Immobilized Horseradish Peroxidase on Discs of Polyvinyl Alcohol-Glutaraldehyde Coated with Polyaniline

Caramori, Samantha Salomão; Fernandes, Kátia Flávia; de Carvalho Junior, Luiz Bezerra

doi:https://doi.org/10.1100/2012/129706

The Scientific World Journal

On this page

Abstract Introduction Materials and Methods Results and Discussion Conclusions Acknowledgments References Copyright Related Articles

Research Article | Open Access

Volume 2012 | Article ID 129706 | https://doi.org/10.1100/2012/129706

Immobilized Horseradish Peroxidase on Discs of Polyvinyl Alcohol-Glutaraldehyde Coated with Polyaniline

Samantha Salomão Caramori,^1,2Kátia Flávia Fernandes,³and Luiz Bezerra de Carvalho Junior²

Academic Editor: Jean-Francois Hausman

Received21 Oct 2011

Accepted11 Dec 2011

Published24 Apr 2012

Abstract

Discs of network polyvinyl alcohol-glutaraldehyde (PVAG) were synthesized and coated with polyaniline (PANI) using glutaraldehyde as a chemical arm (PVAG-PANIG-HRP disc). The best conditions for the immobilization were established as about 1.0 mg mL⁻¹ of protein, for 60 min and pH 5.5. The soluble enzyme lost all of its activity after incubation at 70°C for 15 min, whereas the PVAG-PANIG-HRP disc retained about half of the initial activity for pyrogallol. The same PVAG-PANIG-HRP disc was used consecutively three times without any activity lossbut presented 25% of the initial activity after the 7th use. PVAG-PANIG-HRP disc retained approximately 80% and 60% of its initial activity after 60 and 80 days of storage, respectively. Resorcinol, m-cresol, catechol, pyrogallol, α-naphthol, βnaphthol, and 4, 4′-diaminodiphenyl benzidine were efficiently oxidized by the PVAG-PANIG-HRP disc (from about 70% to 90%), and it was less efficient towards aniline, phenol, and 2-nitrosonaphthol.

1. Introduction

Peroxidases (Enzyme Commission number 1.11.1.7) are a huge family of heme-containing enzymes that catalyze oxidation and reduction reactions of large families of substrates.

Their broad substrate specificity, polyfunctionality, and availability from different sources allow their application in various biotechnological processes. Oxidative destruction of colored compounds is significantly stimulated by peroxidase and it is a practical interest for decoloration processes used in food, textile, and paper industry as well as in washing powders [1, 2]. Peroxidases have a variety of biotechnology application due to this catalytic mechanism. For instance, they are capable of oxidizing many compounds bearing the functional group R-N=N-R′ (azo-dyes), in which R and R′′ can be either aryl or alkyl groups. These compounds are widely used in the textile industry and discarded in water collections. They are defined as pollutants because of their mutagenic and carcinogenic effects. Additionally, azo-dyes can cause biological cycles alteration [3, 4]. Peroxidases are also extensively used in clinical and immunological analysis, such as glucose [5, 6], cholesterol [7, 8], and urea [9] determinations, procedures involving H₂O₂ releasing. Horseradish peroxidase (HRP) is the most popular source among the peroxidases. It can use a variety of organic compounds as donors and acceptors of electron.

The immobilization of these enzymes has been used to enhance the potential applications of them. Immobilized peroxidase obtained from bitter gourd (Momordica charantia) has been reported to present more advantages than the free enzyme in the treatment of wastewater contaminated with phenols [10]. Immobilized Saccharum spontaneum peroxidase [11] and potato polyphenol oxidase [12] have also been proposed to decompose textile dyes.

Previously in our laboratories, HRP was successfully immobilized on powder of PANIG [13, 14]. This enzymatic derivative presented difficulties to be separated from the reaction mixture. Attempts to overcome the separation step were also conducted by our research group, culminating in the preparation of PET-PANIG composite as strips with immobilized HRP, which could be manually removed from reaction medium. However, this material presented low protein loading [15].

