Graphene-Multiwalled Carbon Nanotube Hybrids Synthesized by Gamma Radiations: Application as a Glucose Sensor

Shahriary, Leila; Ghourchian, Hedayatollah; Athawale, Anjali A.

doi:https://doi.org/10.1155/2014/903872

Journal of Nanotechnology

On this page

Abstract Introduction Experimental Results and Discussion Conclusion Acknowledgments Supplementary Materials References Copyright Related Articles

Research Article | Open Access

Volume 2014 | Article ID 903872 | https://doi.org/10.1155/2014/903872

Graphene-Multiwalled Carbon Nanotube Hybrids Synthesized by Gamma Radiations: Application as a Glucose Sensor

Leila Shahriary,^1,2Hedayatollah Ghourchian,²and Anjali A. Athawale¹

Academic Editor: Thomas Thundat

Received20 Jan 2014

Accepted05 May 2014

Published01 Jun 2014

Abstract

Three-dimensional hybrid nanomaterial of graphene-multiwalled carbon nanotubes (G-MWCNTs) was synthesized using gamma rays emitted by a ⁶⁰Co source with a dose rate of 3.95 Gy min⁻¹. The products were characterized by fourier transform infrared (FTIR), ultraviolet-visible (UV-Vis), photoluminescence (PL), and micro-Raman spectroscopy, X-ray diffraction analysis (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). FTIR and UV-Vis analysis reveals the formation of hybrid nanomaterial which is confirmed by XRD, micro-Raman analysis, and PL. SEM micrograph depicts the composite structure of graphene layers and MWCNTs, while the TEM micrograph exhibits graphene layers covered by MWCNTs. The G-MWCNTs hybrid used as electrode for electrochemical studies in K₃Fe(CN)₆ shows enhancement in electrocatalytic behavior, compared to each individual starting material, therefore, has been applied for amperometric sensing of glucose in alkaline solution and exhibits sensitivity of 12.5 AmM^-1cm⁻² and low detection limit 1.45 M () in a linear range of 0.1 to 14 mM ().

1. Introduction

Carbon is one of the most abundant elements found in nature existing in various allotropic forms. It has four electrons in its outer valence shell and is a conducting in nature. In the last two decades, novel nanostructures have emerged such as fullerenes, carbon nanotubes, and graphene. The flat monolayer of sp² carbon atoms tightly packed in two-dimensional honeycomb-like lattice is the building block for graphene. Due to its remarkable mechanical, optical, thermal, electronic, and magnetic [1–5] properties it has been used in various areas of nanosize research such as electronics, batteries, fuel cells, super capacitors, sensors, and biosensors [6–11]. Compared to carbon nanotubes, graphene exhibits potential advantages of high surface area, ease of processing, low cost, safety [12], and high purity (absence of transition metals, Fe, Ni, etc.) [13]. Thus, it provides a good platform to study the electrocatalytic effects of carbon materials. In fact, graphene oxide (GO) sheets are rich in oxygen-containing functional groups such as alkoxy, hydroxyl, and carboxyl groups [14, 15] and, hence, can be well dispersed in polar solvents. However, the formation of reduced GO in aqueous solution results in aggregation of sheets due to hydrophobic nature and induces strong π-π interactions when the oxygen-containing functional groups are removed during the reduction process [16]. Important drawbacks in the synthesis of graphene are difficulty in isolating single layer and its tendency to curl, fold, and corrugate due to the flexibility of sheets [17]. The large folds arise during processing [18], whereas smaller ripples tend to be inherent in the structure of isolated layers [19]. As a result, graphene shows lower surface area and conductivity compared to the predicted theoretical value. Hence, preparation of individual graphene sheets is rather critical. On the other hand, carbon nanotubes (CNTs), consisting of cylindrical graphene sheets with nanometer diameter, have high mechanical strength and chemical stability, good electrical conductivity, rich optical properties, and high surface area. Therefore, CNTs constitute important materials as well as electrodes for sensing applications [20]. Electrical conductivity of CNTs is also affected due to the nonuniform contact and discontinuities between all the CNTs in the heterogeneous structure [21], thereby limiting their application as sensors [17, 22–24]. Therefore, an intelligent and unique graphene-carbon nanotube hybrid film, consisting of CNTs connected perpendicularly to graphene layers, could overcome some of the shortcomings and limitations of individual components [25–29]. Thus, many efforts have been made so as to obtain graphene-carbon nanotube hybrids by different methods of synthesis [25–32].

Gamma (γ) radiations have been used for many years as a competitive method to develop new materials, metal nanoparticles, and their composites [33–35]. Advantages of this technique over the other methods are self-generation of reducing agent, avoiding the use of toxic reducing agents such as hydrazine, simultaneous control of ion reduction and suppression of undesired oxidation products [33], formation of products under ambient conditions, simplicity, and economic.

In the present paper, an efficient, highly reproducible, and clean route towards synthesis of three-dimensional graphene-multiwalled carbon nanotube (G-MWCNT) hybrids has been reported. The hybridization of GO and acid functional multiwalled carbon nanotubes (f-MWCNTs) was carried out by γ-ray irradiation of the deoxygenated mixture of GO and MWCNTs in alcohol-water solution (Figure 1). Probable mechanism involving the formation of hybrid has been proposed. The differences observed in the resistance of the hybrid nanomaterials indicate that GO : MWCNTs ratio can further be optimized to improve the interface and nanostructures. Additionally, the electrocatalytic behavior of G-MWCNTs hybrids with different ratios of GO and MWCNTs has been examined. The G-MWCNTs hybrids show an improvement in electrocatalytic properties in comparison to each of the individual starting materials. The highest activity is observed for 1 : 1 hybrid G-MWCNTs. Increase in ratio to 1 : 3 does not show significant difference. Therefore, performance of 1 : 1 G-MWCNTs hybrid has been investigated as an amperometric glucose sensor.

