Journal of Powder Technology / 2014 / Article / Tab 2 / Research Article
Synthesis, Characterization, and Crystal Structure Refinement of Lanthanum and Yttrium Substituted Polycrystalline 2M Type Zirconolite Phases: Ca1-x Mx ZrTi2 O7 (M = Y, La and x = 0.2) Table 2 Refined atomic coordinate of
ZrTi
2 O
7 and
ZrTi
2 O
7 ceramic powders at room temperature.
Atom Occupancy (Å2 ) ZrTi2 O7 Ca 0.38053 0.13313 0.49857 0.80257 0.01789 Y 0.38053 0.13313 0.49857 0.21057 0.01789 Zr 0.12371 0.11665 −0.02253 0.892 0.02874 Ti1 0.2506 0.125 0.7445 0.78474 0.00621 Ti2 0.4655 0.018 0.27 0.50797 0.00648 Ti3 0.0001 0.124 0.25 0.5759 0.00674 O1 0.318 0.12031 0.28196 1.0 0.05487 O2 0.48094 0.17522 0.13916 1.0 0.05487 O3 0.22596 0.08815 0.5784 1.0 0.05315 O4 0.405 0.154 0.719 1.0 0.05485 O5 0.715 0.105 0.568 1.0 0.05379 O6 −0.007 0.14 0.419 1.0 0.05789 O7 0.115 0.055 0.778 1.0 0.05748 ZrTi2 O7 Ca 0.37732 0.13897 0.49715 0.8 0.02756 La 0.37732 0.13897 0.49715 0.097 0.02556 Zr 0.12567 0.11477 −0.02248 0.935 0.02537 Ti1 0.2506 0.125 0.7445 0.94854 0.01285 Ti2 0.4655 0.018 0.27 0.42369 0.0 1487 Ti3 0.0001 0.124 0.25 0.54178 0.01235 O1 0.318 0.12031 0.28196 1.0 0.06679 O2 0.48094 0.17522 0.13916 1.0 0.05678 O3 0.22596 0.08815 0.5784 1.0 0.06658 O4 0.405 0.154 0.719 1.0 0.05617 O5 0.715 0.105 0.568 1.0 0.05618 O6 −0.007 0.14 0.419 1.0 0.05614 O7 0.115 0.055 0.778 1.0 0.05674