PVAG has been used for protein immobilization because of the plasticity and high surface area of this material [16–18]. The hydrophilic behavior of PVA, on the other hand, interferes in the microenvironment of the immobilized protein when nonpolar substrates/products are involved. Moreover, comparisons of PVA and PVA-PANI composites indicated a less immobilization capacity of PVA when it is not covered by PANI [19]. Trying to overcome the limitation of PANI powder and PET-PANI composites, and using the interesting properties of PVA, discs of PVAG covered with PANI are proposed as a matrix for HRP immobilization. The resulting composite was investigated to propose an alternative immobilized HRP preparation to be used in the detoxification of wastewater containing phenolic compounds. Some features affecting the immobilization procedure and properties of this derivative were then investigated.

2. Materials and Methods

2.1. Materials

Pyrogallol and catechol were obtained from Sigma-Aldrich (Saint Louis CA, USA). Alpha- and beta-naphthol, m-cresol, resorcinol, and phenol were purchased from Vetec Química Fina Ltda. (São Paulo SP, Brazil). Aniline, 2-nitrosonaphthol, 4,4′ diamine-diphenyl-benzidine were purchased from Merck (Darmstadt, Germany). HRP was kindly provided by Dr. Elba Bon (Universidade Federal do Rio de Janeiro, Rio de Janeiro, Brazil).

2.2. PVAG-PANIG Discs Synthesis

The PVAG-PANIG disc synthesis was based on procedures described by Carvalho et al. [17] and Fernandes et al. [13], modified by Caramori et al. [19]. Briefly 2% (w/v) polyvinyl alcohol (10 mL) was dissolved at 65°C, and then 2.5% (v/v) glutaraldehyde (1.5 mL) was added in order to form a PVA-glutaraldehyde network [19]. Aliquots (20 μL) of this mixture were transferred to 96 wells of a microplate containing 3.0 M HCl (120 μL) and kept at 25°C for 24 h, after which the discs were formed (PVAG synthesis). Afterwards, the discs were removed and incubated with 0.61 M ammonium persulphate, prepared in 2.0 M HCl, for 30 min. Then, they were incubated with 0.44 M aniline for 60 min (PVAG coating with polyaniline: PVAG-PANI). Finally, the PVAG-PANI discs were activated using 2.5% (v/v) glutaraldehyde for 60 min and exhaustively washed with 0.1 M phosphate buffer, pH 6.0 (PVAG-PANIG synthesis). This process yielded 240 discs (wet) weighting about 15 mg each.

2.3. HRP Immobilization

One disc of PVAG-PANIG was incubated with HRP (1.0 mL containing 12,500 U mL⁻¹; 7 μg mL⁻¹ prepared in different solutions of 0.1 M sodium acetate buffer at pH 4.0–5.5 or phosphate buffer at pH 6.0–7.5) for 60 min, under orbital shaking (80 rpm) at 4°C. Afterwards, the immobilized enzyme on the HRP-PVAG disc, from now on abbreviated as PVAG-PANIG-HRP, was washed 3-folds with 0.1 M sodium acetate or phosphate buffer, twice with 1.0 M NaCl and twice with the same buffer. Discs of PVAG were used to immobilize HRP in the same conditions described above. HRP activity was not detected in the final washing buffer.

2.4. Enzyme Determinations

The activities of the soluble and immobilized HRP were established according to Halpin et al. [20] using pyrogallol and H₂O₂ as substrates. Briefly, either one disc of PVAG-PANIG-HRP (15.0 mg) or 0.1 mL of soluble HRP (874 U mL⁻¹) was incubated at room temperature (28°C) with 0.5 mL of 12.69 mM pyrogallol (0.5 mL), 5.0 mM H₂O₂ (0.25 mL) prepared in 0.1 M sodium acetate buffer, pH 4.5, or 0.1 M sodium phosphate buffer, pH 7.0 (1.4 mL), and after one min (soluble HRP) or 10 min (PVAG-PANIG-HRP) the formed product (purpurogallin) was spectrophotometrically established at 420 nm (Ultrospec 2000, GE Health Care). One unit of enzyme activity (U) was defined as the amount of enzyme capable of oxidizing one micromole of pyrogallol per minute under experimental conditions (ε = 961 M cm⁻¹).

