Design of Thermal Barrier Coatings Thickness for Gas Turbine Blade Based on Finite Element Analysis

Li, Biao; Fan, Xueling; Li, Dingjun; Jiang, Peng

doi:https://doi.org/10.1155/2017/2147830

Mathematical Problems in Engineering

On this page

Abstract Introduction Conclusion Conflicts of Interest Acknowledgments References Copyright Related Articles

Research Article | Open Access

Volume 2017 | Article ID 2147830 | https://doi.org/10.1155/2017/2147830

Design of Thermal Barrier Coatings Thickness for Gas Turbine Blade Based on Finite Element Analysis

Biao Li,¹Xueling Fan,¹Dingjun Li,^1,2and Peng Jiang¹

Academic Editor: Fabrizio Greco

Received08 May 2017

Accepted05 Jun 2017

Published06 Jul 2017

Abstract

Thermal barrier coatings (TBCs) are deposited on the turbine blade to reduce the temperature of underlying substrate, as well as providing protection against the oxidation and hot corrosion from high temperature gas. Optimal ceramic top-coat thickness distribution on the blade can improve the performance and efficiency of the coatings. Design of the coatings thickness is a multiobjective optimization problem due to the conflicts among objectives of high thermal insulation performance, long operation durability, and low fabrication cost. This work developed a procedure for designing the TBCs thickness distribution for the gas turbine blade. Three-dimensional finite element models were built and analyzed, and weighted-sum approach was employed to solve the multiobjective optimization problem herein. Suitable multiregion top-coat thickness distribution scheme was designed with the considerations of manufacturing accuracy, productivity, and fabrication cost.

1. Introduction

Thermal barrier coatings (TBCs) are widely used in advanced gas turbines to provide the thermal and oxidation protection to metallic substrate against high temperature gas [1, 2]. Application of TBCs can significantly improve the performance and efficiency of the turbines. A typical TBC system is composed of a load carrying substrate, a ceramic top-coat (TC), a metallic bond-coat (BC), and the thermally grown oxide (TGO) that forms between TC and BC.

Generally, the temperature decreases across TBCs at specific operation condition are governed by the material and geometrical properties of the TC layer, especially the thermal conductivity and thickness [3–9]. For a given ceramic material, the thermal insulation capability of the coatings enhances with the increase of TC thickness. Nevertheless, the thermal mismatch stress within the coatings may also increase simultaneously. It is recognized that there exists a balance between the thermal insulation capability and thermal stress level. Determination of suitable TC thickness for the hot components becomes an optimization problem.

Optimal design of TBCs thickness for gas turbine blade can improve the performance and efficiency of the coatings. It is desirable to have an available, simple, and efficient approach to design the coatings for engineering application. Unfortunately, little work has been reported on this issue. Most investigations about the turbine blade deal with the substrate without TBCs, which fails to take into account the influence induced by the coatings, such as failure analysis of the blade [10–12], heat transfer simulation [13, 14], or design of cooling channels [15]. A few works raised concerns about TBCs on the real turbine blade. For instance, Sohn et al. [16] experimentally investigated the microstructural development of TBCs in high pressure turbine blade before and after the service. Significant sintering and phase transformation were observed, and localized spallation of yttria partially stabilized zirconia (YSZ) was found near the tip of the serviced blade. Gurrappa and Rao [17] conducted the hot corrosion experiments on cylindrical specimens having various TBCs thicknesses and figured out that an optimum thickness of TBCs can enhance the life of underlying superalloy by about six hundred times. Yang et al. [18] developed finite element (FE) model for the blade with TBCs to investigate the failure behavior under cyclic thermal loading. Zhu et al. [19] studied the effect of morphology of TGO on stress distribution in a turbine blade with TBCs under cyclic thermal loading.

