Abstract

U-10wt%Zr spherical particles for use as particulate fuel were prepared by centrifugal atomization and subjected to pressureless sintering, which is one of the simplest powder processing techniques. At sintering temperature of 1100°C for 30 or 60 min, all samples ranging from +50 to −325 mesh showed no apparent bonding between the particles. However, at 1150°C (80 min), all samples formed a bulk body and the microstructures showed apparent sintering stages. Particularly, sample B (50–70 mesh) and sample C (70–100 mesh) showed pore characteristics suitable for a particulate fuel. The results suggest that pressureless sinterability for U-10Zr particulate fuel can be improved by adding small-size (–325 mesh) particles.

1. Introduction

Fast reactors are an attractive energy source which manages nuclear waste by closing the fuel cycle, thus making the best use of limited nuclear fuel resources [13]. Therefore, sodium-cooled fast reactors (SFRs) have been developed in combination with the pyroelectrochemical processing of spent fuel at the Korea Atomic Energy Research Institute (KAERI) of Korea.

Currently, there are two kinds of promising fuels for fast reactors under consideration. One is metal fuel and the other is mixed oxide (MOX) fuel. Metal fuel features high thermal conductivity, a high density of fissile and fertile materials, a negative reactivity factor, and an increase in the passive safety of fast reactors [48]. The disadvantages of metal fuel are its lower processability, fuel-cladding interaction, large swelling at high burn-up, and the needed availability of sodium in the fuel-cladding gap. MOX fuel features high irradiation resistance and a more mastered technology [9, 10]. However, MOX fuel has disadvantages such as low thermal conductivity, high operating central temperature, relatively low uranium content, and low serviceability under transients.

Particulate fuel is one of the innovative fuel forms for fast reactors, combining the favorable features of both metal fuel and MOX fuel [1113]. It is fabricated by introducing fuel alloy particles directly into the fuel cladding without a mold. This not only promises major savings on mechanical devices, such as grinding machines and presses, but also offers an almost dustless operation. This simple and environmentally friendly production process results in even greater advantages when treating spent fuel, which includes minor actinide. Such alloys are highly radioactive and should be treated in facilities equipped with remote handling devices.

The low melting temperature of metal fuels such as pure U, Pu, and U-Pu alloys makes them unsuitable for high-temperature applications because of the dangers associated with molten elements penetrating the cladding. The addition of certain high-melting-temperature elements such as Cr, Mo, Ti, and Zr has therefore been investigated to boost the liquidus temperature and enhance the thermal and mechanical stability of the alloy system. The excellent corrosion resistance and mechanical stability during the cycling of U-Zr-based alloys make them promising fuels for fast reactors. Moreover, Zr metal has a low thermal-neutron cross section and is unique in suppressing interdiffusion between the nuclear fuel and the stainless steel cladding. These favorable properties have led to the development of U-Zr fuel systems for SFRs [14].

Pressureless sintering is a more affordable manufacturing technology than alternative powder processing techniques such as hot isostatic pressing (HIP), spark plasma sintering (SPS), and reactive hot pressing. Because it does not involve any preconditioning of the materials, the time, cost, and materials waste can be reduced [15, 16]. Furthermore, pressureless sintering does not typically remove all of the pores or pore structures during consolidation, which is beneficial in a reactor fuel, because they allow fission products developed during irradiation to travel easily to the plenum. This simple fabrication procedure offers greater advantages during mass production in hot-cell facilities.

Particulate fuel concepts have been proposed and tested at several experimental fast reactor systems [17]. However, much less work has been reported for particulate fuel development. In this study, a U-10wt%Zr alloy, a proposed metal fuel for an SFR, was used for the fabrication of particulate fuel. The U-10wt%Zr alloy was fabricated in the form of spherical particles by a centrifugal atomization process developed at Korea Atomic Energy Research Institute (KAERI) of Korea. The prepared particles were loaded into a surrogate tube cladding according to its size, and then pressureless sintering behaviors were investigated.

2. Experimental

Figure 1 shows the centrifugal atomization process (Figure 1(a)) and a schematic of the equipment (Figure 1(b)) used in this experiment. Centrifugal atomization involves melting, atomizing, and collecting. U and Zr raw materials were heated to a temperature approximately 200 K higher than the melting point, 1650 K, of the alloy [18], and the molten metal was fed through a small nozzle onto a rotating disk. The alloy-melt droplets, which formed from the melt by centrifugal force, were spread from the disk toward the atomizing chamber wall.