2.5. Immobilization Optimization Conditions

The PVAG-PANIG-HRP disc was synthesized as above described using enzyme concentration varying from 0.502 to 0.912 μg mL⁻¹. Increasing amounts of HRP prepared in 0.1 M sodium phosphate buffer, pH 7.0 were incubated with the PVAG-PANIG disc for 60 min at 4°C. The derivative was washed 3-folds with 0.1 M sodium acetate buffer pH 5.0, followed by twice with 1.0 M NaCl and twice with the same buffer. The PVAG-PANIG-HRP disc activity was established and the retained protein estimated by the difference between offered protein and that found in the washing solutions. Firstly, the optimum pH was established incubating samples of soluble HRP with PVAG-PANIG discs, in the appropriated buffer (4.0–5.5 using 0.1 M sodium acetate buffer and 6.0–7.5 using 0.1 M sodium phosphate buffer). After that, the incubation time (30–210 min) was optimized. After washing the PVAG-PANIG-HRP discs their activities were measured as described above. All of these experiments were performed in triplicates and the results expressed as mean ± standard deviation.

2.6. Immobilized HRP Properties

The following properties of the soluble and immobilized HRP (preparation synthesized under the best conditions) were investigated: the time course of the pyrogallol oxidation, the activity of the preparations as above described at pH varying from 3.5 to 7.0 (3.5–5.5 using 0.1 M acetate buffer and 6.0–7.0 using 0.1 M sodium phosphate buffer) and at temperatures varying from 30°C to 60°C. Soluble HRP (0.1 mL) or one disc of PVAG-PANIG-HRP were incubated with 12.69 mM pyrogallol (0.5 mL), 5 mM H₂O₂ (0.25 mL) either at the indicated pH, 28°C, or at the indicated temperatures, pH 4.5. Then, after either 1 min (soluble) or 10 min (immobilized), aliquots were withdrawn and the formed product (purpurogallin) spectrophotometrically established at 420 nm. One enzyme unit (U) was defined as the amount of HRP capable of forming 1 μmol of purpurogallin per min.

The thermal stability of both free (0.1 mL) and immobilized enzymes (one disc) was established by incubating the preparations at 50°C and 70°C. Samples were then withdrawn at time intervals (15–45 min) and after equilibration at 37°C their activities were determined as described above. Kinetics was evaluated by assaying the preparation activities at pyrogallol concentrations varying from 4.0 to 48.7 mM. The HRP activity versus pyrogallol concentration was plotted. In order to estimate apparent Vmax and Km, a nonlinear regression (hyperbolic fit) was performed, using Sigmaplot 2000, version 6 (Systat Software Inc., USA). The reuse of the immobilized enzyme was evaluated by assaying the same preparation seven times and washing it with buffer (0.1 M sodium acetate, pH 4.5) between each procedure. Finally, the shelf life was analyzed by keeping several PVAG-PANIG-HRP discs in 0.1 M acetate buffer, pH 4.5, at 4°C and assaying the stored disc activity every seven days up to 80 days. The 100% value was established as the activity at the initial incubation time. All of these experiments were performed in triplicates and the results expressed as mean ± standard deviation. Figures 2–6 were plotted using Sigmaplot 2000, version 6 (Systat Software Inc., USA).

2.7. Treatment of Phenolic Compounds by the Soluble and PVAG-PANIG-HRP Disc

The soluble enzyme (0.1 mL) and PVAG-PANIG-HRP (one disc) containing both similar activity (about 90 U) were incubated at 37°C for 1.5 h with 0.1 mM sodium acetate buffer (2.0 mL), pH 4.5, containing 0.75 mmol H₂O₂ and 1.0 mM of the following phenolic compounds: resorcinol; m-cresol; catechol; pyrogallol; aniline; phenol; α-naphthol; β-naphthol; 4,4′-diaminodiphenyl benzidine; 2-nitrosonaphthol. Afterwards, the remaining phenolic compounds were spectrophotometrically (750 nm) established according to Lowry et al. [21] and compared with the amount found in the untreated phenolic solutions (100%). All these experiments were performed in triplicates and the results expressed as mean ± standard deviation.

3. Results and Discussion

The PVAG-PANIG disc synthesis is carried out in two steps: firstly, a network of polyvinyl alcohol molecules is formed using glutaraldehyde as an arm under acid catalysis [16, 19] yielding the disc, which is coated with polyaniline chemically synthesized from aniline [13]. The PVAG and PVAG-PANIG discs presented 4.0 mm in diameter due to the microplate wells used as mold (Figure 1).