Above works provided insight into the influence of TBCs on turbine blade. However, none of them deals with the issue of design of TBCs thickness. Actually, due to the difficulty in meshing a real gas turbine blade having complex external and internal geometry shapes, most numerical works instead utilized two-dimensional or simplified three-dimensional model in their simulations. For example, Yang et al. [18] and Zhu et al. [19] used the simplified three-dimensional FE models in which the blade airfoil uniformly and straightly extends from platform to the tip, and a single cooling passage is assumed as well. It should be pointed out that the simplified models can hardly reflect temperature and stress fields in the real blade which thus leads the obtained conclusions to become circumscribed.

This work aims to develop a procedure for designing TBCs thickness distribution for gas turbine blade. Sophisticated three-dimensional FE model of the turbine blade with TBCs is built and analyzed. The optimization design procedures are presented and applied to obtain the preliminary thickness distributions. Finally, suitable TC thickness distribution scheme is determined according to the quantitative comparison. This work provides a primary coating distribution scheme for turbine blade.

2. Finite Element Modeling

2.1. Geometry and Meshing

The blade investigated in this work is a first-stage rotor blade in a gas turbine, as shown in Figure 1. It has complex external and internal geometries, which includes an airfoil having concave pressure side and convex suction side, a platform defining the boundary for the hot gas, and a supporting shank positioned below the platform. The blade is hollow and includes multiple serpentine cooling passages for receiving the pressurized cooling air. The blade root which can attach the blade to rotor disk is not included in present model, since it has little influence on the problem we are concerned with. As can be seen in Figure 1(d), the airfoil has a feature of twisting around the radial centerline when extending radially outward from the platform to the blade tip. The dimension of a cross section of the airfoil is shown in Figure 1(e).

(a)

(b)

(c)

(d)

(e)

(f)

The complexity of geometry makes it challenging to mesh the turbine blade. We built the three-dimensional FE model by using a combination of Altair HyperMesh and ABAQUS packages. Generally, the geometrical model of the substrate built in CAD software was firstly imported into HyperMesh and then meshed with hexahedron and tetrahedron elements. The FE model was subsequently imported into ABAQUS as orphan mesh geometry. The mesh offset technique provided by ABAQUS, which can generate solid mesh layers by offsetting a mesh surface along its normal direction, was then applied to generate mesh layers of TC, TGO, and BC. Small geometrical details of the substrate were defeatured to avoid small elements when generating mesh using HyperMesh. The blade airfoil, platform, and bottom part of the shank were mostly meshed with 8-node solid hexahedron elements except those with bad quality which were replaced by linear tetrahedron elements. The remaining part of the shank was meshed with linear tetrahedron elements, since it is impossible for it to be meshed with hexahedron elements, attributing to its complex external and internal geometries. According to the engineering practice, as shown in Figure 2, the outer surface of the airfoil and the top surface of the platform are coated with TBCs.

The nominal mesh sizes of the airfoil and platform were chosen as 0.8 mm, and the nominal mesh size is 2.5 mm for the shank. The thickness of TC varies in different analysis cases. BC is constantly 150 μm thick and is meshed with two layers of elements in all models. TGO is also modelled in the analysis with a thickness of 5 μm. It should be pointed out that this work does not intend to simulate the growth of TGO, but the large elastic modulus mismatch among TGO and neighboring layers has a significant influence on the stress field [20, 21], which makes it necessary to include TGO layer in the models. However, dividing TGO into multiple layers of elements can lead to very large element aspect ratio. Thus, it is modeled with one single layer of elements. This choice of mesh density may cause some numerical disturbance, but the analysis accuracy is believed to be sufficient to obtain the design scheme.

The total number of elements is approximately 1.0 million, including 0.62 million of hexahedron elements (C3D8R), 0.36 million of tetrahedron elements (C3D4), and 0.02 million of triangular prism elements (C3D6). The mesh sensitive analysis was conducted. The mesh sizes used in the simulations can obtain adequate computational accuracy and ensure acceptable cost.