2. Experimental

2.1. Materials

Extra pure graphite powder and MWCNTs (carbon purity: min. 95%, number of walls: 3–15, outer diameter: 5–20 nm, inner diameter: 2–6 nm, and length: 1–10 μm) were supplied by LOBA-Chemie and Reinste Nano Ventures Pvt. Ltd. (Delhi, India), respectively. Concentrated sulphuric acid and 30% hydrogen peroxide (H₂O₂) solution were from Qualigens (India). Alcohols (methanol, ethanol, isopropanol, and tert-butyl alcohol), KMnO₄, concentrated HCl, and HNO₃ were obtained from SD-Fine Chemical (SDFCL) (India). Sodium nitrate was purchased from Sigma-Aldrich (USA).

2.2. Instrument

The ⁶⁰Co γ-source was from the Department of Chemistry, University of Pune, supplied by BARC (Bhabha Atomic Research Center), Mumbai, India, with a dose rate of 3.95 Gy min⁻¹. The solutions were sonicated using a sonicator supplied by IMECO, India (34 KHz frequency, 500 W). Voltammetric measurements were performed on a Potentiostat/Galvanostat (model 263-A, EG&G USA) controlled by power suite software package and GPIB interface, in a conventional three-electrode system, together with a Pt loop as counter and Ag/AgCl (saturated KCl), as a reference electrode. Bare glassy carbon (GC) and GC modified with GO, -COOH functionalized multiwall carbon nanotubes (f-MWCNTs), and G-MWCNT hybrids electrodes were used as working electrodes. All measurements were performed in air atmosphere and room temperature. Prior to experiments, GC electrodes were polished with 0.3 and 0.05 μm alumina and rinsed with copious amount of Milli-Q water.

2.3. Synthesis of GO

GO was synthesized from graphite powder using modified Hummer’s method [36]. In brief, 1 g of graphite and 0.5 g of sodium nitrate were added in 23 mL of concentrated sulphuric acid under constant stirring. KMnO₄ (3 g) was added gradually to the above solution while keeping the temperature less than 20°C to prevent overheating and explosion. The mixture was stirred at 35°C for 1 h and the resulting solution was diluted by adding 500 mL of double distilled water under vigorous stirring. To ensure the completion of reaction with KMnO₄, the suspension was further treated with 30% H₂O₂ solution (5 mL). The graphene oxide sheets thus obtained were washed with HCl and H₂O, followed by filtration and drying.

2.4. Synthesis of f-MWCNTs

f-MWCNTs (functionalized with COOH groups) were synthesized by refluxing purified MWCNTs in concentrated HNO₃ (ca. 15.8 M) for 8 h.

2.5. Synthesis of G-MWCNT Hybrids

G-MWCNT hybrids were prepared by γ-irradiation method with three different weight ratios of 3 : 1, 1 : 1, and 1 : 3 (ratio of GO to MWCNTs). Initially, appropriate amount of GO was dispersed in Milli-Q water (1 mg mL⁻¹ of solid) by sonication (1 h) followed by addition of f-MWCNTs and alcohol (methanol, ethanol, isopropanol, or tert-butanol); the mixture was further sonicated for 30 min. The homogenous suspension was transferred into a glass bottle fitted with a septum, bubbled with nitrogen gas for 10 min to remove the dissolved oxygen, and then irradiated at room temperature for different time intervals (12 h–60 h, the corresponding doses being 2.84, 5.70, 11.38, and 14.22 kGy, resp.) at a dose rate of 3.95 Gy min⁻¹. The product thus obtained was collected, washed with Milli-Q (18 MΩ cm⁻¹) water, and dried under vacuum. UV-Vis spectra of samples (S1) indicated significant effect on the extent of reduction of GO + f-MWCNTs; the best conversion was observed for a total dose of 11.38 kGy, and hence further experiments were carried out at a dose of 11.38 kGy. Results for f-MWCNTs, GO, and GO + f-MWCNTs (1 : 1) irradiated at 11.38 kGy in ethanol/water solution are discussed in detail with other systems included wherever necessary.

2.6. Preparation of Modified GC Electrodes

GC electrode (3.0 mm diameter) was polished with 0.3 and 0.05 μm alumina slurries to obtain a mirror-like surface and rinsed with Milli-Q water and dried. Fresh dispersions of GO, f-MWCNTs, and G-MWCNTs were prepared by adding 1.0 mg of sample in 1.0 mL of Milli-Q water followed by sonication. From this, 10 μL of solution was drop-casted on the precleaned GC disk electrode and dried under vacuum at room temperature to obtain modified GC electrodes. Bare GC and modified electrodes were used for electrochemical measurements.

2.7. Characterization Techniques

Fourier transform infrared (FTIR) spectra of all the samples were recorded on a FTIR spectrophotometer (Thermo Scientific NICOLET 6700) using KBr as the mulling agent. Ultra violet-visible (UV-Vis) and photoluminescence (PL) spectra of the samples were obtained on a UV-Vis spectrophotometer (PerkinElmer LAMBDA 950) and spectrofluorometer (JASCO, FP8300), respectively. X-ray diffraction (XRD) analysis of powders was carried out on a Bruker AXSD-8 advance X-ray diffractometer with monochromatic radiation ( Å). Data were collected from 10° to 60° at a scan rate of 0.1° min⁻¹. The morphologies of the samples were observed under scanning electron microscope (SEM, JEOL JSM-6360) and transmission electron microscope (TEM, TECNAT G2 20ULTRA-TWIN, FEI instrument). Suspensions of the samples in Milli-Q water were loaded on grids of 200 mesh size. Micro-Raman spectra of the samples were recorded by using HORIBA Jobin Yvon (France Instrument), at 532 nm laser power 1.7 mW, 100x objective lens and 0.9 NA. HAMEG programmable LCR-Bridge hm8118 was used to measure the resistance of the samples. For measurement of resistance, pellets of the samples (1 cm² and 500 μm in thickness) were prepared by placing 50 mg of each powder between two iron plates of a die and compressed at a pressure of 78 KN.

