Influence of Core Thickness and Boundary Condition on the Modal Characteristics of Composite Structure with Metallic Damping Core

Table 4

Displacement deviation at measure points (D1 ∼ D12) under different boundary conditions. (unit: μm).

	C-C-C-C						C-C-C-F						C-C-F-F
	First order		Second order		Third order		First order		Second order		Third order		First order		Second order		Third order
	MV	SD	MV	SD	MV	SD	MV	SD	MV	SD	MV	SD	MV	SD	MV	SD	MV	SD
D1	32.26	0.113	4.79	0.076	1.45	0.098	31.56	0.035	5.07	0.092	0.86	0.137	31.94	0.073	5.09	0.091	1.01	0.134
D2	32.31	0.147	5.04	0.154	1.62	0.142	31.49	0.027	5.22	0.107	0.82	0.144	31.86	0.182	5.04	0.143	0.99	0.097
D3	32.29	0.125	4.94	0.095	1.71	0.117	31.44	0.056	5.27	0.113	1.06	0.202	31.77	0.061	5.03	0.112	0.99	0.137
D4	32.22	0.118	4.97	0.082	1.32	0.134	31.45	0.043	5.33	0.086	1.13	0.183	30.72	0.062	5.11	0.083	1.12	0.146
D5	31.93	0.094	4.83	0.106	1.67	0.187	31.49	0.022	5.31	0.094	0.96	0.116	31.82	0.124	5.08	0.137	0.97	0.133
D6	32.18	0.157	5.22	0.233	1.75	0.143	31.55	0.016	5.41	0.083	1.27	0.134	31.79	0.153	5.02	0.224	1.08	0.212
D7	32.44	0.201	5.31	0.162	1.82	0.126	31.52	0.047	5.43	0.117	1.18	0.246	31.55	0.115	5.04	0.068	1.03	0.107
D8	31.97	0.193	5.09	0.066	1.87	0.132	31.49	0.028	5.13	0.104	1.21	0.209	31.23	0.092	4.95	0.047	1.15	0.093
D9	32.05	0.115	4.85	0.074	1.37	0.145	31.55	0.043	5.06	0.097	0.91	0.177	30.53	0.146	4.89	0.118	1.03	0.278
D10	32.12	0.174	4.92	0.096	1.58	0.184	31.48	0.034	5.17	0.105	0.92	0.092	30.76	0.128	4.91	0.132	0.89	0.139
D11	32.17	0.164	5.18	0.118	1.65	0.088	31.45	0.053	4.96	0.132	0.99	0.106	31.02	0.079	4.88	0.124	0.93	0.223
D12	32.09	0.247	5.11	0.125	1.51	0.139	31.44	0.064	5.34	0.109	0.87	0.102	30.44	0.134	4.76	0.083	0.86	0.064