Effects of Hydrogen Contents on Oxidation Behavior of Alloy 690TT and Associated Boron Accumulation within Oxides in High-Temperature Water

Jeon, Soon-Hyeok; Song, Geun Dong; Hur, Do Haeng

doi:https://doi.org/10.1155/2018/7845176

Scanning

On this page

Abstract Introduction Experimental Results and Discussion Conclusions Conflicts of Interest Acknowledgments References Copyright Related Articles

Research Article | Open Access

Volume 2018 | Article ID 7845176 | https://doi.org/10.1155/2018/7845176

Effects of Hydrogen Contents on Oxidation Behavior of Alloy 690TT and Associated Boron Accumulation within Oxides in High-Temperature Water

Soon-Hyeok Jeon,¹Geun Dong Song,¹and Do Haeng Hur¹

Academic Editor: Eliane D'Elia

Received30 Nov 2017

Revised19 Apr 2018

Accepted10 May 2018

Published10 Jun 2018

Abstract

The aim of this work is to characterize the oxide layer structure of Alloy 690TT in high-temperature water with different dissolved hydrogen (DH) contents by using an X-ray photoelectron spectroscopy. Under the low DH contents (0.4494–0.8988 mg/kg), the oxide layers were composed of an outermost layer of Ni(OH)₂ and Cr(OH)₃ enriched in Ni, an intermediate layer of hydroxides and oxides enriched in Cr, and an inner Cr₂O₃ layer. Outermost NiO coexists with small amount of Cr₂O₃ layer, while in the inner oxide only Cr₂O₃ remains. The oxide layers at medium and high DH contents (3.1458– 8.9880 mg/kg) consisted of an outermost layer of Ni(OH)₂ and Cr(OH)₃ enriched in Cr, an intermediate layer of metallic Ni, hydroxides and oxides enriched in Cr, and an inner Cr₂O₃ layer. In addition, boron compounds containing B³⁺ ions were accumulated in the thick and porous NiO layer formed at low DH contents, whereas the accumulation of boron compounds did not occur in the thin and dense polyhedral oxide layer formed at medium and high DH contents.

1. Introduction

Alloy 690, a nickel-based alloy having high chromium content (27–31 wt.%), was developed as a replacement for Alloy 600 steam generator (SG) tubes owing to its excellent resistance to stress corrosion cracking (SCC) in a pressurized water reactor (PWR) [1–4]. Although no in-service SCC failures of Alloy 690 tubes have been reported, its long-term service performance is a highly concerned issue because Alloy 690 still suffers from general corrosion in the primary water of PWRs [5]. The oxidation behavior of Alloy 690 has been one of the interesting topics because the oxide layers formed on alloys act as an important role to their corrosion resistance.

The effects of various water chemistry parameters such as dissolved oxygen (DO) [6], pH [7, 8], temperature [8–10], Li/B coordination [11], and Zn injection [12, 13] on the oxidation behavior of nickel-based alloys have been investigated extensively. Besides, dissolved hydrogen (DH) is also an important parameter because it can significantly affect the oxide formation and the corrosion behavior of nickel-based alloys [14–17].

There are many researches related to hydrogen contents in the primary water of PWRs. For the fuel cladding, Kawamura [18] showed that the amount of crud (Chalk River unidentified deposits) deposition and boron accumulation of the fuel cladding was not affected by a change in hydrogen content. Baek et al. [19] also presented that the DH content did not greatly affect the amount of crud deposits formed on the fuel cladding. In the viewpoint of nickel-based alloys, hydrogen-related researches have been focused mainly on the stress corrosion cracking (SCC). The DH content can significantly affect the crack growth rate (CGR) of nickel-based alloys in the primary water of PWRs [20, 21]. That is, the CGR shows a maximum value at a DH content where the Ni/NiO phase transition occurs. Therefore, it has been generally considered that the oxide layers formed on the surface of nickel-based alloys have a crucial role in the SCC growth rate [16]. Recently, it has been reported that the structure of oxide film of Alloy 690TT was significantly changed and general corrosion decreased with increasing the DH contents (0.4494–8.9880 mg/kg) [22]. In addition, it has shown that the oxide film formed on Alloy 690TT was porous and thick at low DH content (0.4494 mg/kg) in primary water system [22].

Meanwhile, boron accumulation may occur within not only the crud formed on the fuel cladding but also the oxide layer on Alloy 690TT at low DH content because both oxide layers have a thick and porous morphology. However, the effects of the hydrogen contents on the oxide structure and associated boron accumulation within oxide layer of Alloy 690TT have not yet been investigated. Furthermore, the detailed depth profile of the chemical state of the oxide layers formed on Alloy 690TT has not been reported under the broad range of DH contents by using X-ray photoelectron spectroscopy (XPS).

Therefore, the purpose of this study is to characterize the oxide layer structure of Alloy 690TT and associated boron accumulation within its oxide layers in primary water at 330°C and 150 bars in the broad range of DH contents (0.4494–8.9880 mg/kg) by using XPS. To observe the boron accumulation within the oxide layers, the depth profile and chemical species of the oxide layers were analyzed by XPS analysis.