3. Results and Discussion

3.1. Spectroscopic Characterization

The FTIR spectra of GO, f-MWCNTs, GO + f-MWCNTs (physical mixture), and G-MWCNTs are given in Figure 2(a). Spectrum of GO exhibits peaks at 1622, 1730, and 1035 cm⁻¹ corresponding to C=C, C=O, and C–O stretching, respectively. Also, the broad band at 3340 cm⁻¹ is attributed to O–H stretching mode of intercalated water [15]. On the other hand, spectrum related to f-MWCNTs (Figure 2(a)) shows two strong peaks at 3500 and 1710 cm⁻¹ representing O–H and C=O stretching, respectively. The spectrum of GO + f-MWCNTs exhibits bands similar as for GO, while, in the case of G-MWCNTs hybrid material (Figure 2(a)), the characteristic absorption bands of GO, f-MWCNTs, and GO + f-MWCNTs [37] are suppressed drastically. However, two new peaks are observed at ~1450 and ~1580 cm⁻¹ that can be attributed to the C=C stretching of aromatic ring indicating the formation of G-MWCNTs hybrid.

(a)

(b)

These results were further confirmed by UV-Vis analysis of the samples (Figure 2(b)). The peak observed for GO at 230 nm (spectrum (A)) represents the transitions of C–C aromatic ring, while the shoulder at 308 nm corresponds to transition of C=O bond [38, 39]. In case of f-MWCNTs the absorption peak observed at ~260 nm (spectrum (B)) is attributable to the transitions of f-MWCNTs [40, 41]. However, the spectrum of G-MWCNTs hybrid (spectrum (C)) shows distinctly different nature compared to GO or f-MWCNTs. This spectrum consists of four peaks at 208, 225, 275, and 281 nm. To understand the origin of these new peaks, UV-Vis spectrum of unirradiated solution of GO + f-MWCNTs (physical mixture in ethanol-water, Figure 2(b) spectrum (D)) and irradiated samples of GO (spectrum (E)) and f-MWCNTs (spectrum (F)) were recorded. From the results, it is observed that, in case of physical mixture, the spectrum shows the features similar to GO. On the contrary, GO after irradiation exhibits a peak at 275 nm, while f-MWCNTs show peaks at 208, 225, and 281 nm. These results justify the formation of hybrid after irradiation (spectrum (C)). The considerable red shift in peaks (230 to 275 for GO and 260 to 281 for f-MWCNTs) in the hybrid sample is due to increase in electron density and structural ordering consistent with the restoration of sp² carbon atoms [29, 32]. Further, the red shift confirms the π-π stacking interactions between the aromatic basal planes of GO and MWCNTs. Apart from this, the new peaks at 208 and 225 nm can be attributed to the formation of C–H bonds simultaneous to C–C bond breaking [42].

To verify whether the GO nanosheets are electronically coupled to the MWCNTs instead of physical attachment, the photoluminescence (PL) spectra of GO, f-MWCNTs, GO + f-MWCNTs, and G-MWCNTs were obtained at an excitation wavelength of 240 nm and the results are compared in Figure 3. As seen from the figure, the PL spectrum of GO and GO + f-MWCNTs (Figure 3, solid and dotted line) exhibits a strong peak at ~470 nm that can be correlated to the transition of GO. The origin of a sharp emission peak at ~567 nm can be ascribed to the C–O, C=O, and O=C–OH functionalized groups [43].

Similarly, intense emission is observed for f-MWCNTs (Figure 3 dashed line) [44]. On the other hand, in case of G-MWCNTs hybrid significant quenching of the PL spectrum is observed (Figure 3, dashed-dotted line and inset) which could be due to the following reasons: (i) the emission from graphene being quenched due to absorption of electrons by MWCNTs (excellent electron acceptors) [32], (ii) removal of functional groups from GO and f-MWCNTs after irradiation, and (iii) formation of new sp² clusters [43] resulting in the blue shift observed in the spectrum (470 nm in GO to 466 nm in G-MWCNTs hybrid).

3.2. Crystallographic and Structural Analysis

The X-ray diffractograms of GO (A), GO + f-MWCNTs (B), f-MWCNTs (C), and G-MWCNTs hybrid (D) are displayed in Figure 4(a). As observed from the figure, GO and GO + f-MWCNTs (Figures 4 and 4) show a single peak at 11.36° (d-spacing 0.767 nm) and f-MWCNTs (Figure 4(C)) exhibit two peaks at 26.13° (d-spacing: 0.339 nm) and 43.48° (d-spacing 0.206 nm), while, in case of G-MWCNTs hybrid (Figure 4(D)), four peaks are observed at 11.17°, 12.21°, 25.80°, and 42.621° (d-spacing 0.790, 0.724, 0.840, and 0.210 nm, resp.) indicating the presence of both constituents.

