A Comparative Study of Spin Coated Transparent Conducting Thin Films of Gallium and Aluminum Doped ZnO Nanoparticles

Figure 8

Resistivity of GZO and AZO 5 layers with doping ratio of 1 mol.%, deposited on quartz substrate and sintered in air at different temperatures and then postannealed in reducing gas for 90 min at 400°C.