Research Article
Inserting Stress Analysis of Combined Hexagonal Aluminum Honeycombs
Table 2
Compressive parameters of two stack-up CHAH.
| Group | Parameters | 1# | 2# | 3# | Average |
| H1-10 mm + H1-10 mm | [MPa] | 1.260 | 1.556 | 1.447 | 1.421 | [MPa] | 4.645 | 4.831 | 4.917 | 4.798 | Densification displacement [mm] | 16.015 | 15.755 | 15.805 | 15.858 |
| H2-10 mm + H2-10 mm | [MPa] | 5.633 | 5.049 | 5.285 | 5.322 | [MPa] | 14.703 | 14.191 | 14.109 | 14.334 | Densification displacement [mm] | 15.065 | 15.003 | 14.963 | 15.010 |
| H1-10 mm + H2-10 mm | [MPa] | 2.822 | 2.624 | 3.032 | 2.826 | [MPa] | 10.395 | 9.710 | 10.260 | 10.122 | Densification displacement [mm] | 16.090 | 16.120 | 16.068 | 16.093 |
|
|