(a)

(b)

Presence of four peaks in the hybrid with slight shift with reference to those observed in individual substances together with slight increase in d-spacing confirms the formation of new structure. It has been reported that, after irradiation and removal of oxygen-containing functional groups, graphene oxide shrinks and the interlayer spacing decreases [45]. However, in the present reaction, at the time of reduction (during irradiation) MWCNTs are introduced between the graphene layers, and they avoid stacking up of graphene layers,therefore interlayer spacing does not show significant changes. It is worth noting that the data for GO and f-MWCNTs are in good agreement with the previous reports [28, 46]. The electronic and crystallographic structures of the samples were evaluated by micro-Raman spectroscopy. The Raman spectra of carbon materials show three well-known peaks called D, G, and 2D observed at ~1340, ~1540, and ~2650 cm⁻¹, respectively. The G peak corresponds to the optical phonons at the Brillouin zone center and represents the bond stretching of sp² carbon pairs in both rings and chains. The D peak corresponds to the breathing mode of sp² atoms in aromatic rings indicating the presence of defects [31, 47] and 2D band corresponds to second-order dispersion, a characteristic feature of two-phonon double resonance process. Figure 4(b) illustrates the typical micro-Raman spectra of f-MWCNTs, GO, GO + f-MWCNTs, and G-MWCNTs samples obtained at an excitation wavelength of 532 nm. Three distinct peaks are observed in each sample corresponding to D band, G band, and 2D band, respectively, as mentioned earlier. In the Raman spectra the D/G and 2D/D + G intensity ratios (/ and /) are usually used to evaluate the average size of crystalline sp² domains and defect densities in graphene sheets [32]. However, the / and / ratios of G-MWCNTs hybrid (1.30 and 4.10, resp.) are remarkably greater than those of GO (1.03 and 1.62) and GO + f-MWCNTs (1.06 and 1.62) indicating higher degree of topological disorder and defect density together with higher degree of crystallinity within G-MWCNTs hybrid material in which a larger number of smaller sized graphitic demines are present in new hybrid materials. Also, the width of D and 2D bands for G-MWCNTs (Figure 4(b) inset) is narrower than that of the starting materials (GO and f-MWCNTs) [48]. These results indicate the presence of defects caused by irradiation in G-MWCNTs hybrid material which leads to an improved electron transfer as confirmed from the electrochemical measurement discussed in Section 3.5.

Further, on radiolysis of water, γ-ray irradiation decomposes water molecules to both oxidative () and reductive ( and ) species , whereas alcohols act as radical scavengers and thereby convert into reducing radicals which provides a reducing medium for chemical reaction to occur under γ-ray irradiation in the absence of oxygen (oxygen support formation of strong oxidative products such as H₂O₂ and and ) [49]: where RH corresponds to methanol, ethanol, isopropanol, and tert-butanol. However, to study the effect of different alcohol structures on the γ-ray irradiation reaction, a variety of alcohols (methanol, ethanol, isopropanol, and tert-butanol) with 1 : 1 (V/V) ratio with water as a solvent medium were tested. The results revealed that ethanol is the most effective in this reaction system (S2, S3). This can be related to the differences in the rate constants of alcohols for scavenging hydroxyl radicals where ethanol exhibits the highest rate constant in contrast with other alcohols [50]. Alcohol radicals react with the oxygen atoms of the functional groups (epoxide, hydroxyl present on GO, or f-MWCNTs) and carbon radicals are formed. Thereafter, the carbon radicals combine with hydrogen radicals present in the system and after decarboxylation reaction C=C bonds are formed in G-MWCNTs.

3.3. Morphology

Morphology of the samples was studied with the help of SEM and TEM (Figures 5, 6, and 7).

(a)

(b)

(c)

The SEM image of GO (Figure 5(a)) is seen to consist of randomly aggregated wrinkled sheets closely associated with each other. This feature is in agreement with the TEM image of GO (Figure 5(c)). The SEM image of MWCNTs shows dense structure comprised of randomly aggregated tubules (Figure 5(b)).

The SEM images of G-MWCNT hybrids (3 : 1, 1 : 1, and 1 : 3 ratios) are shown in Figure 6 (a1, a2), (b1, b2), and (c1, c2), respectively. As observed from the micrographs, the MWCNTs are seen to be incorporated into the graphene layers and the surface morphology exhibits a mixed structure with MWCNTs dispersed between different GO sheets. This can be due to the possible interactions between hydrophobic region of GO and the side walls of f-MWCNTs.

These interactions avoid stacking up of MWCNTs and keep the dispersion of G-MWCNTs stable for longer time (at least 8 months). However, 1 : 1 ratio (b1 and b2) shows uniform distribution of graphene layers and MWCNTs compared to that observed at other ratios. In case of 1 : 3 ratio (a1, a2) the GO sheets are seen to be covered by a very thin layer of MWCNTs, while, at 3 : 1 ratio (c1, c2), agglomeration of MWCNTs on GO nanosheets can be noted. These observations are confirmed from the TEM images (Figure 7) of GO-MWCNTs 1 : 3 (a1, a2), 1 : 1 (b1, b2), and 1 : 3 (c1, c2) ratios.

3.4. Electrical Resistance

The electrical resistance of the samples was measured to evaluate the conductivity of the synthesized nanomaterials and also the connectivity of layers along the edges in case of G-MWCNTs; Figure S4 in Supplementary Material available online at http://dx.doi.org/10.1155/2014/903872 shows the bar diagram of resistance versus sample (GO, f-MWCNTs, and G-MWCNTs 3 : 1, G-MWCNTs 1 : 1, and G-MWCNTs 1 : 3). It can be seen that GO shows the highest resistance (6 kΩ cm⁻¹) due to the presence of hydroxyl and carboxyl functional groups. But f-MWCNTs show significantly lower resistance (0.52 kΩ cm⁻¹) than GO. However, among the hybrid nanomaterials, the resistance of G-MWCNTs 1 : 1 is significantly lower (~0.006 kΩ cm⁻¹) compared to the resistance of G-MWCNT 3 : 1 (3 kΩ cm⁻¹). Resistance obtained for G-MWCNT 1 : 3 (~0.004) is similar as for 1 : 1 ratio. These results reveal that G-MWCNTs 1 : 1 and 1 : 3 ratios are highly conducting in nature which is perhaps due to the strong coupling between graphene sheets and carbon nanotubes [27].

