Photocatalytic and Antibacterial Properties of a 3D Flower-Like TiO<sub>2</sub> Nanostructure Photocatalyst

Zhang, Yunping; Liu, Xi; Yusoff, Mahani; Razali, Mohd Hasmizam

doi:https://doi.org/10.1155/2021/3839235

Scanning

On this page

Abstract Introduction Materials and Methods Results and Discussion Conclusions Data Availability Disclosure Conflicts of Interest Acknowledgments References Copyright Related Articles

Research Article | Open Access

Volume 2021 | Article ID 3839235 | https://doi.org/10.1155/2021/3839235

Photocatalytic and Antibacterial Properties of a 3D Flower-Like TiO₂ Nanostructure Photocatalyst

Yunping Zhang,¹Xi Liu,²Mahani Yusoff,³and Mohd Hasmizam Razali^4,5

Academic Editor: Guosong Wu

Received27 Aug 2021

Accepted14 Sept 2021

Published28 Sept 2021

Abstract

Flower-like titanium dioxide (TiO₂) nanostructures are successfully synthesized using a hybrid sol-gel and a simple hydrothermal method. The sample was characterized using various techniques to study their physicochemical properties and was tested as a photocatalyst for methyl orange degradation and as an antibacterial material. Raman spectrum and X-ray diffraction (XRD) pattern show that the phase structure of the synthesized TiO₂ is anatase with 80-100 nm in diameter and 150–200 nm in length of flower-like nanostructures as proved by field emission scanning electron microscope (FESEM). The energy-dispersive X-ray spectroscopy (EDS) analysis of flower-like anatase TiO₂ nanostructure found that only titanium and oxygen elements are present in the sample. The anatase phase was confirmed further by a high-resolution transmission electron microscope (HRTEM) and selected area electron diffraction (SAED) pattern analysis. The Brunauer-Emmett-Teller (BET) result shows that the sample had a large surface area (108.24 m²/g) and large band gap energy (3.26 eV) due to their nanosize. X-ray photoelectron spectroscopy (XPS) analysis revealed the formation of Ti⁴⁺ and Ti³⁺ species which could prevent the recombination of the photogenerated electron, thus increased the electron transportation and photocatalytic activity of flower-like anatase TiO₂ nanostructure to degrade the methyl orange (83.03%) in a short time (60 minutes). These properties also support the good performance of flower-like titanium dioxide (TiO₂) nanostructure as an antibacterial material which is comparable with penicillin which is inhibition zone against Staphylococcus aureus.

1. Introduction

Generally, a good photocatalyst material must have superior properties like photoactive, able to absorb visible and UV light, biologically and chemically inert, photostable, inexpensive, and nontoxic. Titanium dioxide (TiO₂) had been reported active and most suitable to be used as a photocatalyst because it is easily available, cheap, and nontoxic [1, 2] and due to its chemical inertness [3]. The surface of TiO₂ is believed to have high oxidation potential which makes it able to break down many organic substances in photocatalysis process. Photocatalysis is referred to the reaction that uses light to activate a photocatalyst and then increase the speed of chemical reaction by lowering the activation energy for the primary reaction to occur [4]. Photocatalytic reaction in general involved six photocatalytic processes which are (1) charge separation process, (2) surface recombination, (3) surface trapping, (4) surface recombination, (5) interfacial charge transfer, and (6) back reaction [5]. This process occurred when the absorption of light generates an electron-hole pair on the surface of TiO₂, whereas the electron is promoted to the conduction band (CB) and the positive hole is made in the valence band. Then, excited electrons and holes will be recombined and disperse the input energy as heat. Then, electron and holes get trapped in metastable surface or react with electron donors and electron acceptors adsorbed on the photocatalyst surface. After reaction with water, these holes produce hydroxyl radicals that are important in the photocatalytic reaction. This reaction will continuously happen as long as the holes and electrons are present, so that it is important to have a long life of holes and electrons allowing them to migrate to the TiO₂ particle surface and thus get trapped by the surface active sites. However, TiO₂ is inactive due to faster electron-hole recombination than the charge transfer process and low adsorption ability thus reduces the photocatalytic reaction rate [5, 6]. On top of that, large band gap energy of TiO₂ also leads to a low degradation rate because only a small percentage of solar spectrums in the UV region could be absorbed by TiO₂.

Therefore, various strategies have been studied to improve the properties of bare TiO₂, thus improved their photocatalytic efficiency as photocatalyst. All strategies are focused on reducing band gap, avoid fast electron-hole recombination, and increase the reactive sites on the surface of TiO₂. Previously, researchers reported that Fe ion-doped TiO₂/spherical activated carbon (SAC) exhibited high total organic carbon (TOC) and chemical oxygen demand (COD) removal on the photodegradation of humic acid under 315~400 nm wavelength irradiation because the Fe ion doping helps in reducing the band gap energy and enhancing the separation of photogenerated electron-hole charges [7], while graphene oxide combined with TiO₂ (GO/TiO₂) nanocomposite enhanced the oil recovery up to 65% of the original oil volume as compared to 56% for pure GO augment solution [8]. Besides that, a ZrO₂-doped HZSM-5 catalyst shows high catalytic activity for methanol conversion and dimethyl ether production [9], suggesting that metal ion and metal oxide doping increased the performance of the materials. However, when the concentration of doping exceeds the optimum amount, the doping materials mainly act as a recombination center for generated electrons and holes, thus reduced the catalytic activity [10].