(a)

(b)

(a)

(b)

(a)

(b)

(a)

(b)

Thus the HRP is covalently fixed onto the PVAG-PANIG disc via glutaraldehyde. It is important to notice that the physical shape of the PVAG occurs depending on the template used during the synthesis. Here, the wells of a microplate were used and therefore discs were obtained. However, PVAG was already used for plasticizing filter paper, which was used as a matrix for protein immobilization [18]. The moldability, flexibility, biocompatibility, and adhesive property of PVA make it a versatile material for bioengineering. Recovering PVA with PANI increases the superficial area of this composite material and hence the protein loading, as mentioned by Caramori et al. [22].

Figure 2 shows the relationship between the offered HRP and the immobilized enzyme expressed in terms of retained activity, protein per disc, and activity per mg of retained protein (specific activity). It is worthwhile to notice that the PVAG disc itself has carbonyl groups available [16, 17] for the HRP immobilization. However, the glutaraldehyde-treated PANI coat would increase these available groups as demonstrated by the increased activity of the PVAG-PANIG-HRP disc compared to that found for the PVAG-HRP preparation (Figure 2(a)). This is also reflected by the difference on the specific activity between them (Figure 2(b)). Intriguingly, the difference in terms of retained protein is negligible (Figure 2(b)). Therefore, one can admit that the PANI coating provides some advantage to the PVAG disc as far as the HRP immobilization is concerned. According to this result there, is a linear relationship between the offered HRP and the catalytically active immobilized HRP per disc (Figure 2(a)). However, this correlation is not followed by the specific activity (Figure 2(b)), which showed a hyperbolic curve suggesting that there is a limit after which inactive enzyme molecules are immobilized. Steric hindrance due to the overloading could be probably attributed to this effect. To avoid this phenomenon, all experiments to characterize the immobilized enzyme were carried out using a preparation synthesized with 7.0 μg mL⁻¹ of the soluble HRP instead 1.0 mg mL⁻¹.

Recovering of PVAG with PANIG improved its capability for HRP immobilization 24.6% (PVAG 1,155 U disc⁻¹ against PVAG-PANIG 1,533 U disc⁻¹). The effectiveness of this material can be better demonstrated when comparing it with PET-PANIG, another composite tested for HRP immobilization [15]. PVAG-PANIG presented 9,650 more active immobilized HRP than PET-PANIG (PVAG-PANIG = 1,219,935.540 U cm⁻² versus PET-PANIG = 126.41 U cm⁻²). Caramori et al. [22], based on UV-Vis spectra, surface area porosimetry, and scanning electron microscopy analyses, reported the PVAG-PANIG disc as a macroporous structure. The authors concluded this macroporous aspect due to PANI coating.

Figure 3(a) shows that 60 min is the best incubation time for the derivative PVAG-PANIG-HRP synthesis, after which longer incubation does not increase the catalytic activity of the immobilized enzyme. This time depends on the support and/or chemical groups involved in the HRP immobilization on different materials [23, 24]. In the case of PANIG, the immobilization of HRP requires generally 60 min [6, 13].

The best pH immobilization value of 5.5 for the HRP immobilization on PVAG-PANIG is shown in Figure 3(b). This pH value also depends on the support and/or chemical groups involved. Fernandes et al. [13] immobilizing HRP on PANIG reported a different optimum immobilization pH (6.0). This discrepancy can be probably attributed to the PVAG influence.

The time course of the pyrogallol oxidation catalyzed by the soluble and PVAG-PANIG-HRP disc showed that under the established experimental conditions a semilog plot (first order kinetics) was attained at the 1st and 10th minute, respectively (data not shown). Furthermore, all substrate was oxidized after 30 min of incubation by using both preparations.