The results of all the above characterizations confirm the formation of new hybrid structure containing grapheme and MWCNTs.

3.5. Electrochemical Analysis

The electrochemical response of G-MWCNT hybrids (1 : 3, 1 : 1, and 3 : 1 ratios), GO, and f-MWCNTs were investigated by using K₃Fe(CN)₆ as the redox system due to its sensitivity/insensitivity to the electronic properties, surface microstructure, and surface chemistry of carbon electrodes [51].

Figure 8(a) shows the electrochemical response of K₃Fe (CN)₆ [5 mM] and KCl [0.5 mM] at GC bare, GO, f-MWCNTs, G-MWCNTs (3 : 1), G-MWCNTs (1 : 1), and G-MWCNTs (1 : 3) modified electrodes at a scan rate of 100 mVs⁻¹. The cyclic voltammogram of K₃Fe (CN)₆ is apparently improved at G-MWCNTs 1 : 1 and 1 : 3 ratios modified electrode, reflected by the enhancement in the peak currents () and a decrease in the peak to peak potential [ΔEp] compared to that of GO modified electrode. These results signify that the electronic structure and the surface properties of G-MWCNTs modified electrode are advantageous for electron transfer [51, 52] which is attributed to the strong coupling between graphene sheets and carbon nanotubes [27]. Figure 8(b) depicts the amperometric responses for GC, GO, f-MWCNTs, and G-MWCNTs modified electrodes with successive addition of glucose concentrations (0.1–18 mM) at an applied potential of +0.6 V (S5) versus Hg/HgO in 0.1 M NaOH. The amperometric response of G-MWCNTs modified electrode exhibits a linear range ( = 0.985) from 0.1 mM to 14 mM (S6), with sensitivity and detection limit of 12.5 μAmM⁻¹ cm⁻² and 1.45 μM, respectively (S7). The reproducibility of the sensor was determined by conducting 4 successive amperometric measurements of glucose using single G-MWCNTs modified electrode (S8). The relative standard deviations (R.S.D.) of the reproducible currents (S9) show that the electrode was not poisoned by the oxidation products and is highly reproducible. Oxidizable species, such as ascorbic acid (AA) and uric acid (UA), usually coexist with glucose in biological fluids on different electrodes, particularly on nonenzymatic glucose sensors [53].

(a)

(b)

Figure 8

(a) CVs of bare GC electrode and that modified with GO, f-MWCNTs, G-MWCNTs (3 : 1), G-MWCNTs (1 : 1), and G-MWCNTs (1 : 3). The experiments were carried out in 5.0 mM K₃[Fe(CN)₆] containing 1.0 M KCl and the potentials were applied versus Ag/AgCl reference electrode at a scan rate of 100 mVs⁻¹. (b) Amperometric responses of GC, GO, f-MWCNTs, and G-MWCNTs modified electrodes for successive addition of glucose concentrations (0.1–18 mM) at an applied potential of +0.6 V, versus Hg/HgO in 0.1 M NaOH.

The normal physiological level of glucose is 3–8 mM, which is much higher than that of the interfering species, AA, and UA (~0.1 mM). However, electron transfer rates of the interfering species are highly greater than that of glucose. Consequently, their oxidation currents are comparable to that from highly concentrated glucose. Therefore, the amperometric responses of the modified electrode at +0.6 V in solutions of 0.1 M NaOH for 0.1 mM UA, 0.1 mM AA, and 3 mM glucose were evaluated. For a better comparison, the response current of 3 mM glucose is set as 100%, and the responses of the interfering species are normalized by this value. The current responses obtained for UA and AA were ~0.10 μA and ~0.12 μA, 8.06% and 9.60%, respectively, which are significantly lower as compared to that of glucose (~1.24 μA) (S10). The results show that the interference from UA and AA is negligible.

These results indicate that the selectivity of G-MWCNTs is good enough to be used as a sensor for glucose. The batch-to-batch reproducibility was estimated from the current responses of 6 different sensors toward 3.0 mM glucose, and an RSD of 4.89% was obtained, indicative of the reliability of the proposed method. The long-term stability is also a significant parameter for evaluating the performance of the sensor. A response current of 3 mM glucose was determined every two days. The results show that the response current is ~75.30% of its initial value after 15 days (S11), which indicate that the stability of the sensor is good.

4. Conclusion

The γ-ray irradiation method appears to be a clean, simple, and cost-effective method to synthesize highly stable G-MWCNT hybrid nanomaterials. Characterization results proved that the G-MWCNT hybrid shows significant decrease in the self-aggregation and stacking of GO and MWCNTs due to appropriate coupling and interconnected network between MWCNTs and GO layers. This results in an increase in the stability, electrocatalytic activity, and electrical conductivity of hybrid nanomaterial compared to GO and MWCNTs individually. The amperometric sensor based on the G-MWCNTs modified electrode exhibits sensitivity of 12.5 μAmM⁻¹ cm⁻² and low detection limit 1.45 μM, with a linear range from 0.1 mM to 14 mM ( = 0.985) and negligible interference due to the presence of ascorbic acid and uric acid. These improvements in the properties of G-MWCNTs qualify it as an important material to develop electrical as well as electrochemical sensing devices. Therefore, it appears to be promising for the fabrication of sensors based on the G-MWCNTs hybrid for other applications.

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

Acknowledgments

The financial supports provided by Department of Chemistry, University of Pune, and University of Tehran are gratefully appreciated. The authors acknowledge CNQS, Department of Physics, University of Pune, for XRD, SEM, and FTIR facilities and Professor Pavankumar, IISER, Pune, for Raman spectra.

