Improvement of Cochineal Extract (<i>Dactylopius coccus</i> Costa) Properties Based on the Green Synthesis of Silver Nanoparticles for Application in Organic Devices

Stael, Carina; Cruz, Ricardo; Naranjo, Blanca; Debut, Alexis; Angulo, Yolanda

doi:https://doi.org/10.1155/2018/3751419

Journal of Nanotechnology

On this page

Abstract Introduction Materials and Methods Results and Discussion Conclusion Conflicts of Interest Acknowledgments Supplementary Materials References Copyright Related Articles

Special Issue

Nanoparticles for Environment, Engineering, and Nanomedicine

View this Special Issue

Research Article | Open Access

Volume 2018 | Article ID 3751419 | https://doi.org/10.1155/2018/3751419

Improvement of Cochineal Extract (Dactylopius coccus Costa) Properties Based on the Green Synthesis of Silver Nanoparticles for Application in Organic Devices

Carina Stael,¹Ricardo Cruz,¹Blanca Naranjo,¹Alexis Debut,¹and Yolanda Angulo¹

Academic Editor: Lee Blaney

Received18 Oct 2017

Revised11 Jan 2018

Accepted07 Feb 2018

Published21 May 2018

Abstract

The UV-Vis absorption and conductivity properties of the organic sample cochineal (Dactylopius coccus Costa) were modified by using it as a reducing agent in the biosynthesis of silver nanoparticles. This was done in a straightforward way in order to allow its possible application in organic devices. The biosynthesized solution exhibited a hybrid material with a UV-Vis absorbance range from 205 to 650 nm. The sizes of silver nanoparticles of the hybrid material were between 5 and 10 nm. X-ray diffraction (XRD) revealed silver structures, when samples were dried at 100°C. At 40°C, the structures detected were chlorargyrite (AgCl) and silver oxide (Ag₂O). The nucleation and subsequent growth of the hybrid thin film on the substrates indicated an increase of clusters and roughness in comparison to thin films made solely from cochineal. The thin films of hybrid materials showed an improvement of 40% in their electrical potential. The stability at room temperature demonstrated that the hybrid material could be useful as a potential candidate for photoactive thin films in organic devices.

1. Introduction

Organic semiconductors have witnessed considerable development in recent years, with increasing research activity on this class of materials and their potential applications. The interest in this area is to obtain new organic compounds with improved, more efficient properties for the manufacture of organic, light-emitting diodes (OLEDs) [1], organic photovoltaic cells (OPVs) [2, 3], and thin film transistors (TFTs) [4]. The biosynthesis of new hybrid structures using natural organic compounds for development of photoreactive compounds is straightforward and significantly reduces the cost of organic devices.

Cochineal insects (Dactylopius coccus C.) from the city of Loja, Ecuador, were used here to form a new hybrid structure. Cochineal is not only the main red dye used in Central America, but it was also used in Ecuador and Peru by the Incas, before the Spanish conquest. Cochineal is made up of 80% carminic acid (CA). In the 16th century, it was exported to Europe and began to replace the domestic kermes insect (Kermes vermilio) [5, 6]. Cochineal insects are nowadays widely used in the food industry to replace synthetic colorants, and its antioxidant properties have been well known for a long time [7, 8].

In this study, we observed the increased UV-Vis spectral absorbance and electrical conductivity of the natural pigment through biosynthetic silver nanoparticles [5]. To improve the optical and electrical properties of cochineal, it was used as the reducing agent during the biosynthesis of silver nanoparticles (AgNPs) without submitting the cochineal to any kind of separation of its primary compounds. The cochineal extract was used as the reducing agent for the biosynthesis of AgNPs, since green synthesis of the AgNPs has been an easy, affordable, inexpensive technique and is potentially not harmful to human health and the environment [9–14]. Different volumes of cochineal dye (pH = 12, [5]) in 1 ml of AgNO₃ solution (10 mM, pH = 5.6) were analyzed with UV-Vis spectrometry, Commission Internationale de l’Eclairage (CIE) chromaticity diagram, cyclic voltammetry (CV), scanning transmission electron microscopy (STEM), energy dispersive X-ray spectroscopy (EDS), dynamic light scattering (DLS), and X-ray diffraction (XRD). The surface morphology and electrical properties of the thin films were analyzed using atomic force microscopy (AFM). This suite of analytical tools facilitated the study of the thin films from multiple perspectives and explained their increased conductivity properties.

