Burst Diaphragms Based on Carbon Black/Silica Hybrid Filler Reinforced Nitrile Rubber Compounds
Table 4
Mechanical properties of the prepared samples.
| Property | Test method | Dimensions | NBR | NC50S0 | NC25S25 | NC0S50 |
| Hardness | IRHD | — | 50 | 66 | 70 | 76 | Modulus 100% | D412 | MPa | 0.70 | 6.30 | 3.32 | 2.95 | Modulus 200% | D412 | MPa | 1.50 | 7.60 | 6.71 | 4.94 | Modulus 300% | D412 | MPa | 2.70 | 12.12 | 10.72 | 7.27 | Tensile strength | D412 | MPa | 1.80 | 21.33 | 22.20 | 24.21 | Elongation at break | D412 | % | 231.1 | 319.2 | 478.2 | 657.8 | Abrasion | D5963 |
mm3 | 380.0 | 291.3 | 279.18 | 273.05 | Burst strength | — | barg | — | 21.1 | 18.3 | 14.6 |
|
|