2. Experimental

2.1. Specimen Preparation

Alloy 690TT tubes, which are commonly used as a SG tubing material, were used in this study. Alloy 690TT tubes have a dimension of a 19.07 mm outer diameter (OD) and a 16.93 mm inner diameter (ID). The specimens were cut into a size of 10 mm × 10 mm × 1.07 mm for the oxidation tests and various oxide layer analyses. The specimens were cleaned in acetone and distilled water. After the specimens had been cleaned, the piece specimens were directly dried in a vacuum oven at 60°C. While the preparing for the oxidation tests, the samples were stored in a vacuum desiccator at room temperature to prevent the oxidation reaction in the air. In addition, because Alloy 690TT is a high-alloyed steel having excellent corrosion resistance, the surface composition of the Alloy 690TT before the oxidation test could be considered to the same as that of the matrix. The chemical composition of Alloy 690TT was analyzed in accordance with the standard of ASTM E353-14 for method for chemical analysis of stainless, heat-resisting, maraging, and other similar chromium-nickel-iron alloys [23]. The chemical composition of Alloy 690TT tubes is given in Table 1.

2.2. Oxidation Tests

Oxidation tests for the oxide formation were performed in an autoclave connected to a high-temperature water circulating system. The circulation system consisted of the following main components: a primary solution tank, high-pressure pump, preheater for solution inlet temperature control, back pressure regulator for pressure control, heat exchanger, and an autoclave for placing the specimens. The test solution was preheated and entered into the autoclave where the piece specimens were hung on a specimen holder.

The test solution was maintained consistently at 330°C under 150 bars in the autoclave because the saturation pressure of the high-temperature water at 330°C is about 128 bars. The simulated primary water was made using the demineralized water with the resistivity above 18 MΩ·cm, nuclear-grade lithium hydroxide (LiOH), and boric acid (H₃BO₃). The solution was 2.2 ppm Li as LiOH and 1200 ppm B as H₃BO₃ in weight. These test conditions such as temperature, pressure, and the content of Li and B were chosen to simulate a typical primary coolant in PWRs [24]. The exposure time for oxidation tests was selected to 500 h based on the experimental conditions of the previous studies regarding the corrosion behavior of nickel-based alloys such as Alloy 600 [16], Alloy 690 [6], and Alloy 182 [25].

The simulated primary water was stored in the solution tank with a capacity of 150 L. The DH contents were selected to 0.4494, 0.8988, 3.1458, 4.4940, 5.8422, and 8.9880 mg/kg (5, 10, 35, 50, 65, and 100 cc/kg H₂O) at standard temperature and pressure (STP), which is a temperature of 0°C and a pressure of 1 bar by controlling the hydrogen overpressure of the solution tank. DO content was controlled in the range of 2–3 ppb to eliminate the oxygen effect on the corrosion potential and oxidation reaction. After the oxidation tests were finished, the specimens were directly cleaned in distilled water and dried in a vacuum oven at 60°C. Then, before analyzing the oxide layer by various analyses, the specimens were quickly stored in a vacuum desiccator at room temperature to avoid the variation on the oxide layer structure. In a previous study, the oxidation tests were conducted to Alloy 690TT under the same experimental conditions [22]. In this study, the oxidation tests were also carried out under the same conditions to clarify the relationship between oxide structure of Alloy 690TT and boron accumulation and the detailed chemical states of oxide layer by using XPS analysis, which was not performed in a previous study.

2.3. Analysis of Oxide Layer

The outer surface of the oxide layer formed on Alloy 690TT specimens was observed by using a SEM with Hitachi S-4800, of which acceleration voltage was 10 kV. The cross-section of oxide layer was also examined by using focused ion beam FIB (FEI company QUANTA 3D FEG)-SEM. The thickness of oxide layers was measured from the cross-sectional images obtained by FIB-SEM analysis. The thickness measurement was done at least at three different positions.

To elucidate the effect of oxide layer structure on the boron accumulation within the oxide, the depth profiles and chemical species of the oxide layers were analyzed by using XPS. The XPS analysis was carried out by using a Thermo Fisher Scientific (Theta Probe AR-XPS) X-ray photoelectron spectrometer with an Al Kα X-ray source (1486.6 eV) operated at 15 kV and 150 W under a base pressure of 2.7 × 10⁻⁷ Pa. If necessary, the surface of the specimens was slightly etched using 1.0 kV argon ion beam. The binding energies of all peaks were corrected with the reference C1s peak at 284.5 eV.

The removal (ex situ) of Alloy 690TT specimen from the PWR primary water environment may result in a modification of the oxide layer structure. However, in previous studies [26, 27], there is no significant differences between in situ and ex situ characterization of surface oxide films of nickel-based alloys. Wang performed the in situ surface-enhanced Raman spectroscopy (SERS) to characterize oxide films formed on Alloy 600 and Alloy 690 in PWR primary water and compare the differences between in situ and ex situ characterizations of surface oxide films [26]. He presented that there is no significant changes to the oxide layer of Alloy 690 and only slight changes to the oxide layer of Alloy 600 are possible: partial conversion of Cr₂O₃ to α-CrOOH of Cr(OH)₃ on cooling to room temperature, and a small increase in the relative amount of spinel upon exposure to air at room temperature [26]. Recently, Kim et al. [27] performed the in situ and ex situ Raman spectroscopy to analyze the oxide films formed on dissimilar metal weld (DMW) interfaces of nickel-based alloy/low alloy steel under hydrogenated high-temperature water condition. There was also no significant change in the oxide structure and only a slight difference in the intensity of the Fe₃O₄ and NiCr₂O₄ peaks [27].