2. Materials and Methods

2.1. Materials

Dactylopius coccus Costa samples were obtained from the city of Loja, Ecuador. The insects, which were found in the tuna (fruit) of Opuntia ficus-indica, secrete a white and cottony substance that serves to protect them from external, environmental conditions. The interesting property of these insects is that they generate a natural red pigment inside their body. The goal of this research was to improve the properties of the cochineal by the synthesis of silver nanoparticles. The silver nitrate and all the solvents used in the sample preparation were obtained from Sigma-Aldrich (Missouri, United States).

2.2. Hybrid Material Synthesis

Ten grams (10.0 g) of the cochineal sample was dissolved in 3.0 L of methanol and distilled water (9 : 1, resp.). This solution was evaporated using a Rotavapor (Buchi R-220) at 40°C and a pressure of 44000 Pa before being vacuum-filtered (a filter paper of 0.45 μm). For the reduction of AgNO₃, the pigment was diluted with NaOH to obtain a pH of 12 [9]. For the biosynthesis of AgNPs, different volumes (0.1 ml and 0.4 ml) of the alkaline solution (cochineal at pH 12) were diluted with 1 ml of AgNO₃ solution (10 mM; pH = 5.6), and this mixture was incubated for 1 h at 40°C.

2.3. Physical and Chemical Characterization of the Hybrid Material

The stability of the nanoparticles in solution at room temperature was measured after 8 days using UV-Vis spectrometry (Analytik Jena S600). CIE chromaticity diagram was analyzed using OSRAM Sylvania, Inc. (2009) software. Cyclic voltammetry was done using a three-electrode system (Metrohm Autolab PGSTAT 128N). The working electrode was a carbon electrode; a calomel (Hg/HgCl) electrode was used as reference and a platinum strand served as the auxiliary electrode. The analyses were conducted in a background electrolyte solution of 0.1 M KCl. Prior to each analysis, dissolved oxygen in the KCl solution was removed by bubbling with N₂ (g) for 15 min. The voltammetry scan rate was 0.05 V·s⁻¹ at room temperature in the range from −1.2 to 1.2 V of the standard hydrogen electrode versus saturated calomel electrode (SHE versus SCE).

Particle size and morphology of the samples were analyzed by a scanning transmission electron microscope (TESCAN MIRA3) operating at an accelerating voltage of 25 kV equipped with a Bruker EDS XFlash 6130 detector. Dynamic light scattering (Horiba LB-550) was used to determine the hydrodynamic diameter of the AgNPs. All DLS measurements were performed at a 25°C fixed temperature.

Organic layers were grown onto quartz, silicon, and indium tin oxide (ITO)/glass substrates for the optical spectroscopy and morphology study of the samples’ thin films. Before spin coating (40°C) the thin films, the substrates were cleaned with detergent, rinsed with deionized water, sonicated in organic solvents and acetone, and rinsed with alcohol before being dried in a N₂ (g) stream. X-ray patterns of the thin films from different samples were collected on an Empyrean diffractometer (PANalytical) in the Bragg–Brentano configuration at 40 kV and 45 A with monochromatic X-rays of Cu K-alpha wavelength (λ = 1.541 Å). The morphology in the ScanAsyst mode and surface conductivity in the conductive atomic force microscopy mode of the thin films were studied with a Bruker Icon atomic force microscope.

