Computations of Ultrasonic Parameters in Alloys
Table 1
SOEC, TOEC, and Bulk Modulus (
) in the unit of 10
10 Nm
−2 of ZrSn alloys at room temperature.
(a) |
| Alloys | | | | | | | |
| 1 | 22.416 | 5.505 | 4.712 | 22.312 | 5.652 | 8.791 | 10.775 | 2 | 19.116 | 4.694 | 3.904 | 17.962 | 4.683 | 7.500 | 9.003 | 3 | 20.215 | 4.964 | 4.147 | 19.162 | 4.974 | 7.928 | 9.551 | 4 | 20.424 | 5.015 | 4.176 | 19.240 | 5.009 | 8.009 | 9.628 | Zr [24] | 14.10 | 6.76 | 6.43 | 16.69 | 2.58 | 3.68 | | Sn [25] | 7.01 | 3.81 | | | 3.68 | | |
|
|
(b) |
| Alloys | | | | | | | | | | |
| 1 | −365.54 | −57.96 | −12.09 | −15.36 | −75.37 | −70.66 | −17.90 | −11.93 | −289.23 | −278.90 | 2 | −311.73 | −49.42 | −10.01 | −12.73 | −60.67 | −56.88 | −14.83 | −9.88 | −246.65 | −218.15 | 3 | −329.65 | −52.26 | −10.64 | −13.52 | −64.72 | −60.68 | −15.75 | −10.50 | −260.83 | −233.73 | 4 | −333.06 | −52.81 | −10.71 | −13.61 | −64.99 | −60.92 | −15.86 | −10.57 | −263.52 | −233.95 |
|
|