely amorphous (not shown) with even more Mn content as impurity. It is clear from these results that Cl⁻ interferes with the redox process by channeling the reaction through a different pathway. It is also likely that Cl⁻ reacts with permanganate rather than with hydrazine to contribute to the observed effect. Thus, this reaction is very sensitive to experimental conditions used. Minor modification of the original procedure may result in the formation of mixed nanosized crystalline and poorly crystalline solids.

The element composition and purity of these nanomaterials were analyzed using EDXS. Figure 2(a) depicts typical EDX spectra recorded for the crystalline nanorods sample showing the presence of the elements Sb and Se. Interestingly, for the third reaction (not shown), the EDX pattern confirms the presence of Sb/Se and Mn as impurity for the Sb₂Se₃ particles, suggesting that changed the crystallinity of the sample. Figure 2(b) shows a typical XPS survey spectrum of the as-prepared Sb₂Se₃ nanorods synthesized in the presence of hydrazine hydrate (reactions (1) and (2)) at 40°C and sonication for 40 min and suggests that the nanorods are composed of pure Sb and Se. The high resolution spectrum shown in Figures 2(b) and 2(c) indicates that the binding energies for Sb3d and Se3d in Sb₂Se₃ agree well with the published data [16].

(a)

(b)

(c)

(d)

3.3. SEM, TEM, and HRTEM Studies

The nanostructures of both crystalline and poorly crystalline Sb₂Se₃ are studied using SEM, TEM, and HRTEM imaging. Figure 3 shows the SEM images of rods obtained for nanosized nanocrystalline and poorly crystalline Sb₂Se₃. For the crystalline samples (first and second reactions), (cf. Figures 3(a)–3(d)), the images show rods with orthorhombic shapes with lengths of about 100 nm to about 2 µm. Furthermore, the rods from the first reaction (cf. Figures 3(a) and 3(b)) appear thicker (0.1 µm) than the ones from the second reaction (0.05 µm) (cf. Figures 3(c) and 3(d)). We attribute this effect to the OH⁻ used in the first reaction (pH 10). At this solution pH, the production of solids is very fast, making the nanorods thicker. At near neutral pH, the production of solids is slower and this plus the salt type influences the size of the nanorods appearing thinner. The exact role of N₂H₄ in the formation of nanostructures is not known. We speculate that the role of N₂H₄ is both a reducing agent and a coordinator for the formation of the rod-like morphology. For the poorly crystalline sample (third reaction) (cf. Figures 3(e) and 3(f)), the images depict particles with bead-like shape with size of less than 20 nm that bundle together to form aggregates. In this reaction, it can be seen that the acetate and Cl⁻ (from SbCl₃) clearly affect the structure and morphology of the particles obtained, particularly when is present. The effect of acetate is currently under investigation.

(a)

(b)

(c)

(d)

(e)

(f)

The TEM images shown in Figures 4(a)–4(f) display the crystal structure of the as-prepared Sb₂Se₃ nanorods (from the first and second reactions) and confirm the particle size of about 100 to 2 µm observed in the SEM images. The First Fourier Transform (FFT) patterns of the nanorods shown in the insets of Figures 4(c) and 4(f) suggest that Sb₂Se₃ obtained from the first and second reactions is indeed crystalline in nature with a growth direction. The SEM and TEM images also show that the products of the first and second reactions consist of mixtures of large (cf. Figure 4(a)) and small (cf. Figure 4(d)) nanorods, both of which appear faceted, with rectangular cross sections. Some of the rods in Figure 4(a) have stripes perpendicular to the nanorod axis. We speculate this to be a physical effect most likely due to local bending since the TEM images did not show any noticeable atomic disregistry across the glide plane.

(a)

(b)

(c)

(d)

(e)

(f)

(g)

(h)

(i)

The TEM and HRTEM images of the poorly crystalline Sb₂Se₃ are shown in Figures 4(g)–4(i). The TEM images display the bead-like distribution obtained for the light-colored Sb₂Se₃ particles with size of less than 20 nm. Some of these particles appear to bundle together to form nanoaggregates of about 100 nm. The SAED pattern (inset in Figure 4(i)) supports this observation as it indicates that there is no growth direction and suggests what appears as poorly crystalline to amorphous phase of Sb₂Se₃.

