Abstract
Tungsten heavy alloys (WHAs) belong to a group of two-phase composites, based on W-Ni-Cu and W-Ni-Fe alloys. Due to their combinations of high density, strength, and ductility, WHAs are used as radiation shields, vibration dampers, kinetic energy penetrators and heavy-duty electrical contacts. This paper presents recent progresses in processing, microstructure, and mechanical properties of WHAs. Various processing techniques for the fabrication of WHAs such as conventional powder metallurgy (PM), advent of powder injection molding (PIM), high-energy ball milling (MA), microwave sintering (MW), and spark-plasma sintering (SPS) are reviewed for alloys. This review reveals that key factors affecting the performance of WHAs are the microstructural factors such as tungsten and matrix composition, chemistry, shape, size and distributions of tungsten particles in matrix, and interface-bonding strength between the tungsten particle and matrix in addition to processing factors. SPS approach has a better performance than those of others, followed by extrusion process. Moreover, deformation behaviors of WHA penetrator and depleted uranium (DU) Ti alloy impacting at normal incidence both rigid and thick mild steel target are studied and modelled as elastic thermoviscoplastic. Height of the mushroomed region is smaller for and it forms sooner in each penetrator as compared to that for .
1. Introduction
The name of “tungsten” is derived from the Swedish term meaning “heavy stone.” Tungsten has been assigned the chemical symbol W after its German name wolfram. Tungsten, the metal with the highest meting point (3422°C), has many advantages, such as high temperature strength, high creep resistance and high thermal conductivity, high electric resistance, the lowest vapor pressure, and the lowest coefficient of thermal expansion. These properties make tungsten a premium candidate for high temperature applications like, for example, in fusion reactor [1]. Another important industrial property of tungsten is its high density of 19.3 g/cm3, which makes it an ideal material for shielding or collimating energetic α- and γ-radiation. The disadvantage of tungsten, however, is its inherent brittleness because tungsten has a transition from brittle to ductile fracture. Its treatment is realized at temperatures that are higher than brittleness limit. This temperature varies for commercially pure tungsten (99.95%) in the interval between 300 and 400°C, in case of recrystallized tungsten around 500°C. Undesirable mixtures such as oxygen, nitrogen, and carbon significantly influence mechanical and physical properties of pure tungsten. They mainly precipitate at the grain boundaries in the form of oxides, nitrides, and carbides [2]. It is possible to reduce the transition temperature of pure tungsten by rotary sawing at temperatures 1550–1450°C, transition temperature drops at 150°C. Tungsten’s strength and plastic characteristics increase with making the tungsten alloy, which can be divided into three basic groups: (a) solid solution alloys, (b) heterogeneous alloys like dispersion-hardening alloys, and (c) precipitation-hardening alloys. Alloying elements like Nb, Ta, Mo, Zr, Rh, B, C, and others influence tungsten’s strength properties and its plastic deformability. Pure tungsten has a body-centered cubic (BCC) material whose single crystals are virtually elastically isotropic at low pressures. The major uses for pure tungsten are in wire form in electrical lamps and electronic vacuum tubes, glass-metal sealing rods, cathode materials, electrical contacts, and heating elements [3]. Tungsten powder with an average particle size from 0.5 to 40 μm is used for producing tungsten carbide as cutting tools, milling tools, and mining drills. Furthermore, since the late 1960s, tungsten carbide has been considered as an anode material for hydrogen or methanol fuel cells [4, 5].
Tungsten heavy alloys (WHAs) are a typical class of two-phase composites consisting of nearly spherical tungsten particles embedded in a ductile matrix phase with lower melting point elements such as nickel, iron, copper, and cobalt [6]. The spheroidized phase microstructure is essentially pure tungsten, which is surrounded by a metallic binder phase containing some dissolved tungsten particles over 80 wt.% [7]. WHAs have been processed through PM route for some specific applications like mechanical alloying and infiltration since 1980s [8]. These heavy alloys contain mainly pure tungsten as principal phase in association with a matrix phase containing transition metals. Ni to Cu ratio in the heavy alloys can range from 3.2 to 4.1. Price et al. [9] are the first to propose the Ni-Cu as the binder for tungsten heavy alloys. Over the last several years, these alloys have been extensively investigated for densification mechanism and microstructural evaluation and properties [10, 11]. WHAs are usually fabricated by liquid-phase sintering (LPS) process from micron-sized W-Ni-Fe or W-Ni-Cu elemental powder mixtures at a temperature above 1460°C [12]. During LPS, the nickel alloy melt, which has a high solubility for tungsten, dissolves the tungsten-tungsten bonds that are formed during solid-state sintering. When the solid bonds are penetrated, particle rearrangement and pour filling occur, resulting in rapid densification of the compact. Therefore, tungsten solubility and tungsten grain shapes retention are two main concerns in determining the mechanical properties of sintered heavy alloys. Use of prealloyed powder improves homogeneity. The homogenization process also accelerates sintering and promotes densification. Ramakrishnan and Upadhayaya [13] and Kuzmic [14] study the effects of composition, temperature, and rapid cooling on densification and microstructure of the heavy alloys. The heavy alloys can be produced in a variety of near-net shapes, but the most frequently encountered shapes are those of cylindrical rods. After sintering, the final microstructure consists of coarsened-large spherical BCC tungsten grains dispersed in FCC solidified matrix. The final tungsten grain size is typically about 20–60 μm in diameter. The properties of LPS materials in general are degraded by prolonged final stage of sintering time. Hence, short sintering times are preferred in practice. However, the liquid-phase sintered WHAs are susceptible to distortion and slumming due to the large difference between tungsten and liquid matrix. Thus, understanding and controlling the microstructure evaluation in terms of composition, densification, processing like heating rate, solubility properties, and the structural rigidity are of great importance to materials engineers and scientists in the processing of WHAs.
Due to the outstanding combination of the properties related to body-centered cubic tungsten phase and face-centered cubic matrix, such as high physical and mechanical properties, such as high density (16–18 g/cm3), high strength (1000–1700 MPa), and high ductility (10–30%) [15], thermal conductivity, and good corrosion resistance, WHAs are widely used in radiation shields, counterbalance, vibration dampers, kinetic energy (KE) penetrators and rocket nozzles in space crafts [16–20]. The major disadvantage of WHAs is that they have a lesser penetration capability than depleted uranium alloys (DUs), which are another penetrator material [21]. The DUs show superior penetration performance because of self-sharpening behavior. WHAs, however, develop mushroom-like heads (blunt behavior) during penetration due to adiabatic shear deformation, which result in a lower penetration depth when compared to depleted uranium alloys. For penetrators, there are two key factors affecting the penetration ability which are good penetration and high density in addition to low heat capacity and low strain rate hardening [8, 21]. So far, most investigators focused mainly on enhancement of the mechanical properties of WHAs in order to improve the penetration capabilities for kinetic energy penetration applications. For achievement of this purpose, several techniques are proposed including grain size control of W, alloying elements like Mo, Re, solid state interring, mechanical alloying, cold working followed by recrystalline, cyclic heat treatment, and oxide dispersion strengthening and many useful experimental results have been obtained [17–24]. This paper reviews recent progress on the processing, microstructure, and mechanical properties of WHAs. In addition, the Johnson-Cook relation [25] and Zhou et al. [26] thermal softening function are reviewed to model the axisymmetric, elastic thermoviscoplastic deformations of DU and WHA rods penetrating a mild steel target.
