Electrical Transport Properties of Multilayered Single-Walled Carbon Nanotube Films
Table 1
The fabrication parameters, thickness, sheet resistance, and TCR at 300 K of the SWCNT thin films.
| Sample name | Sample Description | Thickness (nm) | Sheet resistance at room environment (Ω/□) | TCR (at 300 K) |
| 1 | 1 mL SWCNT suspension, 2 layers | 45 | 45780 | −0.146 | 2 | 2 mL SWCNT suspension, 1 layer | 35 | 10750 | −0.112 | 3 | 2 mL metallic SWCNT suspension, 1 layer | 35 | 5693 | −0.060 | 4 | 2 mL SWCNT suspension, 3 layers | 105 | 3210 | −0.088 | 2a | Sample 2 after annealing at 300°C, 12 hours | 35 | 104500 | −0.136 | 4a | Sample 4 after annealing at 300°C, 12 hours | 105 | 24100 | −0.101 | 2aN | Sample 2a after HNO3 treatment | 35 | 19780 | −0.055 | 4aN | Sample 4a after HNO3 treatment | 105 | 1012 | −0.0186 |
|
|