Abstract

An accelerated life testing investigation was conducted on a composite cylinder that consists of aluminum alloy and T700 carbon fiber. The ultimate failure stress predictions of cylinders were obtained by the mixing rule and verified by the blasting static pressure method. Based on the stress prediction of cylinder under working conditions, the constant stress accelerated life test of the cylinder was designed. However, the failure data cannot be sufficiently obtained by the accelerated life test due to the time limitation. Therefore, most of the data presented to be high censored in high stress level and zero-failure data in low stress level. When using the traditional method for rupture life prediction, the results showed to be of lower confidence. In this study, the consistency of failure mechanism for carbon fiber and cylinder was analyzed firstly. According to the analysis result, the statistical test information of carbon fiber could be utilized for the accelerated model constitution. Then, rupture life prediction method for cylinder was proposed based on the accelerated life test data and carbon fiber test data. In this way, the life prediction accuracy of cylinder could be improved obviously, and the results showed that the accuracy of this method increased by 35%.

1. Introduction

In recent years, T700 carbon fiber replacing T300 becomes the new general carbon fiber since densification gives the T700 higher tensile strength [16]. The cylinder of new special equipment consists of T700 carbon fiber composite materials, glass fiber composites, and aluminum alloy. The main role of aluminum alloy is to improve the axial modulus and corrosion resistance of cylinder, the glass fiber composite material is to guarantee the aluminum alloy being adapted to higher working because of large prestress, and the carbon fiber composite material is to improve the strength and modulus of the cylinder and it is also the main load-bearing material between the three-layer materials.

The introduction of carbon fiber into the new generation cylinder improves the failure stress of the cylinder, but it also brings new problem to the reliability evaluation of the cylinder. The cylinder wound by T700 carbon fiber exhibits long life and high reliability in high-speed rotation mode, and the sufficient data cannot be obtained by the traditional life tests. Therefore, the accelerated test must be introduced, and the reliability index in the normal stress could be extrapolated by the statistical analysis using the high stress level data [7]. The maximum likelihood estimation method [8, 9] is very suitable for the censored data analysis, but this method only has good properties for the large sample. And it needs to iterate for the transcendental equations; sometimes the computation is difficulties and not convergence. The integral best linear unbiased estimation method [10, 11] solves problems by regression analysis based on linear transformation acceleration model. The information between different stresses is used comprehensively, and the estimation accuracy can be improved. But the evaluation accuracy is still unable to meet the actual engineering requirement of the cylinder structure with great life dispersion.

This study found that the failure mode of the cylinder wound by T700 carbon fiber was carbon fiber breakage in the working mode with high-speed rotation. Therefore, there would be some relationship between the rupture life of fiber carbon and the cylinder. In this study, we analyzed the mechanical properties of the cylinder composite material and obtained the ultimate failure stress by mixing rules, which were verified by the static pressure burst test method. Then we designed accelerated life tests on the carbon fiber and the cylinder. According to the test results, we proposed the integral best unbiased estimate method for the cylinder life prediction. The evaluation accuracy was greatly improved by comprehensive evaluation using the information of T700 carbon fiber based on the test results of the accelerated equivalence and failure mechanisms.

2. Mechanical Analysis

2.1. Mechanical Analysis of the Composite Material

The new generation cylinder consists of aluminium alloy, glass fiber, and T700 carbon fiber, and its structure is illustrated in Figure 1.

The main role of the aluminium alloy is to improve the axial modulus and anticorrosion of the cylinder. The glass fiber is to impose prestress to the aluminium alloy according to winding, and so it could improve the maximum capacity. The carbon fiber is the main bearing materials and for their high strength and modulus the ultimate failure stress of cylinder is greatly improved. The mechanical properties of the glass fiber and the carbon fiber can be obtained by mixing rules according to tensile strength, modulus, and the volume content of each fiber. Thus, the overall mechanical properties of the cylinder could also be estimated by the mixing rule basing on the material properties and structures.

According to the property test of T700 carbon fiber, the tensile strength is 4900 Mpa, the modulus is 230 GPa, and the strain is approximately 2%. Also, the matrix strength of the composite material is 85 MPa, the modulus is 2.8 Gpa, and the strain is 4%. The mix rule iswhere the is tensile strength of composite, is the tensile strength of fiber, is the tensile strength of matrix, and is the fiber volume. Therefore, for the fiber volume of composite material used in this study is 72%, the tensile strength of this composite would be calculated as 3551.8 MPa.