2.2. Material Properties and Boundary Conditions

The TBCs are composed of APS ZrO₂-8 wt% Y₂O₃ (8YSZ) TC layer, α-Al₂O₃ TGO layer, NiCrAlY BC layer, and nickel superalloy substrate. All layers are considered to be isotropic, homogenous, and temperature-independent. The materials properties are listed in Table 1.

A uniform temperature boundary condition was imposed on the blade without taking into account the thermal radiation and convection. According to the typical thermal conditions in turbine engine [13, 18, 22], the TC surface is heated from 20°C to 1150°C, and the inner surface of cooling passages is heated from 20°C to 700°C simultaneously, both of which are assumed to be implemented in sufficient time to reach a steady state. The ENCASTRE boundary condition is assigned to the bottom surface of blade shank in stress analysis.

2.3. Thermal and Stress Analysis

The evaluations of stress and temperature fields are carried out in ABAQUS by using the sequentially coupled method. This method considers a one-way interaction between stress/deformation and temperature, which is often used for problems where stress field depends on the temperature field, but the reverse is not significant. It is implemented by first conducting an uncoupled steady-state heat transfer analysis and then a stress analysis. Nodal temperature taken from the former analysis is imported into stress analysis as a predefined temperature field.

3. Design of Top-Coat Thickness for Turbine Blade

3.1. Optimization Approach

Generally, the in-service performance, durability, and fabrication cost are three main objectives in determining TBCs thickness for a gas turbine blade. Parameters should be carefully selected to represent above objectives.

For in-service performance aspect, thermal insulation capability is the most important requirement. Application of high thermal insulation TBCs can reduce the temperature of substrate to prolong its lifetime or allows increasing the turbine inlet temperature and thereby improving the engine efficiency. Thus, the temperature difference between TC surface and substrate surface is considered as a performance parameter. Larger temperature decreases across the coatings mean better thermal insulation performance.

The durability of TBCs is mainly related to the intrinsic failure mechanisms of the coatings. Interfacial delamination is one of the major weaknesses of the coatings. Higher thermal stress gives rise to premature delamination and shorter lifetime. Delamination may be avoided when the stresses are low enough. Therefore thermal stress is considered as a parameter controlling the durability of TBCs, which should not exceed a critical value and should be kept as low as possible.

Moreover, the fabrication cost and technical difficulties increase while using thick TBCs, which indicates that thinner TBCs are preferred. The TC thickness is chosen as a parameter to characterize the fabrication cost.

Taking into account the above factors, design of TBCs thickness is a multiobjective optimization problem, which can be formulated as follows.where is design variable that denotes the TC thickness, is the maximum von Mises stress within TC, and is the temperature difference between the TC surface and the substrate surface.

In this work, and are assumed to be 100 μm and 800 μm, respectively. It is known that thick TC can cause high residual stress during spraying and may potentially have influence on the gas flowing area. Thus, we assign the upper limit of TC thickness, , as 800 μm. The critical allowed stress in TC, , is assigned as an experimentally measured biaxial strength of 174 MPa [25]. The temperature on the superalloy substrate, , is assumed to be no higher than the critical value, = 1000°C.

To make the problem easier, an evaluation parameter, , is defined to estimate the comprehensive thermal and mechanical performances of the TBCs as follows:

Obviously, smaller value of means better performance of the TBCs. By using the single scalar evaluation parameter, the objectives of low stress level and high thermal insulation are combined together.

The objective function in (1) is defined to have the targets of low stress level, high thermal insulation, and low fabrication cost. However, there are conflicts among these objectives. For instance, the thermal insulation performance improves with the increase of TC thickness, but the induced thermal stress and fabrication cost are also enhanced. No optimal solution exists to minimize all the functions simultaneously. Rather, the optimization is likely to result in a set of points that constitute Pareto front [26–28]. Many weakly Pareto optimal solutions exist for the problem. It is often necessary to incorporate preference conditions in order to determine a single suitable solution.