Recently, unique TiO₂ nanostructures like nanoparticles [11], nanotubes [12], nanofibers [13], nanowires [14], and nanorods [15] have been synthesized using several methods including sol-gel, hydrothermal, spin coating, microwave-assisted solvothermal, and metal organic chemical vapor deposition methods. However, a hydrothermal method, in particular, showed high potential for morphology control of TiO₂ and it is possible to grow different nanostructures by dissolution and crystallization of precursors, thereby creating distinctive difference in their characteristics at nanoscale level. Different nanostructured materials possessed different morphologies and characteristics that affected the performance of the synthesized nanostructure materials significantly. For these reasons, TiO₂ nanostructures were used in various applications such as photocatalytic processes [16], photovoltaic [17], and sensor [18]. In general, TiO₂ nanostructures can be categorized into zero- (0D), one- (1D), two- (2D), and three-dimensional (3D) materials. The materials with all the dimensions within the nanoscale (≤100 nm) size are classified as 0D nanostructure materials. 1D nanostructure materials are the materials which have one dimension of their structure that is outside the nanoscale. While 2D nanostructure materials are those in which two of the dimensions are not confined to the nanoscale. On the other hand, 3D materials are the materials constructed from these low dimensional materials.

1D and 2D nanostructures offer high rate of charge carrier transportation high interfacial free energies due to providing direct pathways for these photogenerated charge carrier movement [19, 20]. They also have high interfacial free energies, resulting in their aggregation and loss of active surface area during storage or photocatalytic testing [21]. To overcome this limitation, researchers are now actively exploring hierarchical photocatalyst structures, which contain 1D or 2D TiO₂ components organized into more complex 3D architectures. 3D flower-like nanostructures, with 1D or 2D nanostructured components as “petals”, are promising in this regard. Thus, in this study, 3D flower-like anatase TiO₂ nanostructures were synthesized, characterized, and tested as photocatalysts for methyl orange degradation and as antibacterial materials. Researchers reported that brookite TiO₂ nanoflowers could be synthesized using TiOSO₄ as a precursor material using a hydrothermal method and the product exhibits larger light adsorption and larger permittivity than anatase TiO₂ powder [22, 23], while Liu and coworkers found out that the photochemical degradation rate of anatase flower-like TiO₂ hierarchical structures on methylene blue is two times that of commercial P25 TiO₂ powders [24]. They used Ti powder as a precursor to produce flower-like TiO₂ with high specific surface area and a large light harvesting efficiency.

To the best of our knowledge, most studies were carried out to investigate the properties and application of nanoflower TiO₂ as a photocatalyst, but no study has been conducted on antibacterial properties of the nanostructures. Therefore, this paper reported dual application of flower-like TiO₂ nanostructures as photocatalytic and antibacterial materials due to their unique physical and chemical properties. In this study, titanium tetraisopropoxide has been used as a precursor for flower-like TiO₂ nanostructure synthesis because it is easy to be hydrolysed to produce TiO₂ particles, is inexpensive, and is nontoxic as compared to other precursors such as TiOSO₄, Ti powder, and TiCl₄.

2. Materials and Methods

2.1. Preparation of the TiO₂ Photocatalyst

Titanium tetraisopropoxide, Ti(OC₃H₇)₄, and distilled water were mixed with a molar ratio of 1 : 4, and the pH of mixture was adjusted using hydrochloric acid (HCl) of 0.2 molarity for restraining the hydrolysis process of the solution. The solution was stirred continuously at slow speed for 30 min and transferred into Teflon-lined autoclave. A 100 ml of HCl (0.5 M) was added and stirred for 15 to produce homogeneous solution in Teflon-lined autoclave. The acidic condition of solution () is important in order to produce the flower-like morphology of TiO₂ using a hydrothermal method. The Teflon-lined autoclave containing the solution was putted in the furnace for hydrothermal treatment at 150°C overnight. After the reaction, the product was washed with distilled water until pH 7 of washing solution was obtained. Then, the white solid was separated and collected from solution and subsequently dried at 80°C for 24 h. After drying, the obtained powder was calcined at 500°C in air for 2 hours for characterization.

2.2. Characterization

Raman analysis was carried out at room temperature using a Horiba Jobin-Yvon HR800 UV Raman spectrometer. The data was collected using an increment of 1 cm^-1 and an integration time of 1 second. The wavelength was obtained from 100 to 1000 cm^-1. Bruker D8 diffractometer with Cu-Kα () X-ray powder diffraction (XRD) was used for a crystal structure study. Scans were performed in a step of 0.2°/second over the range of from 20 up to 80°. The morphology of the sample and images was captured by a ZEISS SUPRA™ 35VP field emission scanning electron microscope (FESEM). The energy-dispersive X-ray spectroscopy (EDX) for the elemental composition was analyzed using GENESIS 2000 X-ray Microanalysis System (XMS) which is equipped with SUPRA™ 35VP FESEM. High-resolution transmission electron microscopy (HRTEM) Philips CM12 was used for phase structure identification. The crystallographic structure of the samples was further investigated by selected area electron diffraction (SAED). Micromeritics ASAP 2000 instrument was used for the nitrogen gas adsorption analysis at the temperature of -196°C (boiling temperature of liquid nitrogen) in order to determine the Brunauer-Emmett-Teller (BET) surface area and porosity. A PerkinElmer Lambda 35 UV-Vis spectrometer was used for band gap measurements. The elemental and oxidation state analyses were conducted using X-ray photoelectron spectroscopy (XPS) Ultra Axis PLD, Kratos, employing Al (mono) Kα radiation (). The broad survey scan was performed in the energy range from 0 to 1000 eV. The binding energy (BE) for the samples was calibrated by setting the BE of C 1s to 284.6 eV.