3. Results and Discussion

3.1. Hybrid Material Characterization

The UV-Vis absorption spectra of the cochineal solutions were obtained at pH 3.8 and 12.0 (Figure 1(a)). This pH change improves the cochineal reducing properties, which are conducive for the formation of AgNPs. Both solutions were stable at room temperature throughout the analysis. The inset in Figure 1(a) shows the corresponding CIE chromaticity diagram. The chromaticity of the solutions changed as a function of pH (inset in Figure 1(a); pH 3.2: x = 0.318, y = 0.346; pH 12.0: x = 0.304, y = 0.372). Gaussian fitting of the curves (Figure 1(b), pH 3.2: χ² = 0.14; Figure 1(c), pH 12: χ² = 0.04) shows a red shift in their wavelengths and a decrease in their half width at half maximum (HWHM). These changes are due to the predominance of carminic acid in cochineal, which has an anthraquinone nucleus. When diluted in distilled water (pH = 3.8) or in methanol (pH = 12), maximum absorption peaks can be observed in three bands: 243∼243.5 nm, 280∼282 nm, and 324∼331 nm, respectively, with a slight bathochromic shift, but with a strong hypsochromic shift at a wavelength from 383.6 nm to 302.5 nm. This effect is caused not only by the carboxyl group in the C2 position but also by the deprotonation of hydroxyls in positions C3, C5, C6, and C8, which are stable at pH 12 and responsible for the hydroxyanthraquinone chromophore properties. The red color of the molecule is explained by the degree of oxidation of the anthraquinone nucleus with the maximum absorbance at 496 nm [15–17], similar to the one found in the analyzed extract.

(a)

(b)

(c)

Figures 2(a) and 2(b) show absorption spectra of the biosynthesis of silver nanoparticles (AgNPs) from the cochineal extract, and the difference of the two spectra is the volume of cochineal. Insets in Figures 2(a) and 2(b) show the time-dependent stability of AgNPs (Figure 2(a): λ = 443 nm; Figure 2(b): λ = 428.5 nm). From Figure 2(a), one can observe that the sample prepared with 0.1 ml of the cochineal extract in 1 ml of silver nitrate reached stability at 72 h. On the contrary, Figure 2(b) shows faster kinetics for the biosynthesis of AgNPs from 0.4 ml of the cochineal extracts in 1 ml of silver nitrate, reaching stability around 24 h. The faster reaction kinetics of the last sample (0.4 ml of the cochineal extract in 1 ml of AgNO₃) likely stems from the fourfold increase in the reducing agent volume.

(a)

(b)

Figure 3(a) shows the UV-Vis spectra of the cochineal extract at pH 12.0 and after the biosynthesis of AgNPs on the eighth day. The inset in Figure 3(a) shows the CIE chromaticity diagram for the extracts at pH 12 (x = 0.251, y = 0.406) and the biosynthesis of AgNPs with 0.1 ml (x = 0.255, y = 0.238) and 0.4 ml (x = 0.275, y = 0.315) of the cochineal extract. The results show that the biosynthesis of AgNPs with 0.4 ml of the cochineal extract has greater spectral absorbance in the UV-Vis region, indicating a possible candidate for photoactive thin films of organic solar cells [18–21].

(a)

(b)

(c)

Figure 3

(a) Comparison of UV-Vis spectra of cochineal pigment (pH 12.0), silver nitrate, and AgNPs synthesized from (b) 0.1 ml and (c) 0.4 ml of the cochineal extract. The inset in (a) shows the corresponding CIE chromaticity diagram: cochineal pigment (pH 12.0, x = 0.251, y = 0.406), AgNPs (0.1 ml of the cochineal extract, x = 0.255, y = 0.238), and AgNPs (0.4 ml of the cochineal extract, x = 0.275, y = 0.315). Linear least-squares models (dashed red lines) of UV-Vis spectra (solid blue lines) with Gaussian components are shown in (b) AgNPs (0.1 ml of the cochineal extract) and (c) AgNPs (0.4 ml of the cochineal extract).

According to Mie’s theory, optical properties of metal nanoparticles are dominated by localized surface plasmon resonance (LSPR), and the profile of LSPR bands depends on the shape of the particle [21, 22]. The AgNP mixture with 0.4 ml of the cochineal extract presented a single surface plasmon absorption band at 428.5 nm (Figure 3(c) and Table 1); however, the AgNP mixture with 0.1 ml of the cochineal extract presented two plasmon bands at 443 nm with a weak shoulder peak at 379 nm (Figure 3(b) and Table 1), possibly suggesting nonspherical (irregularly shaped) particles [22, 23]. Hence, the two plasmon bands (at 379 nm and 433 nm; Table 1) presented by the Gaussian fit shown in Figure 3(b) (0.1 ml of the cochineal extract) imply the nonspherical nanoparticles [21, 22–24]. The nanoparticles formed with 0.4 ml of the cochineal extract are more likely being spherical in shape because only one band was observed at 428.5 nm (Figure 3(c) and Table 1). As the number of plasmon bands observed is indicative of the shape of the nanoparticles, those nanoparticles formed in the presence of 0.4 ml of the cochineal extract had a higher probability of being spherical in shape [21].