It should be mentioned that this work aims to develop a procedure to design the TBCs thickness instead of focusing on complex optimization algorithm. Thus, the classical weighted-sum approach is employed to solve the multiobjective problem herein. However, other advanced optimization algorithms, such as evolutionary algorithm [29], genetic algorithm [30], particle swarm algorithm [31], and simulated annealing algorithm [32], are still valid in the design procedure.

By using the weighted-sum approach, the multiple objectives are scalarized into a single scalar objective aswhere and are objectives of performance and TC thickness, respectively, which are expressed as

Generally, the sum of all scalar weights equals one; namely, , with . Selection of scalar weights affects the optimal TC thickness at a representative position. Larger means better performance is preferred and thicker TC should be used.

In general, the assignment of weights depends on the designer’s decision. In this work, considering that higher performance of TBCs is more attractive, we empirically choose the weight for the performance objective and for the fabrication cost objective. Actually, we have examined the sensitivity of design scheme to the scalar weights. It is found that different weights in part affect the optimal TC thickness at some representative positions, but this weight has insignificant influence on the determination of design scheme when the weights are within some extent; for example, schemes resolved from and 0.7 are identical to each other.

The objective function in (3) only aims at finding suitable TC thickness for a single position on the blade. To evaluate the superiority of a thickness distribution scheme, a series of representative positions on the blade need to be selected and their total sum of objective functions is employed, which is given aswhere is the number of selected representative positions, is the objective function of th position, and is the sum of all objective functions. It seems that an optimization design scheme having smaller value of is preferred. However, the feasibility and complexity of the fabrication process are other important factors that must be taken into account during the final selection of scheme.

3.2. Optimization Design Procedure

The optimization design procedure can be divided into three main processes: preliminary analysis, optimization design, and scheme verification:(i)In the preliminary analysis process, FE models with uniform TC thickness are analyzed, and at the every representative position is calculated. Ten uniform-thickness schemes are considered in this work, in which TC thicknesses range from 100 μm to 1000 μm with an increment of 100 μm. There are totally 91 positions in this analysis, including 84 on the blade airfoil and 7 on the platform, as shown in Figure 3.(ii)In the optimization design process, the weighted-sum method is applied for each representative position to find an optimal TC thickness. Note that the representative position stands for a region having the same TC thickness. According to the preliminary optimal thickness distributions, the overall coating region is divided into multiple subregions to form the multiregion scheme.(iii)In the scheme verification process, FE model using the multiregion scheme is built and analyzed, and the total objective function is calculated. Note that the magnitude of depends on the quantity and distribution of the representative positions. It is difficult to predefine a universal value of to evaluate the superiority of a scheme for any given analysis. Thus, the available way is to compare of a multiregion scheme with those of the uniform-thickness schemes. The superiority of different optimization schemes will be known from the reduction in total objective function.

The detailed optimization procedure is shown in Figure 4 and can be described in the following steps.

Step 1. Build FE model for the turbine blade using uniform-thickness scheme, where TC is assigned to be uniform throughout the coating region.

Step 2. Perform thermal and stress analysis using the sequentially coupled method, and the overall temperature and stress fields are obtained.

Step 3. Select the representative positions on the blade and determine their objective functions . Calculate the total objective function for current uniform-thickness scheme.

Step 4. Judge whether all the uniform-thickness schemes have been finished. If not yet, go back to Step 1. Otherwise, calculate the optimal TC thickness using the weighted-sum method for each representative position.

Step 5. Design a multiregion TC thickness distribution scheme.

Step 6. Build FE model using the multiregion scheme obtained in Step 5 and perform thermal and stress analysis.

Step 7. Calculate the total objective function .

Step 8. Compare of the multiregion scheme with those of the uniform-thickness schemes. If the reduction in total objective function is satisfied, the optimization design is finished. Otherwise, go back to Step 5.