2.3. Photocatalytic Study

The photocatalytic activity of the synthesized TiO₂ and commercial TiO₂ is evaluated for the photodegradation of methyl orange (MO) dye. For photodegradation, 10 mg powder of each catalyst was separately dispersed in a 60 ml MO dye aqueous solution at a specific concentration (5 ppm). Proceeding to the photocatalytic test, the mixture solution was stirred magnetically in dark for 1 h to attain adsorption/desorption equilibrium between dye and catalyst. Then, the solution was exposed to 8 W UV lamp as the source of irradiation for 1 h. A 5 ml sample was drawn at every 10 minutes interval for absorbance measurement. The removed suspensions were centrifuged (6000 rpm for 10 min) for solid-liquid separation. The clear solution was analyzed using UV-Vis spectrometer (PerkinElmer Lambda 35 UV-Vis) to quantify the extent of dye degradation. The photodegradation efficiency () was calculated using Equation (1): where is the initial absorption of MO and is the absorption of MO after the reaction at time.

2.4. Antibacterial Study

For antibacterial study, gram-positive Staphylococcus aureus microbes were used for an antibacterial assay. The standard growth medium (Mueller-Hinton, MH, Difco™) agar was prepared by sterilizing with an autoclave for 15 min at 120°C. Prior to the bacterial inoculation, the Staphylococcus aureus is subculture in MH agar and was incubated aerobically at 37°C for 24 h to make sure the bacteria are in a stable condition without any contamination. The bacterial concentrations were measured via simple optical density measurement using a BioMerieux DensiCHEK Plus spectrophotometer at 600 nm. In this study, the bacterial suspensions were adjusted to equivalent turbidity at 0.5 McFarland standards. Inoculants of Staphylococcus aureus were evenly spread in sterile petri plates contained in the MH agar. Using a sterile cotton swab, all bacteria were swabbed over the surface of the agar plates. 0.1 mg of flower-like TiO₂ nanostructures, commercial TiO₂ powder sample, and penicillin as the control were gently pressed on the agar. The penicillin was used as a standard antibiotic for the positive control in this study. The plates contained samples and agar with bacteria were incubated at 37°C for 24 h in triplicates. The observations on clear zone of each plate were recorded after 24 h incubation at 37°C. It is recorded as an indication of growth against microbial species.

3. Results and Discussion

Figure 1(a) shows the Raman spectra of the synthesized sample. The peaks at 147 cm^-1 (), 197 cm^-1 (), 399 cm^-1 (), 516 cm^-1 ( unresolved doublet), and 640 cm^-1() were observed which are assigned to TiO₂ anatase which is in good agreement with the published data [25]. Furthermore, the strongest peak at 147 cm⁻¹ () was attributed to the external vibration of the anatase structure; therefore, it could be concluded that the prepared sample is an anatase TiO₂ [26, 27]. This result was supported by XRD result as sharp and narrow peaks were appeared at of 25.57°, 38.05°, 48.28°, 54.10°, 55.29°, 62.90°, 68.92°, 70.45°, 75.24°, and 82.83° (Figure 1(b)), which were indexed to the diffraction planes (101), (112), (200), (105), (211), (204), (116), (220), and (215) assigned to tetragonal structure of anatase TiO₂ (JCPDS # 02-0406), respectively. This finding proved that the synthesized sample is TiO₂ anatase phase. It was well reported that anatase TiO₂ displays better photocatalytic activity as compared to other phases of TiO₂-like rutile and brookite due to their higher electron mobility [28]. Thus, formation of anatase TiO₂ in this research could enhance the photocatalytic activity to degrade methylene blue and bacterial decomposition.

(a)

(b)

The FESEM image of anatase TiO₂ is depicted in Figure 2. Homogeneous flower-like TiO₂ nanostructure was observed, and the diameter and length of flower-like TiO₂ were found to be within 80-100 nm and 150–200 nm, respectively. Flower-like nanostructures are interlaced and stacked together, exhibiting a good dispersion. The image in Figure 2(a) was taken at lower magnification, while the other images (Figure 2(b) were captured at higher magnification. It can be seen in the SEM micrographs that the petals of the flowers were in the size range of 20–90 nm. The formation of flower-like nanostructures can be explained by multistep growth mechanism. First, under high-temperature hydrothermal conditions, the reaction system has crystal nuclei, because the system has a large surface energy at this time, the rapid growth of crystal nuclei into titanium dioxide particles. In order to reduce the surface energy of the system, the titanium dioxide particles are self-assembled together to form the ball aggregation structure. The titanium dioxide particles continue to produce, attached to the ball aggregate structure around it, and its structure begin to change; the morphology of product began to become ellipsoid, when the hydrothermal time is longer; the nucleation process of the product has been completed. In this process, the titanium dioxide particles simultaneously self-assembled to form nanorods adhered to the aggregate structure of the nanocrystal. And overtime flower-like TiO₂ nanostructures were formed. The formation of flower-like TiO₂ nanostructures is good for photocatalytic activity because it will help to maximize the light harvesting due to the multiple reflections of light within the interior nanoflowers [29]. The elemental analysis of the synthesized TiO₂ nanoflowers was carried out using energy-dispersive X-ray spectroscopy (EDS). As can be seen in Figure 3, only oxygen and titanium elements were present, with no evidence of any significant impurities. Therefore, it was confirmed that the synthesized TiO₂ nanoflower was pure titanium dioxide with no impurities.