2. Processing Techniques
As tungsten based materials are refractory materials, melting and casting of these materials are extremely difficult. Therefore alternative-processing techniques are required, which are discussed below.
2.1. Powder Metallurgy
Powder metallurgy (P/M) is a process, in which a material powder is compacted as a green body and sintered to a net shape at elevated temperature. The basic steps consist of blending or mixing of elemental/alloy WHAs powders (a), followed by compacting the mixture in a suitable die or mold (b), and heating the resulting green compacts in a controlled atmosphere furnace so as to bond the particles metallurgically (c); this heating process is called “sintering” [27]. The resulting parts are solid bodies of material with sufficient strength and density for use in diverse fields of applications. In some times, steeps (a) and (b) are combined, which is called “hot isostatic pressing,” because the powder mix is subjected simultaneously to pressure and elevated temperature. The sintered parts may be subjected to one or more secondary finishing operations like grinding and plating. The first production of WHAs and tungsten carbide materials by P/M method started in the early part of the last century. To obtain homogeneous distributions of rounded W solid phases in the alloy is important to tackle in the processing step. Solid solution alloy is produced when, for example, the element Re is added to a 93W-4.9Ni-2.1Fe alloy, inhibiting tungsten grains from precipitation growth [28]. However, adding the element Cr causes the interphases with elements W, Ni, Fe, and O to accumulate along interface alloy, resulting in lower mechanical properties of the alloys. Addition of Mo reduces the concentration of W in the liquid matrix phase during sintering and, consequently, fines the microstructure of alloys [29, 30]. Former studies indicate the liability of forming a precipitated phase with the addition of high concentration of Mo, which lead to brittleness of the alloy [31]. The coprecipitation of W, Mo, Ni, and Fe results in the formation of an intermetallic phase at the interface like W4Mo and Ni7Fe, which is in good agreement with the early work [32, 33]. As Mn/Ni ratio increases, W solubility in the matrix decreases due to the presence of Mn in matrix and causes refinement of W grains [34].
LPS at various temperatures [35–38] prepare microstructure and mechanical properties of WHAs with different compositions. All results are dependent on grain size, alloying content, compositions, and sintering time. The first two show increase in tensile properties and hardness in the presence of a finer W grain size. The tensile strength and elongation remarkably deteriorate at higher temperatures. The third indicates that both microstructure and mechanical properties are sensitively depending on alloy compositions, while the effect of varying W content significantly affects the microstructure of WHAs [38]. By increasing the Ni/Fe ratio, there is higher solubility for W in the matrix, giving a slightly larger grain size with a lower contiguity. The tensile strength and elongation are the highest for sintering times from 30 to 90 min, reflecting a minimum in the residual porosity [39, 40]. However, decreasing the yield strength with increasing sintering time is in agreement with the Hall-Petch behavior of 93W-4.9Ni-2.1Fe heavy alloy [41, 42]. Densification, microstructure, and mechanical properties of 90W-4Ni-6Mn heavy alloys indicate that temperature most critically influences the microstructure because sintering density decreases rapidly with increasing temperature while temperature decreases with decreasing the grain size [43]. The grain coalescence and distortion are induced by prolonging the sintering time or elevating sintering temperature [44]. In comparison to 93W-4.9Ni-2.1Fe alloy, 93W-7(Ni-Fe-Mo) heavy alloy has a higher tensile strength and a better ductility [45]. Heating rate during sintering is another parameter that affects the densification and distortion. The grain growth rate constant varies inversely with the volume fraction of liquid to 2/3 power [46]. The grain size, volume fraction of binding phase, and microhardness vary gradually due to the graded distribution of Mo [29]. The general trend is an increase in solid volume fraction, contiguity, and grain size with increasing W content [47, 48]. The strength of the alloy increases significantly due to greater hardening of the matrix phase. The strength properties result in an embrittlement behavior with decreasing the temperature [49].
Deformation properties of WHAs are studied under different conditions; the strength of the alloy increases significantly due to a greater hardening of the matrix phase and W grains are elongated significantly after deformation mechanism [50]. However, strength and elongation of WHAs are deteriorated very rapidly when tested over 650°C. The strength properties result in an embrittlement behavior with decreasing the temperature. The dynamic compression failure study indicates that shear band formation (ASB) is a failure mechanism for WHAs [51–53]. The microstructure evaluation of ASB formation is mainly based on the dynamic deformation process and the initial temperature [54–56]. ASB and penetration performance will be discussed within a more detailed way at the end of the mechanical behavior section. Powder metallurgy techniques can generally be classified into powder injection molding, mechanical alloying, microwave, and spark plasma sintering; these are discussed briefly in the following.
2.2. Powder Injection Molding
The powder injection molding (PIM) process is a combination of powder metallurgy and plastic injection molding technologies. This process offers three main advantages such as precise and reproducible components, complex shape, and high densification due to use of very fine ceramic or metal powders in the feedstock [57]. The process consists of mixing a small amount of organic polymer materials like wax polymer, polyacetal, and so forth with the desired inorganic powder, followed by granulation or pelletisation of the mixture [58]. The processing steps consist of feedstock preparation, injection molding, debinding, and consolidation [59]. The control of binder removal and maintaining its shape integrity are a challenge for the process. Unless the binder is removed gradually and the removal of the organic binder phase is completed, numerous defects can be formed when producing WHAs. The tensile properties are comparable to the conventional press and sinter alloys of a similar composition [60]. The solvent debinding temperature and thermal debinding atmosphere are found to be the principal factors affecting the mechanical properties of the alloy [61, 62]. Effect of agglomerates with different contents on the green and sintered properties of 97W-2.1Ni-0.9Fe heavy alloys for tensile specimens indicates that particle characteristics have no effect on the microstructure and mechanical properties because agglomeration remains as porous structure in the molded green compacts [63, 64]. The feedstock formed by mechanically alloyed (MAed) for W-Ni-Fe nanocrystalline composite powder and wax multicomponent binder has good flow ability and mold ability. 90W-7Ni-3Fe composites by PIM are widely investigated [65–69] mainly due to unique combination of high density, high strength, good ductility, and corrosion resistance of these materials. Solid-state sintering in the range between 1350 and 1450°C [70] produces fully densified parts with high mechanical properties and negligible distortion. The results indicate that the ultimate tensile strength exhibits the highest value at a sintering temperature of 1500°C and an isothermal holding time of 40 min [71, 72]. Micropowder injection molding (μPIM) is another new and fast-developing micromanufacturing technique for the production of metal and ceramic component.