4. Numerical Results and Discussions

4.1. Results of Uniform-Thickness Scheme

When using the uniform-thickness scheme, the TC thickness is uniform throughout the coating region. Typical temperature field and that of the substrate are shown in Figure 5 (taking the 500 μm uniform thickness scheme as example). The high temperature region on the substrate is generally located at root of the airfoil, especially at the blade platform. The trailing edge has much lower temperature than leading edge due to the thin substrate and effective internal cooling therein.

(a)

(b)

(c)

Overall, the FE analysis shows that as the TC thickness increases, the temperature on the airfoil of the substrate is impressively decreased, but the platform is not apparent. To explain the difference between these two parts, typical representative positions A and B are selected and their temperature distributions are given in Figure 6, where paths are defined to be from TC surface to the BC/substrate interface. The distributions are generally bilinear, in which lines at left side represent the decrease within TC and the right ones denote the variation within TGO and BC. The thermal barrier effect at position B is not significant due to the fact that the platform is far away from internal cooling passages. For example, when the TC thickness is 1000 μm, the temperature reduction at position A is about 240°C, while it is 100°C at position B. The temperature gradient is reduced for thicker TC at position A, but it is almost unchanged at position B.

(a)

(b)

The von Mises stress distributions are presented in Figure 7, where paths are defined from TC surface to the TC/TGO interface. It is shown that stresses at both positions increase from TC surface and reach the maximum at TC/TGO interface, and surface stress in thinner TC is higher than that of thick TC. It is interesting that the maximum stress increases with the increase of TC thickness for position A, but it is reverse for position B. It can be explained by the low temperature gradient at the platform, which also leads to the low stress gradient. The above results imply that the blade platform should be coated with as thick TC as possible.

(a)

(b)

The Pareto sets for typical representative positions A, C, D, and E (see Figure 3) represent suction side, leading edge, pressure side, and trailing edge on the airfoil, respectively, as shown in Figure 8. The Pareto fronts of these four representative positions are convex. Actually, the Pareto fronts of all representative positions on the blade are convex and meet the requirement of weighted-sum method.

The optimal TC thicknesses for all the representative positions on the airfoil are determined and the preliminary optimal thickness distribution is illustrated in the form of region contour, as shown in Figure 9(a). The thickness distribution has the qualitatively similar appearance to the temperature field on substrate. The blade tip and bottom area need thicker TC than the middle region.

(a)

(b)

(c)

(d)

4.2. Optimization Designed Multiregion Thickness Distribution

According to the preliminary results, we proposed three design schemes and then made comparison among them to find a suitable TC thickness distribution. In general, the design of coatings thickness distribution should take the practical spraying process into account. Due to the twisting feature of the airfoil, it is easier to spray the coatings by dividing the subregions along the vertical direction.

The proposed multiregion schemes are illustrated in Figures 9(b)–9(d), in which the pressure side and the suction side of the airfoil are dealt with separately. Both sides may be further divided into multiple subregions, where the TC thickness within a subregion is the same. Since a subregion contains several representative positions having different optimal TC thicknesses, we conservatively determine the thickness of a subregion equal to the highest value predicted within it. Generally, scheme is designed having the fewest subregions and easiest fabrication process, but scheme is reverse. The TC thickness of the platform in all schemes is assigned as 800 μm.

The FE model using the above three multiregion schemes was built and analyzed. And then were calculated. For comparison, of all the uniform-thickness schemes along with multiregion schemes are illustrated in Figure 10. It is seen that the values of for uniform-thickness schemes rapidly increase for TC thickness above 500 μm, which indicates the low efficiency of TBCs with uniform TC thicker than it. Although the scheme of 300 um uniform thickness has low , it fails to satisfy the thermal constraint condition, which is the temperature on the substrate of airfoil being no higher than 1000°C.

