Abstract

Carbon nanotubes have attracted interest as contrast agents for biomedical imaging because they strongly absorb electromagnetic radiation in the optical and microwave regions. This study applies thermoacoustic (TA) imaging and spectroscopy to measure the frequency-dependent absorption profile of single-walled carbon nanotubes (SWNT) in the ranges of 2.7–3.1 GHz and 7–9 GHz using two tunable microwave sources. Between 7 and 9 GHz, the peak TA signal for solutions containing semiconducting and metallic SWNTs increased monotonically with a slope of 1.75 AU/GHz () and 2.8 AU/GHz (), respectively, relative to a water baseline. However, after compensating for the background signal from water, it was revealed that the TA signal from metallic SWNTs increased exponentially within this frequency band. Results suggest that TA imaging and spectroscopy could be a powerful tool for quantifying the absorption properties of SWNTs and optimizing their performance as contrast agents for imaging or heat sources for thermal therapy.

1. Introduction

The extraordinary electrical, optical, and mechanical properties of single-walled carbon nanotubes (SWNTs) make them attractive for a variety of applications. For example, they have demonstrated unique capabilities in fields ranging from nanoelectronics for creating highly functional integrated circuits to biomedicine as sensors of in vivo disease biomarkers [1, 2]. Their low toxicity, large surface area, and ability to penetrate the cell membrane indicate that functionalized SWNTs can be effective agents to deliver exogenous biomolecules like proteins, DNA, and RNA directly into cells [37]. These nanoagents can be molecularly conjugated to specific ligands, such as folic acid, antibodies, and peptides, enabling targeted delivery of anticancer or antibacterial agents [813]. Additionally, SWNTs have been used in mouse models to deliver therapeutics passively via the enhanced permeability and retention effect (EPR) [14]. In the biomedical arena, these nanoparticles have also been employed as contrast agents for medical imaging and heat sources for thermal ablation due to their strong electromagnetic absorption [1, 15, 16].

Their large microwave absorption makes SWNTs excellent candidates in contrast to agents for thermoacoustic imaging (TAI) [1719]. In TAI a short microwave pulse (~1 μs) is absorbed by a sample, producing transient heating, thermoelastic expansion, and generation of an ultrasound (US) pressure field with a magnitude proportional to the local microwave absorption. In recent work, we demonstrated that thermoacoustic spectroscopy (TAS) can be used to enhance the specificity of TAI by detecting and identifying materials based on the frequency dependence of their microwave absorption [20]. This study expands our previous findings by utilizing TAS to characterize the spectral dependence of the TA signal generated by SWNTs. The generated TA pressure () is given bywhere is the speed of sound, is the isobaric volume expansion coefficient, is the specific heat, is the intensity of the microwave pulse, is the position from the transducer, is the microwave excitation frequency, and is the microwave absorption coefficient, which is represented by the cumulative contribution from all absorbers:where is the concentration of the th absorber and is the absorption coefficient of the th absorber. Equation (2) is useful for separating contributions from different colocalized absorbers to the cumulative microwave absorption. The microwave absorption coefficient is defined aswhere is the permeability, is the permittivity, and is the conductivity. Thus, the microwave absorption coefficient and TA signal produced by an absorber are ultimately derived from the underlying dielectric properties of the sample.

Single-walled carbon nanotubes are constructed out of graphene, a two-dimensional sheet of individual carbon atoms arranged in a hexagonal pattern and conceptualized to be rolled into a tube. These nanoparticles typically have a diameter of about one nanometer and can be up to several millimeters in length. Their electromagnetic properties depend on the geometrical orientation of the carbon atoms in the nanotube [21]. For example, carbon nanotubes with a zig-zag atomic structure behave as a semiconductor, while carbon nanotubes with an armchair atomic structure behave like a metal.

The spectral absorption properties of SWNTs are largely unexplored. However, previous studies have revealed that their electromagnetic properties, such as permittivity and permeability, can have large frequency dependence in the 1–10 GHz range [22, 23]. Carbon nanotubes exhibit both linear and nonlinear dielectric properties, so their resulting absorption spectra, as measured by TAS, may be complex in nature [24]. Furthermore, by manipulating the permittivity, permeability, and/or thickness of the nanoparticles, their properties can be frequency-tuned [2427]. This study employs TAS to ascertain the microwave absorption properties of SWNTs. If these nanoparticles exhibit a distinct spectral signature, this feature could be exploited to enable highly sensitive in vivo discrimination from endogenous background signal generated by tissue (e.g., muscle and blood) [20].