2.3. High Energy Ball Milling
Mechanical alloying (MA), which represents a high-energy ball milling process, has established itself as a viable solid state-processing route for the synthesis of a variety of equilibrium and nonequilibrium phase mixtures. It was originally developed to produce oxide-dispersion strengthened (ODS) nickel- and iron-base super alloys for applications in aerospace industry. Benjamin [73] developed this technique around 1966. The powders are mixed in the mill along with the steel balls. This mix is then milled for the desired length of time until a steady state is reached. During this high-energy milling, the powder particles are repeatedly flattened, cold-welded, fractured, and rewelded [74]. Figure 1 shows the schematic ball movement in typical ball mills used for MA [75]. Among the laboratory mills, the SPEX shaker mills, which mill about g of powder at a time, are most commonly used for alloy screening purposes. The energy transfer to the powder particles in these mills takes place by a shearing action or impact of the high velocity balls with the powder. This transfer is governed by many parameters such as type of mill, milling speed, type, size and size distribution of balls, ball/powder weight ratio, extent of filling of the vial, dry or wet milling, temperature of milling, atmosphere in the mill, and, finally, the duration of milling [74, 75]. The mechanical alloying process of 93W-5.6Ni-1.4Fe tungsten heavy alloys shows that steady state stage is reached after milling for 48 hours and the grain size is refined to 16 μm at the steady state stage. When solid-state sintered at 1300°C for 1 h in a hydrogen atmosphere, MAed WHA indicates ultrafine tungsten particles of about 3 μmin diameter with high density (above 99%) [76]. These solid-state sintered WHAs with MA powders exhibit high yield strength of about 1100 MPa due to a fine microstructure but show reduced elongation and impact energy mainly caused by a large area fraction of brittle W-W interface [77–79].
(a)
(b)
(c)
(d)
Figure 2 shows the SEM micrographs of two-stage sintered 93W-5.6Ni-1.4Fe WHA secondarily sintered at 1470°C for 4 min and 90 min after solid-state sintering at 1300°C for 1 h [77]. The composition of 93W-4.9Ni-2.1Fe alloy is mechanically alloyed (MAed) and nanocrystalline supersaturated solid solutions with grain size of 11 nm and amorphous phase are achieved during MA [80–83]. When sintered at 1150°C for 30 min, the MAed powders show homogeneous microstructure and ultrafine tungsten particles of approximately 2 μm with high density above 95%. When 90W-7Ni-3Fe nanocrystalline composite powder dispersed with Y2O3 addition fabricated by MA method, the maximum tensile strength obtained is 1050 MPa and the elongation is 30% [84]. Milling increases solubility of W in γ phase and the solubility decreases with an increase of temperature [85]. 93W-3Ni-2Fe-2Co and 93W-3.5Ni-1.5Fe-2Copre-alloyed powders with crystal cell size about 16 nm are synthesized by MA, and the hardness of these sintered WHA exhibits a trend with increasing sintering temperature and sintering time [86]. However, the nanosized powders by MA process exhibit that the average W grain size in the range of 1.7–3.0 μm is obtained. The tensile strength more than 1200 MPa is achieved at a sintering temperature of 1350°C.
(a)
(b)
Significant improvements in mechanical properties of WHAs are achieved by hot extrusion, hot isostatic extrusion, and cold deformation, forged and swaging of compacts prepared from ball milled powder or powder mixtures [87–90], but the last one indicates that the mechanical properties depend on the amount of deformation imparted during swaging. Rapid heat experiments of the order of seconds are performed on a 90W-7Ni-3Fe alloy, which is cold worked by rotary swaging to 50 and 82% reduction in diameter [90]. Refined and elongated W grains into small round ones are obtained and increased deformation enhances the process of partition of W grains. Figure 3 shows a SEM micrograph of the longitudinal microstructure of the liquid-phase sintered and hot-hydrostatically extruded 93W-4.9Ni-2.1Fe alloy samples [91, 92]. W particles in the alloy are elongated along the extrusion direction. Figure 3(b) shows that the higher the average aspect ratio of the elongated W particles the bigger the extrusion ratio (2.86 : 1) used for hot-hydrostatic extrusion (Figure 3(b)). The ultimate tensile strength and hardness of the alloy were enhanced significantly and the increment in tensile strength and hardness is in proportion to the extrusion ratio [92].
(a)
(b)
2.4. Microwave Sintering Method
Microwave (MW) heating is a process in which the materials couple with microwaves, absorb the electromagnetic energy volumetrically, and transform into heat [93]. Microwaves directly interact with particulates within the pressed compacts rather than being conducted into the specimen from an external heat source, thereby providing rapid volumetric heating [94]. The sintering behavior of 92.5W-6.4Ni-1.1Fe compacts consolidated in MW furnace and in conventional furnace (CF) indicates that no intermetallic phase formation occurs during MW processing [95]. MW sintered W-Ni-Fe microstructure shows significantly lower coarsening of W grains. The effect of heating rate on MW sintered 90W-7Ni-3Fe heavy alloys exhibits excellent properties with the relative density over 99% [96]. With increasing the heating rate, W grain size decreases from 13.6 to 9.6 μm while the W-W contiguity increases from 0.25 to 0.35. The heating rate of 80°C/min results in the best combination of microstructure and mechanical performance. Sintering under optimized conditions leads to enhanced mechanical properties, namely, 1020 MPa tensile strength and 21% elongation.
The sintering behavior of 90W-7Ni-3Fe alloy compared with prealloyed 90W-PA (Ni-Cu) alloy in both CF and MW furnace, at various temperatures [97], shows that MW sintering requires about 80% less processing time than required by CF method. Additionally, MW sintering provides relatively fine microstructure and better mechanical properties and consumes much less energy than CF sintering. The microstructures of the differently sintered alloys are compared in Figure 4 [97]. Despite such fast heating rate, no micro- or macrocracking nor distortion is observed in MW-sintered samples.
(a)
(b)
A comparison on mechanical properties of CF and MW sintered alloys shows that the CF method gives some advantages like average grain size, tensile strength, and hardness [97, 98]. Average grain sizes are about 17.3 and 9.4 μm for CF and MW samples. Tensile strengths for CF and MW are about 642, 805 MPa while hardness is about 210, 295 HV for CF and MW applications, respectively. It is observed that better grain distribution and lack of intermetallic phase formation result in better mechanical properties in MW sintered compacts [99, 100].