(a)

(b)

The purity of the sample was investigated further using HRTEM. The lattice fringes of flower-like TiO₂ nanostructures are clearly observed in Figure 4(a), which indicated that these samples had high degrees of crystallinity and phase purity. The lattice fringe distance ( spacing) was determined to be about 0.35 nm, which could be undoubtedly assigned to the lattice facet of anatase TiO₂ hexagonal (1 0 1) [30], while Figure 4(b) illustrates the selected area electron diffraction (SAED) patterns of the sample. A series of rings were observed which confirmed the polycrystalline nature. The SAED pattern displays five fringe patterns with spacing of 3.512 Å, 2.293 Å, 1.841 Å, 1.626 Å, and 1.442 Å which were consistent with (0 1 1), (1 0 1), (2 0 0), (2 1 1), and (0 0 2) of anatase TiO₂ index, respectively. The result of these investigations is consistent with the Raman and XRD results obtained.

(a)

(b)

The BET surface areas of flower-like rutile TiO₂ nanostructures and commercial TiO₂ were 108.24 m²/g and 23.12 m²/g, respectively (Table 1). Higher surface area of the TiO₂ nanostructure attributed to their flower-like morphological structure which is able to prevent the agglomeration of the particles. Similar trend was observed on pore diameter and pore volume of the studied samples. Larger pore volume of flower-like TiO₂ nanostructures as compared to commercial TiO₂ is due to their elongated morphology and smaller particles. Figure 5 shows the isotherm plot of the samples, while types of isotherms, hysteresis, pores, and shape of pores of flower-like TiO₂ nanostructure and commercial TiO₂ are tabulated in Table 2. Both samples exhibit similar types of isotherms, having a type IV isotherm indicating the presence of mesopore in the system which supports the result of pore diameter of the samples. Mesopore materials have pore sizes generally in the range of 2 to 50 nm. For type IV isotherm, it could be observed that the adsorption of the nitrogen gas is low at the initial relative pressure (), but then increases markedly at higher values of where pore capillary condensation takes place. A hysteresis effect associated with the pore condensation and studied samples displays closely with type H3 hysteresis loops, implying the slit-shaped mesoporous characteristics of materials [31].

As shown in Figure 6, the band energy of flower-like TiO₂ nanostructures is 3.26 eV slightly larger than anatase TiO₂ (3.2 eV) as reported by previous researchers [32]. Their large band gap energy is due to the size quantization in nanomaterials. In nanosized materials, the effect of size quantization was due to localization of electrons and positive holes in a confined volume of the materials. This will result in a change of energy band structure, due to the separation of individual energy levels and an increase in effective optical band gap of the nanomaterials as compared with bulk materials [33]. In general, the ideal band gap is less than 3.1 eV, because the materials with lower band gap could demonstrate the photocatalytic properties under ultraviolet (UV) and visible light as well as sunlight. Therefore, more efficient materials could be produced.

The XPS survey spectrum of flower-like TiO₂ nanostructures is shown in Figure 7(a). The peak appearances which are attributed to Ti 2p, O 1s, and C 1s reveal the existence of Ti, O, and C on the surface of the sample. Ti and O elements correspond to the synthesized sample, while the presence of C element was ascribed to adventitious carbon from the XPS [34]. Figure 7(b) shows the high-resolution XPS spectra of Ti 2p. An unsymmetrical peak was observed, which means that there exist two chemical forms of Ti in the sample. Two strong peaks located at 457.1 and 462.8 eV binding energies were attributed to the Ti⁴⁺ 2p_1/2 and Ti⁴⁺ 2p_3/2 spin orbital splitting photoelectrons, respectively, showing the presence of Ti⁴⁺ [35]. Besides these predominant Ti⁴⁺ peaks, a minor species of titanium was also found located at 456.0 and 461.7 eV binding energies. These could be identified as Ti³⁺ 2p_3/2 and Ti³⁺ 2p_1/2, respectively, suggesting the presence of Ti³⁺ species in the sample [36]. Interestingly, the existence of Ti³⁺ surface state can act as electron trapper to prevent the recombination of electron (e^-) and positive holes (h⁺) [37]. As shown in Figure 7(c), after deconvolution of high-resolution XPS spectra O 1s, two peaks were observed. The main peak of O 1s is located at about 528.6 eV, which corresponds to lattice oxygen of TiO₂ [O–Ti], while another one shoulder peak at higher binding energy (530.2 eV) could be identified attributed to the hydroxyl surface species of [O–H] [34]. The presence of the hydroxyl groups can enhance the performance of the photocatalyst due to the longer electron lifetime [38].

(a)

(b)

(c)

For photocatalytic activity study, MO was used as the targeted pollutant because MO was widely used in various industries such as textile and food processing for coloring. Due to their high stability against photolysis and self-degradation, it is remained in an aqueous solution for a long time. This situation will contribute to the water pollution and toxicity to aquatic life. Therefore, the MO is an appropriate pollutant to evaluate the photocatalytic activity of materials. Figure 8(a) shows the photocatalytic degradation rate of methyl orange (MO) under ultraviolet (UV) light using various photocatalysts. After 60 minutes, 83.03% and 16.44% of MO were degraded using flower-like TiO₂ nanostructure and commercial TiO₂, respectively. Their UV-Vis spectra of MO degradation are shown in Figures 8(b) and 8(c), respectively. The degradation of MO did not reach the stable trend because the degradation still can be increased if the reaction was carried out over a longer period suggesting the performance of the photocatalyst remained during the reaction. For comparison, the degradation rate of MO using other TiO₂ nanostructures is listed in Table 3. The flower-like TiO₂ nanostructure exhibits better photocatalytic activity in MO degradation.