In general, the difficulty in spraying the TBCs on the turbine blade is definitely enhanced when the thickness distributions scheme becomes complex. For multiregion schemes, decreases with the increasing number of subregions, which means that more detailed dividing of subregions can help improve the comprehensive superiority of the scheme. However, the ideal thickness scheme contains so many subregions having different thicknesses that it is difficult to be implemented in the practical spraying process. Considering that of scheme are close to that of scheme but the fabrication process is much easier, we suggest that scheme is more suitable for engineering application.

Actually, of these multiregion schemes have been initially estimated before above verification process. For a given multiregion scheme, of each position is directly calculated by using the results from uniform-thickness schemes. It is found that estimated for schemes to 3 are 37.5, 36.4, and 36.2, respectively. The corresponding values obtained in verification process are 37.4, 36.3, and 36.0, respectively. The differences are less than 6%. Therefore, we conclude that estimating the superiority of a design scheme can be easily and quickly accomplished by using the results of uniform-thickness schemes.

The temperature fields of the blade using design scheme are illustrated in Figure 11. The temperature distribution on the airfoil of substrate is basically the superposition of the temperature fields of corresponding uniform-thickness schemes. The relative high temperature region is enlarged and temperature distributes more uniformly compared with that of uniform-thickness schemes.

(a)

(b)

(c)

The thermal stress distributions in TC and substrate are shown in Figure 12. The stresses within TC on the platform are higher than the ones of airfoil. Due to the imposed ENCASTRE boundary condition, the thermal stress at bottom part of the blade shank reaches a very high level, which is consistent with results from other studies [11].

(a)

(b)

(c)

(d)

5. Conclusion

This paper proposed a design method to obtain suitable thermal barrier coatings (TBCs) thickness distribution for a real gas turbine blade. Three-dimensional finite element model of the turbine blade with TBCs was built and analyzed, and the weighted-sum approach was used to solve the multiobjective optimization problem. The design method provides quantitative comparison for the selection of TBCs thickness so as to improve the efficiency of the coatings. It is found that the thermal insulation capability and stress level within the coatings on the blade airfoil are enhanced with the increase of top-coat thickness. Nevertheless, the thermal barrier effect of the coatings on the blade platform is not significant. For multiregion schemes, more detailed dividing of subregions can improve the comprehensive superiority of the scheme, but the fabrication difficulty should be considered accordingly. A three-subregion scheme is found to be suitable for engineering application.

Conflicts of Interest

The authors declare that there are no conflicts of interest regarding the publication of this paper.

Acknowledgments

This work is supported by China 973 Program (2013CB035700) and National Natural Science Foundation of China (11472204 and 11602188).