The XRD patterns and the TEM images confirm the structures of Sb₂Se₃ nanorods and suggest that the preferred ratio of Sb to Se is the one from the second reaction in which hydrazine hydrate was used in near neutral solution (cf. Figure 2(c)). We note that the redox-assisted formation of nanorods, in our system, is different from the chalcogenide nanoparticles formation by sheet rolling [23] and cation exchange reactions [24]. This “redox-assisted” synthesis of nanorods may permit the independent control of nanostructure composition and morphology by means of judiciously selecting counter ions for Sb(III) and hydrazine and dose in the synthesis. The exact role of permanganate in reaction (3) is not known but we speculate that the acetate and Cl⁻ ions from Sb(III) play a more important role than was expected. It is clear that this may be the case in the third reaction where structural and morphological changes are induced by by either incorporation of Mn into the lattice and/or coprecipitation of Mn during synthesis. Furthermore, the redox-stimulated shape evolution may occur during nanostructure growth as a possible mechanism. The question as to why structural and morphological changes were induced by is still under investigation. The best reproducible reaction condition for quantifying yield to produce in large scales depends on the size of the nanorods desired. For large nanorods, the first reaction is preferred, while for fine nanorods, the second reaction is recommended.

The UV-vis absorption spectrum of the crystalline and amorphous Sb₂Se₃ samples is shown in Figure 5. The spectrum of the crystalline samples shows an absorption maximum of 750 nm for reaction (1) and 760 nm for reaction (2), while the poorly crystalline samples show a maximum of 730 nm with corresponding band gaps of 1.65, 1.63, and 1.70 eV, respectively. This observation suggests a red shift compared to the bulk sample consistent with common knowledge that the smaller the size of the particle, the higher the band gap. A solar cell under construction in our laboratory showed potential when Sb₂Se₃ was paired with CdS.

The efficiency of the semiconductor nanoparticles and nanorods with different band gap to function as photocatalyst was measured using RhB as a model organic pollutant in the presence of natural light. Figure 6 shows the UV absorption spectra of RhB in solution at different time intervals (0, 2, and 4 h) for nanoparticles (since decolorization of RhB by nanoparticles was slightly higher than nanorods; only results for nanoparticles are shown). In 2 h, about 50% of the RhB is decolorized followed by a 75% decolorization in 4 h. The photodecolorization of RhB by semiconductor nanoparticles may be explained by an adsorption-oxidation-desorption mechanism where oxygen accepts an electron forming a superoxide radical anion. These can react with water to form highly reactive hydroxyl radicals.

4. Conclusion

A new method using hydrazine hydrate and permanganate was developed to prepare Sb₂Se₃ nanorods and nanoparticles with uniform size and morphology. The use of hydrazine hydrate in basic solution (in the presence of selenite and antimony acetate) channels the reaction towards the production of large rod-like Sb₂Se₃ nanocrystals, while the use of hydrazine hydrate in near neutral solution (in the presence of selenite and antimony chloride) channels the reaction in the direction of producing small rod-like Sb₂Se₃ nanocrystals. The use of permanganate, hydrazine, Sb(CH₃COO)₃, and selenite produces Sb₂Se₃ nanocrystals with Mn as an impurity. One attractive feature for our system is that it is simple, cost-effective, and reproducible. Large scale production would depend on what is desired. For large nanorods, the first reaction is recommended, while for fine nanorods, the second reaction is best. The photocatalytic study demonstrated that semiconductor nanoparticles are more effective in the decolorization of RhB via possibly free radical formation. Antimony selenide nanoparticles may find potential application not only in thermoelectric, photovoltaic, and phase-change memory devices but also as catalyst for the transformation of organic pollutants.

Conflicts of Interest

The authors declare that they have no conflicts of interest.

Acknowledgments

This work was supported by the National Research Foundation of Korea (Grant NRF-2015-002423).

