Micelle-Assisted Synthesis of Al<sub>2</sub>O<sub>3</sub>·CaO Nanocatalyst: Optical Properties and Their Applications in Photodegradation of 2,4,6-Trinitrophenol

Imtiaz, Ayesha; Farrukh, Muhammad Akhyar; Khaleeq-ur-rahman, Muhammad; Adnan, Rohana

doi:https://doi.org/10.1155/2013/641420

The Scientific World Journal

On this page

Abstract Introduction Materials and Methods Results and Discussion Conclusion Acknowledgments References Copyright Related Articles

Research Article | Open Access

Volume 2013 | Article ID 641420 | https://doi.org/10.1155/2013/641420

Micelle-Assisted Synthesis of Al₂O₃·CaO Nanocatalyst: Optical Properties and Their Applications in Photodegradation of 2,4,6-Trinitrophenol

Ayesha Imtiaz,¹Muhammad Akhyar Farrukh,¹Muhammad Khaleeq-ur-rahman,¹and Rohana Adnan²

Academic Editor: O. Gonzalez Diaz, J. Yu

Received26 Aug 2013

Accepted19 Sept 2013

Published07 Nov 2013

Abstract

Calcium oxide (CaO) nanoparticles are known to exhibit unique property due to their high adsorption capacity and good catalytic activity. In this work the CaO nanocatalysts were prepared by hydrothermal method using anionic surfactant, sodium dodecyl sulphate (SDS), as a templating agent. The as-synthesized nanocatalysts were further used as substrate for the synthesis of alumina doped calcium oxide (Al₂O₃·CaO) nanocatalysts via deposition-precipitation method at the isoelectric point of CaO. The Al₂O₃·CaO nanocatalysts were characterized by FTIR, XRD, TGA, TEM, and FESEM techniques. The catalytic efficiencies of these nanocatalysts were studied for the photodegradation of 2,4,6-trinitrophenol (2,4,6-TNP), which is an industrial pollutant, spectrophotometrically. The effect of surfactant and temperature on size of nanocatalysts was also studied. The smallest particle size and highest percentage of degradation were observed at critical micelle concentration of the surfactant. The direct optical band gap of the Al₂O₃·CaO nanocatalyst was found as 3.3 eV.

1. Introduction

Metal oxide nanoparticles play effective role in degradation of hazardous chemicals. Their highly intrinsic surface area and catalytic properties have made them destructive adsorbents. These metal oxides not only adsorb hazardous chemicals on their surface but also destroy them into smaller and less harmful by-products [1, 2]. They can destroy a wide range of such chemicals, for example, chlorobenzenes, organosulfurs, organophosphates, and nitroaromatics. These chemicals are present or used in synthesis of explosive materials, insecticides, pollutants, and chemical warfare agents [3–15]. Their increased consumption and improper disposal have become serious environmental risk. Some of them are penetrating into the ground water through soil, causing serious environmental and health problems [16].

Nitrophenols (NPs) are primarily concerned toxic pollutants by the United States Environmental Protection Agency (USEPA) [17], as these compounds have been found in industrial and agricultural wastes. These are anthropogenic, noxious, inhibitory, and biorefractory organic compounds and are considered as hazardous substances [18]. Among these, 2,4-dinitrophenol (2,4-DNP), 2,5-dinitrophenol (2,5-DNP), 2,6-trinitrophenol (2,6-DNP), and 2,4,6-TNP (2,4,6-TNP) are the most common and multipurpose industrial chemicals with wide-ranging applications as insecticides, dyes, drugs, and ordnance compounds [19–25]. Due to biorefractory properties of these pollutants, the biological techniques appear futile or take protracted incubation time on the degradation [26–28]. Thus, it is significantly important to develop new remediation methods for the decomposition of these organic pollutants.

Magnesium oxide nanoparticles were found as an effective adsorbent for the 2,4-dinitrotoluene (2,4-DNT) and 2,4,6-trinitrotoluene (2,4,6-TNT) [29]. Photocatalytic degradation of nitrophenols and nitroamines was also observed on titanium oxide [12, 30, 31], iron oxide [16], and gold loaded aluminium oxide [32]. Activity of calcium oxide nanoparticles was studied against the degradation of dimethyl methylphosphonate (DMMP) and it was found that these nanoparticles have the ability to degrade other warfare chemical agents [5, 33]. Degradation of such compounds was also observed when aluminium oxide nanoparticles were used [3, 6, 9, 32].

Surfactants play an important role in the preparation of metal oxide nanoparticles because of their influence on particle growth, coagulation, and flocculation. Under hydrothermal condition, smallest particle size was reported by using anionic surfactant (SDS) as compared to cationic surfactant (CTABr) and nonionic surfactant (PEG) [34, 35]. Several methods like anodization [36], wet oxidation [37], sol-gel [38], hydrothermal treatment [34], deposition precipitation [22, 32], and thermal vapor deposition [39] methods are being applied for the synthesis of nanoparticles.