3. Results and Discussion

3.1. SEM Analysis

Figure 1 shows the SEM micrographs of the oxide layers formed on Alloy 690TT in simulated PWR primary water with the broad DH range of 0.4494–8.9880 mg/kg. The morphologies of the external oxide layers were greatly changed corresponding to DH content. It was clear that the external oxide layer formed at DH = 0.4494 mg/kg was covered with numerous needle-like oxides and small planer oxide particles (Figure 1(a)). The needle-like oxide particles with a diameter of less than 100 nm were randomly tangled. The planer oxide particles were randomly dispersed with the needle-like oxides. The size of the planer oxide particles was approximately 150–400 nm. Whereas, a great number of needle-like oxides were only observed without the planar oxide particles on the surface of the specimen under the condition of DH = 0.8988 mg/kg (Figure 1(b)). The needle-like oxides at DH = 0.8988 mg/kg were much larger and thicker than the needle-like oxides at DH = 0.4494 mg/kg. As shown in Figures 1(c)–1(f), the morphology and number of the outer oxide particles formed at medium and high DH contents (DH = 3.1458–8.9880 mg/kg) are greatly different from the oxide particles formed at low DH contents (DH = 0.4494–0.8988 mg/kg). In the DH range of 3.1458–8.9880 mg/kg, the fine polyhedral oxide particles with a size of 20–200 nm were formed on the whole surface of specimens. The number of the oxide particles decreased with increasing the DH content.

(a)

(b)

(c)

(d)

(e)

(f)

Figure 2 presents the FIB-SEM images of the cross-section of oxide layers formed under the conditions of DH = 0.4494 and 3.1458 mg/kg. In case of DH = 0.4494 mg/kg, the outer oxide layer had a thick and porous structure, whereas the inner oxide layer was compact and continuous. However, under the condition of DH = 3.1458 mg/kg, the external oxide layer had a thin and dense structure. In addition, the inner oxide layer appeared not to be continuous. The cross-sectional structure of the external oxide layers was well consistent with the top view images shown in Figure 2. The thickness of oxide layers decreased with increasing the DH content. The mean thickness of the oxide layer at DH = 0.4494 mg/kg was about 880 nm and approximately 185 nm at DH = 3.1458 mg/kg, respectively. In particular, the thickness of outer needle-like oxide at DH = 0.4494 mg/kg is very thick (about 800 nm).

(a)

(b)

3.2. XPS Depth Profile and Spectrum Analyses

Figure 3 shows the XPS depth profiles of the oxide layers. From the half-height of the oxygen theory [14, 28], the thickness of oxide layers could be quantitatively estimated. That is, the point where the intensity of oxygen content reaches 50% of its initial value is taken as the interface between the oxide layer and steel substrate. The oxide layers formed at DH = 0.4494 mg/kg require approximately 21 min of sputtering time to reach 50% of its initial value. Under the conditions of DH = 3.1458, 4.4940 and 5.8422 mg/kg, the sputtering time of oxide films which the oxygen content was half of the initial value was about 1 min. Among the DH contents, the sputtering time of oxide layers at DH = 5.8422 mg/kg was the shortest about 0.84 min. These results indicate that the oxide layer formed at low DH content grew thicker, and the oxide layer formed at medium and high DH contents became thinner. These results could be supported by the fact the thickness of oxide layers decreased with increasing the DH content, which was observed in Figure 2. In addition, the B element content was detected about 10 at.% in the outermost NiO layer at DH = 0.4494 mg/kg (Figure 3(a)). In this layer, the content of B element in the NiO layer gradually decreased with the increase of sputtering time. Finally, the B element disappeared in the inner Cr-rich oxide layer. However, the B element was not detected under other DH contents (DH = 3.1458, 4.4940, and 5.8422 mg/kg).

(a)

(b)

(c)

(d)

In this work, the thickness of oxide layers could be associated with the thermodynamics and kinetics of corrosion and incorporation of boric oxide. In the viewpoint of corrosion thermodynamics, Cr₂O₃ and Fe₃O₄ are stable phases under all DH contents handled in this work. However, Ni/NiO phase transition is expected to be characterized by the effect of DH content on the electrochemical potential (ECP). The ECP of Alloy 690TT with various DH contents was calculated using Nernst equation for hydrogen-hydrogen ion exchange reaction, and the ECP gradually decreased with increasing DH content [22]. Alloy 690TT is located in the NiO stable region at low DH contents (DH = 0.4494–0.8988 mg/kg), whereas the stable state of Alloy 690TT is metallic Ni at medium and high DH contents (DH = 3.1458–8.9880 mg/kg) [22]. In the NiO stable region, Ni dissolution spontaneously occurs through an oxidative dissolution reaction as shown in the following reaction:

However, the oxidative dissolution reaction of Ni is reduced in the Ni stable region because Ni is no longer a thermodynamically oxidized state. Second, the corrosion kinetics is not only dependent on the microstructure and chemical composition but also dependent on the electronic property of oxide layer. These parameters are crucial to the stability of the oxide layers. Peng et al. [16] presented that increasing DH content decreases the ionic defect transport resistance in the oxide layer and leads to a more defective microstructure of the oxide layers using the in situ measurement of contact electric resistance (CER) and electrochemical impedance. They suggested that the increasing DH content leads to a decrease of the oxide layer thickness due to the differences of these corrosion kinetic parameters [16]. Third, the thickness of oxide layers formed on Alloy 690TT may be affected by the incorporation with boric oxide. Machet et al. [29] presented that a considerable amount of boric trioxide (B₂O₃) is incorporated in the oxide films formed on nickel-based alloy in simulated PWR primary water at 320°C and 155 bars. In this work, boric oxide could be incorporated in the oxide layer and results in a thicker oxide layer.