The fabricated particles were classified by sieve analysis and loaded into the quartz mold according to size. The quartz mold, which had a diameter of approximately 8 mm, which is similar to the diameter of the cladding, was coated with Y2O3 to prevent interactions with the U-Zr alloy at elevated temperatures. The molds packed with particles were set in the graphite crucible. The interfaces between the molds and the graphite were also coated with Y2O3 to prevent interactions during sintering and to allow for easy separation after sintering.

Table 1 shows the sintering conditions performed in this study. Because they are important sintering factors affecting the final densification and microstructure, including pore size and shape, the sintering temperature, sintering time, sintering atmosphere, and heating rate were controlled. Since atmospheric gas could hinder the densification, sintering was conducted under high vacuum (<10−4 Torr) conditions in this experiment and the heating rate was fixed at 2°C/min.

The chemical compositions of the atomized particles and other impurities were assessed by means of inductively coupled plasma atomic emission spectrometry (ICP-AES) and elemental analysis (EA). The sintered samples were cross-sectioned using a slow-speed diamond cut-off wheel and polished using standard techniques. The morphologies of the prepared particles and the microstructures of the sintered samples were examined using an optical microscope (Olympus GX51) and a scanning electron microscope (SEM; JEOL JSM-5800) equipped with X-ray energy dispersive spectroscopy (EDS). Image analysis techniques (iSolution DT image analyzer) were used to quantify the porosity from the cross sections of the sintered samples.

3. Results and Discussion

The U-10Zr alloy particles prepared by centrifugal atomization are shown in Figure 2. Figure 2(a) shows the three-dimensional (3D) morphology and Figure 2(b) shows a cross-sectional view. Most of the particles have a smooth surface and a near-perfect spherical shape, with few attached satellites. The sized particles used in this study ranged from +50 mesh to −325 mesh and particle size distributions are shown in Table 2. From the results of the chemical composition analysis, the contents of U and Zr are within 1% of the target composition and the total impurities of carbon, hydrogen, nitrogen, and oxygen are less than 2000 ppm (Table 3).

The positions of the loaded particle’s neighbors and the internal structures of the approximating particles in the quartz mold are important in the evolution of a structure during sintering. Figure 3 shows the initial packing state of the loaded particles. Figure 3(a) shows sample A with coarse particles (+50 mesh) and Figure 3(b) shows sample D with fine particles (100–170 mesh). It can be observed that particles are in contact with their neighbors and that all contacts among neighboring particles constitute a complex contact network. Pores, or holes, are formed between spherical particles, and the shapes and sizes of the pores are dependent on the arrangement of the particles. The packing density of randomly loaded particles for sample A was approximately 9.6 g/cm3, and the packing density increased as the loaded particle size decreased, such that the particle porosity and the interstices between the particles were regarded as empty space.

Microscopically, sintering minimizes the total sum of system energies such as the surface energy and the grain boundary energy. Macroscopically, sintering could be described as densification resulting from an increase in bulk density with decreasing pore volume [19]. In that sense, the sintering processes can be described by analyzing the microscopic evolution of the arranged particles. At a sintering temperature of 1000°C for 30 min, all samples showed no apparent bonding between the particles, suggesting that these sintering conditions were not suitable to produce any measurable densification. The sintered bodies also broke easily into granules. Therefore, the results of the microstructure examination of these samples are not shown here.

The sinterability at 1100°C for 1 h also showed no significant difference except for the sample having fine particles (−325 mesh), which showed some sintering progress. The results of the microstructure examination conducted on samples C (70–100 mesh) and E (−325 mesh) are shown in Figure 4. Slender sintering necks began to form between the particles in sample E. However, sample C shows the original sphere structure without necking or bonding. A higher-magnification image of sample E (Figure 5(a)) shows some inclusions within the particles and at the interface of the particles, as indicated by the arrows in Figure 5(a). These inclusions were found to be rich in Zr (Figures 5(b) and 5(c)).

In order to increase the degree of sintering, the particle samples were sintered at higher temperatures and the sintering time was extended. The effect of temperature and sintering time on the density can be explained by the following equation [20]:where is the sintered fractional density, is the fractional density at the beginning of the second sintering stage, is Boltzmann’s constant, is the absolute temperature, is a collection of constants that depend on surface energies, atomic size, atomic vibration frequencies, and system geometry, and is the time. Because the temperature is given as an exponential term, small temperature changes can have a large effect, whereas the effect of time is relatively small.

