In Vitro Degradation Behaviors of Manganese-Calcium Phosphate Coatings on an Mg-Ca-Zn Alloy
Table 1
Composition of solutions and Mn content in the coatings of samples.
| | Composition of phosphating solution (mol/L) | Mn content in phosphating coating (EDS in Figure 3) (wt%) |
| Sample 1 | Base solution | 0 | Sample 2 | Base solution with 0.01 mol/L Mn2+ | 0.13% | Sample 3 | Base solution with 0.03 mol/L Mn2+ | 0.96% | Sample 4 | Base solution with 0.05 mol/L Mn2+ | 13.83% | Sample 5 | Base solution with 0.07 mol/L Mn2+ | 14.16% |
|
|
Composition of base solution: 0.26 mol/L CaNO 3⋅4H 2O, 0.17 mol/L H 3PO 4 aqueous solution at pH 2.7. |