References

N. P. Padture, M. Gell, and E. H. Jordan, “Thermal barrier coatings for gas-turbine engine applications,” Science, vol. 296, no. 5566, pp. 280–284, 2002.
View at: Publisher Site | Google Scholar
X. Fan, R. Xu, and T. J. Wang, “Interfacial delamination of double-ceramic-layer thermal barrier coating system,” Ceramics International, vol. 40, no. 9, pp. 13793–13802, 2014.
View at: Publisher Site | Google Scholar
X. Q. Cao, R. Vassen, and D. Stoever, “Ceramic materials for thermal barrier coatings,” Journal of the European Ceramic Society, vol. 24, no. 1, pp. 1–10, 2004.
View at: Publisher Site | Google Scholar
X. Fan, W. Jiang, J. Li, T. Suo, T. J. Wang, and R. Xu, “Numerical study on interfacial delamination of thermal barrier coatings with multiple separations,” Surface and Coatings Technology, vol. 244, pp. 117–122, 2014.
View at: Publisher Site | Google Scholar
R. Ghasemi, R. Shoja-Razavi, R. Mozafarinia, and H. Jamali, “Comparison of microstructure and mechanical properties of plasma-sprayed nanostructured and conventional yttria stabilized zirconia thermal barrier coatings,” Ceramics International, vol. 39, no. 8, pp. 8805–8813, 2013.
View at: Publisher Site | Google Scholar
B. Li, Y. Li, and J. Su, “A combined interface element to simulate interfacial fracture of laminated shell structures,” Composites Part B: Engineering, vol. 58, pp. 217–227, 2014.
View at: Publisher Site | Google Scholar
P. F. Zhao, C. A. Sun, X. Y. Zhu, F. L. Shang, and C. J. Li, “Fracture toughness measurements of plasma-sprayed thermal barrier coatings using a modified four-point bending method,” Surface and Coatings Technology, vol. 204, no. 24, pp. 4066–4074, 2010.
View at: Publisher Site | Google Scholar
Y. Sun, W. Zhang, J. Li, and T. J. Wang, “Local stress around cap-like portions of anisotropically and nonuniformly grown oxide layer in thermal barrier coating system,” Journal of Materials Science, vol. 48, no. 17, pp. 5962–5982, 2013.
View at: Publisher Site | Google Scholar
S. Kim, J. Go, Y.-G. Jung, and J.-H. Lee, “Thermoelastic characteristics in thermal barrier coatings with a graded layer between the top and bond coats,” Mathematical Problems in Engineering, vol. 2013, Article ID 515792, 8 pages, 2013.
View at: Publisher Site | Google Scholar
Y.-S. Choi and K.-H. Lee, “Investigation of blade failure in a gas turbine,” Journal of Mechanical Science and Technology, vol. 24, no. 10, pp. 1969–1974, 2010.
View at: Publisher Site | Google Scholar
J. Hou, B. J. Wicks, and R. A. Antoniou, “An investigation of fatigue failures of turbine blades in a gas turbine engine by mechanical analysis,” Engineering Failure Analysis, vol. 9, no. 2, pp. 201–211, 2002.
View at: Publisher Site | Google Scholar
V. N. Rao, I. N. N. Kumar, N. Madhulata, and A. Abhijeet, “Mechanical analysis of 1st stage marine gas turbine blade,” International Journal of Advanced Science and Technology, vol. 68, pp. 57–64, 2014.
View at: Publisher Site | Google Scholar
M. Alizadeh, A. Izadi, and A. Fathi, “Sensitivity analysis on turbine blade temperature distribution using conjugate heat transfer simulation,” Journal of Turbomachinery, vol. 136, no. 1, Article ID 011001, 2013.
View at: Publisher Site | Google Scholar
K. M. Kim, J. S. Park, D. H. Lee, T. W. Lee, and H. H. Cho, “Analysis of conjugated heat transfer, stress and failure in a gas turbine blade with circular cooling passages,” Engineering Failure Analysis, vol. 18, no. 4, pp. 1212–1222, 2011.
View at: Publisher Site | Google Scholar
T. Sadowski and P. Golewski, “The influence of quantity and distribution of cooling channels of turbine elements on level of stresses in the protective layer TBC and the efficiency of cooling,” Computational Materials Science, vol. 52, no. 1, pp. 293–297, 2012.
View at: Publisher Site | Google Scholar
Y. H. Sohn, E. Y. Lee, B. A. Nagaraj, R. R. Biederman, and R. D. Sisson Jr., “Microstructural characterization of thermal barrier coatings on high pressure turbine blades,” Surface and Coatings Technology, vol. 146-147, pp. 132–139, 2001.