The XPS depth profile of the three major elements (Ni, Cr, and Fe) normalized to 100% is also shown in Figure 4. As shown in Figure 4(a), at DH = 0.4494 mg/kg, the outer oxide layer is Ni-enriched while depletion of Cr is observed. With the increase of sputtering time, Ni dominant oxide layer disappeared, and the Cr content gradually increased to 48 at.%. Ni enrichment in the inner oxide layer occurred once again, and Cr content slightly decreased. The variation of Ni and Cr may be attributed to the effect of the chemical composition of the matrix. These depth profiles suggest that the outer oxide layer mainly consists of NiO layer, and the inner layer of the oxide layer is dominantly Cr₂O₃ layer. However, the distribution of elements exhibited a significant change in a range of DH = 3.1458–5.8422 mg/kg. The distribution of all elements is very similar under these DH conditions. As shown in Figures 4(b)–4(d), Cr is enriched while Ni is depleted in the outer oxide layer. The increase of Ni content and decrease of Cr content were observed from the surface to the oxide/substrate interface with increasing sputtering time. The variation of Ni and Cr may be due to the matrix.

(a)

(b)

(c)

(d)

Figure 5 shows the XPS spectra of Ni 2p_3/2, Cr 2p_3/2, Fe 2p_3/2, and O 1s for the oxide layers formed at DH = 0.4494 mg/kg. The binding energies () obtained from the deconvoluted XPS profiles of the primary compounds in the layers are listed in Table 2. First, the XPS spectra of Ni 2p_3/2 show that a peak of Ni(OH)₂ and a satellite peak of Ni(OH)₂ could be observed at the outermost oxide surface. At the sputtering time of 540 s, a Ni⁰ peak and a satellite Ni⁰ peak were observed in addition to the NiO peak, while the Ni(OH)₂ peaks disappeared. Following a sputtering time of 1080 s, an increase of Ni⁰ and decrease of NiO peak intensities were observed. At the final sputtering time of 1620 s, only the Ni⁰ peak was identified. The formation of Ni(OH)₂ at the outer oxide layer is most likely owed to the hydration of Ni²⁺. Second, the Cr 2p_3/2 spectrum exhibits a peak related to Cr(OH)₃ on the outermost surface of the oxide layer. Underneath the surface layer, the Cr 2p_3/2 spectrum exhibits a Cr₂O₃ and Cr(OH)₃ peak at the sputtering time of 540 s. At the sputtering time of 1080 s, an increase of the Cr₂O₃ peak intensity and a decrease of the Cr(OH)₃ peak intensity were observed. The peak corresponding to Cr⁰ was also observed. Further increasing the sputtering time to 1620 s, a significant increase of the Cr⁰ peak intensity and a decrease of Cr₂O₃ peak intensity were observed in association with the disappearance of the Cr(OH)₃ peak. Third, only the Fe³⁺ peak was observed at the outermost surface of the oxide layer. However, following a 540 s sputtering, the Fe²⁺ peak was observed in addition to the Fe³⁺ peak. Increasing the sputtering time to 1080 s resulted in the detection of Fe⁰, along with Fe²⁺ and Fe³⁺ peaks. At the final sputtering time of 1620 s, Fe²⁺ peak was not observed, while the increase of Fe⁰ peak and decrease of Fe³⁺ peak could be identified. Finally, the XPS spectra of O 1s show that two peaks could be identified at the outermost surface of the oxide layer (O²⁻ and OH⁻ peaks). Increasing the sputtering time to 540 s and further to 1080 s led to enhanced O²⁻ but weakened OH⁻ peaks. Only O²⁻ peak was observed at the final sputtering times of 1620 s. This was consistent with the above results that the inner layer of the oxide layer consisted of Cr₂O₃ peak, while the surface of the external oxide layer was segregated by Ni(OH)₂ and Cr(OH)₃ due to the hydration of Ni²⁺ and Cr³⁺.