The pH profiles for the soluble and PVAG-PANIG-HRP activities are displayed in Figure 4(a). Higher pH values than 7.0 were not studied because of the pyrogallol “autoxidation”. There is a marked difference of the pH influence on the enzyme activities. The immobilized enzyme presents optimum pH value at 4.5 whereas the soluble form at approximately 7.0 as already reported in the literature [25]. Fernandes et al. [14] reported a value of 7.0 for the HRP immobilized on PANI. Negatively and positively charged matrices are known to displace the pH profile towards to alkaline and acid pH values, respectively, as compared to the native enzymes, at low ionic strength. This left shift of optimum pH for the PVAG-PANIG-HRP suggests that the PVAG-PANIG presents positive charges on its surface. Li and Townshend [26] also reported different optimum pH for the HRP activity before (7.0) and after immobilization (5.8) on polytetrafluorethylene tubing.

The effect of the temperature on the soluble and PVAG-PANIG-HRP is shown in Figure 4(b) and optimal temperatures were found to be 40°C and 40–50°C, respectively. The decays of the descending arms of the curves denote different effects of the temperature on the soluble and immobilized enzyme. No activity was detected for the soluble enzyme assay at 60°C, whereas the immobilized enzyme assay still presented some activity (30% of that at 50°C). Similar results were reported by El-Essi et al. [27] and Lai and Lin [28] for HRP immobilized on sol-gel matrices and porous glass, respectively. Further evidences for the higher thermal stability for the PVAG-PANIG-HRP can be seen in Figure 5 which showed that the soluble enzyme activity decreased faster than the immobilized preparation when both were incubated at 50°C and 70°C. The soluble enzyme lost all activity after 15 min at 70°C, whereas the immobilized one retained about 20% of its initial activity. Increase of the thermal resistance after HRP immobilization has already been reported in the literature [24, 29–31].

The action of the soluble and PVAG-PANIG-HRP on pyrogallol followed the Michaelis-Menten kinetics. Values of apparent Michaelis constants were estimated to be mM and mM for the soluble and immobilized HRP (apparent value), respectively. This discrepancy showed to be statistically different ( and ). Conformational/steric, partitioning, diffusional/mass-transfer, and microenvironmental effects are well known to influence immobilized enzyme kinetics. Kinetic parameters, particularly, the apparent Km, can provide the degree of these interferences when compared to that calculated for the soluble enzyme. This apparent constant usually increases as the result of impairment of the enzyme action under those effects.

The reuse of the PVAG-PANIG-HRP is presented in Figure 6(a). The same disc was used three times without activity loss and retained 25% of the initial activity after the 7th use. It is worthwhile to draw attention to the fact that this preparation was incubated with H₂O₂, a traditional HRP inhibitor and protein denaturing agent. The HRP derivatives (aluminum-pillared interlayered clay-HRP with addition of polyethylene glycol) synthesized by Cheng et al. [32], showed to be not reusable were and Akhtar et al. [33] reported poorer performance reusing immobilized bitter gourd peroxidase on Sephadex G-50. The storage stability (shelf life) of the PVAG-PANIG-HRP was investigated for 80 days at 4°C in 0.1 M sodium acetate buffer, pH 4.5 and Figure 6(b) resumes the results. The immobilized enzyme derivative retained approximately 80% and 60% of its initial activity after 60 and 80 days of storage, respectively. This behavior is superior to those reported by Rojas-Melgarejo et al. [34] and Cheng et al. [32].

The enzymatic approach has attracted much interest in the decolorization/degradation of textile and other industrially important dyes from wastewater as an alternative strategy to conventional chemical, physical and biological treatments [35]. Cheng et al. [32] removed, after 4 h, more than 90% of phenol using polyethylene glycol as aluminum-pillared-interlayered clay-peroxidase stabilizer in the reaction medium. The ability of the soluble HRP and PVAG-PANIG-HRP disc to remove phenolic compounds up to 1.5 h is demonstrated in the Table 1. Most of them were efficiently oxidized by both soluble and immobilized enzyme and no stabilizer was added. Pyrogallol, α-naphthol, catechol, β-naphthol, 4,4′-diaminodiphenyl benzidine, m-cresol, resorcinol, and 2-nitrosonaphthol were oxidized by the PVAG-PANIG-HRP disc in percents varying from 70% to 90%, except for 2-nitrosonaphthol (c.a. 18%). As mentioned above, pyrogallol was completely oxidized after 30 min of incubation by both enzymatic preparations. Therefore, the reusability and higher thermal stability of the PVAG-PANIG-HRP disc would offer advantage compared to the soluble enzyme. The PVAG-PANIG-HRP disc showed to be more efficient than the immobilized bitter gourd (Momordica charantia) peroxidase on Con A adsorbed-Sephadex G 50 [10]. According to these authors, resorcinol, m-cresol, catechol, pyrogallol, under similar experimental conditions, were only removed 18%, 11%, 45%, and 0%, respectively.