Supplementary Materials

Figure S1: UV-Vis spectra of un-irradiated and irradiated GO +MWCNTs obtained in water-ethanol solutions for different gamma doses. Figure S2: UV-Vis spectra obtained before (dashed line) and after (solid line) γ irradiation of 1:1 (V/V) water-alcohol solvent mixtures: methanol (a) ethanol (b) isopropanol (c) and tert-butanol(d). Figure S3: PL spectrum of G-MWCNTs after γ irradiation using 1:1 water-alcohol solvent mixtures tert-butanol (a), iso-propanol (b), methanol (c) and ethanol (d). Figure S4: Comparison between the resistances of GO, f-MWCNTs, G-MWCNTs (3:1), G-MWCNTs (1:1) and G-MWCNTs (1:3). Figure S5: Amperometric responses of G-MWCNTs modified electrodes at various applied potentials (+0.4 to +0.7 V) in presence of 2 mM glucose solution. Error bars show variation in result for four amperometric experiments at each potential. Figure S6: Calibration curves obtained from amperometric response for glucose sensing at (from bottom to top) GO, f-MWCNTs and G-MWCNTs modified electrodes. S7: Linear equation. Figure S8: Calibration curve of G-MWCNTs modified electrode with error bars obtained for four successive amperometric measurements of glucose under similar conditions. S9: Relative standard deviations (RSD) for four successive amperometric measurements of glucose with G-MWCNTs modified electrode. Figure S10: The amperometric response of G-MWCNTs modified electrode to the 0.1 mM AA, 0.1 mM UA (interferences), 0.1 and 3 mM glucose. Figure S11: Amperometric response current of G-MWCNTs modified electrode as a function of Time(every two day) measured at +0.6 V for 3 mM glucose concentration.