For the glass fiber, the tensile strength is 3400 MPa, the modulus is 91 GPa, and the strain is approximately 3.7%. And the matrix is the same with the T700 carbon fiber reinforced composite. While the percentage of fiber volume is 76%, according to the mix rule, the tensile strength of this glass fiber reinforced composite would be calculated as 2604.4.

The lining of the cylinder is aluminium alloy, its elastic modulus is 70 GPa, yield strength is 610 Mpa, tensile strength is 640 Mpa, and strain is greater than 4% [12].

2.2. Failure Stress Analysis of the Cylinder

The tensile modulus of the glass fiber and the aluminium alloy is significantly lower than the outer carbon fiber composite material by the previous analysis. And according to the thickness of each laminate listed in Table 1, it is obvious that the carbon fiber is the main load-bearing material in the entire cylinder. When the outer T700 carbon fiber reinforced composite is destructed, the glass fiber and aluminum alloy would be instantaneously destroyed due to the large load. The stress-strain curves of glass fiber and carbon fiber reinforced composite materials presented to be linear like the tensile stress-strain curves of glass fiber and carbon fiber that are shown in Figures 2 and 3.

The bearing stress of glass fiber is 380 Mpa that is the reverse stress to impose on the aluminum alloy; therefore, its bearing stress is 1777 Mpa when the conditions are the same with the outer carbon fiber. The tensile strength of aluminum alloy is 640 MPa, we consider that it imposed the reverse prestress of 380 MPa, its bearing stress is 260 Mpa when the breaking elongation is 2%, and its thickness is 1.2 mm. The thickness of glass fiber and the carbon fiber is 0.85 mm and 1.5 mm, respectively. Therefore, according to the mixing rule, the ultimate failure stress of the cylinder is theoretical as

The strip tensile test method [13] for ultimate failure stress of the cylinder cannot meet the requirements of test accuracy with a few samples. The NOL [13] ring stretching method is sensitive to the boundary effects and sample processing is very difficult. Therefore, we chose the blasting static pressure method [14] for the ultimate failure stress testing which dealt with the data as a whole and thus could reflect the mechanical properties better.

The test samples were produced according to the national standard GB/T15560, and the processing technical, raw materials were the same with the cylinder. Figure 4 shows the size of this test sample. As shown, two ends of the cylinder were strengthened by carbon fiber layers of 30 mm width. Table 2 shows the parameters of this static pressure burst test. Table 3 shows the test result.

It can be seen from Table 3 that the mean of the ultimate test failure stress is 2067.6 MPa, which is slightly higher than the theoretical prediction of 2004 Mpa. It may be the reason that the overall performance of the cylinder material would be slightly higher than fiber samples. The parameters used for theoretical prediction were the mean value of the tensile test results of fiber sample, and thus its volatility is relatively large. Another main reason may be that the length of the test sample in the static pressure burst test was required to be at least 5 times greater than the diameter in test standard of GB/T15560. But this long diameter ratio of our test sample is only 2.7. As the shorter sample is sensitive to the effects of the end portion in the testing process, this may be the main reason that the test results are slightly higher than the prediction result. In all, the test results of the static pressure burst test made a good agreement with the prediction result, and it is feasible to verify the overall performance of the cylinder. This test result would be taken as the important reference for the constant stress accelerated life test in the following research.

3. Accelerated Life Test

3.1. Experiment Preparation

In the working conditions, the bearing stress of cylinder is about 913.8 Mpa, which is equivalent to 45.5% of the ultimate failure stress. We calculated the stress level of the cylinder by the finite element method, and the result shows that the bearing stress of the lining aluminum alloy is 240 MPa, the bearing stress of the glass fiber is 1060 Mpa, and the bearing of carbon fiber is 1350 MPa. The related parameters are shown in Table 1.

The cylinder used in the accelerated life test is the same as that used in the static pressure burst test, as shown in Figure 5. Then, the cylinder is filled with hydraulic oil up to certain pressure and maintains this pressure for a long time so that the cylinder bears a uniform inner pressure in every direction. The test device is placed in one oven where working temperature could be maintained. The pressure can be tested by the pressure sensor. If the pressure of the cylinder drops significantly, the cylinder was considered to be failure and the failure time is automatically recorded.