Both enzymatic preparations showed to be less efficient towards aniline and phenol. However, the immobilized HRP presented better performance than soluble form. Different results were obtained with the immobilized bitter gourd peroxidase, which was more efficient to remove phenol (about 90%) than PVAG-PANIG-HRP disc (about 35%).

4. Conclusions

More than 200 discs of the network polyvinyl alcohol-glutaraldehyde (PVAG) coated with polyaniline (PANIG) can be synthesized by a simple and inexpensive procedure. HRP can also be covalently fixed onto these discs via glutaraldehyde (PVAG-PANIG-HRP disc). The immobilization efficiency of this material was more than 9,000 fold higher than the obtained with PET-PANIG composite. The optimum pH of the PVAG-PANIG-HRP disc is lower than that reported for the soluble enzyme, whereas the optimum temperature is higher. The PVAG-PANIG-HRP disc is more thermal resistant than the soluble enzyme. The same PVAG-PANIG-HRP disc can be reused and stored for months without significant activity loss. Resorcinol, m-cresol, catechol, pyrogallol, α-naphthol, β-naphthol, and 4,4′-diaminodiphenyl benzidine are efficiently oxidized by the PVAG-PANIG-HRP disc (approximately about 60% to 90%), while aniline, phenol, and 2-nitrosonaphthol are less efficiently oxidized. The flexibility of PVA and the advantages obtained in the immobilization procedure make the PVAG-PANIG composite a possible target for applications in the treatment of wastewater.

Acknowledgments

The authors are thankful to the Brazilian National Research Council (CNPq) for financing this research and Dr. Elba Bon for providing the peroxidase.