References

X. W. Zheng, Y. Xie, L. Y. Zhu et al., “Growth of Sb₂E₃ (E = S, Se) polygonal tubular crystals via a novel solvent-relief-self-seeding process,” Inorganic Chememistry, vol. 41, p. 455, 2002.
View at: Publisher Site | Google Scholar
N. S. Patil, A. M. Sargar, S. R. Mane, and P. N. Bhosale, “Growth mechanism and characterisation of chemically grown Sb doped Bi2Se3 thin films,” Applied Surface Science, vol. 254, no. 16, pp. 5261–5265, 2008.
View at: Publisher Site | Google Scholar
S. Subramanian and D. P. Padiyan, “Effect of structural, electrical and optical properties of electrodeposited bismuth selenide thin films in polyaniline aqueous medium,” Materials Chemistry and Physics, vol. 107, p. 392, 2008.
View at: Google Scholar
C. Mastrovito, J. W. Lekse, and J. A. Aitken, “Rapid solid-state synthesis of binary group 15 chalcogenides using microwave irradiation,” Journal of Solid State Chemistry, vol. 180, no. 11, pp. 3262–3270, 2007.
View at: Publisher Site | Google Scholar
S. K. Batabyal, C. Basu, A. R. Das, and G. S. Sanyal, “Solvothermal synthesis of bismuth selenide nanotubes,” Materials Letters, vol. 60, no. 21-22, pp. 2582–2585, 2006.
View at: Publisher Site | Google Scholar
X. Qiu, C. Burda, R. Fu, L. Pu, H. Chen, and J. Zhu, “Heterostructured Bi2Se3 nanowires with periodic phase boundaries,” Journal of the American Chemical Society, vol. 126, no. 50, pp. 16276-16277, 2004.
View at: Publisher Site | Google Scholar
Y. Jiang, Y. J. Zhu, and G. F. Cheng, “Synthesis of Bi₂Se₃ nanosheets by microwave heating using an ionic liquid,” Crystal Growth & Design, vol. 6, p. 2174, 2006.
View at: Google Scholar
S. Messina, M. T. S. Nair, and P. K. Nair, “Solar cells with Sb₂S₃ absorber films,” Thin Solid Films, vol. 517, no. 7, pp. 2503–2507, 2009.
View at: Publisher Site | Google Scholar
Y. H. Kwon, M. Jeong, H. W. Do, J. Y. Lee, and H. K. Cho, “Liquid-solid spinodal decomposition mediated synthesis of Sb₂Se₃ nanowires and their photoelectric behavior,” Nanoscale, vol. 7, no. 30, pp. 12913–12920, 2015.
View at: Publisher Site | Google Scholar
H. M. Yang, X. H. Su, and A. D. Tang, “Microwave synthesis of nanocrystalline Sb₂Se₃ and its electrochemical properties,” Materials Research Bulletin, vol. 42, Article ID 421357, p. 1357, 2007.
View at: Google Scholar
M. Lallakantouri, A. G. Marison, and G. E. Manoussakis, “Thermal decomposition of tris(N, N-disubstituted dithiocarbamate) complexes of As(III), Sb(III) and Bi(III),” Journal of Thermal Analysis, vol. 29, no. 5, pp. 1151–1169, 1984.
View at: Publisher Site | Google Scholar
Y. Yang, H. Zeng, S. H. Yu, L. Yang, and Y. H. Zhang, “Pressure-controlled fabrication of stibnite nanorods by the solvothermal decomposition of a simple single-source precursor,” Chemistry of Materials, vol. 12, no. 10, pp. 2924–2929, 2000.
View at: Publisher Site | Google Scholar
W. J. Lou, M. Chen, X. B. Wang, and W. M. Liu, “Novel single-source precursors approach to prepare highly uniform Bi₂S₃ and Sb₂S₃ nanorods via a solvothermal treatment,” Chemistry of Materials, vol. 19, no. 4, pp. 872–878, 2007.
View at: Publisher Site | Google Scholar