3.2. The Accelerated Test Plan of the Cylinder

We know the ultimate failure stress is 2067.6 Mpa given by the static pressure burst test and the working stress is 913.8 Mpa, which is equivalent to 45.5% of the ultimate failure stress of the cylinder. The stress-strain curve is close to linear in the scope of the ultimate failure stress of the cylinder.

According to GB 2689.1-81, we divided the cylinders into five groups for constant stress accelerated life test. And we set the minimum stress level to be 1315 MPa (almost 63.6% of the ultimate failure stress) and the maximum stress level to be 1861 MPa (almost 90% of the ultimate failure stress). Also, other stress levels were set to be 72.7%, 80%, and 85% of the ultimate failure stress, respectively. According to the test standard of GB 2689.1-81, this test level setting could ensure that the failure mechanism of cylinders was the same. The working temperature of the cylinder will not exceed 40°C, so the test temperature is controlled at °C.

4. Results and Discussion

4.1. The Method on Rupture Life Evaluation of the Cylinder

We assume that there are samples prepared for type-I censored test in the    stress level and the censored time is . There are    failures and the censored data is .

Hypothesis 1. The product life follows Weibull distribution in the stress level.

Hypothesis 2. The failure mechanisms of the carbon fiber and the cylinder are the same in each stress level.

Hypothesis 3. The relationship between characteristic life and stress level follows the inverse power law model: ,  . And are parameters that should be estimated.

The linear expression can be obtained by logarithmic transformation on the accelerated model in Hypothesis 3:Then the logarithmic life follows the extreme value distribution and the relationship between the logarithmic life and the logarithmic stress can be written aswhere ,  ,  , and . Parameter reflects the characteristic of test product; parameter reflects the acceleration characteristic of the test; is the scale parameter of the extreme value distribution and the measure parameter for the consistency of the failure mechanism.

In the condition of Hypothesis 1, type-I censored data can be taken as the value of the former order statistics for the extreme value distribution with size . can be taken as the value of the interval statistics with the same sample.

From literature [9, 10], we can obtain the estimations of , , and by partial derivative for The estimations of , , and   arewhere

And the covariance matrix of , and   iswhere ,   is the mean of the order statistic for the standard extreme value distribution with size , is the covariance of the and order statistic for the standard extreme value distribution with size ,   is the mean of the order statistic for the standard extreme value distribution with size , and   is the covariance of the and order statistic for the standard extreme value distribution with size . These values could be all obtained by formula or table lookup [15].

The reliability rupture life with reliability of and its upper and lower limits with confidence level could be calculated as follows:where are elements of the matrix ,  , and .

The Failure Mechanism Consistency Analysis. This analysis focused on the consistency of failure mechanism and accelerated model parameter between the carbon fiber and cylinder in the accelerated life test. Denote the model parameters of the carbon fiber and the cylinder as , , and   and , , and  , respectively. We assume the following.(1)The distribution parameters , are two independent normal populations. If the failure mechanism of the carbon fiber is the same with the cylinder, the mean and variance of the two normal populations are the same [16, 17].(2)Parameters of and reflect the life characteristic of carbon fiber and cylinder, and then and have no relation.(3)The model parameters , are two independent normal populations. If the acceleration of the carbon fiber is the same with the cylinder, the mean and variance of the two normal populations are the same.

Based on the above assumptions, and can be taken as two bivariate normal populations. We can judge the consistency of the mean vector and covariance matrix of the two bivariate normal populations by hypothesis test.

(1) The Consistency Judgment of the Mean Vector. The two independent normal populations are denoted by and . We sample ,   specimens from them, respectively, and denote the mean vectors by ,  , respectively, and the variance matrix by . The hypothesis isWhen and they were unknown, the test statisticwhereAnd .

Then the rejection region with the significance level is

(2) The Consistency Judgment of the Variance Matrix. The hypothesis isThe amendatory likelihood ratio statistic isThen,whereand .

