Round Robin Tests to Determine Fiber Content of Carbon Fiber-Reinforced Thermoplastic Composites by Combustion and Thermogravimetry
Table 2
Calculated fiber content of the CFRTP with 9 plies after resin removal by combustion according to ISO 14127.
| Organization | Number of specimens | Initial weight (g) | Weight with wire (g) | Weight after combustion (g) | Fiber content in weight (%) | Average | Standard deviation | Average | Standard deviation | Average | Standard deviation | Average | Standard deviation |
| A | 5 | 0.32436 | 0.00297 | 0.36034 | 0.00350 | 0.23474 | 0.00393 | 61.279 | 0.261 | B | 5 | 0.31903 | 0.00408 | 0.35990 | 0.00434 | 0.23580 | 0.00261 | 61.101 | 0.157 | C | 5 | 0.32410 | 0.00236 | 0.35404 | 0.00242 | 0.22764 | 0.00107 | 61.002 | 0.256 | D | 3 | 0.32455 | 0.00199 | 0.36442 | 0.00209 | 0.23810 | 0.00339 | 61.082 | 0.407 | E | 3 | 0.32247 | 0.00102 | 0.34893 | 0.00696 | 0.22253 | 0.00625 | 60.802 | 0.261 | F | 3 | 0.32291 | 0.00539 | 0.83230 | 0.05987 | 0.70320 | 0.06174 | 60.028 | 0.538 | G | 3 | 0.31970 | 0.00417 | 0.36330 | 0.01383 | 0.23907 | 0.01234 | 61.143 | 0.330 | H | 3 | 0.32203 | 0.00272 | 0.39320 | 0.00545 | 0.26443 | 0.00242 | 60.020 | 0.600 | I | 3 | 0.32167 | 0.00125 | 0.38700 | 0.00245 | 0.26300 | 0.00707 | 61.447 | 1.672 | J | 3 | 0.32107 | 0.00333 | 0.38653 | 0.00836 | 0.26223 | 0.00651 | 61.287 | 0.199 | K | 3 | 0.32297 | 0.00208 | 0.37904 | 0.01112 | 0.25272 | 0.01276 | 60.889 | 0.362 | L | 5 | 0.32298 | 0.00189 | 0.34562 | 0.00201 | 0.22252 | 0.00129 | 61.887 | 0.337 | M | 5 | 0.32144 | 0.00295 | 0.36070 | 0.00294 | 0.23604 | 0.00145 | 61.220 | 0.340 | N | 5 | 0.32338 | 0.00230 | 0.37468 | 0.00747 | 0.25030 | 0.00793 | 61.537 | 0.570 | O | 5 | 0.32365 | 0.00179 | 0.38249 | 0.00141 | 0.25691 | 0.00200 | 61.201 | 0.286 | P | 5 | 0.32286 | 0.00453 | 0.36392 | 0.00787 | 0.23838 | 0.00580 | 61.120 | 0.299 | Q | 3 | 0.32433 | 0.00125 | 0.37333 | 0.00189 | 0.24833 | 0.00245 | 61.459 | 0.002 |
| Total | 67 | 0.32278 | 0.00324 | 0.38813 | 0.09803 | 0.26265 | 0.09726 | 61.129 | 0.657 |
| Interlaboratory | 17 | 0.323 | 0.002 | 0.396 | 0.110 | 0.270 | 0.109 | 61.088 | 0.461 |
|
|