3.2. Physical and Chemical Characterization of the Hybrid Material

The spherical AgNPs were also indicated by a STEM image in the sample synthesized from 0.4 ml of the cochineal extract (Figure 4(b)) in agreement with the suggested results obtained of the LSPR bands. In the other sample, Figure 4(a) shows a diffuse image with very small particle sizes and, therefore, inconclusive results about the true morphology of the particles. EDS (Figure 4(c)) analysis confirmed that the particles were composed of silver when synthesized from cochineal solutions. The weight percentage of Ag in each sample (0.1 ml and 0.4 ml of the cochineal extract) was similar because the volume of silver nitrate in the reagent was the same (Table 2). The size distribution of the different AgNPs ranged between 5 and 15 nm using DLS (Figure 4(d)).

(a)

(b)

(c)

(d)

The X-ray pattern was recorded from the same batch of samples (Figure 5). The inset in Figure 5 shows ApNPs synthesis with 0.4 mL of the cochineal extract, which was dried at 100°C as well as a graphical representation of the scattering of X-rays in the film. When the thin film was dried at 40°C, chlorargyrite (AgCl), silver oxide (Ag₂O), and other structures were observed (Table 3). The reason is that the organic matrix which surrounds the AgNPs produces increased scattering of X-rays, limiting observation of the silver crystals. When the thin film was dried at 100°C, silver crystals were detected (Table 3) [25–28]. The clear detection of silver crystals was observed due to the degradation of organic compounds at that temperature. The relation detected by XRD for the two volumes of the cochineal extract of 0.4 ml and 0.1 ml for AgCl and Ag₂O shows that the AgNPs formation was greater at the higher cochineal volume, which was confirmed by STEM micrographs, the physical-chemical analysis by EDS, and UV-Vis absorption spectroscopy.

3.3. Cyclic Voltammetry Characterization

Figure 6 shows the cyclic voltammogram of the cochineal pigment and of the two hybrid materials within a potential window of −1.0 to 1.2 V. The cochineal extract exhibited no reduction peak; however, three oxidation peaks were observed at −0.14, −0.32, and −0.61 V in the aqueous medium. Curves b (0.1 ml of the cochineal extract) and c (0.4 ml of the cochineal extract) exhibit the reduction of AgNO₃ by oxidation of the cochineal pigment with concomitant formation of AgNPs. The two curves (b and c) exhibit the oxidation (+0.88 V) and reduction (−0.18 V) of the cochineal extract. 0.4 ml of the cochineal extract sample (curve c) also shows a reduction event occurring at −0.66 V. Curves b (0.1 ml of the cochineal extract) and c (0.4 ml of the cochineal extract) exhibit the reduction of the Ag⁺ ions to elemental Ag⁰ by cochineal oxidation leading to stable AgNPs; however, the two curves also show the contribution of AgNO₃. Likewise, the oxidation of Ag⁺ to Ag₂O is observed, especially in 0.1 ml of the cochineal extract sample in which the amount of reductant to AgNO₃ ratio was smaller. These results show that a higher volume of cochineal is required to avoid the formation of Ag₂O and ascertain the reduction of AgNO₃ with reasonable reaction kinetics [29, 30].

The reduction of AgNO₃ is probably due to electron transfer from carboxyl/hydroxyl groups of cochineal to Ag⁺ resulting in stable AgNPs. The energy gap and ionization potential of the biosynthesis of AgNPs from cochineal were estimated with optical and electrochemical techniques [31]. Based on these values, the highest occupied molecular orbital (HOMO) and lowest unoccupied molecular orbital (LUMO) energy levels could be determined (Table 4). These results show that the AgNPs synthesized from 0.4 ml of the cochineal extract have a smaller energy gap and thus have better photon absorbance (2.169 eV) than the corresponding AgNPs synthesized from 0.1 ml of the cochineal extract (2.669 eV) in the UV-Vis region.