2.5. Spark Plasma Sintering
Spark plasma sintering (SPS) is a newly developed process, synthesis, and processing technique at low temperatures and short periods. The SPS process involves the sintering of powders under the simultaneous influence of current and pressure. In this process, powders are placed in a die (typically graphite). Heating is affected by passing a current (typically pulsed DC) through the die and the sample while a pressure is applied on the powder. The characteristics, therefore, include high heating rate, application of pressure, and effect of current [101]. Higher densification is obtained since powders are sintered under an applied pressure. The SPS process is schematically shown in Figure 5 [101]. It simultaneously applies an electric current along with mechanical pressure in order to consolidate powders or synthesize and simultaneously densify specific products.
However, the SPS technology has been successfully used to prepare WHAs within limited numbers [102–108]. Almost full densification is attained at 1250°C to produce fine-grained 90W-7Ni-3Fe heavy alloys with W grain sizes of less than 5 μm. During heating, the hardness of the alloy tends to first rise, reaching the maximum value of 72.2 HRA at 1100°C, and then goes down. The microstructure of the specimen after high energy MA and pulse plasma sintering (PPS) tends to form a structure with an average grain size of ~500 nm at a sintering temperature of 1100°C [105–107]. The maximum mechanical properties up to 2500 MPa for nano- and ultradispersed W-Ni-Fe (WNF) and W-Ni-Fe-Co (WNFC) alloys are obtained. However, the PPS at high temperature above 1050°C deteriorates the strength characteristics of the alloy. For the SPS alloyed specimen, oxide film elimination of powders may improve the binding strength of the interface [108]. According to the literature [109], by optimizing the sintering times of pulsed- and constant-currents on the milled W-4Ni-2Co-1Fe powders, the density, hardness, and transverse rupture strength of the sintered alloy reach 16.78 g/cm3, HRA 84.3, and 968 MPa, respectively. Meanwhile, W grain growth in sintering is effectively inhibited, and full density is obtained at approximately 1230°C with 5 min holding time [110, 111]. Moreover, the grain growth by the SPS method can be essentially prevented [112].
3. Microstructures
Microstructure is a signature of the material processing. The microstructure is characterized by variants like grain size, shape, distributions of each phase, interface between the solid grains and matrix, porosity, and pore size in addition to processing factors such as temperature, heating rate, and holding time.
3.1. Interfacial Characteristics
To obtain composites with the desired microstructures and properties, the interfacial reaction should be controlled through selecting an appropriate matrix alloy and controlling the process parameters like temperature and holding time correctly. Wettability is related to surface energies of the interacting species by Young’s equation. The contact angle, , is associated with the balance of three interfacial energies, , , and , as follows: where the subscripts , , and represent solid, liquid, and vapor, respectively. The contact angle is altered by factors that change solubility or surface chemistry. For example, the addition of Mo to TiC-Ni system decreases the contact angle from 30° to 0° [113]. The gradual variation of Mo content results in gradients of interfacial tension [114]. A low-contact angle induces liquid spreading over the solid grains, providing a capillary attraction that helps densify the system while a high-contact angle indicates poor wetting, so the liquid retreats from the solid. This results in compact swelling and liquid extruding from pores. XRD observation reveals that bcc solid solution W phase, Fe7W6 intermetallic phase, and Fe-Ni solid solution phase form after 1 h at different temperatures.
3.2. Grain Size
Grain size is usually reported as the number of grains per unit area. The yield strength of the alloy is related to the inverse square root of its grain size, as shown by the Hall-Petch equation: where is the yield stress, is the yield strength of a single crystal, is a constant, and is the grain size. Figure 6 shows that the yield strengths of WHAs are well represented as a function of [78, 79]. These alloys exhibit a direct Hall-Petch relation above a crystallite size of 12 nm but an inverse Hall-Petch relation below 12 nm [43, 83].
The grain size of crystalline W in powders decreases with increasing the milling times [81, 87, 111, 115]. Increasing the milling times, amorphous transition takes place rapidly and the volume fraction of amorphous phase increases significantly [29]. Figure 7 shows the grain size of the MAed powders with increasing the milling time [82]. MA leads to a fast decrease of the grain size to less than about 11 nm after extended milling of 60 h. In addition, the residual crystalline W decreases with the milling time.
The isothermal grain growth kinetics during LPS follows a simple power law: where is the initial grain size, is the mean grain size, is the sintering time, and is the grain growth rate constant, which is related to the transport mechanism [23]. The mean grain volume increases linearly with time whereas the number of grains decreases with inverse time. The growth rate of W grain size drastically increases with annealing temperature higher than 1150°C [82]. The adding of Re and Mo prevents W atoms from solution-diffusion and inhibits W grains from precipitation growth [78, 116, 117]. Nearly full density of 90W-4Ni-6Mn alloys with sintering temperature in the 1100–1200°C range and ultimate tensile strength (UTS) of 1000 MPa with a 25% elongation are achieved [118, 119]. The capacity of atomic diffusion can be markedly improved by the thermal activation [14]. In most of WHAs systems, the solids content exceeds 60 vol. percentages.
3.3. Porosity and Pore Size
Pores are initially present as interparticle voids, but they might also arise from inhomogeneous particle packing or volatile phases in the green body like entrapment of gases, hydrogen production, and holding time. Porosity and inclusions are detrimental to the mechanical properties of heavy alloys. If the porosity is over 0.5%, the properties of the materials, especially ductility, remarkably reduce [118–123]. As the smaller pores are filled, the mean pore size increases while the number of pores decreases. Compact swelling due to pore formation at prior particle sites is observed if the liquid forming particles have substantial solubility in the solid during heating [124, 125]. However, swelling is reduced by the use of small melt-forming particles with a similar size as the interparticle voids. The reason for the swelling or bubbles is related to impurities and oxygen led by MA process. Another approach is to use a dry-wet hydrogen combination along with Ar to avoid gas pores and hydrogen-embrittlement [83, 126]. Since the grain size increases with sintering time, liquid filling of larger pores takes considerable time.
As for the case of the SPS, neck growth enhances by applying pressure and temperature [127–129]. The material plasticity increases substantially with decreasing the W content and the deformation capability being determined by the condition of the W-W and W-matrix zone interface [130]. As the solid content increases, a rapid increase in grain size is observed [47], but the larger grain size clearly indicates more rapid grain growth. The higher the contiguity with weak cohesive strength between the contacting grains, the poorer the mechanical properties [131]. The contiguity increases with increasing the heating rate because it causes more contacts between grains [122]. The contiguity decreases as the volume fraction of liquid phase increases.