References

M. Shakeri and M. Shoda, “Efficient decolorization of an anthraquinone dye by recombinant dye-decolorizing peroxidase (rDyP) immobilized in silica-based mesocellular foam,” Journal of Molecular Catalysis B, vol. 62, no. 3-4, pp. 277–281, 2010.
View at: Publisher Site | Google Scholar
V. Yousefi and H. R. Kariminia, “Statistical analysis for enzymatic decolorization of acid orange 7 by Coprinus cinereus peroxidase,” International Biodeterioration and Biodegradation, vol. 64, no. 3, pp. 245–252, 2010.
View at: Publisher Site | Google Scholar
V. S. Houk, “The genotoxicity of industrial wastes and effluents: a review,” Mutation Research, vol. 277, no. 2, pp. 91–138, 1992.
View at: Publisher Site | Google Scholar
K. T. Chung and C. E. Cerniglia, “Mutagenicity of azo dyes: structure-activity relationships,” Mutation Research, vol. 277, no. 3, pp. 201–220, 1992.
View at: Publisher Site | Google Scholar
V. Sanz, S. de Marcos, and J. Galbán, “Direct glucose determination in blood using a reagentless optical biosensor,” Biosensors and Bioelectronics, vol. 22, no. 12, pp. 2876–2883, 2007.
View at: Publisher Site | Google Scholar
F. M. Lopes, S. Mitidieri, and K. F. Fernandes, “A mini-reactor for glucose analysis in human serum samples,” Revista Processos Químicos, vol. 2, pp. 83–88, 2008.
View at: Google Scholar
H. H Yu, G. S. Ginsbrug, and N. Harris, “Evaluation and clinical application of a direct low density lipoprotein cholesterol assay in normolipemic and hyperlipidemic adults,” American Journal of Cardiology, vol. 80, pp. 1295–1299, 1997.
View at: Google Scholar
S. Singh, P. R. Solanki, M. K. Pandey, and B. D. Malhotra, “Cholesterol biosensor based on cholesterol esterase, cholesterol oxidase and peroxidase immobilized onto conducting polyaniline films,” Sensors and Actuators B, vol. 115, no. 1, pp. 534–541, 2006.
View at: Publisher Site | Google Scholar
F. Mizutani, S. Yabuki, Y. Sato, T. Sawaguchi, and S. Iijima, “Amperometric determination of pyruvate, phosphate and urea using enzyme electrodes based on pyruvate oxidase-containing poly(vinyl alcohol)/polyion complex-bilayer membrane,” Electrochimica Acta, vol. 45, no. 18, pp. 2945–2952, 2000.
View at: Publisher Site | Google Scholar
S. Akhtar and Q. Husain, “Potential applications of immobilized bitter gourd (Momordica charantia) peroxidase in the removal of phenols from polluted water,” Chemosphere, vol. 65, no. 7, pp. 1228–1235, 2006.
View at: Publisher Site | Google Scholar
T. S. Shaffiqu, J. J. Roy, R. A. Nair, and T. E. Abraham, “Degradation of textile dyes mediated by plant peroxidases,” Applied Biochemistry and Biotechnology A, vol. 102-103, pp. 315–326, 2002.
View at: Publisher Site | Google Scholar
A. A. Khan and Q. Husain, “Decolorization and removal of textile and non-textile dyes from polluted wastewater and dyeing effluent by using potato (Solanum tuberosum) soluble and immobilized polyphenol oxidase,” Bioresource Technology, vol. 98, no. 5, pp. 1012–1019, 2007.
View at: Publisher Site | Google Scholar
K. F. Fernandes, C. S. Lima, H. Pinho, and C. H. Collins, “Immobilization of horseradish peroxidase onto polyaniline polymers,” Process Biochemistry, vol. 38, no. 9, pp. 1379–1384, 2003.
View at: Publisher Site | Google Scholar
K. F. Fernandes, C. S. Lima, F. M. Lopes, and C. H. Collins, “Properties of horseradish peroxidase immobilised onto polyaniline,” Process Biochemistry, vol. 39, no. 8, pp. 957–962, 2004.
View at: Publisher Site | Google Scholar
S. S. Caramori and K. F. Fernandes, “Covalent immobilisation of horseradish peroxidase onto poly(ethylene terephthalate)-poly(aniline) composite,” Process Biochemistry, vol. 39, no. 7, pp. 883–888, 2004.
View at: Publisher Site | Google Scholar
A. M. Araújo, M. T. Neves Jr., W. M. Azevedo et al., “Polyvinyl alcohol-glutaraldehyde network as a support for protein immobilization,” Biotechnology Techniques, vol. 112, pp. 67–72, 1996.
View at: Google Scholar
L. B. Carvalho Jr., A. M. Araújo, A. M. P. Almeida, and W. M. Azevedo, “The use of polyvinyl alcohol glutaraldehyde antigen coated discs for laser induced fluorescence detection of plague,” Sensors and Actuators B, vol. 36, no. 1–3, pp. 427–430, 1996.
View at: Google Scholar
G. H. T. S. Barbosa, E. M. Santana, A. M. P. Almeida, A. M. Araújo, O. Fatibello-Filho, and L. B. Carvalho Jr., “The use of filter paper plasticized with polyvinyl alcohol-glutaraldehyde in ELISA,” Brazilian Journal of Medical and Biological Research, vol. 33, no. 7, pp. 823–827, 2000.
View at: Google Scholar