3.4. AFM and Electrical Measurements

Figures 7(a)–7(d) show AFM images from the samples of the cochineal pigment and AgNPs (0.4 ml and 0.1 ml of the cochineal extract) on silicon. The roughness of the clusters was calculated to be 2.06 ± 0.19 nm (Figure 7(a), cochineal pigment), 5.94 ±1.30 nm (Figure 7(b), 0.4 ml of the cochineal extract sample), and 2.96 ± 0.35 nm (Figure 7(c), 0.1 ml of the cochineal extract sample). Figure 7(d) shows an enlargement of the AFM image of AgNPs synthesized from 0.4 ml of the cochineal extract on a silicon substrate. The differences between the nanoparticles from the two ((Figure 7(b), 0.1 ml of the cochineal extract) and (Figure 7(c), 0.4 ml of the cochineal extract)) are clearly observed by the surface roughness being less in the case of AgNPs with 0.1 ml of the cochineal extract compared to 0.4 ml of the cochineal extract, which might contribute to the size increase of the AgNPs due to cochineal adsorption. Studies show that, to obtain a good efficiency of a hybrid device, it must have roughness around 2 nm [32]. In this case, the 0.4 ml sample of the cochineal extract that exceeds this value due to the size of the AgNPs must undergo an optimization of the spin-coating technique. This finding is in agreement with the size distributions shown in Figure 4(d). The effect of the potential size regulation is demonstrated in Figure 7(e) for thin films of the cochineal pigment and AgNPs (0.4 and 0.1 ml of the cochineal extract). The potential offset is positive indicating the level of conductivity possible for each sample for application in organic devices.

(a)

(b)

(c)

(d)

(e)

4. Conclusion

This work demonstrates that, despite maintaining reaction time, temperature, and silver nitrate concentration, a change of the LSPR band of AgNPs was observed as a function of the amount of cochineal applied. The higher cochineal concentration (0.4 ml of the cochineal extract) generated spherical AgNPs of 5 to 10 nm and good stability at room temperature. The trace of Ag₂O observed in the sample (electrochemistry and XRD) probably stems from the concentration of cochineal used in the preparation process. If a slightly lowered concentration was used, incomplete reduction of silver nitrate is likely. Coating AgNPs with the cochineal pigment through direct biosynthesis improved the absorption spectrum in the UV-Vis range of the nanoparticles. The AgNPs in turn improve the electrical properties of the cochineal pigment converting it into a promising photoactive layer of organic solar cells.

Conflicts of Interest

The authors declare that they have no conflicts of interest.

Acknowledgments

This work was supported by a research grant (Grant no. 2014-PIT-034) of Universidad de las Fuerzas Armadas ESPE.

Supplementary Materials

Graphical abstract is included in this manuscript as a supplementary file. (Supplementary Materials)