Supplementary Materials

References

S. Park, J. W. Suk, J. An et al., “The effect of concentration of graphene nanoplatelets on mechanical and electrical properties of reduced graphene oxide papers,” Carbon, vol. 50, no. 12, pp. 4573–4578, 2012.
View at: Publisher Site | Google Scholar
W. Wei and X. Qu, “Extraordinary physical properties of functionalized graphene,” Small, vol. 8, no. 14, pp. 2138–2151, 2012.
View at: Publisher Site | Google Scholar
Y. Zhu, S. Murali, W. Cai et al., “Graphene and graphene oxide: synthesis, properties, and applications,” Advanced Materials, vol. 22, no. 35, pp. 3906–3924, 2010.
View at: Publisher Site | Google Scholar
N. O. Weiss, H. Zhou, L. Liao et al., “Graphene: an emerging electronic material,” Advanced Materials, vol. 24, no. 43, pp. 5782–5825, 2012.
View at: Publisher Site | Google Scholar
R. Ribeiro, J.-M. Poumirol, A. Cresti et al., “Unveiling the magnetic structure of graphene nanoribbons,” Physical Review Letters, vol. 107, no. 8, Article ID 086601, 5 pages, 2011.
View at: Publisher Site | Google Scholar
G. Jo, M. Choe, S. Lee, W. Park, Y. H. Kahng, and T. Lee, “The application of graphene as electrodes in electrical and optical devices,” Nanotechnology, vol. 23, no. 11, Article ID 112001, 20 pages, 2012.
View at: Publisher Site | Google Scholar
Q. Li, B. Guo, J. Yu et al., “Highly efficient visible-light-driven photocatalytic hydrogen production of CdS-cluster-decorated graphene nanosheets,” Journal of the American Chemical Society, vol. 133, no. 28, pp. 10878–10884, 2011.
View at: Publisher Site | Google Scholar
W. Qian, R. Hao, J. Zhou et al., “Exfoliated graphene-supported Pt and Pt-based alloys as electrocatalysts for direct methanol fuel cells,” Carbon, vol. 52, pp. 595–604, 2013.
View at: Publisher Site | Google Scholar
J. Yang and S. Gunasekaran, “Electrochemically reduced graphene oxide sheets for use in high performance supercapacitors,” Carbon, vol. 51, no. 1, pp. 36–44, 2013.
View at: Publisher Site | Google Scholar
Y. Shao, J. Wang, H. Wu, J. Liu, I. A. Aksay, and Y. Lin, “Graphene based electrochemical sensors and biosensors: a review,” Electroanalysis, vol. 22, no. 10, pp. 1027–1036, 2010.
View at: Publisher Site | Google Scholar
F. Liu, Y. Piao, K. S. Choi, and T. S. Seo, “Fabrication of free-standing graphene composite films as electrochemical biosensors,” Carbon, vol. 50, no. 1, pp. 123–133, 2012.
View at: Publisher Site | Google Scholar
M. Segal, “Selling graphene by the ton,” Nature Nanotechnology, vol. 4, no. 10, pp. 612–614, 2009.
View at: Publisher Site | Google Scholar
C. E. Banks, A. Crossley, C. Salter, S. J. Wilkins, and R. G. Compton, “Carbon nanotubes contain metal impurities which are responsible for the “electrocatalysis” seen at some nanotube-modified electrodes,” Angewandte Chemie—International Edition, vol. 45, no. 16, pp. 2533–2537, 2006.
View at: Publisher Site | Google Scholar
G. I. Titelman, V. Gelman, S. Bron, R. L. Khalfin, Y. Cohen, and H. Bianco-Peled, “Characteristics and microstructure of aqueous colloidal dispersions of graphite oxide,” Carbon, vol. 43, no. 3, pp. 641–649, 2005.
View at: Publisher Site | Google Scholar
H.-L. Guo, X.-F. Wang, Q.-Y. Qian, F.-B. Wang, and X.-H. Xia, “A green approach to the synthesis of graphene nanosheets,” ACS Nano, vol. 3, no. 9, pp. 2653–2659, 2009.
View at: Publisher Site | Google Scholar
G.-H. Moon, Y. Park, W. Kim, and W. Choi, “Photochemical loading of metal nanoparticles on reduced graphene oxide sheets using phosphotungstate,” Carbon, vol. 49, no. 11, pp. 3454–3462, 2011.
View at: Publisher Site | Google Scholar
W. Yang, K. R. Ratinac, S. R. Ringer, P. Thordarson, J. J. Gooding, and F. Braet, “Carbon nanomaterials in biosensors: should you use nanotubes or graphene,” Angewandte Chemie—International Edition, vol. 49, no. 12, pp. 2114–2138, 2010.
View at: Publisher Site | Google Scholar
Z. H. Ni, H. M. Wang, J. Kasim et al., “Graphene thickness determination using reflection and contrast spectroscopy,” Nano Letters, vol. 7, no. 9, pp. 2758–2763, 2007.
View at: Publisher Site | Google Scholar
J. C. Meyer, A. K. Geim, M. I. Katsnelson, K. S. Novoselov, T. J. Booth, and S. Roth, “The structure of suspended graphene sheets,” Nature, vol. 446, no. 7131, pp. 60–63, 2007.
View at: Publisher Site | Google Scholar
J. J. Gooding, A. Chou, J. Liu, D. Losic, J. G. Shapter, and D. B. Hibbert, “The effects of the lengths and orientations of single-walled carbon nanotubes on the electrochemistry of nanotube-modified electrodes,” Electrochemistry Communications, vol. 9, no. 7, pp. 1677–1683, 2007.
View at: Publisher Site | Google Scholar
P. Avouris, Z. Chen, and V. Perebeinos, “Carbon-based electronics,” Nature Nanotechnology, vol. 2, no. 10, pp. 605–615, 2007.
View at: Publisher Site | Google Scholar
M. Pumera, “Carbon nanotubes contain residual metal catalyst nanoparticles even after washing with nitric acid at elevated temperature because these metal nanoparticles are sheathed by several graphene sheets,” Langmuir, vol. 23, no. 11, pp. 6453–6458, 2007.
View at: Publisher Site | Google Scholar
C. P. Jones, K. Jurkschat, A. Crossley, R. G. Compton, B. L. Riehl, and C. E. Banks, “Use of high-purity metal-catalyst-free multiwalled carbon nanotubes to avoid potential experimental misinterpretations,” Langmuir, vol. 23, no. 18, pp. 9501–9504, 2007.
View at: Publisher Site | Google Scholar
K. Gong, S. Chakrabarti, and L. Dai, “Electrochemistry at carbon nanotube electrodes: is the nanotube tip more active than the sidewall?” Angewandte Chemie—International Edition, vol. 47, no. 29, pp. 5446–5450, 2008.
View at: Publisher Site | Google Scholar
M.-Y. Yen, M.-C. Hsiao, S.-H. Liao et al., “Preparation of graphene/multi-walled carbon nanotube hybrid and its use as photoanodes of dye-sensitized solar cells,” Carbon, vol. 49, no. 11, pp. 3597–3606, 2011.
View at: Publisher Site | Google Scholar
Z. Fan, J. Yan, L. Zhi et al., “A three-dimensional carbon nanotube/graphene sandwich and its application as electrode in supercapacitors,” Advanced Materials, vol. 22, no. 33, pp. 3723–3728, 2010.
View at: Publisher Site | Google Scholar
Y.-S. Kim, K. Kumar, F. T. Fisher, and E.-H. Yang, “Out-of-plane growth of CNTs on graphene for supercapacitor applications,” Nanotechnology, vol. 23, no. 1, Article ID 015301, 7 pages, 2012.
