Research Article
Fabrication of Surface Level Cu/SiCp Nanocomposites by Friction Stir Processing Route
Figure 5
X-ray diffraction pattern of (a) nanosized SiCp and (b–d) nanocomposites at process parameter combinations.
(a) Nanosized SiCp |
(b) 500 rpm/50 mm/min/1° |
(c) 750 rpm/50 mm/min/2° |
(d) 1000 rpm/50 mm/min/1° |