4. Mechanical Properties
Strength and stiffness are the two most important characteristics among the mechanical properties. Furthermore, yield strength, hardness, creep resistance, fatigue, and even wear resistance are decisive for structural applications. These properties can be improved or deteriorated with many factors such as alloying, composition, heat treatment, adding reinforcement, methods, production parameters, and environment. When considering WHAs, the most effective factors determining the properties are individual constituents, volume fraction of reinforcement and matrix phase, distributions of solid particles, particle size and shape, interface bonding, and microstructural factors [127–134].
4.1. Tensile Strength and Hardness
Mechanical properties are essentially functions of manufacturing processes. Both tensile hardness and elastic modulus increase with introducing the reinforcement phase and its distribution, grain size, volume fraction, matrix content, heat treatment, and production type [129]. Particle strengthening, work hardening, load transfer from particle to matrix, grain size, and uniform distributions are the key strengthening mechanisms in WHAs. For example, the dispersion of hard and fine particles in the heavy alloy drastically blocks the motion of dislocations and therefore strengthens the matrix material. Work hardening also occurs when the composite strained since the higher density of dislocation in the matrix usually took place due to the strain mismatch between the particle and matrix, thus strengthening the material [130]. In addition, load transfer is very important strengthening mechanism. The applied stress can be transferred from the soft matrix to the particle phase if the interface bonding between the hard particle and matrix is strong enough. The room-temperature tensile properties of the as-swaged tungsten alloy samples show that the ultimate tensile strength of the alloy increases significantly (Figure 8). The ultimate tensile strength increases from 750 MPa for sintered to 1640 MPa for 75% swaged alloy [90].
The percent elongation to failure decreases from 20% to 6% that again can be attributed to strain hardening of both W and matrix phases. A fine-grained 90W-7Ni-3Fe alloy with high tensile strength and elongation properties is obtained, with the maximum tensile strength of 1050 MPa and elongation of 30%. In addition, the hardness for 93W-4.9Ni-2.1Fe and 93W-4.9Ni-2.1Fe-0.03Y compact significantly increases with the increase in the temperature [36, 78, 83]. The maximum hardness increased up to HV 439 ± 25 for 93W-4.9Ni-2.1Fe alloy and HV 482 ± 5 for 93W-4.9Ni-2.1Fe-0.03Y alloy after sintering at 1410°C for 1 h. Table 1 shows some mechanical and physical properties of WHAs after sintering, extruding, and heat treatment. This table shows that sintering temperature, time, composition and alloying element, milling time, method applied, and environment are the main influencing factors on microstructure and mechanical properties of heavy alloys. Among these parameters, with increasing the milling time, its grain size decreases considerably. Thus, it leads to the improvement of the tensile and hardness of these samples at room temperature. Furthermore, novel production techniques like SPS extrusion provide some advantages over the other methods. The SPS method is found to have higher yield strength than the others. The higher tensile strength is combined with approximately 24% elongation. However, extrusion method also enhances the mechanical properties significantly because of the high aspect ratio of the elongated W particles during this process, followed by two-stage MA sintered samples.
Improvements of the tensile strengths in SPS and extrusions are about 51% and 40.6%, respectively. However, this reaches up to 47% when the extrusion ratio increases to 75%. For the MW heating, 13% improvements are achieved when compares to conventional one. In the case of conventional sintered samples associated with different compositions and temperature/times, 38% improvements are obtained for the tensile strength while the elongation is lower than 21%. As a result, development of method is found to be more effective on improvements of mechanical properties of WHAs than those of other parameters.
4.2. Fracture Surfaces
It is observed that there are four possible fracture paths for WHAs microstructure: matrix failure, W cleavage, W-W intergranular failure, and W-matrix interfacial separation [131]. The most fractured interfaces are composed of W-W interface boundaries in solid-state sintered 93W-5.6Ni-1.4Fe WHA and two-stage sintered 93W-5.6Ni-1.4Fe WHA [115]. Failure under tension starts by separation of W-W interface areas and develops by producing cleaved W grains after strain hardening of the matrix phase. However, at the same time, the ductility of the alloy decreases as W content increases, and above 93% W the ductility of the alloys decreases drastically. The strength of WHAs increases as the fracture surface changes from flat facets, river like, to sheared W grains [90]. Lower strength and ductility in 90W-6Ni-2Fe-0.5Co-1.5Mo alloy are attributed to the presence of a higher fraction of flat faceted W grains. Oxides at W-W and W-matrix interface severely promote fracture and thus elongation decreases [80, 83]. However, the fracture surface by impact test reveals a change of the W-W interface failure mechanism towards ductile failure of penetrated matrix with many dimples by increasing the matrix penetration [43, 50].
The microstructure and processing factors of the heavy alloys are the key to affect their mechanical properties. For WHAs, the main influencing factors of mechanical properties include compositions [27–33, 36–39, 83], processing type [71–73, 85, 95, 99, 103, 122, 132, 133] and temperature/time [41, 43, 62, 76, 86, 97, 104, 105, 134], tungsten grain size and shape effect [47, 81, 87, 118], grain growth [46, 82, 110, 112, 117], interface bonding between W and matrix [80, 90, 114, 130, 131], and porosity and pore size distribution [49, 83, 118, 124, 125, 127].
4.3. Penetrator Performance
In order to increase the penetration performance it is desirable to promote adiabatic shear banding localized to small areas and at higher shear strains. For WHAs, first, W/W interfacial area without altering W content should be reduced. Secondly, the W grain size should be increased and thus contiguity decreases. Thirdly, the coated powder should be used. Table 2 indicates requirements of an ideal KE penetrator. Among all types of penetrator materials, there are two key factors affecting the penetration ability, which are good penetration and high density [135].
Traditionally, depleted uranium (DU) alloys U-3/4Ti are used as penetrators in all cannon-fired KE projectiles. However, due to environmental issue and health hazardous of DU, there is a drive to replace DU alloys by alternative materials. The development of a large mushroomed head on the penetrator is observed for pure tungsten, WHAs, and a uranium-6% niobium alloy is shown in Figure 9 [135, 136].
(a)
(b)
However, other U-3/4Ti alloy penetrators, which rapidly develop localized adiabatic shear failure, create smaller diameter penetrator cavities than WHAs penetrators. This type of failure results in a chiseled head formation (self-sharpening effect), which improves KE penetrators performance. As stated above, the former indicates self-sharpening effect, whereas the latter shows a mushrooming effect. This is the fact that the very high melting of W entails a low thermal softening associated with high rate sensitivity of W with the strength increasing with an increasing strain-rate. These effects delay flow softening at high strain rates. Because of delaying onset of shear stress localization, WHAs develop “mushroom heads” during penetration.