2. Materials and Methods

Stock solutions of nanoparticles were obtained from Buckeye Composites containing SWNTs exhibiting semiconducting (MC1138-1) and metallic (MC1138-2) properties. These samples were tested for their frequency-dependent absorption properties using TAS. The nanotubes in the semiconducting solution had an average diameter of 1 nm and a base concentration of 300 mg/L water (i.e., 300 ppm). The nanotubes in the metallic solution had an average diameter of 2 nm and a concentration of 100 mg/L water (i.e., 100 ppm).

Two microwave sources were employed for TAI with excitation frequencies between 2.7 and 9 GHz. The first source was a high-energy microwave oscillator (PG5KB, Epsco,  kW, Figure 1(a)) tunable between 2.7 and 3.1 GHz. The second source was a high-frequency microwave power amplifier provided by Raytheon Company (see Figure 1(b)). This source exploited a helix traveling wave tube (TWT) amplifier to generate microwave pulses with a peak power of 1 kW between 7 and 9 GHz.

For TAI, a custom tank was designed and fabricated on a rapid prototype 3D printer (Connex350, Objet). A single-element, spherically focused 2.25 MHz US transducer (V395, Olympus) detected the TA signals, which were generated with a 300 ns square microwave excitation pulse. The radiating antenna, a WR-187 waveguide for the 3 GHz system, was filled with mineral oil and sealed with a thin layer of Mylar. A ceramic matching layer (Eccostock HiK, Emerson & Cuming, , loss tangent < 0.002) was positioned on top of the waveguide to optimize microwave transmission into the sample. A calibrated spectrum analyzer (Hewlett-Packard, 8560A) measured the frequency-dependent power of the microwave source. The imaging tank was filled with deionized water (diH2O) for acoustic coupling to the US transducer. The setup for the 3 GHz system, including imaging tank, overhead transducer, and arm of the motorized 3D translation stage (Velmex Inc.), is displayed in Figure 1(c).

For the 9 GHz system, the imaging tank was fitted with a WR-90 waveguide. Both the waveguide and imaging tank were filled with mineral oil and separated by a thin layer of Mylar. The microwave output was sampled with a directional coupler. The attenuated output of the coupler was connected to a crystal detector (432A, Hewlett Packard) to convert the microwave power to a voltage. The crystal detector was calibrated at each microwave frequency and used to record the frequency-dependent fluctuations in the output microwave power. It also enabled accurate tuning of the microwave pulse width.

For both systems, US signals were recorded on a fast data acquisition board (PDA12, Signatec), which sampled signals at 32 MHz. During TAI, the envelope of the output microwave pulse was also recorded. The lateral position of the transducer was placed at the center of the waveguide where the microwave power was highest. The acoustic focus was then positioned at the depth of the sample. The motorized translation stage was attached to the sample, which was scanned across the waveguide aperture to ensure uniform and consistent microwave exposure for each sample. Next, the sample was scanned at different microwave excitation frequencies to produce spectroscopic cross-sectional (B-mode) TA images. The sample consisted of three polyolefin tubes (NTE Electronics, dia. = 3 mm) with solutions of semiconducting SWNTs, metallic SWNTs, and deionized water (see Figure 1(c)). The sample was suspended 2 mm above the waveguide aperture with a center-to-center spacing of 5 mm between each tube. The typical scan time for a single B-mode acquisition was less than 1 minute with lateral steps of 500 μm. The US signal at each lateral position was bandpass filtered (1–3 MHz) and demodulated by taking the magnitude of the Hilbert transform. For display purposes, the envelope was linearly interpolated and log-compressed. Images were filtered laterally with a low-order median filter followed by a Gaussian smoothing filter (1.5 mm). Thermoacoustic images were normalized to the power of the microwave pulse, which varied slightly with frequency.

3. Results and Discussion

Solutions of SWNTs were initially imaged with the tunable 3 GHz microwave source. A test sample consisting of solutions of semiconducting SWNTs and metallic SWNTs and a reference solution of deionized water was imaged with excitation frequencies of 2.7, 2.9, and 3.1 GHz. A schematic cross-section of the samples is shown in Figure 2(a), displaying the order of each solution. A TA image acquired with 3.1 GHz radiation is presented in Figure 2(b). The tube of semiconducting SWNTs generated the largest TA signal of the three samples. This is consistent with expectations, because its nanoparticle concentration was higher than that of the metallic nanoparticles. For example, at 3.1 GHz, this sample generated 48% and 90% larger signal than the metallic and water samples, respectively. Additionally, the normalized spectral profiles of the SWNTs between 2.7 and 3.1 GHz are depicted in Figure 2(c). Both SWNT solutions generated significantly larger signal (20%–100%) than the water reference. Over this narrow frequency range, the spectrum of each sample increased linearly () but with different frequency-dependent slopes. Referenced to the unit normalized slope of deionized water, the metallic SWNT solution had a spectral slope of 0.95 AU/GHz, which was slightly less than that of water, whereas the semiconducting SWNT solution had a slope significantly greater than the water baseline (2.32 AU/GHz).