O. Savadogo and K. C. Mandal, “Studies on new chemically deposited photoconducting antimony trisulphide thin films,” Solar Energy Materials and Solar Cells, vol. 26, no. 1-2, pp. 117–136, 1992.
View at: Publisher Site | Google Scholar
D. Choi, Y. Jang, J. Lee et al., “Diameter-controlled and surface-modified Sb2Se3 nanowires and their photodetector performance,” Scientific Reports, vol. 4, article 6714, 2014.
View at: Publisher Site | Google Scholar
Y. Q. Liu, M. Zhang, F. X. Wang, and G. B. Pan, “Facile microwave-assisted synthesis of uniform Sb₂Se₃ nanowires for high performance photodetectors,” Journal of Materials Chemistry C, vol. 2, no. 2, pp. 240–244, 2014.
View at: Google Scholar
X. C. Ma, Z. D. Zhang, X. Wang, S. T. Wang, F. Xu, and Y. T. Qian, “Large-scale growth of wire-like Sb₂Se₃ microcrystallines via PEG-400 polymer chain-assisted route,” Journal of Crystal Growth, vol. 263, p. 491, 2004.
View at: Google Scholar
S. K. Batabyal, C. Basua, G. S. Sanyal, and A. R. Das, “Synthesis of Sb₂Se₃ nanorods using B-cyclodextrin,” Materials Letters, vol. 58, pp. 169–171, 2003.
View at: Google Scholar
D. B. Wang, C. X. Song, X. Fu, and X. Li, “Growth of one-dimentional Sb₂Se₃ and Sb₂Se₃ crystals with straw-tied like architectures,” Journal of Crystal Growth, vol. 28, p. 611, 2005.
View at: Google Scholar
Q. Xie, Z. P. Liu, M. W. Shao, L. F. Kong, W. C. Yu, and Y. T. Qian, “Polymer-controlled growth of Sb₂Se₃ nanoribons via a hydrothermal process,” Journal of Crystal Growth, vol. 252, p. 570, 2003.
View at: Google Scholar
J. W. Wang, Z. X. Deng, and Y. D. Li, “Synthesis and characterization of Sb₂Se₃ nanorods,” Materials Research Bulletin, vol. 37, no. 3, pp. 495–502, 2002.
View at: Publisher Site | Google Scholar
D. B. Wang, D. B. Yu, M. S. Mo, X. M. Liu, and Y. T. Qian, “Preparation and characterization of wire-like Sb₂Se₃ and flake-like B₁₂Se₃ nanocrystals,” Journal of Crystal Growth, vol. 253, p. 445, 2003.
View at: Google Scholar
M. Bar-Sadan, I. Kaplan-Ashiri, and R. Tenne, “Inorganic fullerenes and nanotubes: wealth of materials and morphologies,” European Physical Journal: Special Topics, vol. 149, no. 1, pp. 71–101, 2007.
View at: Publisher Site | Google Scholar
B. Zhang, Y. Jung, H.-S. Chung, L. Van Vugt, and R. Agarwar, “Nanowire transformation by size-dependent cation exchange reactions,” Nano Letters, vol. 10, no. 1, pp. 149–155, 2010.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2017 Ning Hu et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

2413

Downloads

1578

Citations

Journal of Nanomaterials

Synthesis, Characterization, and Catalytic Performance of Sb2Se3 Nanorods

Abstract

1. Introduction

2. Experimental Section

2.1. Synthesis

2.2. Characterization Techniques

3. Results and Discussion

3.1. Creation of Sb2Se3 Nanorods Using Hydrazine Hydrate (N2H4H2O) and Morphological Changes Induced by Permanganate ()

3.2. X-Ray Powder Diffraction, EDX, and XPS

3.3. SEM, TEM, and HRTEM Studies

4. Conclusion

Conflicts of Interest

Acknowledgments

References

Copyright

Synthesis, Characterization, and Catalytic Performance of Sb₂Se₃ Nanorods

3.1. Creation of Sb₂Se₃ Nanorods Using Hydrazine Hydrate (N₂H₄H₂O) and Morphological Changes Induced by Permanganate ()