WHAs such as the one studied here have been studied extensively, primarily as potential materials for KE projectiles [136]. Mechanical properties and physical phenomena at high strain rates have been obtained or observed using Hopkinson bar techniques [137], normal plate impact [138–140], and oblique flyer-plate impact [141]. In most of these, the bulk mechanical properties of the homogenized multiphase material (e.g., stress-strain curves and spall strengths) and microstructure such as fracture surfaces or shear localization initiation sites have been reported.
The dynamic deformation and fracture behavior of an oxide (0.1 wt.% Y2O3) dispersed WHAs fabricated by MA show that interfacial bonding between W particles occurs over broad deformed areas in this alloy, suggesting the possibility of adiabatic shear banding (ASB) formation [18]. Combined dynamic compression and shear tests are carried out to study the deformation and failure behavior of pretwisted WHA at high strain rates of 103 s−1 [54]. It is found that the initial microstructures such as the aspect ratio and orientation of the W grains have significant effect on the tendency to the shear band formation. Presumably the ASB initiates at one side, where the direction of the maximum shear stress is approximately parallel to the direction of the major axis of W grains, and then develops at the other side due to the loss of load-bearing capacity. The ASB has general trends to propagate along the Ni-Fe matrix because more energy is needed to shear the W grains. The influence of the microstructure such as heterogeneity, the content of matrix, and the particle shape on shear band formation is reported [29, 142]. The quasistatic and dynamic failure of ultrafine grained (UFG ~ 500 nm) tungsten (W) under uniaxial compression is investigated under uniaxial dynamic compression (strain rate ~ 103 s−1) [143]. The true stress-true strain curves of the UFG-W exhibit significant flow softening, and the peak stress is ~3 GPa. The strain rate sensitivity of the UFG-W is reduced to half the value of the conventional W. Furthermore, WHAs rod penetrators processed by hydrostatic extrusion and hot torsion (HE + HT) subjected to ballistic impact maintain an acute shape and show good self-sharping ability, while mushroom-like heads are observed in the as-sintered and as-extruded WHA penetrators [93]. Microstructure analysis shows that ASBs form at the edge of the HE + HT WHA penetrator heads during the penetration and deformed parts of penetrator fall along the ASBs, which are responsible for the good self-sharpening ability and evidently improved the penetration performance (see Figures 10 and 11).
Deformation behavior of W-Ni-Fe alloy by impact loading over a practical range of temperatures ranging from 25 to 1100°C and strain rates ranging from 8 × 102 to 4 × 103 s−1 has been studied by Lee et al. [144]. The flow stress of the composites increases with the strain rate, but an increase in the test temperature has opposite effects. Moreover, work hardening decreases considerably as both the temperature and the strain rate increase. However, a decrease in strain rate sensitivity is observed when the temperature goes above 700°C. Tensile impact tests performed on a tungsten heavy alloy at strain rates ranging from 100 to 1300 s−1 indicate that strain softening is evidenced [145]. Previous work on pressure-shear plate effects to simple shear under shearing strain rates up to 7 × 105 s−1 shows that alloys exhibit significant rate sensitivity and thermal softening due to plastic dissipation. Shear bands form when the plastic strains become sufficiently large [26, 146]. Uranium alloys are better penetrators due to the use of strain onset for shear banding than tungsten alloys, but the assumption that ASB plays a major role in the erosion process of WHAs remains to be verified [147, 148].
Dynamic compression failure testing against steel targets of hardness ranging from 303 to 330 hardness Brinell (HB) is conducted with an impact symmetric Taylor test allowing the quantification of ABS as a function of the impact velocity [53]. The equivalent failure strains for ABS are identified through numerical simulations of the Taylor tests with a finite element hydrocode implemented with Johnson-Cook constitutive models [25]. These data along with the chiseled nose observations are the first evidences that shear banding is one of the failure processes influencing the penetration performance of conventional WHAs penetrators. The reverse ballistic impact tests on WHAs rods are conducted at a speed of 173 m·s−1 and 228 m·s−1 by Dick et al. [149]. The mushroomed end has a slight ellipticity which attribute to radial cracks in the body at low speed while the deformation is more localized along a curved path extending from the mantle near the transition between the mushroomed region and the relatively undeformed rod toward the impact face. A cusp formed in the lateral boundary where the shear band intersects it. Opposite to a point where a shear band is formed, they observe the ductile fracture along a similar path, but no data is obtained for materials properties.
For WHAs, ASB is defined as narrow regions of rapid intense plastic deformation, forming near the transition between the mushroomed region and the relatively undeformed portion of the rod, when its material is either a mixture of Fe-N-W and W particles or a homogenous alloy [55, 150]. The ASB is observed under all specimens subjected to various initial temperatures. Figures 10(a), 10(b), and 10(c) show the SEM micrographs of ASB within specimens subjected to 26°C, −20°C, and −50°C, respectively. It can be observed that the as-extruded WHAs exhibit a good susceptibility to ASB even subjected to cryogenic temperatures. Furthermore, with the decrease of initial temperature, the shear strain within ASB shows a decreasing tendency, demonstrating that the initial temperature has some influences on adiabatic shear banding of WHAs. The shear banding in a liquid phase sintered 90W-7Ni-3Fe alloy at 5400 s−1 appeared [129]. Several W-Ni-Fe alloys using compressing Kolsky test at high strain rates for dynamic deformations involving large plastic strains, the response of the WHAs, are controlled by the behavior of W grains [137]. The overall mechanical properties can be improved when the W particles are of fine size and the interfacial area between W particles is reduced [104]. However, penetrators that have too high strength are easily embrittled, and, thus, their penetration performance deteriorates because of fragmentation during penetration. It is desirable for a penetrator to have deformation behavior that can be induced self-sharpening and possess sufficient fracture toughness to minimize fragmentation during high-speed impact [142]. A shear band forms at the point on the rods mantle where the mushroomed region transitions into the straight rod, which agreed qualitatively with Dick et al. [149]. However, the rod is made of either homogeneous tungsten or homogeneous Fe-Ni-W and no such shear band is computed.
Thermomechanical deformations of a WHA rod impacting at normal incidence of a smooth rigid target are modeled based on Fe-Ni-W particles randomly distributed in W particles, homogenous WHAs, pure tungsten, and pure Fe-Ni-W [150]. The role of microstructure on dynamic mechanical properties of WHAs has been investigated via constitutive modelling and numerical simulation. An isotropic elastoviscoplastic constitutive model with realistic grain structures to capture shear location in oblique impact (pressure-shear conditions) has used [26] and shows high rate nominally uniform shear deformation [151].
These deformation models and their applications for WHAs rods will be described in the following section.
4.3.1. Formulation
In order to describe dynamic, thermomechanical, and axisymmetric deformations of a cylindrical rod affecting at normal incidence a rigid and planar surface, the Lagrangian or referential description of motion is used. The deformations of rod materials are governed by the following balance laws of mass, linear momentum, moment of momentum, and internal energy.