Figure 6 shows the XPS spectra of Ni 2p_3/2, Cr 2p_3/2, Fe 2p_3/2, and O 1s for the oxide layers formed at DH = 4.4940 mg/kg. First, Ni 2p_3/2 spectrum exhibits the peak of Ni⁰ and peak of Ni(OH)₂ at the outer oxide surface. At the sputtering time of 60 s, the increased Ni⁰ peak was observed in addition to the NiO peak, while the Ni(OH)₂ peak disappeared. At the final sputtering time of 120 s, the Ni⁰ peak was only observed. Second, the XPS spectra of Cr 2p_3/2 show only a Cr(OH)₃ peak could be examined at the outer surface of the oxide layer. At the sputtering time of 60 s, the weakened Cr(OH)₃ peak could be detected in addition to the Cr⁰ peak and Cr₂O₃ peak. The increase of the Cr⁰ and Cr₂O₃ peak intensity in association with the disappearance of the Cr(OH)₃ peak was observed at the sputtering time of 120 s. Third, Fe 2p_3/2 spectrum shows the Fe³⁺ peak was only observed on the outermost surface of the oxide layer. At the sputtering time of 60 and 120 s, the Fe³⁺ peak was observed along with Fe⁰ peak and Fe³⁺ peak. Finally, the XPS spectra of O 1s show that O²⁻ peak and OH⁻ peak could be observed at the surface of the oxide layer. Increasing the sputtering time to 60 s and further to 120 s led to enhanced O²⁻ but weakened OH⁻ peaks.

Figure 7 presents the XPS spectra of B 1s for the oxide layers formed at DH = 0.4494 mg/kg. As shown in Figure 7(a), B 1s spectrum exhibits the peak of B³⁺ at the outer oxide surface. At the sputtering time of 300 s, the slightly weakened peak of B³⁺ was still observed within the oxide layer (Figure 7(b)). However, the peak of B³⁺ was not detected at DH = 4.4940 mg/kg. These results indicate that the boron compounds containing B³⁺ were accumulated within the thick and porous NiO layer at low DH contents, whereas the accumulation of boron compounds did not occur in the dense and thin polyhedral (Ni, Cr, and Fe)O layer at medium and high DH contents.

(a)

(b)

Based on the deconvoluted XPS profiles, the depth profile of chemical species on the oxide layers could be presented. Figure 8 shows the depth profile of chemical species on the oxide layers formed at DH = 0.4494 and 4.4940 mg/kg. As mentioned above, the outer part of the oxide layer formed at DH = 0.4494 mg/kg consisted predominantly of Ni²⁺ (Figure 8(a)). By contrast, Cr³⁺ and Ni⁰ were primarily located in the inner part of the oxide layer under this condition. These results indicate that the double-structured oxide layers composed of the outer NiO layer and inner Cr₂O₃ layer were formed at DH = 0.4494 mg/kg. In the oxide layer formed at DH = 4.4940 mg/kg, the outer part of the oxide layer predominantly consisted of Ni²⁺ and Cr³⁺. The Ni²⁺ and Cr³⁺ content gradually decreased, and Ni⁰ content increased with the increase of sputtering time (Figure 8(b)). Finally, the Ni⁰ dominated in the inner part of the oxide layer. These results can indicate that the oxide layer formed at DH = 4.4940 mg/kg consists of outer spinel oxides such as NiCrFeO₄ and metallic Ni-rich layer. However, in this case, the inner Cr₂O₃ layer was not detected because the inner Cr₂O₃ layer appeared not to be continuous.

(a)

(b)

According to the XPS results, the oxide layers formed on Alloy 690TT were composed of oxides and hydroxides under all hydrogen conditions. The formation of Ni(OH)₂ and Cr(OH)₃ at the outer oxide layer is most likely due to the hydration of Ni²⁺ and Cr³⁺. The oxide layers at low DH content were composed of an outermost layer of Ni(OH)₂ and Cr(OH)₃ enriched in Ni, an intermediate layer of hydroxides and oxides enriched in Cr, and an inner Cr₂O₃ layer. Outermost NiO coexists with a small amount of Cr₂O₃ layer; while in the inner oxide, only Cr₂O₃ remains. The oxide layers at medium and high DH contents were composed of an outermost layer of Ni(OH)₂ and Cr(OH)₃ enriched in Cr, an intermediate layer of metallic Ni, hydroxides and oxides enriched in Cr, and an inner Cr₂O₃ layer.

3.3. Effect of Oxide Layer Structure on Boron Accumulation

Boron, in the form of boric acid (H₃BO₃), is added into primary water to control the neutron flux while lithium hydroxide (LiOH) is also dosed to control the pH of the primary water. As presented in the EPRI report [38], boron can accumulate in the pores of crud on the fuel cladding as a concentrated solution or a solid phase when the crud was built upon cladding.

Previous studies have reported that there are only a few different forms of boron species in fuel crud originating from PWR core. It is well known that boric acid may be thought of as hydrates of boric trioxide (B₂O₃). Doncel et al. [39] presented that boron-containing compound is crystalline lithium tetraborate (Li₂B₄O₇), which previously has been identified in simulated fuel crud. Recently, nickel-iron oxyborate known as bonaccordite- (Ni₂FeBO₅-) containing boron was discovered and characterized in fuel crud samples taken from some high fuel-duty PWRs [40]. However, it is not yet known in what form boric acid or oxide is deposited in a PWR fuel crud, although some researchers believe that a predominant form of boron in axial offset anomaly (AOA) fuel crud is lithium metaborate (LiBO₂) [41].