To further explore the spectral absorption properties of the SWNTs, the nanoparticle solutions were imaged with the broadband TWT oscillator. Thermoacoustic images, displayed in Figure 3, were acquired with excitation frequencies between 7 and 9 GHz in 0.25 GHz intervals. These images indicate that the solutions of SWNTs generated stronger TA signals than deionized water, especially above 8 GHz. This is particularly significant because water itself has substantial absorption in this frequency range.

The TA signal’s amplitude at each microwave frequency, averaged over the cross-section of each tube, is displayed in Figure 4(a). Both solutions of SWNTs manifested a TA signal that increased linearly as a function of microwave frequency. The stock solutions of semiconducting and metallic SWNTs had respective slopes of 1.75 AU/GHz (, ) and 2.8 AU/GHz (, ) compared to the unit normalized slope of deionized water. Figure 4(b) presents an image of the sample cross-section based on the slope of the best-fit line at each pixel. The three samples have distinct spectral signatures, allowing each to be uniquely identified from their frequency-dependent TA signal without relying on the magnitude of the signal at any particular frequency.

Because most of the solutions were composed of water (>99% by weight) with significant background absorption, we also estimated the individual contribution of the nanoparticles to the cumulative TA signal. Equation (2) was used to decompose the contributions of the total TA signal into two discrete sources of microwave absorption (i.e., water and SWNTs) using the known nanoparticle concentration of each solution ( ppm,  ppm) and the measured TA spectrum of deionized water. This approach also compensates for different nanoparticle concentrations and, thereby, enables better quantification of the nanoparticle’s true absorption profile. The expected TA signals from samples of pure SWNTs are displayed in Figure 5 on the same scale as Figure 4. The semiconducting SWNTs exhibited a strong absorption profile that increased linearly with frequency. The metallic SWNTs, on the other hand, revealed a much stronger signal than both deionized water and semiconducting SWNTs between 7 and 9 GHz with the TA signal increasing exponentially within this frequency range.

Although the TA signal is directly proportional to the absorption coefficient of each sample, it is not a direct measure of microwave absorption due to other factors that affect the TA signal, such as the thermoelastic expansion and specific heat (see (1)). However, we expected the frequency-dependence of the microwave absorption between 1 and 10 GHz to be dominated by changes in its absorption properties. The linear absorption spectrum of semiconducting nanoparticles near 3 GHz and between 7 and 9 GHz is consistent with previous reports describing slowly varying dielectric properties for SWNTs in this frequency range [24]. Conversely, TAI and spectroscopy revealed an exponentially increasing signal for the metallic SWNTs between 7 and 9 GHz. Other studies have reported spectrally varying dielectric properties of SWNTs near this frequency range using other methods, such as field emission scanning electron microscopy [24, 25, 27, 28]. The exact mechanism of the increase could be explained by a plasmon resonance, specific to the size and distribution of the metallic SWNTs, modulating the attenuation coefficient of the nanoparticles [29]. The sharp spectral signature and large signal enhancement of metallic SWNTs may facilitate clinical application of contrast-enhanced TAS for diagnostic cancer imaging. Exploiting their frequency-dependent absorption may also improve their heating efficiency for deeper imaging and therapy in soft tissue using high-frequency microwaves.

4. Conclusions

This study employed spectroscopic thermoacoustic imaging to characterize the spectral dependence of semiconducting and metallic single-walled carbon nanotubes (SWNTs) between 2.7 and 9 GHz. These nanoparticles were found to have distinct and differentiable absorption spectra in this frequency range. In particular, after compensating for effects of the background water signal, metallic SWNTs displayed an exponentially increasing thermoacoustic signal between 7 and 9 GHz. In tissue, the strong and distinct microwave absorption properties of metallic SWNTs could be separated from endogenous background absorbers (e.g., blood, muscle, and fat) using spectral decomposition to facilitate in vivo detection of small tumors. Molecularly targeted SWNTs combined with thermoacoustic spectroscopy could lead to highly sensitive and specific detection and imaging of cancer cells followed by delivery of therapeutics. These agents could also be used with microwave heating for targeted ablation and cancer therapy.

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

Acknowledgments

The authors are grateful to Raytheon Corporation for providing access to their 7+ GHz microwave transmitter, which made this study possible. They also acknowledge the Center for Gamma Ray Imaging for maintaining and running the rapid prototyping printer, which was used to fabricate the imaging tank for this study.