S. S. Caramori, F. N. De Faria, M. P. Viana, K. F. Fernandes, and L. B. Carvalho Jr., “Trypsin immobilization on discs of polyvinyl alcohol glutaraldehyde/ polyaniline composite,” Materials Science and Engineering C, vol. 31, no. 2, pp. 252–257, 2011.
View at: Publisher Site | Google Scholar
B. Halpin, R. Pressey, J. Jen, and N. J. Mondy, “Purification and characterization of peroxidase isoenzymes from green peas (Pisum sativum),” Journal of Food Science, vol. 54, pp. 644–669, 1989.
View at: Google Scholar
O. H. LOWRY, N. J. ROSEBROUGH, A. L. FARR, and R. J. RANDALL, “Protein measurement with the Folin phenol reagent,” The Journal of Biological Chemistry, vol. 193, no. 1, pp. 265–275, 1951.
View at: Google Scholar
S. S. Caramori, K. F. Fernandes, and L. B. Carvalho Jr., “Synthesis and characterization of polyvinyl alcohol-polyaniline-glutaraldehyde composite disc: a probable matrix for protein immobilization,” Revista Processos Químicos, vol. 7, pp. 46–52, 2010.
View at: Google Scholar
Z. M. Liu, S. Tingry, C. Innocent, J. Durand, Z. K. Xu, and P. Seta, “Modification of microfiltration polypropylene membranes by allylamine plasma treatment. Influence of the attachment route on peroxidase immobilization and enzyme efficiency,” Enzyme and Microbial Technology, vol. 39, no. 4, pp. 868–876, 2006.
View at: Publisher Site | Google Scholar
F. Rojas-Melgarejo, J. N. Rodríguez-López, F. García-Cánovas, and P. A. García-Ruiz, “Cinnamic carbohydrate esters: new polymeric supports for the immobilization of horseradish peroxidase,” Carbohydrate Polymers, vol. 58, no. 1, pp. 79–88, 2004.
View at: Publisher Site | Google Scholar
B. Chance and A. C. Maehly, “Assay of catalases and peroxidases,” Methods in Enzymology, vol. 2, pp. 764–775, 1955.
View at: Publisher Site | Google Scholar
Y. Z. Li and A. Townshend, “Evaluation of the adsorptive immobilisation of horseradish peroxidase on PTFE tubing in flow systems for hydrogen peroxide determination using fluorescence detection,” Analytica Chimica Acta, vol. 359, no. 1-2, pp. 149–156, 1998.
View at: Publisher Site | Google Scholar
F. A. El-Essi, A. Z. Abu Zuhri, S. I. Al-Khalil, and M. S. Abdel-Latif, “Spectrophotometric determination of enzymatically generated hydrogen peroxide using Sol-Gel immobilized horseradish peroxidase,” Talanta, vol. 44, no. 11, pp. 2051–2058, 1997.
View at: Publisher Site | Google Scholar
Y. C. Lai and S. C. Lin, “Application of immobilized horseradish peroxidase for the removal of p-chlorophenol from aqueous solution,” Process Biochemistry, vol. 40, no. 3-4, pp. 1167–1174, 2005.
View at: Publisher Site | Google Scholar
E. Miland, M. R. Smyth, and C. ÓFágáin, “Increased thermal and solvent tolerance of acetylated horseradish peroxidase,” Enzyme and Microbial Technology, vol. 19, no. 1, pp. 63–67, 1996.
View at: Publisher Site | Google Scholar
U. Bora, P. Sharma, S. Kumar, K. Kannan, and P. Nahar, “Photochemical activation of a polycarbonate surface for covalent immobilization of a protein ligand,” Talanta, vol. 70, no. 3, pp. 624–629, 2006.
View at: Publisher Site | Google Scholar
S. Musthapa, S. Akhtar, A. A. Khan, and Q. Husain, “An economical, simple and high yield procedure for the immobilization/stabilization of peroxidases from turnip roots,” Journal of Scientific and Industrial Research, vol. 63, no. 6, pp. 540–547, 2004.
View at: Google Scholar
J. Cheng, S. Ming Yu, and P. Zuo, “Horseradish peroxidase immobilized on aluminum-pillared interlayered clay for the catalytic oxidation of phenolic wastewater,” Water Research, vol. 40, no. 2, pp. 283–290, 2006.
View at: Publisher Site | Google Scholar
S. Akhtar, A. A. Khan, and Q. Husain, “Potential of immobilized bitter gourd (Momordica charantia) peroxidases in the decolorization and removal of textile dyes from polluted wastewater and dyeing effluent,” Chemosphere, vol. 60, no. 3, pp. 291–301, 2005.
View at: Publisher Site | Google Scholar
F. Rojas-Melgarejo, J. N. Rodríguez-López, F. García-Cánovas, and P. A. García-Ruiz, “Immobilization of horseradish peroxidase on cinnamic carbohydrate esters,” Process Biochemistry, vol. 39, no. 11, pp. 1455–1464, 2004.
View at: Publisher Site | Google Scholar
Q. Husain, “Potential applications of the oxidoreductive enzymes in the decolorization and detoxification of textile and other synthetic dyes from polluted water: a review,” Critical Reviews in Biotechnology, vol. 26, no. 4, pp. 201–221, 2006.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2012 Samantha Salomão Caramori et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

1592

Downloads

1045

Citations