Direct Synthesis and Morphological Characterization of Gold-Dendrimer Nanocomposites Prepared Using PAMAM Succinamic Acid Dendrimers: Preliminary Study of the Calcification Potential

<table>TEM and HR-TEM micrographs of (a)–(c): Au-G4-5; (d)–(f): Au-G4-2.5; (g)–(i): Au-G6-5; (j)–(l): Au-G6-2.5 nanocomposites after 48 hours. Specific size-distribution histograms were included. SAED results are representative for gold (fcc) polycrystalline structures.</table>

The Scientific World Journal

fig3

Figure 3

Figure 3: Direct Synthesis and Morphological Characterization of Gold-Dendrimer Nanocomposites Prepared Using PAMAM Succinamic Acid Dendrimers: Preliminary Study of the Calcification Potential 

Figure 3 | Direct Synthesis and Morphological Characterization of Gold-Dendrimer Nanocomposites Prepared Using PAMAM Succinamic Acid Dendrimers: Preliminary Study of the Calcification Potential 