This issue presents a wide variety of insightful work in the synthesis, characterization, and properties of nanomaterials.
Researchers continuously strive to improve material properties and develop novel methods for nanosynthesis. For example, M. Srivastava et al. report a novel method for increasing hydrophobicity of ZnO surfaces through the incorporation of polytetrafluoroethylene (PTFE). The modification of ZnO with PTFE results in a decreased treatment time, and such a material is easily modified by either stearic acid or fluoroalkylsilane to give a low-energy superhydrophobic material. Polymeric materials have also been found useful in nanoscale templates. S. L. Pang et al. present a novel route to the formation of thin-film MnO2 by self-assembly of MnO2 nanoparticles on nickel-coated polyethylene terephthalate utilizing a horizontal submersion process at room temperature. These materials exhibit high capacitance behavior, high cycling reversibility, and stability within the potential range of 0.0 to 0.9 V based on cyclic voltammetry. Furthermore, C. Dwivedi et al. report the synthesis of polyvinyl-alcohol-(PVA-) stabilized selenium nanoparticles by reaction of sodium selenosulfate with various organic acids in room-temperature aqueous media. Although a gamut of organic acids and various PVA concentrations were studied, no significant effects on structure were found. Simply, the spherical selenium nanoparticles ranged in size from about 40 to 100 nm, as readily seen in AFM and TEM imaging.
Soft matter has also played a role in nanoscale synthesis. In this issue, W. N. R. W. Isahak et al. present a comparative study of silicotungstic acid bulk (STAB) and STA-silica sol gel (STA-SG) and their efficacies, both in activity and selectivity, as catalysts in an esterification reaction. STA-SG resulted in lower conversion (96%) compared to STAB (100%) and control H2SO4 (98%); however, STA-SG advantageously delivers selectivity of 95% compared to 89.9 and 81.6% by using STAB and H2SO4, respectively. Such attributes may result from the increased surface area obtained by the sol gel method.
In a different synthetic route, Y. Zhao et al. report the synthesis of Ni/Al layered double hydroxide (LDH) nanorods by a hydrothermal method. Such methods require a pH of 10.0 and temperature of 180°C for nanorod formation. Additionally, reaction time increases not only rod diameter, but also rod length.
The ability to tune magnetic properties of nanoparticles has recently garnered interest in many groups. S. Singhal et al. analyzed cobalt-substituted nickel chromium ferrites (CrCoxNi1-xFeO4, , 0.2, 0.4, 0.6, 0.8, and 1.0) prepared by a sol gel autocombustion method at various annealing temperatures. Here, as annealing temperature increases, particle size increases up to 45 nm, and added Co3+ content increases saturation magnetization and decreases coercivity.
Similarly,R. Shaiboub et al. discusse the demagnetization effects of increasing Er concentrations on nanoparticle Y3-xErxFe5O12 (, 1.0, and 2.0) thin films synthesized by a solgel method. Such films obtain a single-phase garnet and begin crystallization at 800°C, and with increased annealing temperature, the material displays larger crystallite sizes. The loss of magnetization with increased Er content was attributed to the reverse alignment between Er3+ and Fe3+. In contrast to the sol gel method, H. Y. He reports that the properties of Co0.5Zn0.5Fe2O4 nanoparticles formed by a carboxymethyl cellulose template hydrothermal method were analyzed by XRD, SEM, and vibrating sample magnetometer. The increase of template proportion in synthesis results in not only morphological change from granular to platelike but also an increase in superparamagnetic behavior (from 2.81 T without template to 3.13 T with template).
The application of reported nanomaterials is an important topic for researchers. S. Kaviya et al. report the utilization of Polyalthia longifoli leaf extract as both a reducing and capping agent with D-sorbitol for increased stabilization in the synthesis of silver nanoparticles (AgNPs). Additionally, UV-vis spectroscopy revealed a blue shift with increased reaction temperature. These synthesized materials were found to have a wider antimicrobial activity in gram-positive than gram-negative organisms.
Moreover, nanoparticles have found use not only as catalysts, but also as materials for environmental remediation. In the field of catalysis, Z. M. Wang et al. elucidate the important parameters in flame aerosol synthesis of pure TiO2 and TiO2 doped with Fe or V. Here, the photocatalytic properties of the synthesized material were studied by the selective oxidation of 1-phenyl ethanol to acetophenone. The introduction of a Fe or V dopant resulted in increased catalytic activity at lower concentrations of deposited metal ions. Additionally, the morphology of neat TiO2 alters with increased metal doping as witnessed in XRD analysis and the Raman spectroscopy. Researchers compared the efficacy of the photocatalyst in both acetonitrile and water and found the organic solvent to provide higher conversion.
In regards to remediation, S. R. Kanel et al. reports the synthesis of nanoscale (~20 to 50 nm) hydroxyapatite (NHA) through vigorous agitation of Ca(NO3)2·4H2O and (NH4)2HPO4 in alkaline solution. In uranium removal studies, the precipitate performed comparably to commercially available HA. Based on two-dimensional flow cell analysis, the synthesized NHA exhibits transport properties akin to tracers in aqueous environments; consequently, potential applications may include in situ U(VI) remediation. Additionally, M. N. Nadagouda and D. A. Lytle present the novel synthesis of iron oxide/iron-coated carbons like activated carbon, anthracite, cellulose fiber, and silica by combustion and their uses in arsenic adsorption. Generally, the spherical nanoparticles ranged in size from 50 to 400 nm. Such materials were found suitable for arsenic adsorption and may be suitable in environmental remediation, catalysis, and various other applications.