In the current study, CaO and Al₂O₃·CaO nanocatalysts were synthesized using hydrothermal method by varying the concentration of sodium dodecyl sulphate (SDS), an anionic surfactant. The objective of this study is to assess the photodegradation of selected ordnance compound by CaO and Al₂O₃·CaO nanocatalysts. The ordnance compound of concern, 2,4,6-TNP (2,4,6-trinitrophenol or picric acid), was considered of priority for this study. The effects of temperature and surfactant were studied for the synthesis of nanocatalysts, and catalytic properties of nanocatalysts were assessed for degradation of 2,4,6-TNP.

2. Materials and Methods

2.1. Materials

Calcium chloride anhydrous (CaCl₂), sodium hydroxide (NaOH), and sodium dodecyl sulfate (SDS) were purchased from Merck while aluminium chloride (AlCl₃·6H₂O) and methanol (CH₃OH) were from Riedel-de Haën. For the catalytic reaction, 2,4,6-TNP was purchased from Riedel-de Haën. All chemicals were used as received, without any further purification.

2.2. Characterization

The CaO nanocatalysts obtained were subjected to thermogravimetric analysis (TGA) by using SDT Q600 TGA. Structural analysis of CaO and Al₂O₃·CaO nanocatalysts was done using Fourier Transform Infrared (FTIR)—MIDAC 2000 with KBr powder and powder X-ray diffractometer (XRD) using PANalytical MPD X’PERT PRO. The diffraction patterns were compared using the standard database from International Centre for Diffraction Data (ICDD). The morphology and particle size of nanocatalysts was determined by FEI quanta 200 F Field Emission Scanning Electron Microscope (FESEM) and Philips CM12, 80 kV, Transmission Electron Microscope (TEM). HPLC analysis was performed on Shimadzu model LC 20-AT instrument equipped with diode array detector (SPD-M20A, Shimadzu). Chromatographic separation was performed by using C-18 column ( mm, 5 μm packing) with isocratic solution. An injection volume of 20 μL was used for each sample. The peaks were observed at wavelength of 355 nm. GC-MS analyses were performed on Shimadzu model QP-2010 instrument.

2.3. Synthesis of CaO Nanocatalysts by Hydrothermal Method

CaO nanocatalysts were synthesized by changing the experimental parameters, that is, temperature and concentration of surfactant, to study their effect on particle size and catalytic activity. Synthesis method of CaO is depicted in Figure 1(a).

The mixture containing 0.15 M of CaCl₂ and 0.008 M sodium dodecyl sulfate (SDS) was magnetically stirred at ambient temperature. The precursor to surfactant molar ratio was taken as 1 M : 0.05 M. Sodium hydroxide (0.30 M) solution was added dropwise and the reaction solution was stirred for 30 minutes. After stirring, the reaction suspension was placed in a Teflon line autoclave (hydrothermal bomb) and kept in an oven for 4 h at the desired temperatures (250, 180, 160, and ).

After 4 h, the autoclave was removed from the oven and allowed to cool for 2 h at ambient temperature. The precipitates of Ca(OH)₂ were separated and washed 3 times with methanol and 2 times with deionized water to remove any reactant, ions, or surfactant and neutralize their pH by using centrifugation machine at the speed of 13000 rpm. The precipitates were dried and calcined at in a furnace with air flow for 3 h [40].

Similar process (Figure 1(a)) was adopted to study the effect of surfactant on CaO nanocatalysts. Only the molar concentration of SDS (0.004, 0.006, 0.008, 0.01, and 0.012 M) was varied to be close—and far from its critical micelle concentration (CMC) value which is 8.1 mM [41].

2.4. Preparation of Alumina Supported CaO Nanocatalysts by Deposition Precipitation Method

Synthesis of alumina doped CaO nanocatalysts was carried out by deposition precipitation method [32]. AlCl₃·6H₂O and CaO nanocatalysts were used as precursors. 15 mM solution of AlCl₃·6H₂O was prepared in 9 mL deionised water and 50 mg of CaO nanocatalysts was added at different time intervals to attain pH 12.3 (isoelectric point) [42]. Meanwhile, the reaction was constantly stirred on magnetic stirring plate. Teflon line autoclave was filled with reaction solution and kept in the oven for 4 h at the same temperature as that of CaO nanocatalysts precursor. Similarly, the precipitates were washed and calcined. The experimental setup is displayed in Figure 1(b).

3. Results and Discussion

3.1. Thermogravimetric Analyses

Figure 2 shows TGA/DSC profile of the Ca(OH)₂ synthesized with SDS at for 4 h via hydrothermal treatment. A significant weight loss (16.25%) is observed in the temperature range 375–450°C, which can be attributed to the thermal decomposition of Ca(OH)₂. The observed weight loss in the range is smaller than the theoretical value (24.3%) calculated on the assumption of total dehydration of Ca(OH)₂ to CaO [40].

The results indicate that a nearly complete conversion of Ca(OH)₂ to CaO took place below . This implies that the surfactant used in the fabrication of CaO nanocatalysts had been almost removed at around .