Figure 6 shows bulk samples sintered at 1150°C for 80 min. No cracks were found in any of the samples. The geometries of the sintered bodies retained the shape of the original packing state except for sample E, which shows variations in diameter, leading to an apex-truncated cone-shaped body. Figure 7 shows scanning electron micrographs of these samples, which were cross-sectioned for examination. It can be seen that sintering progressed further as compared to the previous results. Samples A (+50 mesh), B (50–70 mesh), and C (70–100 mesh) show the typical initial stage of sintering, where a slender sintering neck begins to form between particles and a number of necks are observed. The pores are open and interconnected. However, sample D (100–170 mesh) shows many interconnected particles (Figure 7(d)), signifying that the densification went beyond necking. Instead, it entered into an intermediate stage or made a transition from an intermediate stage to the final stage. The contact interface between some particles broke because of tensile and pressure forces among the particles, and some particles formed new contacts. As the sintering progressed, it can be observed that the coordination number increased by closing pores.

Sample E with −325 mesh particles and sample F with mixed particles (+50 mesh and −325 mesh) show the final stage of sintering. Most of the micropores disappeared owing to the high diffusivity at the central area of the bulk samples. Figure 8 shows optical micrographs of samples E and F at the outer region of the bulk samples, where some discrete pores are observed. Therefore, it can be concluded that U-10Zr sintering was nearly finished for samples E and F. Because of the low volume and grain boundary diffusion rates, it is known that densification of particles under pressureless sintering conditions requires high temperatures and long sintering times [15, 21, 22]. However, the results for sample F, which contained mixed particles, suggest that the sinterability of U-10Zr alloy particles can be improved by the addition of small particles, without the need to control sintering variables such as temperature and sintering time.

The porosities and densities of the bulk samples are shown in Figure 9. It can be seen that the density increases as the sintered particle size decreases. The density of U-10Zr increases from 10.4 g/cm3 for the sample with +50 mesh particles to 15.9 g/cm3 for the sample with −325 mesh particles. On the other hand, the porosity decreases from 34.8% for the sample with +50 mesh particles to 0.6% for the sample with −325 mesh particles. This indicates that small particles promote the densification of U-10Zr particles. The sample with mixed particles also showed increased density (15.5 g/cm3) and lower porosity (3.1%).

For particulate fuel, interconnected pores or pore structures are important because they allow fission products developed during irradiation to travel easily to the plenum. The swelling-induced fuel-cladding mechanical interaction (FCMI) during irradiation is also expected to decrease because of structural accommodation of the volume increase. The proper porosity level therefore mainly depends on the degree of fission products and FCMI during irradiation. According to [11, 17], the porosity of particulate fuel is in the range of 14–30%. Therefore, it can be said that samples B (50–70 mesh) and C (70–100 mesh) have suitable pore characteristics, that is, porosities of 21.4% and 15.3%, respectively, making them useful as particulate fuel.

4. Conclusions

From this study, it was shown that a U-10wt%Zr particulate fuel can be fabricated through pressureless sintering, which is one of the simplest powder processing techniques. U-10Zr spherical particles were prepared by centrifugal atomization developed at the KAERI, and the pressureless sintering behavior was investigated. The prepared U-10Zr raw particles showed smooth surfaces and a near-perfect spherical shape. At sintering temperatures of 1100°C for 30 min and 1100°C for 60 min, all samples ranging from +50 mesh to −325 mesh showed no apparent bonding between the particles. However, at a sintering temperature of 1150°C for 80 min, all samples were densified to form bulk bodies, and the microstructures showed apparent sintering stages. Particularly, sample B (50–70 mesh) and sample C (70–100 mesh) showed porosities in the range of 15–30%, which are suitable for a particulate fuel. The results of mixed particles suggested that the sinterability for U-10Zr particulate fuel can be improved by the addition of small particles, without needing to control sintering variables such as temperature and sintering time.

Competing Interests

The authors declare that there are no competing interests regarding the publication of this paper.

Acknowledgments

This study was supported by Nuclear Research & Development Program of the National Research Foundation Grant funded by the Ministry of Education, Science and Technology in Korea (Grant no. 2013M2A8A2000676).