Equation (4) is the Johnson-Cook relation [25]. The flow stress, , increases with an increase in the effective plastic strain and the effective plastic strain rate but decreases with an increase in the temperature of a material particle. is the specific heat, the temperature of a material particle, its melting temperature, the room temperature, the homologous temperature, Se the effective stress (), and the effective plastic strain. In (4), parameters and characterize the strain hardening of the material, and characterize its strain-rate hardening, and characterizes its thermal softening. For the Taylor impact test, initially, the cylinder rod is stress free, at room temperature , and is moving with a uniform speed in a direction normal to the plane surface of the target and strikes it at time . All bounding surfaces of the rod except that contacting the target are to be taken traction free. No thermal boundary conditions are needed due to the assumption of locally adiabatic deformations: In physical experiments, fracture in the form of a crack will ensue from the point well before it is heated to its melting temperature. The thermal softening of the WHA they tested is better described by where and are material parameters and for their WHA, and [26]. Its approximate solution is by the finite element method and employs a large-scale explicit code DYNA2D [152] to do so. As the bodies deform, elements near the target/penetrator interface become distorted severely and the time step size drops drastically.
4.4. Taylor Impact Test Simulations
4.4.1. The Johnson-Cook Thermal Softening and Zhou et al. Thermal Softening
The following values are assigned to various material and geometric parameters.
Rod length = 60 mm; Rod diameter = 10 mm; m/s; K.
Depleted Uranium (DU) [153]. ; 079 MPa; ; 120 MPa; ; ; ; ; ; 600 kg/m3; GPa; GPa; J/kg °C, K.
Tungsten Heavy Alloy (WHA). , 506 MPa; MPa; ; ; ; ; ; 600 kg/m3; GPa; GPa; J/kg °C; K.
The values of , , , , , , and for both materials are taken from Rajendran’s report [154] while those of other material parameters are taken from a handbook. It can be noted that the shear modulus for WHA equals 2.76 times that for DU. Computed results for a trial problem indicate that the height of the mushroomed region is approximately 5 mm.
As for Zhou et al. [26] thermal softening, results for the DU and WHA rods with and and 0.3 can be computed, by keeping values of the material and geometric parameters given above. Each one of these values of gives higher thermal softening than that given by the Johnson-Cook relation. Thus, for same values of and , the flow stress will be lower with Zhou et al. softening than that with Johnson-Cook relation. It is found that and provided a good fit to the test data for the WHA they used. Here the same values of for DU are considered because of the lack of data. Thus, the differences for their deformation patterns will be due to the variation in the values of the shear modulus, bulk modulus, and parameters , , , and in (4). It can be noted that the minimum value of the thermal softening function can be taken as zero. The height of the mushroomed region is smaller for and it forms sooner in each rod as compared to that for [153]. The shapes of the mushroomed regions suggest that severe deformations and hence a shear band may initiate at one or more of the following three locations: adjacent to the stagnation point (), near the periphery of the impacted end (), and close to the inflection point in the curve describing the mantle of the deformed rod (). Figures 12(a), 12(b), and 12(c) show the deformed meshes of the DU and WHA rods for each of the three thermal softening functions [154]. For , the aforestated conditions for the initiation of a shear band are satisfied at point for the WHA rod and the distortions in the deformed mesh confirm the initiation of a shear band there. However, for the DU rod, even though the effective plastic strain at point grows rapidly first, its rate of growth tapers off. The deformed mesh shown in Figure 12(b) suggests that no shear band initiates from point since the mesh is regular in the neighborhood of . For each thermal softening considered, the mesh around point is severely deformed. In addition, the effective stress there drops to less than 80% of its peak value. Thus, according to the definition of the drop in the effective stress, a shear band initiates at point for each thermal softening studied.
(a)
(b)
(c)
4.4.2. Rule of Mixture Model
WHA is modeled as a mixture of 10%Fe-Ni-W particles interspersed randomly in hard tungsten particles. The two are modelled as elastic thermoviscoplastic materials with the flow stress given by (4), but with the Zhou et al. thermal softening and the following values are assigned to different materials [26, 153].
Tungsten Particles. MPa; MPa; ; ; GPa; GPa; ; ; ; kg/m3; J/kg °C.
Fe-Ni-W Matrix. MPa; MPa; ; ; GPa; GPa; ; ; ; kg/m3; J/kg °C.
The diameter and the length of the rod are 6.35 mm and 25.4 mm, respectively, and simulations of the Taylor impact test are carried out for two impact speeds of 173 and 228 m/s [154]. For m/s, the observed deformation lengths and the geometric mean diameter of the impact face are 22.8 mm and 9.36 mm, respectively; the corresponding computed values equal 22.25 mm and 10.72 mm. For m/s, the computed diameter equals 9.5 mm. The final observed and computed deformed lengths equal 20.9 mm and 20.5 mm, respectively.
In order to address the effects of crystallographic orientation and dislocation accumulation on the thermomechanical response of WHAs, crystal plasticity based constitutive models have recently been formulated and implemented by some people. The effect of variable ratios of grain and phase boundary strengths on uniaxial tensile failure shows that it is apparent that the variability in spall statistics observed experimentally is due both to the heterogeneous local strengths and flaw distributions and to the multiphase polycrystalline microstructure of the material [154]. Tensile deformation and fracture of realistically rendered [155] and homogenized the microstructures of dual phase tungsten alloys [156]. Numerical results are obtained from a 2D finite element implementation of the crystalline elastoplasticity models for each phase under impact loading. The cohesive laws account for stress state, temperature effects on interfacial strengths, and anisotropic continuum damage mechanics. They correlate with the spall strength of the multiphase material [157]. The results indicate the relationships between microstructural features, fracture patterns, and free surface velocity statistics. Statistical variations of free surface velocity are also found to vary with crystal orientation, texture, and temperature dependence of properties controlling the grain boundary fracture [158]. The role of microstructure in the dynamic deformation and fracture of a dual phase, polycrystalline tungsten alloy oriented either perpendicular or parallel to the extrusion direction under high-rate impact loading is investigated via experiments and modeling [159]. Furthermore, finite deformation crystal plasticity theory describes the behavior of the pure tungsten and binder phases, and a stress- and temperature-based cohesive zone model captures fracture at grain and phase boundaries in the microstructure. The results from both experiments and modeling indicate that the grain orientations affect the free-surface velocity profile and spall behavior.