In this study, to elucidate the relationship between the oxide layer structure and boron accumulation within the oxide layers, the depth profiles and chemical species of the oxide layers formed on Alloy 690TT were analyzed by using XPS. It was observed that the B³⁺ ions were detected in the thick and porous NiO layer formed at low DH contents. This indicates that the boron compounds containing B³⁺ ions were accumulated in the thick and porous NiO layer. The content of B³⁺ ions gradually decreased with the increase of sputtering time. Finally, the B³⁺ ions disappeared in the inner Cr₂O₃ layer. However, the accumulation of B³⁺ ions did not occur in the dense and thin polyhedral NiCrFeO₄ layer formed at medium and high DH contents (DH = 3.1458–8.9880 mg/kg). Based on the results, it is confirmed that the morphology and thickness of oxide layer formed on Alloy 690TT could significantly affect the accumulation of boron compounds within its oxide layer. The effect of DH content on the oxide layer structure of Alloy 690TT and associated boron accumulation within its oxide layer is schematically shown in Figure 9.

According to EPRI report, the DH content has been specified to be controlled in a range of 2.2470–4.4940 mg/kg in the primary water chemistry guidelines [24]. EPRI report showed that the DH contents (0.4494– 5.2130 mg/kg) do not appear to greatly impact the relative boron uptake within the crud of fuel cladding in simulated primary water of PWRs, although some systematic trends in the chemical composition of the crud resulting from change in DH contents could be detected [34]. In addition, several researchers suggest that the content of hydrogen does not greatly affect the amount of crud deposits, boron accumulation, and corrosion resistance of fuel cladding [18, 19]. However, Baek et al. [19] proposed that nuclear power plants should be operated at high DH content to prevent the formation of whisker-structured crud on the fuel cladding and thus mitigate the AOA problem.

We think that boron accumulation could occur within not only the pores of crud on the fuel cladding but also porous oxide layer formed on the Alloy 690TT at low DH contents (0.4494–0.8988 mg/kg) because both oxide layers are porous and thick. Based on the results, it was clear that boron compounds containing B³⁺ were accumulated in the thick and porous NiO layer formed at low DH contents.

Under the operation of nuclear power plants, the accumulation of boron compounds containing B³⁺ ions within the oxide layer of Alloy 690TT should be considered for establishing the operation condition of hydrogen content. Accumulation of boron compounds could accelerate general corrosion and primary water stress corrosion cracking (PWSCC) due to a decrease in pH within the porous oxide layer as through the following precipitation reaction of LiBO₂.

Based on the results obtained from this work, it is concluded that the medium and high DH contents located in the Ni stable region are more desirable for SG tube for prohibiting the boron accumulation within the oxide layer of Alloy 690TT because the hideout of boron compounds does not occur in the external dense and thin oxide layer.

4. Conclusions

(1)In primary water of PWRs at 330°C, the oxide layers at low DH content were composed of an outermost layer of Ni(OH)₂ and Cr(OH)₃ enriched in Ni, an intermediate layer of hydroxides and oxides enriched in Cr, and an inner Cr₂O₃ layer. Outermost NiO coexists with a small amount of Cr₂O₃ layer, while in the inner oxide only Cr₂O₃ remains.(2)The oxide layers at medium and high DH content were composed of an outermost layer of Ni(OH)₂ and Cr(OH)₃ enriched in Cr, an intermediate layer of metallic Ni, hydroxides and oxides enriched in Cr, and an inner Cr₂O₃ layer.(3)By XPS analysis, it was observed that B³⁺ ions were accumulated in the porous NiO layer formed at low DH content, whereas the accumulation of B³⁺ ions did not occur in the dense polyhedral oxide layer at medium and high DH contents.(4)Boron compound accumulation should be considered within not only crud on fuel cladding but also oxide layer on SG tube owing to corrosion problem and the content of boron in primary coolant of PWRs.

Conflicts of Interest

The authors declare that there is no conflict of interests regarding the publication of this paper.

Acknowledgments

This work was supported by the National Research Foundation of Korea (NRF) grant funded by the Korean government (2017M2A8A4015159).