(a)

(b)

(c)

The result shows that the flower-like TiO₂ nanostructure could act as an effective photocatalyst to degrade MO. An ordered and strongly interconnected nanoflower architecture offers the potential for improved electron transport leading to higher degradation efficiencies. The flower-like TiO₂ nanostructure also composed of the very fine rice-like nanorods; consequently, photoinduced carriers are easier to transfer to the surface and initiate the reactions, thus reducing the recombination of photogenerated electrons and holes [43, 44]. Moreover, the layered structure of flower-like TiO₂ can provide sufficient space to polarize the related atoms and orbitals, which can effectively separate the photogenerated electron-hole pairs, thereby enhanced the photocatalytic activity [45]. On the other hand, low photocatalytic activity of commercial TiO₂ is due to their low surface area and zero dimensional (0D) materials (spherical shape of TiO₂). It is well known that the structural disorder at the contact between two crystalline TiO₂ nanoparticles leads to enhanced scattering of free electrons, thus reducing electron mobility. Moreover, the short charge-separation distances within the particle as well as the rapid charge-recombination speed led to a low quantum yield, thus reduces the photocatalytic activity of TiO₂ particles [46].

The antibacterial activity of flower-like TiO₂ nanostructure and commercial TiO₂ was studied against gram-positive Staphylococcus aureus by a qualitative disk method, and their activity was compared with control sample (penicillin) (Figure 9). The inhibition zone was found to be , , and after 24 hours for penicillin, flower-like TiO₂ nanostructure, and commercial TiO₂, respectively, as tabulated in Table 4. The result obtained suggests that the synthesized flower-like TiO₂ nanostructure and commercial TiO₂ were better than penicillin as antibacterial materials. This is due to the capability of TiO₂ in dissolving the outer membranes of bacteria by using reactive oxygen species (ROS) [47]. It is well known that TiO₂ material is a very good oxidation agent to produce ROS by reacting with water (H₂O) and oxygen (O₂). ROS (⋅OH, H₂O₂, and ⋅O₂-) are formed when these photogenerated charge carriers (e^-_CB in conduction band and h_VB in valence band) interact with water and dissolved O₂ molecules. These ROS interact with the cell wall and cell membrane of bacteria and damage them. ROS oxidizes the membrane phosphatidylethanolamine to form malondialdehyde which is a lipid peroxidation product [48]. This malondialdehyde acts as an index to measure the peroxidation and cell damage. Electrostatic force of interaction between the bacteria and photocatalyst is important for enhanced antibacterial activity, due to which catalyst penetrates inside the cell causing more damage to the membrane. This damage to the cell wall and cell membrane leads to the leakage of intracellular substances (K⁺). This K⁺ is the universal substance in bacteria which helps in protein synthesis and regulation of polysome content. Further, cell components like genomic material (DNA and RNA), proteins, and ribosomes are also damaged by these ROS due to altered cell permeability [49]. Flower-like TiO₂ nanostructure shows the highest antibacterial activity because of their larger surface area which helps generating large number of ROS and consequently exhibits better antibacterial activity. On top of that, a flower-like TiO₂ superstructure, or, in other words, a 3D micro-nanomaterial with a hierarchical structure, had good light absorption efficiency and appropriate refractive index to generate more photocarries for ROS production.

4. Conclusions

Flower-like TiO₂ nanostructures with anatase phase were synthesized via a hydrothermal method using titanium isopropoxide as precursors. The existence of anatase TiO₂ was proved by Raman and XRD results as sharp and narrow peaks appeared assigned to anatase TiO₂. FESEM images have shown the existence of flower-like TiO₂ nanostructures with 80-90 nm in diameter and 150-200 nm in length. The BET surface area and pore volume of the nanostructures were found to be 108.4 m²g^-1 and 0.688 m³g^-1, respectively. High surface area, pore volume, and anatase phase of flower-like TiO₂ nanostructure support their good performance for MO degradation (83.03%) in 60 minutes and as antibacterial material with inhibition zone against Staphylococcus aureus. The presence of Ti⁴⁺ and Ti³⁺ in the flower-like TiO₂ nanostructures as confirmed by XPS analysis could retard the charge recombination and improve the photogenerated electrons to increase the generation of reactive oxygen species (ROS) for degradation of MO and bacteria.

Data Availability

The data has been included in the manuscript.

Disclosure

The funders had no role in the design of the study, in the collection, analyses, or interpretation of data, in the writing of the manuscript, or in the decision to publish the results.

Conflicts of Interest

The authors declare no conflict of interest.

Acknowledgments

The authors are grateful to Universiti Malaysia Terengganu (UMT) for the facilities and Malaysia Ministry of Higher Education for the financial support vote (FRGS/1/2019/STG07/UMT/02/2).