As for the case of Spalling; dynamic tensile failure in uniaxial strain loading, typically referred to as spall or spallation, frequently occurs in impact events, including the current plate impact experiments [160]. The spall strength of a similar variety of WHA to that currently studied has been measured to be 1.7–2.0 GPa [161]. In a typical spall experiment, impact sends a shock wave or elastic and plastic waves, depending on stress level, through both the target and impactor. The initial shocked state was defined by stress and particle velocity. When the compression waves reach the back of the target, a stress-free surface, and the back of the impactor, which has a low-impedance material against it, most of the wave reflects as an unloading wave. This unloading wave from the free surface at the back of the target, also referred to as a rarefaction fan because of its tendency to spread as it propagates, unloads the sample to zero stress and the particle velocity. It can be noted that this free-surface velocity is somewhat lower than the impact velocity. Dandekar [162] attempted to determine the impedance of WHA directly through concurrently backing the target material with void and PMMA. By assuming that the same spall strength is reached in the two cases, the impedance can be found. Instead, the slope (impedance) from the shocked state to the unloaded state in the stress plane can be calculated. It is clear that the pullback velocity varies considerably with position in the sample. The average value of spall strength for the experiment is somewhat larger than the spall strength inferred from the spatially averaged particle velocity. Experimentally, higher velocity impacts yield a somewhat higher spall strength for both orientations. Such behavior has been observed previously in other brittle materials [162]. Post mortem inspection of fully fractured (i.e., spalled) specimens would likely indicate both intergranular and cleavage mechanisms [138]. However, crack propagation and macroscopic spall behavior are thought to require substantial grain cleavage: once sufficiently large, a microcrack initiated along grain/phase boundaries will then propagate fully across the specimen, irrespective of the underlying microstructure. Effective stress near the spall plane can be simulated at different materials and impact velocities but not discussed here. A multiscale descriptive framework for describing effects of micro- or mesostructures on wave propagation in solids under impact loading has been developed [163]. The initiation of spall fracture may be controlled by grain and phase boundaries, in agreement with experimental observations.
5. Potential Applications of WHAs
WHAs emerged as the potential candidates for kinetic energy (KE) penetrators in addition to radiation shields and vibration damper applications [41, 65, 88, 131]. These alloys are excellent materials for the shielding against gamma rays and hard X-rays due to their combination of radiographic density, machinability, strength, and low toxicity. Counterbalance weights for fixed and rotary wing aircraft have been used for many years because unlike lead, which creeps under its own weight at room temperature. WHAs are routinely used in high density fragmenting devices and armor piercing ammunition ranging from small caliber of 5.56 mm diameter up to 120 mm antitank projectiles and beyond. Rotational inertial members are, for example, gyroscope rotors in inertial guidance systems and navigation equipment. WHAs serve as flywheels, the rim components of flywheels, or rotating members in governors. WHAs weight blocks offer up to 50% more weight in a given volume with added advantages of direct attachment via threaded holes or thru-bolting and the freedom from deformation, which is the constant problem for the lead in addition to hole logging of oil wells.
6. Concluding Summary
A review of recent progress on the processing such as conventional powder metallurgy (PM), mechanical alloying (MA), microwave sintering (MWS), and spark-plasma sintering (SPS) methods and microstructure and mechanical properties of WHAs is presented in this paper. Key factors affecting the performance of WHAs are given as follows. Firstly, W and matrix composition, their shape, size of W particles, distributions of W particles, and pore size are important. Secondly, improvements in strength/stiffness and hardness are observed in most alloy systems with additions of W in Fe-Ni/Cu alloys. The bonding strength between W particle and matrix interface is very important in the strengthening of alloys since the load transfer depends on the sufficient bonding between the W and matrix phase. In addition, optimal sintering temperature and time are important because of the formation of a strong interface between particles and matrix. Moreover, ultimate tensile strength and hardness of WHAs produced by extrusion method enhanced significantly because of the high aspect ratio of the elongated W particles. Thirdly, novel processing technique like SPS provides some advantages over the other methods. The SPS alloyed is found to have higher yield strength than the others, followed by extruded sintered samples. Fourthly, grain refinement is an effective way for improving ductility and strength at ambient temperature with increasing the milling time. Finally, the yield strength of WHAs depends on the microstructural parameters such as tungsten grain size, matrix volume fraction, pore size, and W-W contiguity. Furthermore, the thermal softening in DU and WHA penetrator rod are modelled by either the Johnson-Cook relation [25] and that proposed by Zhou et al. [26] or rule of mixtures. The flow stress increases with an increase in the effective plastic strain and effective plastic strain-rate but decreases with a rise in the temperature. The height of the mushroomed region is approximately 5 mm, but the height of the mushroomed region is found to be smaller for and it forms sooner in each penetrator rod as compared to that for value.
Nomenclature
| ASB: | Adiabatic shear banding |
| : | Parameters |
| : | Specific heat (J/kg °C) |
| CF: | Conventional heating/furnace |
| DU: | Depleted uranium alloys |
| : | Effective plastic strain (mm/mm) |
| : | Effective plastic strain with temperature (mm/mm) |
| : | Strain-rate hardening |
| : | Initial grain size (μm) |
| : | Mean grain size (μm) |
| HRA: | Hardness Rockwell A (Kg/mm2) |
| HB: | Hardness Brinell (Kg/mm2) |
| HE + HT WHA: | Hydrostatic extrusion and hot torsion |
| HV 482: | Vickers hardness value (Kg/mm2) |
| : | Yield strength (MPa) |
| KE: | Kinetic energy penetrator |
| LPS: | Liquid phase sintering |
| MA: | Mechanical alloying |
| MAed: | Mechanically alloyed |
| MW: | Microwave sintering |
| : | Characterize the strain hardening of the material |
| uPIM: | Micropowder injection |
| ODS: | Oxide dispersion strengthened Ni- and iron base super alloy |
| : | Contact angle (°) |
| : | Room temperature (°C) |
| : | Melting temperature (°C) |
| UDP: | Ultradispersion particles |
| UFG: | Ultrafine grain (~500 nm) |
| UTS: | Ultimate tensile strength (MPa) |
| PM: | Powder metallurgy |
| PPS: | Pulse plasma sintering |
| PIM: | Powder injection molding |
| : | Effective stress (MPa) |
| SEM: | Scanning electron microscope |
| SPS: | Spark plasma sintering |
| XRD: | X-ray diffraction |
| : | Material parameters |
| Y2O3: | Yttrium oxide |
| W: | Tungsten |
| WHAs: | Tungsten heavy alloys |
| W-W: | Tungsten-tungsten grain |
| WC-Co: | Cemented carbides |
| WQ: | Water quenched |
| : | Thermal softening. |
Conflict of Interests
The author declares that there is no conflict of interests regarding the publication of this paper.
Acknowledgments
The Council of Higher Education (Turkey) supports the author’s research. The author also extends his thanks to Associate Professor Alex O. Aning at the Department of Materials Engineering in Virginia Tech & State University during this study.