3.2. Fourier Transform Infrared Analyses

FTIR peaks (Figure 3) at 3427 cm⁻¹ and 3453 cm⁻¹ can be attributed to the stretching and bending vibrations of hydrogen-bonded surface OH groups (physisorbed water). It reveals that only a slight amount of water molecules is retained in the fabricated CaO and Al₂O₃·CaO samples. The appearance of strong IR absorption band at 424 cm⁻¹ may be attributed to the lattice vibrations of CaO [43]. The IR absorption bands at 1415 cm⁻¹ and 1439 cm⁻¹ are due to the symmetric stretching vibration of unidentate carbonate. Weak absorption band at 875 cm⁻¹ further demonstrates the presence of carbonate species. This is due to exposure of highly reactive surface area of CaO to air during calcination which resulted in the formation of considerable amount of CO₂ and H₂O, which are adsorbed on the surface of CaO in the form of free –OH and carbonate species. This indicates that surface –OH and lattice oxygen of CaO do provide oxygen which is more assessable on high surface area samples (Figure 3(a)) [44, 45]. In Figure 3(b), the peaks at 821 cm⁻¹, 722 cm⁻¹, and 569 cm⁻¹ are due to the stretching vibration of Al–O bond [46].

3.3. X-Ray Diffraction Analyses

The XRD pattern (Figure 4) of the CaO obtained with SDS heated at for 4 h after hydrothermal treatment shows that the nanocatalysts can be indexed to cubic CaO. Their lattice parameters agree well with the corresponding standard values given in JCPDS PDF# 82-1690 (CaO). The intense peaks at , , , , and correspond to the (111), (200), (202), (311), and (222) crystal planes, respectively. The average crystallite size (3.15 nm) was determined from the broadenings of corresponding peaks by using Scherrer’s equation: where is the mean crystallite size, is the grain shape dependent constant 0.89, is the wavelength of the incident beam in nm, is the Bragg reflection angle, and is the line broadening at half the maximum intensity in radians.

The 2 values of Al₂O₃·CaO nanocatalysts (Figure 5) were compared with the ICDD database to identify the phase purity and composition formed. Aluminium forms Ca₃Al₂O₆ phase (PDF# 00-006-0495,) with the calcium oxide nanoparticles at due to strong Al–O interaction [47, 48]. The essential peaks at , , , , , , , , , , , , and correspond to the lattice planes (302), (231), (400), (241), (440), (351), (602), (444), (362), (454), (464), (472), and (536), respectively. The average crystallite size of 3.64 nm for Ca₃Al₂O₆ was calculated by using (1). Uniform incorporation and distribution of aluminium into the CaO matrix may be responsible for the smaller crystallite size [49].

3.4. Optical Properties of Al₂O₃·CaO Nanocatalysts

Optical properties of Al₂O₃·CaO nanocatalysts were analyzed by UV-Vis absorption measurement at room temperature and using deionised water as blank. The sample was prepared by dispersing 3.6 mg of Al₂O₃·CaO nanocatalysts in 10 mL of deionised water and stirring by magnetic stirrer for 15 min. A homogeneous suspension solution was prepared and subjected for assessment for optical properties. Figure 6 describes typical absorption spectra of Al₂O₃·CaO nanocatalysts, which shows the shifting of absorption edges to the shorter wavelength (blue shift).

Equation (2) was used to calculate optical absorption coefficient from absorption data: where is the theoretical density of Al₂O₃·CaO (3.03 g cm⁻³), is the absorbance of Al₂O₃·CaO nanocatalyst solution, is the optical path length of quartz cell (1 cm), is the molar concentration of suspension solution, and is the molecular weight of Al₂O₃·CaO nanocatalysts.

Using Urbach’s equation (3), the density of the localized tail state ( eV) in the forbidden energy gap was determined by plotting versus as shown in Figure 7:

Here, a is constant and is the energy of photons.

The optical band gap for direct transition was determined by plotting versus using where is constant and nature of transition has been assumed to have values 1/2, 2, 3/2, and 3 for direct, indirect, forbidden direct, and forbidden indirect transitions, respectively [50, 51]. The direct optical band gap energy is determined by extrapolating the linear portion of the curve in Figure 8; the intersection of the extrapolation gives the value of 3.3 eV, which is much less than band gap energy of Al₂O₃ (7.2 eV) [52].

Proposed behavior of Al₂O₃·CaO nanocatalyst towards organic pollutant due to band gap energy is illustrated in Figure 9.

3.5. FESEM of CaO and Al₂O₃·CaO Nanocatalysts

Figures 10(a) and 10(b) provide the representative FESEM images of the CaO and Al₂O₃·CaO nanocatalysts fabricated with surfactant-assisted hydrothermal treatment at for 4 h and calcination at for 3 h. It was observed in Figure 10(a) that the CaO samples contain rounded coagulated nanocatalysts. After doping of alumina on CaO nanocatalysts, agglomerated particles of sample were observed in Figure 10(b).

(a)

(b)

3.6. TEM of CaO and Al₂O₃·CaO Nanocatalysts

Representative TEM image of the CaO and Al₂O₃·CaO nanocatalysts obtained after hydrothermal treatment is shown in Figure 11. The nanocatalysts exist in coagulated form with the particle size of 16 nm (Figure 11(a)). The particles size is decreased to 3.6 nm after the formation of Al₂O₃·CaO nanocatalysts (Figure 11(b)).