References

A. Fujishima and K. Honda, “Electrochemical photolysis of water at a semiconductor electrode,” Nature, vol. 238, no. 5358, pp. 37-38, 1972.
View at: Publisher Site | Google Scholar
D. Komaraiah, E. Radha, J. James et al., “Effect of particle size and dopant concentration on the Raman and the photoluminescence spectra of TiO₂:Eu³⁺ nanophosphor thin films,” Journal of Luminescence, vol. 211, pp. 320–333, 2019.
View at: Publisher Site | Google Scholar
D. Tekin, D. Birhan, and H. Kiziltas, “Thermal, photocatalytic, and antibacterial properties of calcinated nano- TiO₂/polymer composites,” Materials Chemistry and Physics, vol. 251, article 123067, 2020.
View at: Publisher Site | Google Scholar
C. Belver, J. Bedia, M. Peñas-Garzón, V. Muelas-Ramos, A. Gómez-Avilés, and J. J. Rodriguez, “Structured photocatalysts for the removal of emerging contaminants under visible or solar light,” in Visible Light Active Structured Photocatalysts for the Removal of Emerging Contaminants, O. Sacco and V. Vaiano, Eds., p. 41, Elsevier, 2020.
View at: Publisher Site | Google Scholar
D. Chen, Y. Cheng, N. Zhou et al., “Photocatalytic degradation of organic pollutants using TiO₂-based photocatalysts: a review,” Journal of Cleaner Production, vol. 268, article 121725, 2020.
View at: Publisher Site | Google Scholar
P. S. Basavarajappa, S. B. Patil, N. Ganganagappa, K. R. Reddy, A. V. Raghu, and C. V. Reddy, “Recent progress in metal-doped TiO₂, non-metal doped/codoped TiO₂ and TiO₂ nanostructured hybrids for enhanced photocatalysis,” International Journal of Hydrogen Energy, vol. 45, no. 13, pp. 7764–7778, 2020.
View at: Publisher Site | Google Scholar
M. H. Baek, J. S. Hong, J. W. Yoon, and J. K. Suh, “Photocatalytic Degradation of Humic Acid by Fe-TiO₂ Supported on Spherical Activated Carbon with Enhanced Activity,” International Journal of Photoenergy, vol. 2013, Article ID 296821, 5 pages, 2013.
View at: Publisher Site | Google Scholar
A. Garmroudi, M. Kheirollahi, S. A. Mousavi, M. Fattahi, and E. H. Mahvelati, “Effects of graphene oxide/TiO₂ nanocomposite, graphene oxide nanosheets and Cedr extraction solution on IFT reduction and ultimate oil recovery from a carbonate rock,” Petroleum, vol. 1, 2020.
View at: Publisher Site | Google Scholar
M. Z. Pedram, M. Kazemeini, M. Fattahi, and A. Amjadian, “A physicochemical evaluation of modified HZSM-5 catalyst utilized for production of dimethyl ether from methanol,” Petroleum Science and Technology, vol. 32, no. 8, pp. 904–911, 2014.
View at: Publisher Site | Google Scholar
Z. Mesgari, M. Gharagozlou, A. Khosravi, and K. Gharanjig, “Spectrophotometric studies of visible light induced photocatalytic degradation of methyl orange using phthalocyanine-modified Fe-doped TiO₂ nanocrystals,” Spectrochimica Acta Part A: Molecular and Biomolecular Spectroscopy, vol. 92, pp. 148–153, 2012.
View at: Publisher Site | Google Scholar
O. Ouerghi, M. H. Geesi, E. O. Ibnouf et al., “Sol-gel synthesized rutile TiO₂ nanoparticles loaded with cardamom essential oil: enhanced antibacterial activity,” Journal of Drug Delivery Science and Technology, vol. 64, article 102581, 2021.
View at: Publisher Site | Google Scholar
M. H. Razali and M. Yusoff, “Highly efficient CuO loaded TiO₂ nanotube photocatalyst for CO₂ photoconversion,” Materials Letters, vol. 221, pp. 168–171, 2018.
View at: Publisher Site | Google Scholar
M. Kumaresan, M. Venkatachalam, M. Saroja, and P. Gowthaman, “TiO₂ nanofibers decorated with monodispersed WO₃ heterostruture sensors for high gas sensing performance towards H₂ gas,” Inorganic Chemistry Communications, vol. 129, article 108663, 2021.
View at: Publisher Site | Google Scholar
W. M. Caceres-Ferreira, G. Morales, G. Soria-Arguello et al., “The role of nitrogen plasma surface treatment and TiO₂ seeding onto carbon fibers on the microwave-assisted growth of radially aligned TiO₂ nanowires,” Materials Chemistry and Physics, vol. 273, article 125126, 2021.
View at: Publisher Site | Google Scholar
K. Pillai, “Single crystalline rutile TiO₂ nanorods synthesis by onestep catalyst-free vapor transport method,” Solid State Communications, vol. 333, article 114342, 2021.
View at: Publisher Site | Google Scholar
M. H. Razali, A. F. M. Noor, and M. Yusoff, “Hydrothermal synthesis and characterization of Cu²⁺/F^–Co-doped titanium dioxide (TiO₂) nanotubes as photocatalyst for methyl orange degradation,” Science of Advanced Materials, vol. 9, no. 6, pp. 1032–1041, 2017.
View at: Publisher Site | Google Scholar
