Mathematical Modeling of Multiple Quality Characteristics of a Laser Microdrilling Process Used in Al7075/SiC_p Metal Matrix Composite Using Genetic Programming

Table 5

Comparison between experimental and predicted values of spatter at R² = 99.3.

No.	PP (W) ()	PF (Hz) ()	AGP (kg/cm^2) ()	PW (ms) ()	Spatter (mm)		Error %
					Experimental	GP
1	220	220	10	0.4	0.055	5.49E − 02	0.00013
2	230	220	11	0.6	0.044	4.42E − 02	−0.00018
3	210	250	12	0.6	0.044	4.34E − 02	0.000648
4	240	220	12	0.3	0.043	4.32E − 02	−0.00022
5	230	240	8	0.3	0.04	4.36E − 02	−0.00365
6	210	230	10	0.3	0.042	4.21E − 02	−7.3E − 05
7	250	240	10	0.2	0.065	6.50E − 02	3.18E − 05
8	230	230	12	0.2	0.043	4.31E − 02	−7.8E − 05
9	240	240	9	0.6	0.072	7.16E − 02	0.000406
10	230	220	11	0.2	0.045	4.50E − 02	−1.6E − 05
11	250	230	9	0.2	0.068	6.82E − 02	−0.00024
12	220	240	12	0.6	0.052	5.23E − 02	−0.00028
13	210	250	12	0.5	0.043	4.29E − 02	6.36E − 05
14	220	210	9	0.4	0.059	5.94E − 02	−0.00045
15	210	220	9	0.2	0.0445	0.044101	0.000399
16	220	240	12	0.2	0.05	5.02E − 02	−0.00019
17	230	210	10	0.5	0.072	7.03E − 02	0.001661
18	230	240	8	0.4	0.071	6.97E − 02	0.001265
19	240	210	11	0.2	0.056	5.54E − 02	0.000566
20	230	250	9	0.5	0.074	7.25E − 02	0.001524
21	240	230	8	0.4	0.075	0.064522	0.010478
22	220	250	8	0.3	0.074	0.071546	0.002454
23	250	210	12	0.5	0.046	5.18E − 02	−0.00581
24	210	240	11	0.4	0.043	4.20E − 02	0.000993
25	230	210	10	0.6	0.049	5.21E − 02	−0.00307
26	250	250	11	0.3	0.065	5.50E − 02	0.010003
27	210	230	10	0.4	0.04	4.28E − 02	−0.00277
28	210	210	8	0.6	0.043	0.042277	0.000723
29	210	240	11	0.5	0.045	0.044648	0.000352
30	220	230	11	0.6	0.057	5.40E − 02	0.003045
31	240	220	12	0.4	0.042	4.29E − 02	−0.00093
32	240	250	10	0.2	0.066	6.64E − 02	−0.00042
33	230	230	12	0.3	0.041	4.27E − 02	−0.00171
34	230	250	9	0.4	0.069	6.84E − 02	0.000556