Workability Behaviour of Powder Metallurgy Aluminium Composites
Table 3
Effective strain and stress formability factor at fracture.
| Composition | Relative density | Aspect ratio | | |
| Al-4%TiC | 0.82 | 0.2 | 0.1506 | 3.4845 | 0.4 | 0.1820 | 2.8096 | 0.6 | 0.1698 | 2.0257 | 0.86 | 0.2 | 0.1335 | 4.3333 | 0.4 | 0.1462 | 3.5322 | 0.6 | 0.1559 | 3.0762 |
| Al-4%WC | 0.82 | 0.2 | 0.1557 | 1.8606 | 0.4 | 0.1882 | 1.8209 | 0.6 | 0.1705 | 1.7242 | 0.86 | 0.2 | 0.1132 | 2.5488 | 0.4 | 0.1709 | 1.9264 | 0.6 | 0.2753 | 1.1064 |
| Al-4%Fe3C | 0.82 | 0.2 | 0.1321 | 3.0028 | 0.4 | 0.1444 | 2.6134 | 0.6 | 0.1569 | 2.4027 | 0.86 | 0.2 | 0.1264 | 3.3642 | 0.4 | 0.0901 | 4.5001 | 0.6 | 0.1769 | 2.7961 |
| Al-4%Mo2C | 0.82 | 0.2 | 0.2938 | 2.5641 | 0.4 | 0.1789 | 2.6111 | 0.6 | 0.2161 | 2.4735 | 0.86 | 0.2 | 0.1260 | 3.5085 | 0.4 | 0.1664 | 2.9745 | 0.6 | 0.1706 | 2.8182 |
|
|