High-Temperature Structural Analysis of a Small-Scale PHE Prototype under the Test Condition of a Small-Scale Gas Loop
Table 3
Mechanical properties of Hastelloy-X alloy.
| Average tensile data* | Form | Condition | Test temperature | Ultimate tensile strength | Yield strength at 0.2% offset | Elongation in 2 in. (50.8 mm) | | |
°F |
°C | Ksi | MPa | Ksi | MPa | % |
| Sheet 0.045–0.060 in. (1.1–1.5 mm) thick | Bright annealed at 2150°F (1177°C), hydrogen cooled | Room | | 111.2 | 767 | 54.9 | 379 | 44 | 1000 | 538 | 89.0 | 614 | 35.6 | 245 | 49 | 1200 | 649 | 84.2 | 581 | 35.4 | 244 | 54 | 1400 | 760 | 67.1 | 463 | 34.4 | 237 | 53 | 1600 | 871 | 44.9 | 310 | 28.1 | 194 | 59 | 1800 | 982 | 25.6 | 177 | 13.2 | 91 | 66 | 2000 | 1093 | 14.0 | 97 | 6.3 | 43 | 60 |
|
|
*Strain rate was 0.005-inch/inch/minute to 0.2% yield point and 0.5-inch/inch/minute to failure.
|