(a)

(b)

3.7. Catalytic Activity of CaO and Al₂O₃·CaO Nanocatalysts

A mixture of 5 mg of CaO nanocatalysts and 25 mL solution of 2,4,6-TNP (15 ppm) was placed under UV irradiation with constant stirring for 15 minutes at ambient temperature. On the basis of Beer-Lambert law, calibration was done for 2,4,6-TNP at a wavelength of maximum absorptivity, , 356 nm [53]. The catalytic activity was determined using UV Spectrophotometer (UV-1700 Shimadzu) by measuring the change in absorbance at 356 nm every 60-second interval. Same procedure was adopted to determine catalytic activity of Al₂O₃·CaO nanocatalysts against 2,4,6-TNP [54]. The analysis of samples showed a continuous decrease in absorption at nm, which was used to track the degradation of 2,4,6-TNP [55]. It is evident that reaction kinetics of both CaO (Figure 12(a)) and Al₂O₃·CaO (Figure 12(b)) nanocatalysts with 2,4,6-TNP follows first order. The first order rate constant values, , were determined from the slope of the graphs as shown in Figures 12(a) and 12(b).

(a)

(b)

3.8. Effect of Variation of Temperature on Catalytic Activity of CaO Nanocatalysts

Catalytic activity of CaO nanocatalysts synthesized by varying hydrothermal treatment temperature (140, 160, 180, and ) was studied while keeping other experimental parameters constant. It was observed that an increase in temperature (from to ) resulted in increases in rate constant, value (0.0732, 0.0791, and 0.1283 min⁻¹), but the catalytic activity decreases to 0.1124 min⁻¹ at . This change in the catalytic activity trend suggests that high hydrothermal temperature favors fast reaction which increases the particle size and decreases the surface area and contributes to destructive adsorbent ability.

3.9. Effect of Variation of Surfactant Concentration on Catalytic Activity of CaO and Al₂O₃·CaO Nanocatalysts

The synthesis of CaO nanocatalysts under basic conditions is believed to follow the X⁻I⁺S⁻ module, where S⁻ is the anionic surfactant, I⁺ is the inorganic precursor, and X⁻ is the counter ion [56]. A generalized mechanism of electrostatic interaction between inorganic precursor, surfactant and counter ions was proposed in Figure 13. When sodium hydroxide is added to the system, Na⁺ and OH⁻ ions are supposed to surround Ca²⁺–DS⁻. The electrostatic attraction between Ca²⁺ and DS⁻ is stronger than that between Na and SD⁻ ions; this behavior enhances the particle formation [57]. Na⁺ joins with Cl⁻ to make NaCl in the mixture system due to the electrostatic repulsion of Cl⁻ and DS⁻. The OH⁻ ions self-assembled around the micelle, so Ca²⁺ ions were attracted towards OH⁻ to form Ca(OH)₂ in the presence of surfactant (templating agent). In the final step of the process, the template was removed by calcination at for 3 h to generate pores.

The catalytic activity of CaO and Al₂O₃·CaO nanocatalysts (synthesized via hydrothermal treatment at and 4 h using different surfactant (SDS)) concentration is shown in Tables 1 and 2. It was observed that Al₂O₃·CaO nanocatalysts are more effective catalyst for the degradation of 2,4,6-TNP as compared to the CaO nanocatalysts. The rate constant values, , of different samples of CaO and Al₂O₃·CaO nanocatalyst at the same parameters were compared. Al₂O₃·CaO nanocatalysts have higher rate constant (0.1251 min⁻¹) than CaO nanocatalyst (0.1233 min⁻¹) at 0.004 M concentration of SDS.

It was observed that the highest values for both CaO and Al₂O₃·CaO were found at CMC of SDS in accordance to the small particle size of these nanocatalysts at this concentration. The value increases (particle size decreases) when the nanocatalysts were prepared by using surfactant from 0.004 to 0.008 M as the precursors are well dispersed in the surfactant template. However, further increase in surfactant concentration from 0.008 to 0.012 M decreases the values and increases the particle size due to formation of micelle which coagulates the particles. A parabola is formed showing the relationship between values and surfactant concentration as shown in Figure 14.

3.10. Degradation Mechanism of 2,4,6-TNP

Degradation of 2,4,6-TNP by nanocatalysts was observed by HPLC and GC-MS analysis. A 15 ppm solution of picric acid (0.15 mg) was freshly prepared in 100 mL deionized water and used as standard solution. Mixtures of each (5 mg) calcium oxide and Al₂O₃·CaO nanocatalysts were prepared in 25 mL solution of 2,4,6-TNP (15 ppm) and placed under UV irradiation with constant stirring for 15 minutes at ambient temperature. The sample solutions were filtered and then degassed by sonication before use.

Mobile phase was prepared for HPLC analyses by mixing 70% methanol with 0.1 M acetic acid buffer in the ratio of 97 : 3, v/v. The mobile phase was filtered and then degassed by sonication before use [58]. The data was analyzed by obtaining area under sample peaks at 355 nm. The observed retention time for standard 2,4,6-TNP solution was found 7.425 min as shown in Figure 15.

Each sample solution was injected separately in the HPLC and none of them showed any peak at the wavelength of 355 nm. These results lead to the conclusion that the picric acid was completely degraded by CaO and Al₂O₃·CaO nanocatalysts (Figure 16).