View at: Publisher Site | Google Scholar
S. Wooa, Y. R. Kima, T. D. Chunga, Y. Piaob, and H. Kimc, “Synthesis of a graphene-carbon nanotube composite and its electrochemical sensing of hydrogen peroxide,” Electrochim Acta, vol. 59, pp. 509–514, 2012.
View at: Google Scholar
V. Mani, B. Devadas, and S.-M. Chen, “Direct electrochemistry of glucose oxidase at electrochemically reduced graphene oxide-multiwalled carbon nanotubes hybrid material modified electrode for glucose biosensor,” Biosensors and Bioelectronics, vol. 41, no. 1, pp. 309–315, 2013.
View at: Publisher Site | Google Scholar
S. Das, R. Seelaboyina, V. Verma et al., “Synthesis and characterization of self-organized multilayered graphene-carbon nanotube hybrid films,” Journal of Materials Chemistry, vol. 21, no. 20, pp. 7289–7295, 2011.
View at: Publisher Site | Google Scholar
X. Dong, B. Li, A. Wei et al., “One-step growth of graphene-carbon nanotube hybrid materials by chemical vapor deposition,” Carbon, vol. 49, no. 9, pp. 2944–2949, 2011.
View at: Publisher Site | Google Scholar
X. Dong, G. Xing, M. B. Chan-Park et al., “The formation of a carbon nanotube-graphene oxide core-shell structure and its possible applications,” Carbon, vol. 49, no. 15, pp. 5071–5078, 2011.
View at: Publisher Site | Google Scholar
A. Henglein and D. Meisel, “Radiolytic control of the size of colloidal gold nanoparticles,” Langmuir, vol. 14, no. 26, pp. 7392–7396, 1998.
View at: Google Scholar
N. P. Bayramgil, “Synthesis, characterization and drug release behavior of poly(1-vinyl 1,2,4-triazole) hydrogels prepared by gamma irradiation,” Colloids and Surfaces B, vol. 97, pp. 182–189, 2012.
View at: Publisher Site | Google Scholar
J. V. Rojas and C. H. Castano, “Production of palladium nanoparticles supported on multiwalled carbon nanotubes by gamma irradiation,” Radiation Physics and Chemistry, vol. 81, no. 1, pp. 16–21, 2012.
View at: Publisher Site | Google Scholar
K. Krishnamoorthy, R. Mohan, and S.-J. Kim, “Graphene oxide as a photocatalytic material,” Applied Physics Letters, vol. 98, no. 24, Article ID 244101, 3 pages, 2011.
View at: Publisher Site | Google Scholar
C. Zhu, S. Guo, Y. Fang, and S. Dong, “Reducing sugar: new functional molecules for the green synthesis of graphene nanosheets,” ACS Nano, vol. 4, no. 4, pp. 2429–2437, 2010.
View at: Publisher Site | Google Scholar
K. S. Vasu, B. Chakraborty, S. Sampath, and A. K. Sood, “Probing top-gated field effect transistor of reduced graphene oxide monolayer made by dielectrophoresis,” Solid State Communications, vol. 150, no. 29-30, pp. 1295–1298, 2010.
View at: Publisher Site | Google Scholar
K. Krishnamoorthy, M. Veerapandian, R. Mohan, and S.-J. Kim, “Investigation of Raman and photoluminescence studies of reduced graphene oxide sheets,” Applied Physics A, vol. 106, no. 3, pp. 501–506, 2012.
View at: Publisher Site | Google Scholar
Z. Xu, N. Gao, and S. Dong, “Preparation and layer-by-layer self-assembly of positively charged multiwall carbon nanotubes,” Talanta, vol. 68, no. 3, pp. 753–758, 2006.
View at: Publisher Site | Google Scholar
S. J. Henley, R. A. Hatton, G. Y. Chen et al., “Enhancement of polymer luminescence by excitation-energy transfer from multi-walled carbon nanotubes,” Small, vol. 3, no. 11, pp. 1927–1933, 2007.
View at: Publisher Site | Google Scholar
W. Qian, J. Chen, L. Wei, L. Wu, and Q. Chen, “Gamma-ray irradiation-induced improvement of hydrogen adsorption in multi-walled carbon nanotubes,” Nano, vol. 4, no. 1, pp. 7–11, 2009.
View at: Publisher Site | Google Scholar
J. Shang, L. Ma, J. Li, W. Ai, T. Yu, and G. G. Gurzadyan, “The origin of fluorescence from graphene oxide,” Scientific Reports, vol. 2, pp. 792–800, 2012.
View at: Publisher Site | Google Scholar
Y. Lin, B. Zhou, R. B. Martin et al., “Visible luminescence of carbon nanotubes and dependence on functionalization,” Journal of Physical Chemistry B, vol. 109, no. 31, pp. 14779–14782, 2005.
View at: Publisher Site | Google Scholar
Q. Zhang, Y. Zhang, Z. Gao et al., “A facile synthesis of platinum nanoparticle decorated graphene by one-step γ-ray induced reduction for high rate supercapacitors,” Journal of Materials Chemistry C, vol. 1, no. 2, pp. 321–328, 2013.
View at: Publisher Site | Google Scholar
L. Zhang, J. Liang, Y. Huang, Y. Ma, Y. Wang, and Y. Chen, “Size-controlled synthesis of graphene oxide sheets on a large scale using chemical exfoliation,” Carbon, vol. 47, no. 14, pp. 3365–3368, 2009.
View at: Publisher Site | Google Scholar
G. Eda and M. Chhowalla, “Chemically derived graphene oxide: towards large-area thin-film electronics and optoelectronics,” Advanced Materials, vol. 22, no. 22, pp. 2392–2415, 2010.
View at: Publisher Site | Google Scholar
H. Wang, J. T. Robinson, X. Li, and H. Dai, “Solvothermal reduction of chemically exfoliated graphene sheets,” Journal of the American Chemical Society, vol. 131, no. 29, pp. 9910–9911, 2009.
View at: Publisher Site | Google Scholar
J. Belloni, M. Mostafavi, H. Remita, J.-L. Marignier, and M.-O. Delcourt, “Radiation-induced synthesis of mono- and multi-metallic clusters and nanocolloids,” New Journal of Chemistry, vol. 22, no. 11, pp. 1239–1255, 1998.
View at: Google Scholar
E. Janata, “Direct optical observation of the formation of some aliphatic alcohol radicals. A pulse radiolysis study,” Proceedings of the Indian Academy of Sciences, vol. 114, no. 6, pp. 731–737, 2002.
View at: Google Scholar
W.-J. Lin, C.-S. Liao, J.-H. Jhang, and Y.-C. Tsai, “Graphene modified basal and edge plane pyrolytic graphite electrodes for electrocatalytic oxidation of hydrogen peroxide and β-nicotinamide adenine dinucleotide,” Electrochemistry Communications, vol. 11, no. 11, pp. 2153–2156, 2009.
View at: Publisher Site | Google Scholar
R. L. McCreery, “Advanced carbon electrode materials for molecular electrochemistry,” Chemical Reviews, vol. 108, no. 7, pp. 2646–2687, 2008.
View at: Publisher Site | Google Scholar
L. Tang, Y. Wang, Y. Li, H. Feng, J. Lu, and J. Li, “Preparation, structure, and electrochemical properties of reduced graphene sheet films,” Advanced Functional Materials, vol. 19, no. 17, pp. 2782–2789, 2009.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2014 Leila Shahriary et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

3581

Downloads

2649

Citations