N. Chaurasiya, U. Kumar, S. Sikarwar, B. C. Yadav, and P. K. Yadawa, “Synthesis of TiO₂ nanorods using wet chemical method and their photovoltaic and humidity sensing applications,” Sensors International, vol. 2, article 100095, 2021.
View at: Publisher Site | Google Scholar
P. Bindra and A. Hazra, “Selective detection of organic vapors using TiO₂ nanotubes based single sensor at room temperature,” Sensors and Actuators B: Chemical, vol. 290, pp. 684–690, 2019.
View at: Publisher Site | Google Scholar
J. Prakash, Samriti, A. Kumar et al., “Novel rare earth metal-doped one-dimensional TiO₂ nanostructures: Fundamentals and multifunctional applications,” Materials Today Sustainability, vol. 13, article 100066, 2021.
View at: Publisher Site | Google Scholar
U. Nwankwo, R. Bucher, A. B. C. Ekwealor, S. Khamlich, M. Maaza, and F. I. Ezema, “Synthesis and characterizations of rutile-TiO₂ nanoparticles derived from chitin for potential photocatalytic applications,” Vacuum, vol. 161, pp. 49–54, 2019.
View at: Publisher Site | Google Scholar
C. Daulbayev, F. Sultanov, B. Bakbolat, and O. Daulbayev, “0D, 1D and 2D nanomaterials for visible photoelectrochemical water splitting. A review,” International Journal of Hydrogen Energy, vol. 45, no. 58, pp. 33325–33342, 2020.
View at: Publisher Site | Google Scholar
J. Zhu, S. H. Wang, Z. F. Bian, C. L. Cai, and H. X. Li, “A facile synthesis of hierarchical flower-like TiO₂ with enhanced photocatalytic activity,” Research on Chemical Intermediates, vol. 35, no. 6-7, pp. 769–777, 2009.
View at: Publisher Site | Google Scholar
W. Hu, L. Li, G. Li, C. Tang, and L. Sun, “High-quality brookite TiO₂ Flowers: synthesis, characterization, and dielectric performance,” Crystal Growth & Design, vol. 9, no. 8, pp. 3676–3682, 2009.
View at: Publisher Site | Google Scholar
M. Liu, W. M. Lu, L. Zhao, C. L. Zhou, H. L. Li, and W. J. Wang, “Fabrication and photocatalytical properties of flower-like TiO₂ nanostructures,” Transactions of Nonferrous Metals Society of China, vol. 20, no. 12, pp. 2299–2302, 2010.
View at: Publisher Site | Google Scholar
S. Lee, A. Y. Cho, Y. S. Rim, J. Y. Park, and T. Choi, “Synergistic design of anatase/rutile TiO₂ nanostructured heterophase junctions toward efficient photoelectrochemical water oxidation,” Coatings, vol. 10, no. 6, article 557, 2020.
View at: Publisher Site | Google Scholar
A. Umar, M. M. Rahman, S. H. Kim, and Y. B. Hahn, “Zinc oxide nanonail based chemical sensor for hydrazine detection,” Chemical Communications, vol. 2, no. 2, pp. 166–168, 2008.
View at: Publisher Site | Google Scholar
S. S. Patil, M. G. Mali, A. Roy et al., “Graphene-wrapped Ag₃PO₄/LaCO₃OH heterostructures for water purification under visible light,” Journal of Energy Chemistry, vol. 25, no. 5, pp. 845–853, 2016.
View at: Publisher Site | Google Scholar
S. Varnagiris, A. Medvids, M. Lelis, D. Milcius, and A. Antuzevics, “Black carbon-doped TiO₂ films: synthesis, characterization and photocatalysis,” Journal of Photochemistry and Photobiology A: Chemistry, vol. 382, article 111941, 2019.
View at: Publisher Site | Google Scholar
M. Takeuchi, Y. Shimizu, H. Yamagawa, T. Nakamuro, and M. Anpo, “Preparation of the visible light responsive N³⁻-doped WO₃ photocatalyst by a thermal decomposition of ammonium paratungstate,” Applied Catalysis B: Environmental, vol. 110, pp. 1–5, 2011.
View at: Publisher Site | Google Scholar
L. Li, B. Cheng, Y. Wang, and J. Yu, “Enhanced photocatalytic H₂-production activity of bicomponent NiO/TiO₂ composite nanofibers,” Journal of Colloid and Interface Science, vol. 449, pp. 115–121, 2015.
View at: Publisher Site | Google Scholar
R. Vasilić, S. Stojadinović, N. Radić, P. Stefanov, Z. Dohčević-Mitrović, and B. Grbić, “One-step preparation and photocatalytic performance of vanadium doped TiO₂ coatings,” Materials Chemistry and Physics, vol. 151, pp. 337–344, 2015.
View at: Publisher Site | Google Scholar
X. Zhao, W. Wang, Y. Liang et al., “Three-dimensional plasmonic photoanode of Co₃O₄ nanosheets coated onto TiO₂ nanorod arrays for visible-light-driven water splitting,” International Journal of Hydrogen Energy, vol. 44, no. 29, pp. 14561–14570, 2019.
View at: Publisher Site | Google Scholar
H. M. Tabaei, M. Kazemeini, and M. Fattahi, “Preparation and characterization of visible light sensitive nano titanium dioxide photocatalyst,” Scientia Iranica, vol. 19, no. 6, pp. 1626–1631, 2012.
View at: Publisher Site | Google Scholar
W. M. A. El Rouby, M. Antuch, S. M. You, P. Beaunier, and P. Millet, “Novel nano-architectured water splitting photoanodes based on TiO₂-nanorod mats surface sensitized by ZIF-67 coatings,” International Journal of Hydrogen Energy, vol. 44, no. 59, pp. 30949–30964, 2019.