GC-MS technique was used to determine the intermediates generated during catalytic degradation of 2,4,6-TNP. Sample was prepared by suspending 5 mg Al₂O₃·CaO nanocatalysts in 25 mL solution of 2,4,6-TNP (15 ppm). Then, it was placed under UV irradiation with constant stirring for 15 minutes at ambient temperature. The sample solution was filtered before use.

A schematic diagram is proposed as given in Scheme 1 on the basis of GC-MS chromatogram (Figure 17).

(a)

(b)

(c)

4. Conclusion

CaO and Al₂O₃·CaO nanocatalysts were prepared by varying the temperature and surfactant (SDS) concentration above and below CMC value using hydrothermal and using deposition precipitation method. Catalytic activity of these nanocatalysts was measured against the degradation of 2,4,6-TNP, which proved that the nanocatalysts are effective catalysts. The highest rate constant value, , was observed in those samples which were prepared at CMC value of the anionic surfactant. Compared to CaO nanocatalysts, the Al₂O₃·CaO nanocatalysts have the highest catalytic activity (0.1577 min⁻¹). The band gap of the Al₂O₃·CaO nanocatalyst was calculated as 3.3 eV.

Acknowledgments

XRD facilities provided by the Physics Department of GC University Lahore are gratefully acknowledged. The authors are grateful to The World Academy of Sciences (TWAS) for financial support to purchase scientific equipments to carry out this project and Universiti Sains Malaysia is acknowledged to provide characterization of samples by TEM through Research University (RU) Grant no. 1001/PKIMIA/815099.