Then the rejection region with the significance level isThe information fusion method

Based on the result of the integral best linear unbiased estimation and the consistency analysis of failure mechanism, we proposed an information fusion method for the covariance matrixes of the T700 carbon fiber and the cylinder. The fusion process can be accomplished by the two steps: firstly, fusing the information only related to parameters and in the covariance matrix and then, secondly, to further improve the evaluation accuracy of the covariance matrix for model parameter of the cylinder, fusing the other information related to and .

Denote the point estimations of T700 carbon fiber and the cylinder by , , and   and , , and  , respectively, and their covariance matrix is

Denote the covariance matrix of the bivariate normal distribution of , and , , respectively, by

The elements of the above matrixes are one part of (19).

The first step is fusing the information only related to parameters and in the covariance matrix.

If the covariance matrixes and are certified to be the same by the consistency analysis of the bivariate normal distribution and , the unbiased estimation of the covariance matrix of the bivariate normal distribution can be obtained by the following equation:

Compared to the small ratio of failure and high censored time of the cylinder life test, the data and failures of the carbon fiber are much greater and thus the evaluation result is more accurate. Therefore, when the matrix is replaced by with fusing the information of parameters and according to the above method, the prediction result of the cylinder is more accurate. The covariance matrix of and based on fusion could be written as

The covariance matrix for the cylinder with bottom right four elements replaced by could be written as

The second step is fusing the other elements related to of the covariance matrix.

Based on the same correlation coefficient between the parameters, the value of , with fusing the information of the T700 carbon fiber can be calculated as

According to the above two steps, the covariance matrix can be written as

Comparing with (25) and (19)  , it can be found that the elements of parameter covariance matrix of the cylinder have changed in addition to the variance by fusing the carbon fiber test information, thus making the evaluation result more reasonable. It should be noted that the parameter covariance matrix can be obtained by the integrated best linear unbiased estimation as follows:

In the calculation of the upper and lower limits for the reliability rupture life, the matrix would be used. Therefore, in fusion process of the covariance matrix with T700 carbon fiber information and cylinder information, we can introduce the matrix directly in the above method to make the calculation easier.

4.2. Examples

To verify the design level of the rupture life of a certain type of cylinder, a unit made accelerated life tests for T700 carbon fiber composite material and the cylinder structure, respectively. The test temperature is 40°C, and the test load conditions are shown in Table 4.

The diagram of rupture life data for T700 carbon fiber and the cylinder structure from the test is as in Figures 6 and 7.

(1) The Result of the Integral Best Unbiased Estimation. The results of model parameters and the matrix obtained by the integrated best linear unbiased estimation are shown in Table 5.

(2) The Test of Mean Vector and Covariance Matrix Equal to of the Carbon Fiber and the Cylinder. We consider parameters as a bivariate normal population and test whether the mean vectors and covariance matrixes of for the carbon fiber and the cylinder are equal or not, and the results are shown in Table 6.

From Table 6, the observed values of the test statistic are Then, we can receive the null hypothesis. The mean vectors and the covariance matrixes of for the carbon fiber and the cylinder are equal.

(3) The Information Fusion of the T700 Carbon Fiber and the Cylinder. By using the method in this paper, the matrix information of carbon fiber in Table 5 can be fused into the cylinder and the upper and lower limits of the reliability rupture life at confidence level can be calculated. The comparison results are shown in Table 7.

From Table 7, when the reliability is 0.9, the evaluation accuracy of the reliability life of the cylinder is increased by 35%.

The curves of upper and lower limits of the logarithmic reliability rupture life changed with the reliability are shown in Figure 7.

Figure 8 shows that the upper and lower limits of the reliability rupture life will be more accurate with the reliability changed after fusion of the information of T700 carbon fiber and the interval length is much shorter.

5. Conclusion

(1)Since the carbon fiber bears the main load at work, the acceleration and failure mechanism of T700 carbon fiber and the cylinder are the same. And it can be proved by the structure analysis and the statistic test of the test data.(2)When the acceleration and failure mechanism are the same, the evaluation accuracy of the reliability life for the cylinder can be improved by fusion of the information of the carbon fiber.(3)The method in this paper is based on Weibull distribution and the inverse power law model for structured products. It can be applied to other location-scale family distribution and acceleration models.

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

Acknowledgments

The work described in this paper was supported by the National Natural Science Foundation of China (Grants nos. 61104133 and 61473014). The authors fully appreciate the financial support. The authors would like to thank the reviewers and the editor for many suggestions that helped improve this paper.