The Modification of Polyurethane Foams Using New Boroorganic Polyols (II) Polyurethane Foams from Boron-Modified Hydroxypropyl Urea Derivatives
Table 7
Foams weight loss following the 30-day annealing.
| Foam type |
Foam weight loss (wt%) following the annealing in a given temperature (°C) | 150 | 175 |
| FA1 | 6.52 ± 0.01 | 23.61 ± 0.91 | FA2 | 7.54 ± 0.23 | 23.86 ± 0.01 | FA3 | 15.42 ± 0.67 | 41.03 ± 0.58 | FB1 | 3.68 ± 0.48 | 16.00 ± 0.11 | FB2 | 7.32 ± 0.51 | 21.95 ± 0.91 | FB3 | 9.65 ± 0.75 | 25.85 ± 1.30 | FC1 | 21.57 ± 0.13 | 29.47 ± 0.06 | FC2 | 24.74 ± 0.02 | 26.75 ± 0.04 | FC3 | 37.48 ± 0.35 | 41.06 ± 1.02 |
|
|