References

M. A. Henderson, T. Jin, and J. M. White, “The desorption and decomposition of trinitrotoluene adsorbed on metal oxide powders,” Applied Surface Science, vol. 27, no. 1, pp. 127–140, 1986.
View at: Google Scholar
K. J. Klabunde and R. Richards, Nanoscale Materials in Chemistry, John Wiley & Sons, 2009.
T. Z. Tzou and S. W. Weller, “Catalytic oxidation of dimethyl methylphosphonate,” Journal of Catalysis, vol. 146, no. 2, pp. 370–374, 1994.
View at: Publisher Site | Google Scholar
G. W. Wagner, P. W. Bartram, O. Koper, and K. J. Klabunde, “Reactions of VX, GD, and HD with nanosize MgO,” The Journal of Physical Chemistry B, vol. 103, no. 16, pp. 3225–3228, 1999.
View at: Google Scholar
G. W. Wagner, O. B. Koper, E. Lucas, S. Decker, and K. J. Klabunde, “Reactions of VX, GD, and HD with nanosize CaO: autocatalytic dehydrohalogenation of HD,” The Journal of Physical Chemistry B, vol. 104, no. 21, pp. 5118–5123, 2000.
View at: Google Scholar
G. W. Wagner, L. R. Procell, R. J. O'Connor et al., “Reactions of VX, GB, GD, and HD with nanosize AL₂O₃. Formation of aluminophosphonates,” Journal of the American Chemical Society, vol. 123, no. 8, pp. 1636–1644, 2001.
View at: Publisher Site | Google Scholar
S. M. Kanan, Z. Lu, and C. P. Tripp, “A comparative study of the adsorption of chloro- and non-chloro-containing organophosphorus compounds on WO₃,” The Journal of Physical Chemistry B, vol. 106, no. 37, pp. 9576–9580, 2002.
View at: Publisher Site | Google Scholar
X. Ma, M. Zheng, W. Liu, Y. Qian, B. Zhang, and W. Liu, “Dechlorination of hexachlorobenzene using ultrafine Ca–Fe composite oxides,” Journal of Hazardous Materials, vol. 127, no. 1–3, pp. 156–162, 2005.
View at: Publisher Site | Google Scholar
J. C. Chen and C. T. Tang, “Preparation and application of granular ZnO/Al₂O₃ catalyst for the removal of hazardous trichloroethylene,” Journal of Hazardous Materials, vol. 142, no. 1-2, pp. 88–96, 2007.
View at: Publisher Site | Google Scholar
W. O. Gordon, B. M. Tissue, and J. R. Morris, “Adsorption and decomposition of dimethyl methylphosphonate on Y₂O₃ nanoparticles,” The Journal of Physical Chemistry C, vol. 111, no. 8, pp. 3233–3240, 2007.
View at: Publisher Site | Google Scholar
O. B. Koper, S. Rajagopalan, S. Winecki, and K. J. Klabunde, “Nanoparticle metal oxides for chlorocarbon and organophosphonate remediation,” in Environmental Applications of Nanomaterials: Synthesis, Sorbents and Sensors, pp. 3–24, 2007.
View at: Google Scholar
D. Cropek, P. A. Kemme, O. V. Makarova, L. X. Chen, and T. Rajh, “Selective photocatalytic decomposition of nitrobenzene using surface modified TiO₂ nanoparticles,” The Journal of Physical Chemistry C, vol. 112, no. 22, pp. 8311–8318, 2008.
View at: Publisher Site | Google Scholar
G. W. Wagner, Q. Chen, and Y. Wu, “Reactions of VX, GD, and HD with nanotubular titania,” The Journal of Physical Chemistry C, vol. 112, no. 31, pp. 11901–11906, 2008.
View at: Publisher Site | Google Scholar
A. Saxena, H. Mangal, P. K. Rai, A. S. Rawat, V. Kumar, and M. Datta, “Adsorption of diethylchlorophosphate on metal oxide nanoparticles under static conditions,” Journal of Hazardous Materials, vol. 180, no. 1–3, pp. 566–576, 2010.
View at: Publisher Site | Google Scholar
L. A. Patil, A. R. Bari, M. D. Shinde, V. Deo, and M. P. Kaushik, “Detection of dimethyl methyl phosphonate—a simulant of sarin: the highly toxic chemical warfare—using platinum activated nanocrystalline ZnO thick films,” Sensors and Actuators B, vol. 161, no. 1, pp. 372–380, 2012.
View at: Publisher Site | Google Scholar
A. Halasz, C. Groom, E. Zhou et al., “Detection of explosives and their degradation products in soil environments,” Journal of Chromatography A, vol. 963, no. 1-2, pp. 411–418, 2002.
View at: Publisher Site | Google Scholar
USEPA, Health and Environmental Effects Profile for Nitrophenols, Environmental Protection Agency, Environmental Criteria and Assessment Office, Cincinnati, Ohio, USA, 1985.
R. Belloli, E. Bolzacchini, L. Clerici, B. Rindone, G. Sesana, and V. Librando, “Nitrophenols in air and rainwater,” Environmental Engineering Science, vol. 23, no. 2, pp. 405–415, 2006.
View at: Publisher Site | Google Scholar
M. Shimazu, A. Mulchandani, and W. Chen, “Simultaneous degradation of organophosphorus pesticides and p-nitrophenol by a genetically engineered Moraxella sp. with surface-expressed organophosphorus hydrolase,” Biotechnology and Bioengineering, vol. 76, no. 4, pp. 318–324, 2001.
View at: Publisher Site | Google Scholar
J. B. Lippincot, List of Worldwide Hazardous Chemical and Pollutants, The Forum for Scientific Excellence, New York, NY, USA, 1990.
M. S. Dieckmann and K. A. Gray, “A comparison of the degradation of 4-nitrophenol via direct and sensitized photocatalysis in TiO₂ slurries,” Water Research, vol. 30, no. 5, pp. 1169–1183, 1996.
View at: Publisher Site | Google Scholar
S. Ali, M. A. Farrukh, and M. Khaleeq-ur-Rahman, “Photodegradation of 2,4,6-trinitrophenol catalyzed by Zn/MgO nanoparticles prepared under aqueous-organic medium,” Korean Journal of Chemical Engineering, vol. 30, no. 11, 2013.
View at: Publisher Site | Google Scholar
A. Gutés, F. Céspedes, S. Alegret, and M. del Valle, “Determination of phenolic compounds by a polyphenol oxidase amperometric biosensor and artificial neural network analysis,” Biosensors and Bioelectronics, vol. 20, no. 8, pp. 1668–1673, 2005.
View at: Publisher Site | Google Scholar
K. Tanaka, K. Padermpole, and T. Hisanaga, “Photocatalytic degradation of commercial azo dyes,” Water Research, vol. 34, no. 1, pp. 327–333, 2000.
View at: Publisher Site | Google Scholar
K. W. Hofmann, H.-J. Knackmuss, and G. Heiss, “Nitrite elimination and hydrolytic ring cleavage in 2,4,6-trinitrophenol (picric acid) degradation,” Applied and Environmental Microbiology, vol. 70, no. 5, pp. 2854–2860, 2004.
View at: Publisher Site | Google Scholar
Z. Aleksieva, D. Ivanova, T. Godjevargova, and B. Atanasov, “Degradation of some phenol derivatives by Trichosporon cutaneum R57,” Process Biochemistry, vol. 37, no. 11, pp. 1215–1219, 2002.
View at: Publisher Site | Google Scholar
S. Yi, W.-Q. Zhuang, B. Wu, S. T.-L. Tay, and J.-H. Tay, “Biodegradation of p-nitrophenol by aerobic granules in a sequencing batch reactor,” Environmental Science and Technology, vol. 40, no. 7, pp. 2396–2401, 2006.
View at: Publisher Site | Google Scholar
M. C. Tomei, M. C. Annesini, R. Luberti, G. Cento, and A. Senia, “Kinetics of 4-nitrophenol biodegradation in a sequencing batch reactor,” Water Research, vol. 37, no. 16, pp. 3803–3814, 2003.
View at: Publisher Site | Google Scholar
V. M. Boddu, D. S. Viswanath, and S. W. Maloney, “Synthesis and characterization of coralline magnesium oxide nanoparticles,” Journal of the American Ceramic Society, vol. 91, no. 5, pp. 1718–1720, 2008.
View at: Publisher Site | Google Scholar
Y. Liu, H. Liu, J. Ma, and X. Wang, “Comparison of degradation mechanism of electrochemical oxidation of di- and tri-nitrophenols on Bi-doped lead dioxide electrodeeffect of the molecular structure,” Applied Catalysis B, vol. 91, no. 1-2, pp. 284–299, 2009.
View at: Publisher Site | Google Scholar
