Stress Corrosion Cracking Behavior of TP 439 and 690 TT under Film-Forming Amine Environment

Figure 8

High temperature SSRT test fracture of 690 TT in the environment with FA.
(a) Overview
(b) Central area
(c) Marginal zone
(d) Marginal zone