References

D. L. Harrod, R. E. Gold, and R. J. Jacko, “Alloy optimization for PWR steam generator heat-transfer tubing,” JOM, vol. 53, no. 7, pp. 14–17, 2001.
View at: Publisher Site | Google Scholar
J. J. Kai, G. P. Yu, C. H. Tsai, M. N. Liu, and S. C. Yao, “The effects of heat treatment on the chromium depletion, precipitate evolution, and corrosion resistance of INCONEL alloy 690,” Metallurgical Transactions A, vol. 20, no. 10, pp. 2057–2067, 1989.
View at: Publisher Site | Google Scholar
P. L. Andresen and M. M. Morra, “Stress corrosion cracking of stainless steels and nickel alloys in high-temperature water,” Corrosion, vol. 64, no. 1, pp. 15–29, 2008.
View at: Publisher Site | Google Scholar
P. M. Scott and P. Combrade, “Corrosion in pressurized water reactor,” in ASM Handbook, vol. 13, pp. 362–385, ASM International, 2006.
View at: Google Scholar
R. W. Staehle and J. A. Gorman, “Quantitative assessment of submodes of stress corrosion cracking on the secondary side of steam generator tubing in pressurized water reactors: part 1,” Corrosion, vol. 59, no. 11, pp. 931–994, 2003.
View at: Publisher Site | Google Scholar
W. Kuang, X. Wu, and E. H. Han, “Influence of dissolved oxygen concentration on the oxide film formed on Alloy 690 in high temperature water,” Corrosion Science, vol. 69, pp. 197–204, 2013.
View at: Publisher Site | Google Scholar
J. Huang, X. Wu, and E. H. Han, “Influence of pH on electrochemical properties of passive films formed on Alloy 690 in high temperature aqueous environments,” Corrosion Science, vol. 51, no. 12, pp. 2976–2982, 2009.
View at: Publisher Site | Google Scholar
D. J. Kim, H. C. Kwon, and H. P. Kim, “Effects of the solution temperature and the pH on the electrochemical properties of the surface oxide films formed on Alloy 600,” Corrosion Science, vol. 50, no. 5, pp. 1221–1227, 2008.
View at: Publisher Site | Google Scholar
H. Sun, X. Wu, and E. H. Han, “Effects of temperature on the protective property, structure and composition of the oxide film on Alloy 625,” Corrosion Science, vol. 51, no. 11, pp. 2565–2572, 2009.
View at: Publisher Site | Google Scholar
G. J. Abraham, R. Bhambroo, V. Kain, R. Shekhar, G. K. Dey, and V. S. Raja, “Electrochemical characterization of oxide film formed at high temperature on Alloy 690,” Nuclear Engineering and Design, vol. 243, pp. 69–75, 2012.
View at: Publisher Site | Google Scholar
I. Betova, M. Bojinov, V. Karastoyanov, P. Kinnunen, and T. Saario, “Effect of water chemistry on the oxide film on Alloy 690 during simulated hot functional testing of a pressurised water reactor,” Corrosion Science, vol. 58, pp. 20–32, 2012.
View at: Publisher Site | Google Scholar
S. E. Ziemniak and M. Hanson, “Zinc treatment effects on corrosion behavior of Alloy 600 in high temperature, hydrogenated water,” Corrosion Science, vol. 48, no. 10, pp. 3330–3348, 2006.
View at: Publisher Site | Google Scholar
J. Huang, X. Liu, E. H. Han, and X. Wu, “Influence of Zn on oxide films on Alloy 690 in borated and lithiated high temperature water,” Corrosion Science, vol. 53, no. 10, pp. 3254–3261, 2011.
View at: Publisher Site | Google Scholar
T. Nakagawa, N. Totsuka, T. Terachi, and N. Nakajima, “Influence of dissolved hydrogen on oxide film and PWSCC of Alloy 600 in PWR primary water,” Journal of Nuclear Science and Technology, vol. 40, no. 1, pp. 39–43, 2003.
View at: Publisher Site | Google Scholar
T. Terachi, N. Totsuka, T. Yamada et al., “Influence of dissolved hydrogen on structure of oxide film on Alloy 600 formed in primary water of pressurized water reactors,” Journal of Nuclear Science and Technology, vol. 40, no. 7, pp. 509–516, 2003.
View at: Publisher Site | Google Scholar
Q. Peng, J. Hou, K. Sakaguchi, Y. Takeda, and T. Shoji, “Effect of dissolved hydrogen on corrosion of Inconel Alloy 600 in high temperature hydrogenated water,” Electrochimica Acta, vol. 56, no. 24, pp. 8375–8386, 2011.
View at: Publisher Site | Google Scholar
Y. Qiu, T. Shoji, and Z. Lu, “Effect of dissolved hydrogen on the electrochemical behaviour of Alloy 600 in simulated PWR primary water at 290°C,” Corrosion Science, vol. 53, no. 5, pp. 1983–1989, 2011.
View at: Publisher Site | Google Scholar
H. Kawamura, “Effect of low DH content on crud deposition on heated zircaly-4 in simulated PWR primary water,” in International Conference on Nuclear Plant Chemistry, pp. 638–648, Paris, France, September 2012.
View at: Google Scholar
S. H. Baek, H. S. Shim, C. H. Won, D. H. Hur, and U. C. Kim, “Effects of Ni, Fe chemicals and hydrogen on deposits formed on Zirlo fuel cladding material in nuclear primary water chemistry conditions at 325°C,” Annals of Nuclear Energy, vol. 70, pp. 233–239, 2014.
View at: Publisher Site | Google Scholar
P. L. Andresen, J. Hickling, A. Ahluwalia, and J. Wilson, “Effects of hydrogen on stress corrosion crack growth rate of nickel alloys in high-temperature water,” Corrosion, vol. 64, no. 9, pp. 707–720, 2008.
View at: Publisher Site | Google Scholar
Q. J. Peng and T. Shoji, “Effects of dissolved hydrogen on the primary water stress corrosion cracking behavior of Alloy 600 at 325 °C,” Key Engineering Materials, vol. 261-263, pp. 943–948, 2004.
