The Modification of Polyurethane Foams Using New Boroorganic Polyols (II) Polyurethane Foams from Boron-Modified Hydroxypropyl Urea Derivatives
Table 8
Compressive strength of the obtained polyurethane foams.
| Foam type | Compressive strength (MPa) |
Compressive strength after annealing at 150°C | (MPa) | Growth (%) |
| FA1 | 0.10 ± 0.004 | 0.34 ± 0.014 | 340 | FA2 | 0.22 ± 0.007 | 0.36 ± 0.012 | 164 | FA3 | 0.18 ± 0.007 | — | — | FB1 | 0.54 ± 0.022 | 0.92 ± 0.016 | 70 | FB2 | 0.31 ± 0.019 | 0.41 ± 0.013 | 132 | FB3 | 0.28 ± 0.012 | 0.32 ± 0.007 | 114 | FC1 | 0.04 ± 0.002 | — | — | FC2 | 0.04 ± 0.002 | — | — | FC3 | 0.02 ± 0.001 | — | — |
|
|