Investigation of Structural Formation of Starting Composition 2245 in the Bi-Pb-Sr-Ca-Cu-O System Superconductors
Table 1
Heating profile and results of X-ray diffraction analysis of samples.
| Sample name |
History of heat treatment |
Å
|
Å
|
Å
|
Cell volume (10−30) m3 |
Grain size (in nm) | Temperature (°C) | Duration (hours) |
| M1 | 835 | 42 | 5.387 | 5.301 | 24.574 | 701.747 | 40.116 | M2 | 835 | 42 | 12.247 | 3.780 | 3.259 | 150.871 | 74.570 | M12 A | 850 | 5 | 5.393 | 5.421 | 30.788 | 900.200 | 61.139 | M12 B | 850 | 10 | 5.389 | 5.395 | 30.767 | 894.580 | 75.690 | M12 C | 850 | 15 | 5.392 | 5.365 | 30.874 | 893.198 | 61.137 | M12 D | 850 | 20 | 5.401 | 5.391 | 30.775 | 896.255 | 72.250 | M12 E | 850 | 25 | 5.404 | 5.396 | 37.253 | 1086.570 | 63.580 | M12 F | 850 | 30 | 5.398 | 5.402 | 37.220 | 1085.335 | 58.870 | M12 G | 850 | 40 | 5.390 | 5.415 | 37.216 | 1086.217 | 44.170 | P 2245 | 835 | 45 | 5.423 | 5.407 | 37.003 | 1085.008 | 68.814 |
|
|