View at: Publisher Site | Google Scholar
S. H. Jeon, E. H. Lee, and D. H. Hur, “Effects of dissolved hydrogen on general corrosion behavior and oxide films of alloy 690TT in PWR primary water,” Journal of Nuclear Materials, vol. 485, pp. 113–121, 2017.
View at: Publisher Site | Google Scholar
Annual Book of ASTM Standard, ASTM E353–14, “Standard TEST methods for chemical analysis of stainless, heat-resisting, maraging, and other similar chromium-nickel-iron alloys”.
View at: Google Scholar
K. Fruzzetti, Pressurized Water Reactor Primary Water Chemistry Guidelines-Revision 6, EPRI, Palo Alto, CA, USA, 2007.
J. Xu, T. Shoji, and C. Jang, “The effects of dissolved hydrogen on the corrosion behavior of Alloy 182 in simulated primary water,” Corrosion Science, vol. 97, pp. 115–125, 2015.
View at: Publisher Site | Google Scholar
F. Wang, In-Situ Surface Enhanced Raman Spectroscopy Investigation of the Surface Films on Alloy 600 and Alloy 690 in Pressurized Water Reactor-Primary Water, Ph.D thesis, University of California, Berkeley, 2012.
J. Kim, K. J. Choi, C. B. Bahn, and J. H. Kim, “In situ Raman spectroscopic analysis of surface oxide films on Ni-base alloy/low alloy steel dissimilar metal weld interfaces in high-temperature water,” Journal of Nuclear Materials, vol. 449, no. 1-3, pp. 181–187, 2014.
View at: Publisher Site | Google Scholar
M. Z. Yang, J. L. Luo, Q. Yang, L. J. Qiao, Z. Q. Qin, and P. R. Norton, “Effects of hydrogen on semiconductivity of passive films and corrosion behavior of 310 stainless steel,” Journal of The Electrochemical Society, vol. 146, no. 6, p. 2107, 1999.
View at: Publisher Site | Google Scholar
A. Machet, A. Galtayries, S. Zanna et al., “XPS and STM study of the growth and structure of passive films in high temperature water on a nickel-base alloy,” Electrochimica Acta, vol. 49, no. 22-23, pp. 3957–3964, 2004.
View at: Publisher Site | Google Scholar
F. Huang, J. Q. Wang, E. H. Han, and W. Ke, “Short-time oxidation of Alloy 690 in high-temperature and high-pressure steam and water,” Journal of Materials Science & Technology, vol. 28, no. 6, pp. 562–568, 2012.
View at: Publisher Site | Google Scholar
Z. Duan, F. Arjmand, L. Zhang, F. Meng, and H. Abe, “Electrochemical and XPS investigation of the corrosion behavior of Alloy 690 at high-temperature water,” Journal of Solid State Electrochemistry, vol. 19, no. 8, pp. 2265–2273, 2015.
View at: Publisher Site | Google Scholar
J. Huang, X. Wu, and E. H. Han, “Electrochemical properties and growth mechanism of passive films on Alloy 690 in high-temperature alkaline environments,” Corrosion Science, vol. 52, no. 10, pp. 3444–3452, 2010.
View at: Publisher Site | Google Scholar
H. Sun, X. Wu, E. H. Han, and Y. Wei, “Effects of pH and dissolved oxygen on electrochemical behavior and oxide films of 304SS in borated and lithiated high temperature water,” Corrosion Science, vol. 59, pp. 334–342, 2012.
View at: Publisher Site | Google Scholar
L. Freire, X. R. Nóvoa, M. F. Montemor, and M. J. Carmezim, “Study of passive films formed on mild steel in alkaline media by the application of anodic potentials,” Materials Chemistry and Physics, vol. 114, no. 2-3, pp. 962–972, 2009.
View at: Publisher Site | Google Scholar
W. Xu, K. Daub, X. Zhang, J. J. Noel, D. W. Shoesmith, and J. C. Wren, “Oxide formation and conversion on carbon steel in mildly basic solutions,” Electrochimica Acta, vol. 54, no. 24, pp. 5727–5738, 2009.
View at: Publisher Site | Google Scholar
J. Wang, X. Li, F. Huang, Z. Zhang, J. Wang, and R. W. Staehle, “Comparison of corrosion resistance of UNS N06690TT and UNS N08800SN in simulated primary water with various concentrations of dissolved oxygen,” Corrosion, vol. 70, no. 6, pp. 598–614, 2014.
View at: Publisher Site | Google Scholar
W. A. Brainard and D. R. Wheeler, “An XPS study of the adherence of refractory carbide silicide and boride rf-sputtered wear-resistant coatings,” Journal of Vacuum Science and Technology, vol. 15, no. 6, pp. 1800–1805, 1978.
View at: Publisher Site | Google Scholar
D. Wells, Impact of PWR Primary Water Dissolved Hydrogen Content on Fuel Crud and Boron Accumulation, EPRI, Palo Alto, CA, USA, 2015.
N. Doncel, J. Chen, and H. Bergqvist, “Confirmation of Li₂B₄O₇ presence in fuel CRUD formed under simulated PWR water chemistry conditions,” in International Conference on Water Chemistry of Nuclear Reactor Systems, p. 225, Jeju, Korea, October 2006.
View at: Google Scholar
J. A. Sawicki, “Evidence of Ni₂FeBO₅ and m-ZrO₂ precipitates in fuel rod deposits in AOA-affected high boiling duty PWR core,” Journal of Nuclear Materials, vol. 374, no. 1-2, pp. 248–269, 2008.
View at: Publisher Site | Google Scholar
J. A. Sawicki, “Hydrothermal synthesis of Ni₂FeBO₅ in near-supercritical PWR coolant and possible effects of neutron-induced 10B fission in fuel crud,” Journal of Nuclear Materials, vol. 415, no. 2, pp. 179–188, 2011.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2018 Soon-Hyeok Jeon et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

773

Downloads

698

Citations