View at: Publisher Site | Google Scholar
C. Dwivedi, T. Mohammad, V. Kumar, and V. Dutta, “Ti³⁺ and oxygen defects controlled colored TiO₂ nanoparticles by continuous spray pyrolysis,” Vacuum, vol. 182, article 109612, 2020.
View at: Publisher Site | Google Scholar
Z. Ji, J. Wu, T. Jia et al., “In-situ growth of TiO₂ phase junction nanorods with Ti³⁺ and oxygen vacancies to enhance photocatalytic activity,” Materials Research Bulletin, vol. 140, article 111291, 2021.
View at: Publisher Site | Google Scholar
Z. Fan, F. Meng, J. Gong, H. Li, and A. Li, “Growth mechanism and photocatalytic activity of chrysanthemum-like anatase TiO₂ nanostructures,” Ceramics International, vol. 42, no. 5, pp. 6282–6287, 2016.
View at: Publisher Site | Google Scholar
L. Le, Y. Wu, Z. Zhou, H. Wang, R. Xiong, and J. Shi, “Cu₂O clusters decorated on flower-like TiO₂ nanorod array film for enhanced hydrogen production under solar light irradiation,” Journal of Photochemistry and Photobiology A: Chemistry, vol. 351, pp. 78–86, 2018.
View at: Publisher Site | Google Scholar
K. Santhi, M. Navaneethan, S. Harish, S. Ponnusamy, and C. Muthamizhchelvan, “Synthesis and characterization of TiO₂ nanorods by hydrothermal method with different pH conditions and their photocatalytic activity,” Applied Surface Science, vol. 500, article 144058, 2020.
View at: Publisher Site | Google Scholar
S. Ramezani Sani, F. Mohseni, M. Javid, and A. Mortezaali, “Preparation of TiO₂ one-dimensional nanostructures: the effect of oxidizing solvent on structural properties and photocatalytic activity,” The European Physical Journal Plus, vol. 131, no. 10, p. 1, 2016.
View at: Publisher Site | Google Scholar
S. RamezaniSani, M. Rajabi, and F. Mohseni, “Influence of nitrogen doping on visible light photocatalytic activity of TiO₂ nanowires with anatase-rutile junction,” Chemical Physics Letters, vol. 744, article 137217, 2020.
View at: Publisher Site | Google Scholar
X. Liu, Z. Xing, H. Zhang et al., “Fabrication of 3 D mesoporous black TiO2/MoS2/TiO2Nanosheets for visible-light-driven photocatalysis,” ChemSusChem, vol. 9, no. 10, pp. 1118–1124, 2016.
View at: Publisher Site | Google Scholar
S. Daneshvar e Asl and S. K. Sadrnezhaad, “Anionic and cationic pollutants degradation via TiO₂ nanoleafed nanorods,” Solid State Sciences, vol. 105, article 106263, 2020.
View at: Publisher Site | Google Scholar
N. Cao, M. Gu, M. Gao et al., “A three-layer photocatalyst carbon fibers/TiO₂ seed/TiO₂ nanorods with high photocatalytic degradation under visible light,” Surface Science, vol. 530, article 147289, 2020.
View at: Publisher Site | Google Scholar
Q. Shang, S. Gao, G. Dai, J. Ren, and D. Wang, “Structure and photocatalytic activity of Ti³⁺ self-doped TiO₂ flower shaped nanospheres,” Surfaces and Interfaces, vol. 18, p. 100426, 2020.
View at: Publisher Site | Google Scholar
T. Sreethawong, S. Ngamsinlapasathian, and S. Yoshikawa, “Synthesis of crystalline mesoporous-assembled ZrO₂ nanoparticles via a facile surfactant-aided sol-gel process and their photocatalytic dye degradation activity,” Chemical Engineering Journal, vol. 228, pp. 256–262, 2013.
View at: Publisher Site | Google Scholar
A. A. Menazea and N. S. Awwad, “Antibacterial activity of TiO₂ doped ZnO composite synthesized via laser ablation route for antimicrobial application,” Journal of Materials Research and Technology, vol. 9, no. 4, pp. 9434–9441, 2020.
View at: Publisher Site | Google Scholar
C. Hu, J. Guo, J. Qu, and X. Hu, “Photocatalytic degradation of pathogenic bacteria with AgI/TiO2under visible light irradiation,” Langmuir, vol. 23, no. 9, pp. 4982–4987, 2007.
View at: Publisher Site | Google Scholar
S. K. Ray, D. Dhakal, R. P. Pandey, and S. W. Lee, “Ag-BaMoO₄: Er³⁺/Yb³⁺ photocatalyst for antibacterial application,” Materials Science and Engineering: C, vol. 78, pp. 1164–1171, 2017.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2021 Yunping Zhang et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

576

Downloads

567

Citations

Scanning

Photocatalytic and Antibacterial Properties of a 3D Flower-Like TiO2 Nanostructure Photocatalyst

Abstract

1. Introduction

2. Materials and Methods

2.1. Preparation of the TiO2 Photocatalyst

2.2. Characterization

2.3. Photocatalytic Study

2.4. Antibacterial Study

3. Results and Discussion

4. Conclusions

Data Availability

Disclosure

Conflicts of Interest

Acknowledgments

References

Copyright

Photocatalytic and Antibacterial Properties of a 3D Flower-Like TiO₂ Nanostructure Photocatalyst

2.1. Preparation of the TiO₂ Photocatalyst