References

G. Krucaite, L. Liu, D. Tavgeniene et al., “Electroactive polymers containing 3-arylcarbazolyl units as hole transporting materials for OLEDs,” Optical Materials, vol. 42, pp. 94–98, 2015.
View at: Publisher Site | Google Scholar
H. Duan, J. Yang, L. Fu et al., “Interface modification of organic photovoltaics by combining molybdenum oxide (MoOx) and molecular template layer,” Thin Solid Films, vol. 574, pp. 146–151, 2015.
View at: Publisher Site | Google Scholar
C. Chappaz-Gillot, S. Berson, R. Salazar et al., “Polymer solar cells with electrodeposited CuSC nanowires as new efficient hole transporting layer,” Solar Energy Materials and Solar Cells, vol. 120, pp. 163–167, 2014.
View at: Publisher Site | Google Scholar
G. Lopinski, N. Du, G. Dubey et al., “Cyanoethylated pullulan as a high-k solution processable polymer gate dielectric for SWCNT TFTs,” Organic Electronics, vol. 42, pp. 329–336, 2017.
View at: Publisher Site | Google Scholar
B. Kumar, K. Smita, Y. Angulo, and L. Cumbal, “Green synthesis of silver nanoparticles using natural dyes of cochineal,” Journal of Cluster Science, vol. 27, no. 2, pp. 703–713, 2016.
View at: Publisher Site | Google Scholar
M. Schoeser and J. Macdonald, Silk, Yale University Press, New Haven, CT, USA, 2007.
M. González, M. Gloria Lobo, J. Méndez, and A. Carnero, “Food control, detection of colour adulteration in cochineals by spectrophotometric determination of yellow and red pigment groups,” Food Control, vol. 16, no. 2, pp. 105–112, 2005.
View at: Publisher Site | Google Scholar
M. Shahid, S.-U. Islam, and F. Mohammad, “Recent advancements in natural dye applications: a review,” Journal of Cleaner Production, vol. 53, pp. 310–331, 2013.
View at: Publisher Site | Google Scholar
B. Kumar, Y. Angulo, K. Smita, L. Cumbal, and A. Debut, “Capuli cherry-mediated green synthesis of silver nanoparticles under white solar and blue LED light,” Particuology, vol. 24, pp. 123–128, 2016.
View at: Publisher Site | Google Scholar
B. Kumar, K. Smita, L. Cumbal, and A. Debut, “Ficus carica (fig) fruit mediated green synthesis of silver nanoparticles and its antioxidant activity: a comparison of thermal and ultrasonication approach,” BioNanoScience, vol. 6, no. 1, pp. 15–21, 2016.
View at: Publisher Site | Google Scholar
B. Kumar, K. Smita, L. Cumbal, A. Debut, and R. N. Pathak, “Ionic liquid based silica tuned silver nanoparticles: novel approach for fabrication,” Synthesis and Reactivity in Inorganic, Metal-Organic, and Nano-Metal Chemistry, vol. 46, no. 8, pp. 1265–1271, 2016.
View at: Publisher Site | Google Scholar
K. S. Vizuete, B. Kumar, K. Guzmán, A. Debut, and L. Cumbal, “Shora (Capparis petiolaris) fruit mediated green synthesis and application of silver nanoparticles,” Green Processing and Synthesis, vol. 6, no. 1, pp. 23–30, 2017.
View at: Publisher Site | Google Scholar
M. E. Borges, R. L. Tejera, L. Díaz, P. Esparza, and E. Ibáñez, “Natural dyes extraction from cochineal (Dactylopius coccus). New extraction methods,” Food Chemistry, vol. 132, no. 4, pp. 1855–1860, 2012.
View at: Publisher Site | Google Scholar
E. A. González, E. M. García, and M. A. Nazareno, “Free radical scavenging capacity and antioxidant activity of cochineal (Dactylopius coccus C.) extracts,” Food Chemistry, vol. 119, no. 1, pp. 358–362, 2010.
View at: Publisher Site | Google Scholar
K. Do, C. Kim, K. Song, S. J. Yun, J. K. Lee, and J. Ko, “Efficient planar organic semiconductors containing fused triphenylamine for solution processed small molecule organic solar cells,” Solar Energy Materials and Solar Cells, vol. 115, pp. 52–57, 2013.
View at: Publisher Site | Google Scholar
V. Shanmugam, S. Manoharan, S. Anandan, and R. Murugan, “Performance of dye-sensitized solar cells fabricated with extracts from fruits of ivy gourd and flowers of red frangipani as sensitizers,” Spectrochemical Acta Part A: Molecular and Biomolecular Spectroscopy, vol. 104, pp. 35–40, 2013.
View at: Publisher Site | Google Scholar
M. R. Narayan, “Review: dye sensitized solar cells based on natural photosensitizers,” Renewable and Sustainable Energy Reviews, vol. 16, pp. 208–215, 2012.
