Evolution of Structural-Phase States in TiNi Surface Layers Synthesized by Electron Beam Treatment

Figure 6

Components of the microstrain in the B2 phase lattice in relation to the penetration depth in the TiNi specimens irradiated with 𝐸₁=4 J/cm²: 𝜀_Ψ=90^∘0𝑥00020=90 (1, 2) and ε _{Ψ =0} (3, 4). Curves 1 (○), 3 (◊)—immediately after irradiations, curves 2 (●), 4 (♦)—a year later.