O. V. Makarova, T. Rajh, M. C. Thurnauer, A. Martin, P. A. Kemme, and D. Cropek, “Surface modification of TiO₂ nanoparticles for photochemical reduction of nitrobenzene,” Environmental Science and Technology, vol. 34, no. 22, pp. 4797–4803, 2000.
View at: Publisher Site | Google Scholar
H. Yazid, R. Adnan, and M. A. Farrukh, “Gold nanoparticles supported on titania for the reduction of p-nitrophenol,” Indian Journal of Chemistry A, vol. 52, no. 2, pp. 184–191, 2013.
View at: Google Scholar
Y. Paukku, A. Michalkova, and J. Leszczynski, “Adsorption of dimethyl methylphosphonate and trimethyl phosphate on calcium oxide: an ab initio study,” Structural Chemistry, vol. 19, no. 2, pp. 307–320, 2008.
View at: Publisher Site | Google Scholar
M. A. Farrukh, P. Tan, and R. Adnan, “Influence of reaction parameters on the synthesis of surfactant-assisted tin oxide nanoparticles,” Turkish Journal of Chemistry, vol. 36, no. 2, pp. 303–314, 2012.
View at: Publisher Site | Google Scholar
S. Gnanam and V. Rajendran, “Anionic, cationic and nonionic surfactants-assisted hydrothermal synthesis of tin oxide nanoparticles and their photoluminescence property,” Digest Journal of Nanomaterials and Biostructures, vol. 5, no. 3, pp. 623–628, 2010.
View at: Google Scholar
H.-S. Goh, R. Adnan, and M. A. Farrukh, “ZnO nanoflake arrays prepared via anodization and their performance in the photodegradation of methyl orange,” Turkish Journal of Chemistry, vol. 35, no. 3, pp. 375–391, 2011.
View at: Publisher Site | Google Scholar
K. M. A. Saron, M. R. Hashim, and M. A. Farrukh, “Stress control in ZnO films on GaN/Al₂O₃ via wet oxidation of Zn under various temperatures,” Applied Surface Science, vol. 258, no. 13, pp. 5200–5205, 2012.
View at: Publisher Site | Google Scholar
R. Adnan, N. A. Razana, I. A. Rahman, and M. A. Farrukh, “Synthesis and characterization of high surface area tin oxide nanoparticles via the sol-gel method as a catalyst for the hydrogenation of styrene,” Journal of the Chinese Chemical Society, vol. 57, no. 2, pp. 222–229, 2010.
View at: Google Scholar
K. M. A. Saron, M. R. Hashim, and M. A. Farrukh, “Growth of GaN films on silicon (111) by thermal vapor deposition method: optical functions and MSM UV photodetector applications,” Superlattices and Microstructures, vol. 64, pp. 88–97, 2013.
View at: Publisher Site | Google Scholar
C. Liu, L. Zhang, J. Deng, Q. Mu, H. Dai, and H. He, “Surfactant-aided hydrothermal synthesis and carbon dioxide adsorption behavior of three-dimensionally mesoporous calcium oxide single-crystallites with tri-, tetra-, and hexagonal morphologies,” The Journal of Physical Chemistry C, vol. 112, no. 49, pp. 19248–19256, 2008.
View at: Publisher Site | Google Scholar
H. B. de Aguiar, M. L. Strader, A. G. F. de Beer, and S. Roke, “Surface structure of sodium dodecyl sulfate surfactant and oil at the oil-in-water droplet liquid/liquid interface: a manifestation of a nonequilibrium surface state,” The Journal of Physical Chemistry B, vol. 115, no. 12, pp. 2970–2978, 2011.
View at: Publisher Site | Google Scholar
D. A. Sverjensky, “Zero-point-of-charge prediction from crystal chemistry and solvation theory,” Geochimica et Cosmochimica Acta, vol. 58, no. 14, pp. 3123–3129, 1994.
View at: Google Scholar
M. I. Zaki, H. Knözinger, B. Tesche, and G. A. H. Mekhemer, “Influence of phosphonation and phosphation on surface acid-base and morphological properties of CaO as investigated by in situ FTIR spectroscopy and electron microscopy,” Journal of Colloid and Interface Science, vol. 303, no. 1, pp. 9–17, 2006.
View at: Publisher Site | Google Scholar
O. B. Koper, I. Lagadic, A. Volodin, and K. J. Klabunde, “Alkaline-earth oxide nanoparticles obtained by aerogel methods. Characterization and rational for unexpectedly high surface chemical reactivities,” Chemistry of Materials, vol. 9, no. 11, pp. 2468–2480, 1997.
View at: Google Scholar
Y. X. Li, H. Li, and K. J. Klabunde, “Destructive adsorption of chlorinated benzenes on ultrafine (Nanoscale) particles of magnesium oxide and calcium oxide,” Environmental Science and Technology, vol. 28, no. 7, pp. 1248–1253, 1994.
View at: Google Scholar
J. Hemalatha, T. Prabhakaran, and R. P. Nalini, “A comparative study on particle-fluid interactions in micro and nanofluids of aluminium oxide,” Microfluidics and Nanofluidics, vol. 10, no. 2, pp. 263–270, 2011.
View at: Publisher Site | Google Scholar
B. Viswanath and N. Ravishankar, “Interfacial reactions in hydroxyapatite/alumina nanocomposites,” Scripta Materialia, vol. 55, no. 10, pp. 863–866, 2006.
View at: Publisher Site | Google Scholar
J. Yu, Q. Ge, W. Fang, and H. Xu, “Influences of calcination temperature on the efficiency of CaO promotion over CaO modified Pt/γ-Al₂O₃ catalyst,” Applied Catalysis A, vol. 395, no. 1-2, pp. 114–119, 2011.
View at: Publisher Site | Google Scholar
R. Koirala, G. K. Reddy, and P. G. Smirniotis, “Single nozzle flame-made highly durable metal doped Ca-based sorbents for CO₂ capture at high temperature,” Energy & Fuels, vol. 26, no. 5, pp. 3103–3109, 2012.
View at: Google Scholar
A. Gaber, A. Y. Abdel-Latief, M. A. Abdel-Rahim, and M. N. Abdel-Salam, “Thermally induced structural changes and optical properties of tin dioxide nanoparticles synthesized by a conventional precipitation method,” Materials Science in Semiconductor Processing, vol. 16, no. 6, pp. 1784–1790, 2013.
View at: Google Scholar
E. Filippo, D. Manno, A. R. de Bartolomeo, and A. Serra, “Single step synthesis of SnO₂–SiO₂ core-shell microcables,” Journal of Crystal Growth, vol. 330, no. 1, pp. 22–29, 2011.
View at: Publisher Site | Google Scholar
S. J. Mousavi, M. R. Abolhassani, S. M. Hosseini, and S. A. Sebt, “Comparison of electronic and optical properties of the and phases of alumina using density functional theory,” Chinese Journal of Physics, vol. 47, no. 6, pp. 862–873, 2009.
View at: Google Scholar
V. Pimienta, R. Etchenique, and T. Buhse, “On the origin of electrochemical oscillations in the picric acid/CTAB two-phase system,” The Journal of Physical Chemistry A, vol. 105, no. 44, pp. 10037–10044, 2001.
View at: Publisher Site | Google Scholar
M. Ksibi, A. Zemzemi, and R. Boukchina, “Photocatalytic degradability of substituted phenols over UV irradiated TiO₂,” Journal of Photochemistry and Photobiology A, vol. 159, no. 1, pp. 61–70, 2003.
View at: Publisher Site | Google Scholar
J. Li, H. Qiao, Y. Du et al., “Electrospinning synthesis and photocatalytic activity of mesoporous TiO₂ nanofibers,” The Scientific World Journal, vol. 2012, Article ID 154939, 7 pages, 2012.
View at: Publisher Site | Google Scholar
M. A. Farrukh, B.-T. Heng, and R. Adnan, “Surfactant-controlled aqueous synthesis of SnO₂ nanoparticles via the hydrothermal and conventional heating methods,” Turkish Journal of Chemistry, vol. 34, no. 4, pp. 537–550, 2010.
View at: Publisher Site | Google Scholar
H. Iyota and R. Krastev, “Miscibility of sodium chloride and sodium dodecyl sulfate in the adsorbed film and aggregate,” Colloid and Polymer Science, vol. 287, no. 4, pp. 425–433, 2009.
View at: Publisher Site | Google Scholar
NIOSH Manual of Analytical Methods, vol. 4, method no. S228, US Department of Health and Human Services, Public Health Services, 2nd edition, 1978.