View at: Google Scholar
T. Huang and X.-H. N. Xu, “Synthesis and characterization of tunable rainbow colored colloidal silver nanoparticles using single-nanoparticle plasmonic microscopy and spectroscopy,” Journal of Materials Chemistry, vol. 20, no. 44, pp. 9867–9876, 2010.
View at: Publisher Site | Google Scholar
V. Dal Lago, L. F. de Oliveira, K. D. A. Goncalves, J. Kobarg, and M. B. Cardoso, “Size-selective silver nanoparticles: future of biomedical devices with enhanced bactericidal properties,” Journal of Materials Chemistry, vol. 21, no. 33, pp. 12267–12273, 2011.
View at: Publisher Site | Google Scholar
B. Chudasama, A. K. Vala, N. Andhariya, R. V. Mehta, and R. V. Upadhyay, “Highly bacterial resistant silver nanoparticles: synthesis and antibacterial activities,” Journal of Nanoparticle Research, vol. 12, no. 5, pp. 1677–1685, 2010.
View at: Publisher Site | Google Scholar
J. F. Affonso de Oliveira and M. B. Cardoso, “Partial aggregation of silver nanoparticles induced by capping and reducing agents competition,” Langmuir, vol. 30, no. 17, pp. 4879–4886, 2014.
View at: Publisher Site | Google Scholar
G. Favaro, C. Miliani, A. Romani, and M. Vagnini, “Role of protolytic interactions in photo-aging processes of carminic acid and carminic lake in solution and painted layers,” Journal of the Chemical Society, Perkin Transactions, vol. 2, no. 1, pp. 192–197, 2002.
View at: Publisher Site | Google Scholar
E. H. Anouar, C. P. Osman, J.-F. F. Weber, and N. H. Ismail, “UV/Visible spectra of a series of natural and synthesised anthraquinones: experimental and quantum chemical approaches,” SpringerPlus, vol. 3, p. 233, 2014.
View at: Publisher Site | Google Scholar
D. de Marcano and M. Hasegawa, Fitoquímica Brgánica, Editorial Consejo de Desarrollo Científico y Humanístico, Venezuela, 1st edition, 1991.
M. Šuleková, A. Hudák, and M. Smrcová, “The determination of food dyes in vitamins by RP-HPLC,” Molecules, vol. 21, no. 10, p. 1368, 2016.
View at: Publisher Site | Google Scholar
P. Magudapathy, P. Gangopadhyay, B. K. Panigrahi, K. G. M. Nair, and S. Dhara, “Electrical transport studies of Ag nanoclusters embedded in glass matrix,” Physica B: Condensed Matter, vol. 299, no. 1-2, pp. 142–146, 2001.
View at: Publisher Site | Google Scholar
S. Talekar, A. Joshi, R. Chougle, A. Nakhe, and R. Bhojwani, “Immobilized enzyme mediated synthesis of silver nanoparticles using cross-linked enzyme aggregates (CLEAs) of NADH-dependent nitrate reductase,” Nano-Structures and Nano-Objects, vol. 6, pp. 23–33, 2016.
View at: Publisher Site | Google Scholar
D. K. Lee and Y. S. Kang, “Synthesis of silver nanocrystallites by a new thermal decomposition method and their characterization,” ETRI Journal, vol. 26, no. 3, pp. 252–256, 2004.
View at: Publisher Site | Google Scholar
J. Tian, S. Liu, Y. Zhang et al., “Environmentally friendly, one-pot synthesis of Ag nanoparticle-decorated reduced graphene oxide composites and their application to photocurrent generation,” Inorganic Chemistry, vol. 51, no. 8, pp. 4742–4746, 2012.
View at: Publisher Site | Google Scholar
R. M. Thangavelu, D. Gunasekaran, M. I. Jesse, S. U. Mohammed Riyaz, D. Sundarajan, and K. Krishnan, “Nanobiotechnology approach using plant rooting hormone synthesized silver nanoparticle as “nanobullets” for the dynamic applications in horticulture–an in vitro and ex vitro study,” Arabian Journal of Chemistry, vol. 11, no. 1, pp. 48–61, 2016.
View at: Google Scholar
W.G. Quirino, C. Legnani, R. M. B. dos Santos et al., “Electroluminescent devices based on rare-earth tetrakis β-diketonate complexes,” Thin Solid Films, vol. 517, no. 3, pp. 1096–1100, 2008.
View at: Publisher Site | Google Scholar
C.-C. Chen, S. H. Chang, L.-C. Chen et al., “Improving the efficiency of inverted mixed-organic-cation perovskite absorber based photovoltaics by tailing the surface roughness of PEDOT: PSS thin film,” Solar Energy, vol. 134, pp. 445–451, 2016.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2018 Carina Stael et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

1695

Downloads

1099

Citations