View at: Publisher Site | Google Scholar
I. Gurrappa and A. S. Rao, “Thermal barrier coatings for enhanced efficiency of gas turbine engines,” Surface and Coatings Technology, vol. 201, no. 6, pp. 3016–3029, 2006.
View at: Publisher Site | Google Scholar
L. Yang, Q. X. Liu, Y. C. Zhou, W. G. Mao, and C. Lu, “Finite element simulation on thermal fatigue of a turbine blade with thermal barrier coatings,” Journal of Materials Science & Technology, vol. 30, pp. 371–380, 2014.
View at: Google Scholar
W. Zhu, M. Cai, L. Yang, J. W. Guo, Y. C. Zhou, and C. Lu, “The effect of morphology of thermally grown oxide on the stress field in a turbine blade with thermal barrier coatings,” Surface and Coatings Technology, vol. 276, pp. 160–167, 2015.
View at: Publisher Site | Google Scholar
M. Bäker, “Influence of material models on the stress state in thermal barrier coating simulations,” Surface and Coatings Technology, vol. 240, pp. 301–310, 2014.
View at: Publisher Site | Google Scholar
M. Y. He, J. W. Hutchinson, and A. G. Evans, “Simulation of stresses and delamination in a plasma-sprayed thermal barrier system upon thermal cycling,” Materials Science and Engineering A, vol. 345, no. 1-2, pp. 172–178, 2003.
View at: Publisher Site | Google Scholar
N. Asok Kumar and S. R. Kale, “Numerical simulation of steady state heat transfer in a ceramic-coated gas turbine blade,” International Journal of Heat and Mass Transfer, vol. 45, no. 24, pp. 4831–4845, 2002.
View at: Publisher Site | Google Scholar
Y. C. Zhou and T. Hashida, “Coupled effects of temperature gradient and oxidation on thermal stress in thermal barrier coating system,” International Journal of Solids and Structures, vol. 38, no. 24-25, pp. 4235–4264, 2001.
View at: Publisher Site | Google Scholar
M. Ranjbar-Far, J. Absi, G. Mariaux, and F. Dubois, “Simulation of the effect of material properties and interface roughness on the stress distribution in thermal barrier coatings using finite element method,” Materials and Design, vol. 31, no. 2, pp. 772–781, 2010.
View at: Publisher Site | Google Scholar
L. Su, W. Zhang, X. Chen, and T. J. Wang, “Experimental investigation of the biaxial strength of thermal barrier coating system,” Ceramics International, vol. 41, no. 7, pp. 8945–8955, 2015.
View at: Publisher Site | Google Scholar
I. Y. Kim and O. L. De Weck, “Adaptive weighted-sum method for bi-objective optimization: pareto front generation,” Structural and Multidisciplinary Optimization, vol. 29, no. 2, pp. 149–158, 2005.
View at: Publisher Site | Google Scholar
R. T. Marler and J. S. Arora, “The weighted sum method for multi-objective optimization: new insights,” Structural and Multidisciplinary Optimization, vol. 41, no. 6, pp. 853–862, 2010.
View at: Publisher Site | Google Scholar | MathSciNet
K. Deb, “Multi-objective optimization,” in Search Methodologies, pp. 403–449, Springer, 2014.
View at: Google Scholar
E. Zitzler and L. Thiele, “Multiobjective evolutionary algorithms: a comparative case study and the strength Pareto approach,” IEEE Transactions on Evolutionary Computation, vol. 3, no. 4, pp. 257–271, 1999.
View at: Publisher Site | Google Scholar
S. Y. Wang, K. Tai, and M. Y. Wang, “An enhanced genetic algorithm for structural topology optimization,” International Journal for Numerical Methods in Engineering, vol. 65, no. 1, pp. 18–44, 2006.
View at: Publisher Site | Google Scholar
R. C. Eberhart and Y. Shi, “Particle swarm optimization: developments, applications and resources,” in Proceedings of the Congress on Evolutionary Computation, vol. 1, pp. 81–86, IEEE, Seoul, Republic of Korea, May 2001.
View at: Publisher Site | Google Scholar
P. J. van Laarhoven and E. H. Aarts, Simulated Annealing: Theory and Applications, Kluwer Academic Publishers, 1987.

Copyright

Copyright © 2017 Biao Li et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

9268

Downloads

2850

Citations