Copyright

Copyright © 2013 Ayesha Imtiaz et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

3909

Downloads

1962

Citations

The Scientific World Journal

Micelle-Assisted Synthesis of Al2O3·CaO Nanocatalyst: Optical Properties and Their Applications in Photodegradation of 2,4,6-Trinitrophenol

Abstract

1. Introduction

2. Materials and Methods

2.1. Materials

2.2. Characterization

2.3. Synthesis of CaO Nanocatalysts by Hydrothermal Method

2.4. Preparation of Alumina Supported CaO Nanocatalysts by Deposition Precipitation Method

3. Results and Discussion

3.1. Thermogravimetric Analyses

3.2. Fourier Transform Infrared Analyses

3.3. X-Ray Diffraction Analyses

3.4. Optical Properties of Al2O3·CaO Nanocatalysts

3.5. FESEM of CaO and Al2O3·CaO Nanocatalysts

3.6. TEM of CaO and Al2O3·CaO Nanocatalysts

3.7. Catalytic Activity of CaO and Al2O3·CaO Nanocatalysts

3.8. Effect of Variation of Temperature on Catalytic Activity of CaO Nanocatalysts

3.9. Effect of Variation of Surfactant Concentration on Catalytic Activity of CaO and Al2O3·CaO Nanocatalysts

3.10. Degradation Mechanism of 2,4,6-TNP

4. Conclusion

Acknowledgments

References

Copyright

Micelle-Assisted Synthesis of Al₂O₃·CaO Nanocatalyst: Optical Properties and Their Applications in Photodegradation of 2,4,6-Trinitrophenol

3.4. Optical Properties of Al₂O₃·CaO Nanocatalysts

3.5. FESEM of CaO and Al₂O₃·CaO Nanocatalysts

3.6. TEM of CaO and Al₂O₃·CaO Nanocatalysts

3.7. Catalytic Activity of CaO and Al₂O₃·CaO Nanocatalysts

3.9. Effect of Variation of Surfactant Concentration on Catalytic Activity of CaO and Al₂O₃·CaO Nanocatalysts